CN104292557A - Reinforcing filler for thin-film capacitor potting compound - Google Patents
Reinforcing filler for thin-film capacitor potting compound Download PDFInfo
- Publication number
- CN104292557A CN104292557A CN201410486287.3A CN201410486287A CN104292557A CN 104292557 A CN104292557 A CN 104292557A CN 201410486287 A CN201410486287 A CN 201410486287A CN 104292557 A CN104292557 A CN 104292557A
- Authority
- CN
- China
- Prior art keywords
- parts
- reinforcing filler
- film capacitor
- powder
- potting compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses reinforcing filler for a thin-film capacitor potting compound. The reinforcing filler is characterized by consisting of the following components in parts by weight: 8-12 parts of graphene, 8-12 parts of wood fibers, 18-22 parts of Suzhou soil, 8-12 parts of chloroprene rubber adhesive, 20-30 parts of calcium carbonate, 15-25 parts of silica powder, 4-6 parts of white carbon black, 4-6 parts of sea-foam stone powder, 4-6 parts of diatom ooze, 4-6 parts of seaweed mud, 1.5-2.5 parts of zinc magnesium powder, 4-6 parts of synthetic adhesive, 4-6 parts of coumarone resin, 1-3 parts of paraffin oil, 1-3 parts of guar gum, 2-4 parts of corn starch, 2-3 parts of glyceryl behenate, 2-3 parts of stearic acid, 2-3 parts of olive oil, 3-5 parts of tert-amyl chloride and 2-4 parts of nano boron fibers. The reinforcing filler disclosed by the invention has the advantages of moisture resistance, heat resistance and cold resistance, is non-toxic, non-corrosive and free of impurities and has good service performance, stable electrical property of a metalized film capacitor is guaranteed, and injury of body health of manufacturing workers is avoided in the production process.
Description
Technical field
The present invention relates to capacitor technology field, be specifically related to a kind of film capacitor potting compound reinforcing filler.
Background technology
During metallization film capacitor is produced, main medium and the hole between pole plate and main medium normally carry out embedding with a kind of material, to improve electrical capacity and insulating property, and improve shelf depreciation and resistance toheat., there is under toughness plasticity difference low temperature easily embrittlement and have the defects such as larger contraction in simple commodity in use paraffin or Microcrystalline Wax, uses oils to there is loss large and be easy to seepage, be not suitable with the requirement of current factory.Given this, the application provides a kind of reinforcing filler joined in paraffin or Microcrystalline Wax, improves the performance of paraffin or Microcrystalline Wax with this.
Summary of the invention
Technical problem to be solved by this invention is that providing a kind of is formed simply, can improve the film capacitor potting compound reinforcing filler of potting compound performance.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of film capacitor potting compound reinforcing filler, be made up of the component of following parts by weight: Graphene 8-12 part, wood fibre 8-12 part, Suzhou soil 18-22 part, neoprene latex 8-12 part, calcium carbonate 20-30 part, silicon powder 15-25 part, white carbon black 4-6 part, sepiolite powder 4-6 part, diatom ooze 4-6 part, algae clay 4-6 part, zinc-magnesium powder 1.5-2.5 part, TPR 4-6 part, coumarone indene resin 4-6 part, paraffin oil 1-3 part, guar gum 1-3 part, W-Gum 2-4 part, Glyceryl Behenate 2-3 part, stearic acid 2-3 part, sweet oil 2-3 part, chlorination tertiary pentane 3-5 part, nanometer boron fibre 2-4 part,
The better parts by weight of above-mentioned each component are: Graphene 10 parts, wood fibre 10 parts, 20 parts, Suzhou soil, neoprene latex 10 parts, 25 parts, calcium carbonate, silicon powder 20 parts, white carbon black 5 parts, sepiolite powder 5 parts, diatom ooze 5 parts, algae clay 5 parts, 2 parts, zinc-magnesium powder, TPR 5 parts, coumarone indene resin 5 parts, paraffin oil 2 parts, guar gum 2 parts, W-Gum 2 parts, Glyceryl Behenate 2 parts, stearic acid 2 parts, 2 parts, sweet oil, the tertiary pentane of chlorination 4 parts, nanometer boron fibre 3 parts.
Drop in kneader by unified for said components during preparation, evenly mixing, at 80-120 DEG C, process 2-3 hour.
