CN104293163A - Spray paint for outside surfaces of motors and preparation method thereof - Google Patents
Spray paint for outside surfaces of motors and preparation method thereof Download PDFInfo
- Publication number
- CN104293163A CN104293163A CN201410502683.0A CN201410502683A CN104293163A CN 104293163 A CN104293163 A CN 104293163A CN 201410502683 A CN201410502683 A CN 201410502683A CN 104293163 A CN104293163 A CN 104293163A
- Authority
- CN
- China
- Prior art keywords
- parts
- spraying paint
- trimethylolpropane
- mixing
- dioxan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a spray paint for the outside surfaces of motors and a preparation method thereof. The paint comprises the following raw materials in parts by mass: 15-27 parts of linseed oil, 15-25 parts of trimethylolpropane, 15-27 parts of methyl diisocyanate, 2-5.5 parts of sorbic acid, 2-5.5 parts of phthalic anhydride, 0.7-2.5 parts of dioxin, 0.01-0.03 part of ethyl cellosolve, 2-5 parts of aluminum silver paste, 2-4 parts of oxalic acid, 2-4.5 parts of benzoyl peroxide, 3-6 parts of cobalt naphthenate, 0.5-1 part of sodium peroxide, and 6-15 parts of chlorinated rubber. The paint provided by the invention has the properties of excellent adhesion, impact resistance, water resistance, corrosion resistance, difficult sagging, and the like, and has a good protection effect on the surfaces of the motors, thereby prolonging the service lives of the motors.
Description
Technical field
The present invention relates to a kind of coating, particularly relate to a kind of outer surface of motor spraying paint and preparation method thereof.
Background technology
Motor refers to a kind of calutron realizing electric energy conversion according to the law of electromagnetic induction or transmit.Represent with alphabetical M in circuit.Its Main Function produces driving torque, as the propulsion source of electrical appliance or various machinery.Generator represents with alphabetical G in circuit.Its Main Function utilizes changes mechanical energy for electric energy, and the most frequently used is utilize the pushing generator rotors such as heat energy, water energy to generate electricity at present.
Motor application is in the industry a lot, but the metal on motor surface gets rusty easily, be corroded or by the infringement of other factors extraneous.Therefore, the anti-infringement work carrying out motor surface is very important.The most frequently used is at motor surface coating paint at present, is used for protecting motor.
Coating in the market for motor surface has a lot, but its ubiquity poor adhesive force, and the attachment time is short, easy sagging, the shortcomings such as poor water resistance.Such as Chinese invention patent (patent No. 201210327498.3, the applying date 2012/09/07) discloses a kind of electromechanics protective system, and this anticorrosion with coat performance is good, there is very long anti-corrosion life, have very strong sticking power and ecological, environmental protective, but its water resistance is poor, hardness is low, poor adhesive force; Chinese invention patent (patent No. 201010218394.X, the applying date 2010/07/06) disclose high-solid-content wear-resistant paint for wind power generators and preparation method thereof and application, the paint film of this coating has excellent fast light, weathering resistance, outdoor insolation weather resistance is strong, there are chemical pickup and the corrosive natures such as good acid-and base-resisting, salt, grease, washing composition, hardness is higher, there is stronger wear resisting property, gloss of film degree is high, and fullness ratio is high, good leveling property, sticking power is good, impact resistance is good, but its water resistance is poor, and adhesion strength is low.
Summary of the invention
the technical problem solved:for the shortcoming that existing motor surface coating exists, the invention provides a kind of outer surface of motor spraying paint and preparation method thereof, this paint hardness is high, strong adhesion, water-tolerant, Corrosion Protection are strong.
technical scheme:a kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 15 ~ 27 parts, TriMethylolPropane(TMP) 15 ~ 25 parts, methyl diisocyanate 15 ~ 27 parts, Sorbic Acid 2 ~ 5.5 parts, phthalic anhydride 2 ~ 5.5 parts, dioxan 0.7 ~ 2.5 part, ethyl cellosolve 0.01 ~ 0.03 part, aluminium-silver slurry 2 ~ 5 parts, oxalic acid 2 ~ 4 parts, benzoyl peroxide 2 ~ 4.5 parts, cobalt naphthenate 3 ~ 6 parts, sodium peroxide 0.5 ~ 1 part, chlorinated rubber 6 ~ 15 parts.
