CN104312312A - Reflexive mouldproof paint - Google Patents
Reflexive mouldproof paint Download PDFInfo
- Publication number
- CN104312312A CN104312312A CN201410661693.9A CN201410661693A CN104312312A CN 104312312 A CN104312312 A CN 104312312A CN 201410661693 A CN201410661693 A CN 201410661693A CN 104312312 A CN104312312 A CN 104312312A
- Authority
- CN
- China
- Prior art keywords
- mouldproof
- paint
- mixture
- sanitas
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses reflective mouldproof paint which is prepared by, by weight, 4%-6% of magnesium carbide, 25%-35% of fluorocarbon emulsion, 5%-12% of nanometer hollow glass fiber, 12%-15% of titanium dioxide, 0.7%-1.0% of dispersing agents, 0.5%-0.9% of antifoaming agents, 0.5%-1.0% of antiseptic, 20%-30% of mixture formed by mixing protective mouldproof capsule spore and rubber powder according to the weight ratio of 3:1 and 21%-32% of deionized water. The paint is good in heat-insulating performance and mouldproof performance.
Description
Technical field
The present invention relates to reflectivity mould-repellant coating.
Background technology
In each field, widely, as on exterior wall, industrial warehouse, chemical industry, oil, food service industry class basin and pipe surface, the buildingss such as factory building, modernization plant, freezer, house owed by a citizen, office building are first-class in the application of coating.
Tradition is all the coating for organic solvent, the contaminative of this coating is serious, therefore, now everybody big area bring into use water-borne coatings, and for exterior coating, need the wherein important technological problems solved to be heat insulation and mildew-resistant, but its heat insulation and fungicidal properties of existing water-borne coatings is all not good enough.
Summary of the invention
In order to improve heat insulating reflecting performance and mildew resistance, the invention provides a kind of reflectivity mould-repellant coating.
For achieving the above object, a kind of reflectivity mould-repellant coating, according to weight percent meter, is prepared from by following raw material;
Magnesium carbide 4%-6%
Fluorine carbon emulsion 25%-35%
Nano-hollow glass fibre 5%-12%
Titanium dioxide 12%-15%
Dispersion agent 0.7%-1.0%
Defoamer 0.5%-0.9%
Sanitas 0.5%-1.0%
Weight ratio is the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder
20%-30%
Deionized water 21%-32%.
Further, described defoamer is selected from a kind of in SP-202, XP-1273 or their mixture, and described sanitas is nitrite.
The invention has the beneficial effects as follows: owing to adding magnesium carbide, nano-hollow glass fibre and titanium dioxide, therefore, infrared reflectance can reach more than 90%, and heat insulation rate to 98%, thus can improve effect of heat insulation.The release actives of the protection type mildew-resistant capsule sporozoite energy continuous and effective in the present invention, itself and rubber powder effect, reach permanently effective mildew-proof function, can also improve the elasticity of paint film.
Embodiment
Below in conjunction with specific embodiment, the present invention is further elaborated.
Reflectivity mould-repellant coating according to weight percent meter, by 4%-6% magnesium carbide, 25%-35% fluorine carbon emulsion, 5%-12% nano-hollow glass fibre, 12%-15% titanium dioxide, 0.7%-1.0% dispersion agent, 0.5%-0.9% defoamer, 0.5%-1.0% sanitas, 20%-30% weight ratio be the mixture of the protection type mildew-resistant capsule sporozoite of 3:1 and rubber powder, 21%-32% deionized water is prepared from.Wherein, described defoamer is selected from a kind of in SP-202, XP-1273 or their mixture, and described sanitas is nitrite.
Embodiment 1.
Magnesium carbide 5.3%
Fluorine carbon emulsion 35%
Nano-hollow glass fibre 5%
Titanium dioxide 12%
Dispersion agent 0.7%
Defoamer 0.5%
Sanitas 0.5%
Weight ratio is the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder
20%
Deionized water 21%.
Embodiment 2.
Magnesium carbide 4%
Fluorine carbon emulsion 25%
Nano-hollow glass fibre 12%
Titanium dioxide 15%
Dispersion agent 1%
Defoamer 0.9%
Sanitas 1%
Weight ratio is the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder
20.1%
Deionized water 21%.
Embodiment 3.
Magnesium carbide 6%
Fluorine carbon emulsion 26%
Nano-hollow glass fibre 6%
Titanium dioxide 14%
Dispersion agent 0.8%
Defoamer 0.7%
Sanitas 0.6%
Weight ratio is the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder
24.9%
Deionized water 21%.
Embodiment 4.
Magnesium carbide 4%
Fluorine carbon emulsion 25%
Nano-hollow glass fibre 5%
Titanium dioxide 12%
Dispersion agent 0.7%
Defoamer 0.5%
Sanitas 0.5%
Weight ratio is the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder
20.3%
Deionized water 32%.
Embodiment 5.
Magnesium carbide 4%
Fluorine carbon emulsion 25%
Nano-hollow glass fibre 5%
Titanium dioxide 12%
Dispersion agent 0.7%
Defoamer 0.5%
Sanitas 0.5%
Weight ratio is the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder
30%
Deionized water 22.3%.
The preparation method of reflectivity mould-repellant coating is: in agitator, first add deionized water and dispersion agent, defoamer, sanitas; add magnesium carbide, fluorine carbon emulsion, nano-hollow glass fibre, titanium dioxide in the process slowly stirred after; with the high-speed stirring of 1500 revs/min dispersion 15-25 minute; again with the stirring at low speed of 500 revs/min; be that the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder slowly add dispersion 20-30 minute by weight ratio, make product of the present invention.
In the present invention, owing to adding magnesium carbide, nano-hollow glass fibre and titanium dioxide, therefore, infrared reflectance can reach more than 90%, and heat insulation rate to 98%, thus can improve effect of heat insulation.The release actives of the protection type mildew-resistant capsule sporozoite energy continuous and effective in the present invention, itself and rubber powder effect, reach permanently effective mildew-proof function, can also improve the elasticity of paint film.
Claims (2)
1. a reflectivity mould-repellant coating, is characterized in that, according to weight percent meter, is prepared from by following raw material;
Magnesium carbide 4%-6%
Fluorine carbon emulsion 25%-35%
Nano-hollow glass fibre 5%-12%
Titanium dioxide 12%-15%
Dispersion agent 0.7%-1.0%
Defoamer 0.5%-0.9%
Sanitas 0.5%-1.0%
Weight ratio is the protection type mildew-resistant capsule sporozoite of 3:1 and the mixture of rubber powder
20%-30%
Deionized water 21%-32%.
2. reflectivity mould-repellant coating according to claim 1, is characterized in that: described defoamer is selected from a kind of in SP-202, XP-1273 or their mixture, and described sanitas is nitrite.