CN104293211A - Quick-drying waterproof surface adhesive - Google Patents
Quick-drying waterproof surface adhesive Download PDFInfo
- Publication number
- CN104293211A CN104293211A CN201410552516.7A CN201410552516A CN104293211A CN 104293211 A CN104293211 A CN 104293211A CN 201410552516 A CN201410552516 A CN 201410552516A CN 104293211 A CN104293211 A CN 104293211A
- Authority
- CN
- China
- Prior art keywords
- parts
- glue
- vinyl
- fatty acid
- rapid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a quick-drying waterproof surface adhesive which comprises the following components in parts by weight: 300 parts of deionized water, 8-9 parts of ethyl acrylate, 150 parts of vinyl acetate, 1-2 parts of hydroxypropyl methylcellulose, 8-9 parts of coco fatty acid diethanol amide, 1-2 parts of sodium formaldehyde sulfoxylate, 1-2 parts of ammonium persulfate, 2-3 parts of sodium polyacrylate, 1-2 parts of iso-tridecanol polyoxyethylene ether, 3-4 parts of vinyl trimethoxy silane, 2-3 parts of hydroxymethyl cellulose and 1-2 parts of locust bean gum etherate. The quick-drying waterproof surface adhesive disclosed by the invention has the advantages of good water-resistant property, fast drying, high adhesion strength and good weather resistance.
Description
Technical field
The present invention relates to rapid-curing cutback waterproof overlay glue.
Background technology
Existing overlay glue, bonding strength is inadequate, water resistance is poor, rate of drying is slow, and environmental protection does not reach standard.
Summary of the invention
The object of the present invention is to provide a kind of rapid-curing cutback waterproof overlay glue, its water resistance is good, and rate of drying is fast, and bonding strength is high, and good weatherability.
For achieving the above object, technical scheme of the present invention is a kind of rapid-curing cutback waterproof overlay glue of design, consists of the following composition by weight:
300 parts of deionized waters,
8 ~ 9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1 ~ 2 part of Vltra tears,
8 ~ 9 parts of cocoanut fatty acid diethanolamides,
1 ~ 2 part of rongalite,
1 ~ 2 part of ammonium persulphate,
2 ~ 3 parts of sodium polyacrylates,
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether,
3 ~ 4 parts of vinyltrimethoxy silanes,
2 ~ 3 parts of Walocel MT 20.000PVs,
1 ~ 2 part of locust tree glue etherate.
Preferably, rapid-curing cutback waterproof overlay glue, consists of the following composition by weight:
300 parts of deionized waters,
8.9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1.2 parts of Vltra tearss,
8.9 parts of cocoanut fatty acid diethanolamides,
1.2 parts of rongalites,
1.2 parts of ammonium persulphates,
2.3 parts of sodium polyacrylates,
1.2 parts of isomerous tridecanol polyoxyethylene ethers,
3.4 parts of vinyltrimethoxy silanes,
2.3 parts of Walocel MT 20.000PVs,
1.2 parts of locust tree glue etherates.
Preferably, rapid-curing cutback waterproof overlay glue, consists of the following composition by weight:
300 parts of deionized waters,
8 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1 part of Vltra tears,
8 parts of cocoanut fatty acid diethanolamides,
1 part of rongalite,
1 part of ammonium persulphate,
2 parts of sodium polyacrylates,
1 part of isomerous tridecanol polyoxyethylene ether,
3 parts of vinyltrimethoxy silanes,
2 parts of Walocel MT 20.000PVs,
1 part of locust tree glue etherate.
Preferably, rapid-curing cutback waterproof overlay glue, consists of the following composition by weight:
300 parts of deionized waters,
9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
2 parts of Vltra tearss,
9 parts of cocoanut fatty acid diethanolamides,
2 parts of rongalites,
2 parts of ammonium persulphates,
3 parts of sodium polyacrylates,
2 parts of isomerous tridecanol polyoxyethylene ethers,
4 parts of vinyltrimethoxy silanes,
3 parts of Walocel MT 20.000PVs,
2 parts of locust tree glue etherates.