A kind of outer surface of motor spraying paint described above, comprises the following raw material according to mass fraction meter: oleum lini 18 ~ 24 parts, TriMethylolPropane(TMP) 18 ~ 23 parts, methyl diisocyanate 17 ~ 24 parts, Sorbic Acid 3 ~ 5 parts, phthalic anhydride 3 ~ 5 parts, dioxan 1 ~ 2 part, ethyl cellosolve 0.015 ~ 0.025 part, aluminium-silver slurry 3 ~ 4 parts, oxalic acid 2.5 ~ 3.5 parts, benzoyl peroxide 2.5 ~ 4 parts, cobalt naphthenate 3.5 ~ 5 parts, sodium peroxide 0.6 ~ 0.9 part, chlorinated rubber 8 ~ 13 parts.
A kind of outer surface of motor spraying paint described above, comprise the following raw material according to mass fraction meter: oleum lini 19 ~ 23 parts, TriMethylolPropane(TMP) 19 ~ 22 parts, methyl diisocyanate 19 ~ 22 parts, Sorbic Acid 3.5 ~ 4.5 parts, phthalic anhydride 3.5 ~ 4.5 parts, dioxan 1.2 ~ 1.8 parts, ethyl cellosolve 0.019 ~ 0.023 part, aluminium-silver slurry 3.2 ~ 3.8 parts, oxalic acid 2.8 ~ 3.3 parts, benzoyl peroxide 3 ~ 3.7 parts, cobalt naphthenate 4 ~ 4.5 parts, sodium peroxide 0.7 ~ 0.8 part, chlorinated rubber 10 ~ 12 parts.
A kind of outer surface of motor spraying paint described above, comprises the following raw material according to mass fraction meter: oleum lini 21 parts, TriMethylolPropane(TMP) 20 parts, methyl diisocyanate 21 parts, Sorbic Acid 4 parts, phthalic anhydride 4 parts, dioxan 1.5 parts, ethyl cellosolve 0.022 part, aluminium-silver slurry 3.5 parts, oxalic acid 3 parts, benzoyl peroxide 3.3 parts, cobalt naphthenate 4.2 parts, sodium peroxide 0.75 part, chlorinated rubber 11 parts.
In chlorinated rubber described above, the massfraction of chlorine is 65%.
The preparation method of a kind of outer surface of motor spraying paint described above, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 200 ~ 240 DEG C, insulation 2 ~ 3h, is cooled to 140 ~ 160 DEG C, adds methyl diisocyanate mixing, 4 ~ 5h is heated at 180 ~ 200 DEG C, be cooled to 70 ~ 90 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 1.5 ~ 2.5h, be heated to 160 ~ 180 DEG C, insulation 1.5 ~ 2.5h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 400 ~ 500r/min, then mixes with oxalic acid, gets product.
By oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring in the first step described above, be heated to 220 DEG C, insulation 2.5h, is cooled to 150 DEG C, adds methyl diisocyanate mixing, 4.5h is heated at 190 DEG C, be cooled to 80 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 2h, be heated to 170 DEG C, insulation 2h, obtained multipolymer.
Stirring velocity in second step described above is 450r/min.
beneficial effect:compared with prior art; a kind of outer surface of motor spraying paint provided by the invention and preparation method thereof; this paint has excellent sticking power, shock-resistant, water-fast, anticorrosion, the not easily performance such as sagging, has good provide protection, thus extend the work-ing life of motor to motor surface.
