CN104513560A - Fireproof paint - Google Patents
Fireproof paint Download PDFInfo
- Publication number
- CN104513560A CN104513560A CN201510018260.6A CN201510018260A CN104513560A CN 104513560 A CN104513560 A CN 104513560A CN 201510018260 A CN201510018260 A CN 201510018260A CN 104513560 A CN104513560 A CN 104513560A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- water
- retardant coating
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof paint. The fireproof paint is prepared from the following raw materials in parts by weight: 100 parts of an acrylate elastic emulsion, 2-10 parts of nanometer silicon oxide, 8-15 parts of ethanediol, 10-20 parts of silicate glass, 1-5 parts of a titanate coupling agent, 2-11 parts of an antifoaming agent, 1-10 parts of 12-carbon alcohol ester, 2-12 parts of a fire retardant, 5-15 parts of ground calcium carbonate, 1-3 parts of titanium dioxide, 1-10 parts of antimony trioxide and 5-15 parts of water. In the using process of the paint, inorganic solvents are volatilized, and the inorganic solvents do not contain carcinogenic compounds, so that the paint is free from toxicity and is environment-friendly; the paint has the characteristics of good fireproof and antiseptic properties, strong adhesive force and good weather resistance, and is suitable for being coated on the surface of a cable to be used for fire resistance and protection.
Description
Technical field
The present invention relates to a kind of material of construction, be specifically related to a kind of frie retardant coating.
Background technology
Frie retardant coating is for flammable substrates surface, can reduce by the rapid spread of the combustibility of painting material surface, retardance fire, in order to improve by a kind of speciality coating being coated with material fire endurance.Frie retardant coating is coated in substrate surface, except having fire retardation, also has antirust, waterproof, anticorrosion, wear-resisting, heat-resisting and coating tenacity, tint permanence, adhesion, the easily performance such as dryness and certain gloss.Generally be applied in the fields such as iron structure, concrete structure, timber decorations layer, as steel-structure factory building, concrete tunnel or the cable etc. fire prevention being had to requirement.
Cable is normally by the cable of the similar rope of several or several groups wire strandings, and often organize mutually insulated between wire, and be often twisted into round a center, whole outside is surrounded by the tectum of high-insulation.Multi rack is located at aerial or is contained in underground, the bottom, for telecommunication or power transmission.For playing protection preservative activity further, cable generally can at its surface-coated one deck frie retardant coating before erection.As the application number Chinese patent that is 200610053130.7 discloses a kind of manufacture method of fire retardant coating of aquosity cable, it is made up of by weight percentage following composition of raw materials: water 44.2% ~ 29.9%, emulsifier op-10 0.6% ~ 0.9%, dioctyl ester 1% ~ 2%, 52 degree of clorafins 6% ~ 8%, ammonium polyphosphate 17% ~ 19%, melamine 8% ~ 10%, dipentaerythritol 8% ~ 10%, Rutile type Titanium Dioxide 2.5% ~ 3.5%, wollastonite powder 1% ~ 2%, acrylic ester elastic emulsions 12% ~ 15%.The defect of this kind of cable fire-refractory coating is: containing clorafin and melamine in component, release poisonous halogen gas and carcinogenic substance during burning, the related request of discontented toe ring guarantor and health.
Summary of the invention
For above-mentioned deficiency, technical problem to be solved by this invention is to provide the frie retardant coating being applied to cable surface, the in use inorganic solvent volatilization of this kind of coating, asepsis environment-protecting, has that fire prevention, antiseptic property are good, strong adhesion, the feature of good weatherability.
For solving the problem, the present invention is achieved through the following technical solutions:
Frie retardant coating, is made up of the raw material of following weight part: acrylic ester elastic emulsion 100 parts, nano silicon oxide 2 ~ 10 parts, ethylene glycol 8 ~ 15 parts, silicate glass 10 ~ 20 parts, titanate coupling agent 1 ~ 5 part, defoamer 2 ~ 11 parts, Lauryl Alcohol ester 1 ~ 10 part, fire retardant 2 ~ 12 parts, water-ground limestone 5 ~ 15 parts, titanium dioxide 1 ~ 3 part, antimonous oxide 1 ~ 10 part, 5 ~ 15 parts, water.
Above-mentioned frie retardant coating, further preferably, be made up of the raw material of following weight part: acrylic ester elastic emulsion 100 parts, nano silicon oxide 7 parts, ethylene glycol 12 parts, silicate glass 15 parts, titanate coupling agent 2 parts, defoamer 8 parts, Lauryl Alcohol ester 7 parts, fire retardant 10 parts, water-ground limestone 11 parts, titanium dioxide 2 parts, antimonous oxide 5 parts, 11 parts, water.
In such scheme, described fire retardant can be mixed by identical weight proportioning by ammonium polyphosphate, magnesium hydroxide, zinc borate, hydrotalcite and primary ammonium phosphate.
Preparation method and the auxiliary materials technique routinely of frie retardant coating of the present invention are carried out.