Advantage of the present invention and beneficial effect are: provide a kind of rapid-curing cutback waterproof overlay glue, its water resistance is good, and rate of drying is fast, and bonding strength is high, and good weatherability.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Rapid-curing cutback waterproof overlay glue, consists of the following composition by weight:
300 parts of deionized waters,
8.9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1.2 parts of Vltra tearss,
8.9 parts of cocoanut fatty acid diethanolamides,
1.2 parts of rongalites,
1.2 parts of ammonium persulphates,
2.3 parts of sodium polyacrylates,
1.2 parts of isomerous tridecanol polyoxyethylene ethers,
3.4 parts of vinyltrimethoxy silanes,
2.3 parts of Walocel MT 20.000PVs,
1.2 parts of locust tree glue etherates.
Embodiment 2
Rapid-curing cutback waterproof overlay glue, consists of the following composition by weight:
300 parts of deionized waters,
8 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1 part of Vltra tears,
8 parts of cocoanut fatty acid diethanolamides,
1 part of rongalite,
1 part of ammonium persulphate,
2 parts of sodium polyacrylates,
1 part of isomerous tridecanol polyoxyethylene ether,
3 parts of vinyltrimethoxy silanes,
2 parts of Walocel MT 20.000PVs,
1 part of locust tree glue etherate.
Embodiment 3
Rapid-curing cutback waterproof overlay glue, consists of the following composition by weight:
300 parts of deionized waters,
9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
2 parts of Vltra tearss,
9 parts of cocoanut fatty acid diethanolamides,
2 parts of rongalites,
2 parts of ammonium persulphates,
3 parts of sodium polyacrylates,
2 parts of isomerous tridecanol polyoxyethylene ethers,
4 parts of vinyltrimethoxy silanes,
3 parts of Walocel MT 20.000PVs,
2 parts of locust tree glue etherates.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. rapid-curing cutback waterproof overlay glue, is characterized in that, consists of the following composition by weight:
300 parts of deionized waters,
8 ~ 9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1 ~ 2 part of Vltra tears,
8 ~ 9 parts of cocoanut fatty acid diethanolamides,
1 ~ 2 part of rongalite,
1 ~ 2 part of ammonium persulphate,
2 ~ 3 parts of sodium polyacrylates,
1 ~ 2 part of isomerous tridecanol polyoxyethylene ether,
3 ~ 4 parts of vinyltrimethoxy silanes,
2 ~ 3 parts of Walocel MT 20.000PVs,
1 ~ 2 part of locust tree glue etherate.
2. rapid-curing cutback waterproof overlay glue according to claim 1, is characterized in that, consist of the following composition by weight:
300 parts of deionized waters,
8.9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1.2 parts of Vltra tearss,
8.9 parts of cocoanut fatty acid diethanolamides,
1.2 parts of rongalites,
1.2 parts of ammonium persulphates,
2.3 parts of sodium polyacrylates,
1.2 parts of isomerous tridecanol polyoxyethylene ethers,
3.4 parts of vinyltrimethoxy silanes,
2.3 parts of Walocel MT 20.000PVs,
1.2 parts of locust tree glue etherates.
3. rapid-curing cutback waterproof overlay glue according to claim 1, is characterized in that, consist of the following composition by weight:
300 parts of deionized waters,
8 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
1 part of Vltra tears,
8 parts of cocoanut fatty acid diethanolamides,
1 part of rongalite,
1 part of ammonium persulphate,
2 parts of sodium polyacrylates,
1 part of isomerous tridecanol polyoxyethylene ether,
3 parts of vinyltrimethoxy silanes,
2 parts of Walocel MT 20.000PVs,
1 part of locust tree glue etherate.
4. rapid-curing cutback waterproof overlay glue according to claim 1, is characterized in that, consist of the following composition by weight:
300 parts of deionized waters,
9 parts of ethyl propenoates,
150 parts of vinyl-acetic esters,
2 parts of Vltra tearss,
9 parts of cocoanut fatty acid diethanolamides,
2 parts of rongalites,
2 parts of ammonium persulphates,
3 parts of sodium polyacrylates,
2 parts of isomerous tridecanol polyoxyethylene ethers,
4 parts of vinyltrimethoxy silanes,
3 parts of Walocel MT 20.000PVs,
2 parts of locust tree glue etherates.