Embodiment
embodiment 1
A kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 15 parts, TriMethylolPropane(TMP) 15 parts, methyl diisocyanate 15 parts, Sorbic Acid 2 parts, phthalic anhydride 2 parts, dioxan 0.7 part, ethyl cellosolve 0.01 part, aluminium-silver slurry 2 parts, oxalic acid 2 parts, benzoyl peroxide 2 parts, cobalt naphthenate 3 parts, sodium peroxide 0.5 part, chlorinated rubber 6 parts.
A preparation method for outer surface of motor spraying paint, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 200 DEG C, insulation 2h, is cooled to 140 DEG C, adds methyl diisocyanate mixing, 4h is heated at 180 DEG C, be cooled to 70 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 1.5h, be heated to 160 DEG C, insulation 1.5h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 400r/min, then mixes with oxalic acid, gets product.
embodiment 2
A kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 27 parts, TriMethylolPropane(TMP) 25 parts, methyl diisocyanate 27 parts, Sorbic Acid 5.5 parts, phthalic anhydride 5.5 parts, dioxan 2.5 parts, ethyl cellosolve 0.03 part, aluminium-silver slurry 5 parts, oxalic acid 4 parts, benzoyl peroxide 4.5 parts, cobalt naphthenate 6 parts, sodium peroxide 1 part, chlorinated rubber 15 parts.
A preparation method for outer surface of motor spraying paint, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 240 DEG C, insulation 3h, is cooled to 160 DEG C, adds methyl diisocyanate mixing, 5h is heated at 200 DEG C, be cooled to 90 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 2.5h, be heated to 180 DEG C, insulation 2.5h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 500r/min, then mixes with oxalic acid, gets product.
embodiment 3
A kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 18 parts, TriMethylolPropane(TMP) 18 parts, methyl diisocyanate 17 parts, Sorbic Acid 3 parts, phthalic anhydride 3 parts, dioxan 1 part, ethyl cellosolve 0.015 part, aluminium-silver slurry 3 parts, oxalic acid 2.5 parts, benzoyl peroxide 2.5 parts, cobalt naphthenate 3.5 parts, sodium peroxide 0.6 part, chlorinated rubber 8 parts.
A preparation method for outer surface of motor spraying paint, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 200 DEG C, insulation 2h, is cooled to 140 DEG C, adds methyl diisocyanate mixing, 4h is heated at 180 DEG C, be cooled to 70 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 1.5h, be heated to 160 DEG C, insulation 1.5h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 400r/min, then mixes with oxalic acid, gets product.
embodiment 4
A kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 24 parts, TriMethylolPropane(TMP) 23 parts, methyl diisocyanate 24 parts, Sorbic Acid 5 parts, phthalic anhydride 5 parts, dioxan 2 parts, ethyl cellosolve 0.025 part, aluminium-silver slurry 4 parts, oxalic acid 3.5 parts, benzoyl peroxide 4 parts, cobalt naphthenate 5 parts, sodium peroxide 0.9 part, chlorinated rubber 13 parts.
A preparation method for outer surface of motor spraying paint, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 240 DEG C, insulation 3h, is cooled to 160 DEG C, adds methyl diisocyanate mixing, 5h is heated at 200 DEG C, be cooled to 90 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 2.5h, be heated to 180 DEG C, insulation 2.5h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 500r/min, then mixes with oxalic acid, gets product.
embodiment 5
A kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 19 parts, TriMethylolPropane(TMP) 19 parts, methyl diisocyanate 19 parts, Sorbic Acid 3.5 parts, phthalic anhydride 3.5 parts, dioxan 1.2 parts, ethyl cellosolve 0.019 part, aluminium-silver slurry 3.2 parts, oxalic acid 2.8 parts, benzoyl peroxide 3 parts, cobalt naphthenate 4 parts, sodium peroxide 0.7 part, chlorinated rubber 10 parts.