Beneficial effect of the present invention is:
Frie retardant coating of the present invention is applicable to the coating fire resistance applications of cable surface, the in use inorganic solvent volatilization of this kind of coating, and not containing carcinogenic compound, asepsis environment-protecting, has that fire prevention, antiseptic property are good, strong adhesion, the feature of good weatherability.
Embodiment
Below in conjunction with specific embodiment, the present invention is further explained, but is not limited to these embodiments.
Embodiment 1
Frie retardant coating, be made up of the raw material of following weight part: acrylic ester elastic emulsion 100 parts, nano silicon oxide 10 parts, ethylene glycol 8 parts, silicate glass 20 parts, titanate coupling agent 5 parts, defoamer 11 parts, Lauryl Alcohol ester 1 part, fire retardant 12 parts, water-ground limestone 5 parts, titanium dioxide 3 parts, antimonous oxide 1 part, 15 parts, water, wherein said fire retardant is mixed by identical weight proportioning by ammonium polyphosphate, magnesium hydroxide, zinc borate, hydrotalcite and primary ammonium phosphate.
The preparation method of above-mentioned frie retardant coating can be: take described raw material by weight, puts into stirrer and fully stirs, grind after 40 minutes, leave standstill 30 minutes in 20 DEG C of constant temperature.
Embodiment 2
Frie retardant coating, be made up of the raw material of following weight part: acrylic ester elastic emulsion 100 parts, nano silicon oxide 2 parts, ethylene glycol 15 parts, silicate glass 10 parts, titanate coupling agent 1 part, defoamer 2 parts, Lauryl Alcohol ester 10 parts, fire retardant 2 parts, water-ground limestone 15 parts, titanium dioxide 1 part, antimonous oxide 10 parts, 5 parts, water, described fire retardant is mixed by identical weight proportioning by ammonium polyphosphate, magnesium hydroxide, zinc borate, hydrotalcite and primary ammonium phosphate.
The preparation method of above-mentioned frie retardant coating can be: by weight first by water, acrylic ester elastic emulsion, titanate coupling agent, Lauryl Alcohol ester and defoamer add in pill tank, under 500 revs/min of speed, stirring 5 minutes is carried out by dispersator, then stirring velocity is increased to 800 revs/min, nano silicon oxide is added again by described weight part, ethylene glycol, silicate glass, fire retardant, water-ground limestone, titanium dioxide, antimonous oxide, continue stirring 7 minutes, until become the uniform sizing material of sticky shape, again this slurry is delivered on three-roller and grind 2 times, each 10 minutes, finally add the tackiness agent of slurry 0.01%, uniform stirring 10 minutes, get product.
Embodiment 3
Frie retardant coating, be made up of the raw material of following weight part: acrylic ester elastic emulsion 100 parts, nano silicon oxide 7 parts, ethylene glycol 12 parts, silicate glass 15 parts, titanate coupling agent 2 parts, defoamer 8 parts, Lauryl Alcohol ester 7 parts, fire retardant 10 parts, water-ground limestone 11 parts, titanium dioxide 2 parts, antimonous oxide 5 parts, 11 parts, water, wherein said fire retardant is mixed by identical weight proportioning by ammonium polyphosphate, magnesium hydroxide, zinc borate, hydrotalcite and primary ammonium phosphate.
The preparation method of above-mentioned frie retardant coating and the identical of embodiment 2.
When frie retardant coating of the present invention is coated on cable surface, its technical feature is shown in as following table 1:
Can find out from upper table, frie retardant coating of the present invention is fire-retardant, the performance such as acid and alkali-resistance and slip-off preventing all reaches requirement, easy to use, be worthy to be popularized.
Claims (3)
1. frie retardant coating, it is characterized in that, be made up of the raw material of following weight part: acrylic ester elastic emulsion 100 parts, nano silicon oxide 2 ~ 10 parts, ethylene glycol 8 ~ 15 parts, silicate glass 10 ~ 20 parts, titanate coupling agent 1 ~ 5 part, defoamer 2 ~ 11 parts, Lauryl Alcohol ester 1 ~ 10 part, fire retardant 2 ~ 12 parts, water-ground limestone 5 ~ 15 parts, titanium dioxide 1 ~ 3 part, antimonous oxide 1 ~ 10 part, 5 ~ 15 parts, water.
2. frie retardant coating according to claim 1, is characterized in that being made up of the raw material of following weight part: acrylic ester elastic emulsion 100 parts, nano silicon oxide 7 parts, ethylene glycol 12 parts, silicate glass 15 parts, titanate coupling agent 2 parts, defoamer 8 parts, Lauryl Alcohol ester 7 parts, fire retardant 10 parts, water-ground limestone 11 parts, titanium dioxide 2 parts, antimonous oxide 5 parts, 11 parts, water.
3. frie retardant coating according to claim 1 and 2, is characterized in that: described fire retardant is mixed by identical weight proportioning by ammonium polyphosphate, magnesium hydroxide, zinc borate, hydrotalcite and primary ammonium phosphate.