The invention has the beneficial effects as follows: the present invention has the advantages such as moistureproofness, thermotolerance and winter hardiness are good, nontoxic, corrosion-free, inclusion-free, there is good use properties, demonstrate,proved the stable of metallization film capacitor electrical property, can not cause damage to the healthy of Manufacturing Worker in process of production.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
A kind of film capacitor potting compound reinforcing filler, is made up of the component of following parts by weight: Graphene 10 parts, wood fibre 10 parts, 20 parts, Suzhou soil, neoprene latex 10 parts, 25 parts, calcium carbonate, silicon powder 20 parts, white carbon black 5 parts, sepiolite powder 5 parts, diatom ooze 5 parts, algae clay 5 parts, 2 parts, zinc-magnesium powder, TPR 5 parts, coumarone indene resin 5 parts, paraffin oil 2 parts, guar gum 2 parts, W-Gum 2 parts, Glyceryl Behenate 2 parts, stearic acid 2 parts, 2 parts, sweet oil, the tertiary pentane of chlorination 4 parts, nanometer boron fibre 3 parts.
Drop in kneader by unified for said components during preparation, evenly mixing, at 80-120 DEG C, process 2-3 hour.
Embodiment 2
A kind of film capacitor potting compound reinforcing filler, is made up of the component of following parts by weight: Graphene 12 parts, wood fibre 12 parts, 22 parts, Suzhou soil, neoprene latex 12 parts, 30 parts, calcium carbonate, silicon powder 25 parts, white carbon black 6 parts, sepiolite powder 6 parts, diatom ooze 6 parts, algae clay 6 parts, 2.5 parts, zinc-magnesium powder, TPR 6 parts, coumarone indene resin 6 parts, paraffin oil 3 parts, guar gum 3 parts, W-Gum 4 parts, Glyceryl Behenate 3 parts, stearic acid 3 parts, 3 parts, sweet oil, the tertiary pentane of chlorination 5 parts, nanometer boron fibre 4 parts;
Drop in kneader by unified for said components during preparation, evenly mixing, at 80-120 DEG C, process 2-3 hour.
Embodiment 3
A kind of film capacitor potting compound reinforcing filler, is made up of the component of following parts by weight: Graphene 8 parts, wood fibre 8 parts, 18 parts, Suzhou soil, neoprene latex 8 parts, 20 parts, calcium carbonate, silicon powder 15 parts, white carbon black 4 parts, sepiolite powder 4 parts, diatom ooze 4 parts, algae clay 4 parts, 1.5 parts, zinc-magnesium powder, TPR 4 parts, coumarone indene resin 4 parts, paraffin oil 1 part, guar gum 1 part, W-Gum 2 parts, Glyceryl Behenate 2 parts, stearic acid 2 parts, 2 parts, sweet oil, the tertiary pentane of chlorination 3 parts, nanometer boron fibre 2 parts;
Drop in kneader by unified for said components during preparation, evenly mixing, at 80-120 DEG C, process 2-3 hour.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (2)
1. a film capacitor potting compound reinforcing filler, it is characterized in that, be made up of the component of following parts by weight: Graphene 8-12 part, wood fibre 8-12 part, Suzhou soil 18-22 part, neoprene latex 8-12 part, calcium carbonate 20-30 part, silicon powder 15-25 part, white carbon black 4-6 part, sepiolite powder 4-6 part, diatom ooze 4-6 part, algae clay 4-6 part, zinc-magnesium powder 1.5-2.5 part, TPR 4-6 part, coumarone indene resin 4-6 part, paraffin oil 1-3 part, guar gum 1-3 part, W-Gum 2-4 part, Glyceryl Behenate 2-3 part, stearic acid 2-3 part, sweet oil 2-3 part, chlorination tertiary pentane 3-5 part, nanometer boron fibre 2-4 part.
2. film capacitor potting compound reinforcing filler according to claim 1, it is characterized in that, be made up of the component of following parts by weight: Graphene 10 parts, wood fibre 10 parts, 20 parts, Suzhou soil, neoprene latex 10 parts, 25 parts, calcium carbonate, silicon powder 20 parts, white carbon black 5 parts, sepiolite powder 5 parts, diatom ooze 5 parts, algae clay 5 parts, 2 parts, zinc-magnesium powder, TPR 5 parts, coumarone indene resin 5 parts, paraffin oil 2 parts, guar gum 2 parts, W-Gum 2 parts, Glyceryl Behenate 2 parts, stearic acid 2 parts, 2 parts, sweet oil, the tertiary pentane of chlorination 4 parts, nanometer boron fibre 3 parts.