A preparation method for outer surface of motor spraying paint, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 220 DEG C, insulation 2.5h, is cooled to 150 DEG C, adds methyl diisocyanate mixing, 4.5h is heated at 190 DEG C, be cooled to 80 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 2h, be heated to 170 DEG C, insulation 2h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 400 ~ 500r/min, then mixes with oxalic acid, gets product.
embodiment 6
A kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 23 parts, TriMethylolPropane(TMP) 22 parts, methyl diisocyanate 22 parts, Sorbic Acid 4.5 parts, phthalic anhydride 4.5 parts, dioxan 1.8 parts, ethyl cellosolve 0.023 part, aluminium-silver slurry 3.8 parts, oxalic acid 3.3 parts, benzoyl peroxide 3.7 parts, cobalt naphthenate 4.5 parts, sodium peroxide 0.8 part, chlorinated rubber 12 parts.
A preparation method for outer surface of motor spraying paint, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 220 DEG C, insulation 2.5h, is cooled to 150 DEG C, adds methyl diisocyanate mixing, 4.5h is heated at 190 DEG C, be cooled to 80 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 2h, be heated to 170 DEG C, insulation 2h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 400 ~ 500r/min, then mixes with oxalic acid, gets product.
embodiment 7
A kind of outer surface of motor spraying paint, comprises the following raw material according to mass fraction meter: oleum lini 21 parts, TriMethylolPropane(TMP) 20 parts, methyl diisocyanate 21 parts, Sorbic Acid 4 parts, phthalic anhydride 4 parts, dioxan 1.5 parts, ethyl cellosolve 0.022 part, aluminium-silver slurry 3.5 parts, oxalic acid 3 parts, benzoyl peroxide 3.3 parts, cobalt naphthenate 4.2 parts, sodium peroxide 0.75 part, chlorinated rubber 11 parts.
A preparation method for outer surface of motor spraying paint, comprises the steps:
The first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 220 DEG C, insulation 2.5h, is cooled to 150 DEG C, adds methyl diisocyanate mixing, 4.5h is heated at 190 DEG C, be cooled to 80 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, after mixing, in 2h, be heated to 170 DEG C, insulation 2h, obtained multipolymer;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 400 ~ 500r/min, then mixes with oxalic acid, gets product.
performance test
Test the performance of the embodiment of the present invention 1 ~ 7 product, test result is in table 1.
Table 1 product performance test data
| ? | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 | Embodiment 7 |
| Pencil hardness/H | 2 | 2 | 2 | 2 | 2 | 2 | 2 |
| Impact strength/cm(0.6354cm/500g) | 50 | 53 | 58 | 60 | 62 | 65 | 70 |
| Water tolerance/DEG C | 40 | 45 | 43 | 52 | 58 | 61 | 67 |
| Salt spray resistance/h | 120 | 128 | 132 | 135 | 137 | 142 | 147 |
Above to invention has been detailed introduction, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (8)
1. an outer surface of motor spraying paint, is characterized in that comprising the following raw material according to mass fraction meter: oleum lini 15 ~ 27 parts, TriMethylolPropane(TMP) 15 ~ 25 parts, methyl diisocyanate 15 ~ 27 parts, Sorbic Acid 2 ~ 5.5 parts, phthalic anhydride 2 ~ 5.5 parts, dioxan 0.7 ~ 2.5 part, ethyl cellosolve 0.01 ~ 0.03 part, aluminium-silver slurry 2 ~ 5 parts, oxalic acid 2 ~ 4 parts, benzoyl peroxide 2 ~ 4.5 parts, cobalt naphthenate 3 ~ 6 parts, sodium peroxide 0.5 ~ 1 part, chlorinated rubber 6 ~ 15 parts.
2. a kind of outer surface of motor spraying paint according to claim 1, it is characterized in that comprising the following raw material according to mass fraction meter: oleum lini 18 ~ 24 parts, TriMethylolPropane(TMP) 18 ~ 23 parts, methyl diisocyanate 17 ~ 24 parts, Sorbic Acid 3 ~ 5 parts, phthalic anhydride 3 ~ 5 parts, dioxan 1 ~ 2 part, ethyl cellosolve 0.015 ~ 0.025 part, aluminium-silver slurry 3 ~ 4 parts, oxalic acid 2.5 ~ 3.5 parts, benzoyl peroxide 2.5 ~ 4 parts, cobalt naphthenate 3.5 ~ 5 parts, sodium peroxide 0.6 ~ 0.9 part, chlorinated rubber 8 ~ 13 parts.
3. a kind of outer surface of motor spraying paint according to claim 1, it is characterized in that comprising the following raw material according to mass fraction meter: oleum lini 19 ~ 23 parts, TriMethylolPropane(TMP) 19 ~ 22 parts, methyl diisocyanate 19 ~ 22 parts, Sorbic Acid 3.5 ~ 4.5 parts, phthalic anhydride 3.5 ~ 4.5 parts, dioxan 1.2 ~ 1.8 parts, ethyl cellosolve 0.019 ~ 0.023 part, aluminium-silver slurry 3.2 ~ 3.8 parts, oxalic acid 2.8 ~ 3.3 parts, benzoyl peroxide 3 ~ 3.7 parts, cobalt naphthenate 4 ~ 4.5 parts, sodium peroxide 0.7 ~ 0.8 part, chlorinated rubber 10 ~ 12 parts.
4. a kind of outer surface of motor spraying paint according to claim 1, is characterized in that comprising the following raw material according to mass fraction meter: oleum lini 21 parts, TriMethylolPropane(TMP) 20 parts, methyl diisocyanate 21 parts, Sorbic Acid 4 parts, phthalic anhydride 4 parts, dioxan 1.5 parts, ethyl cellosolve 0.022 part, aluminium-silver slurry 3.5 parts, oxalic acid 3 parts, benzoyl peroxide 3.3 parts, cobalt naphthenate 4.2 parts, sodium peroxide 0.75 part, chlorinated rubber 11 parts.
5. a kind of outer surface of motor spraying paint according to claim 1, is characterized in that the massfraction of chlorine in described chlorinated rubber is 65%.
6. the preparation method of a kind of outer surface of motor spraying paint as claimed in claim 1, it is characterized in that comprising the steps: the first step: by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, be heated to 200 ~ 240 DEG C, insulation 2 ~ 3h, be cooled to 140 ~ 160 DEG C, add methyl diisocyanate mixing, 4 ~ 5h is heated at 180 ~ 200 DEG C, be cooled to 70 ~ 90 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, in 1.5 ~ 2.5h, 160 ~ 180 DEG C are heated to, insulation 1.5 ~ 2.5h, obtained multipolymer after mixing;
Second step: aluminium-silver slurry is dissolved in benzoyl peroxide, then the multipolymer obtained with the first step, cobalt naphthenate, sodium peroxide, chlorinated rubber mix, low whipping speed is mix under 400 ~ 500r/min, then mixes with oxalic acid, gets product.
7. the preparation method of a kind of outer surface of motor spraying paint according to claim 6, to it is characterized in that in the described the first step, by oleum lini, TriMethylolPropane(TMP) and ethyl cellosolve mixing and stirring, being heated to 220 DEG C, insulation 2.5h, be cooled to 150 DEG C, add methyl diisocyanate mixing, at 190 DEG C, heat 4.5h, be cooled to 80 DEG C, add Sorbic Acid, dioxan and phthalic anhydride, in 2h, 170 DEG C are heated to, insulation 2h, obtained multipolymer after mixing.
8. the preparation method of a kind of outer surface of motor spraying paint according to claim 6, is characterized in that the stirring velocity in described second step is 450r/min.