CN103351509B - A kind of cable insulation compositions and preparation method thereof - Google Patents
A kind of cable insulation compositions and preparation method thereof Download PDFInfo
- Publication number
- CN103351509B CN103351509B CN201310243554.XA CN201310243554A CN103351509B CN 103351509 B CN103351509 B CN 103351509B CN 201310243554 A CN201310243554 A CN 201310243554A CN 103351509 B CN103351509 B CN 103351509B
- Authority
- CN
- China
- Prior art keywords
- powder
- minute
- cable insulation
- antioxidant
- silicon carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
nullA kind of cable insulation compositions and preparation method thereof，It is characterized in that being prepared by the raw materials in: high density polyethylene (HDPE) 50-55、Antioxidant 1010 1-2、Sepiolite powder 23-26、Smoke sheet rubber 2-3、Nanoclay brick ground-slag end 1-2、Silicon carbide powder 1-2、Vanadium diboride 3-4、Zirconium diboride 2-3、P-tert-butyl benzoic acid 1-2、Cellulose acetate 2-3、Isocyanates 1-2、Aluminium hydrate powder 1-2、Cis-1，4-polyisoprene rubber 12-14、Cyanuric acid zinc 1-2、Sepiolite powder 23-25、Vermiculite power 10-12、Celestite powder 4-6、Captax 3-4、Antioxidant MB 1-2、Anti-scorching agent CTP 1-2、Vinyl three ('beta '-methoxy ethyoxyl) silane 3-4、Propionate 1-2、Modification infusorial earth 6-8.The present invention uses cis-Isosorbide-5-Nitrae-polyisoprene rubber to add the fragility improving high density polyethylene (HDPE), improves the flexible toughness of CABLE MATERIALS, increases silicon carbide powder, can preferably improve its anti-wear performance, expand the range of CABLE MATERIALS.
Description
Technical field
The invention belongs to CABLE MATERIALS technical field, more specifically, relate to a kind of cable insulation compositions and preparation thereof
Method.
Background technology
Wire cable material, is mainly mixed by resin material, inserts, plasticizer, age resistor, fire retardant, antioxidant etc.,
Formula material focuses primarily upon some conventional compositions, thus causes CABLE MATERIALS technical specification the highest or high in cost of production problem, such as
Specific insulation is on the low side, high temperature resistant, low temperature resistant, anti-flammability, insulating properties etc. can not meet cable producer to insulation-grade protective cover material more
The requirement of high electrical performance.
Summary of the invention
It is an object of the invention to provide a kind of cable insulation compositions and preparation method thereof.
The technical solution adopted in the present invention is:
A kind of cable insulation compositions, it is characterised in that be prepared by the raw materials in:
High density polyethylene (HDPE) 50-55, antioxidant 1010 1-2, sepiolite powder 23-26, smoke sheet rubber 2-3, nanoclay brick slag
Powder 1-2, silicon carbide powder 1-2, vanadium diboride 3-4, zirconium diboride 2-3, p-tert-butyl benzoic acid 1-2, cellulose acetate 2-
3, isocyanates 1-2, aluminium hydrate powder 1-2, cis-Isosorbide-5-Nitrae-polyisoprene rubber 12-14, cyanuric acid zinc 1-2, sepiolite powder
23-25, vermiculite power 10-12, celestite powder 4-6, captax 3-4, antioxidant MB 1-2, anti-scorching agent CTP 1-2, vinyl three
('beta '-methoxy ethyoxyl) silane 3-4, propionate 1-2, modification infusorial earth 6-8.
Described modification infusorial earth is prepared by following methods:
Kieselguhr is put into 450-500 DEG C calcine 3-4 hour, take out, cooling, put into immersion 1-in 10-12% hydrochloric acid solution
2 hours, take out, clean with pure water, dry and be ground into powder；Add and be equivalent to the aluminium nitride of kieselguhr weight 35-40%, 2-
The calcium stearate of 3%, the Zirconium tetrafluoride. of 2-3%, the alum powder of 3-4%, mixed grinding 30-40 minute, spray into the most again and be equivalent to silicon
The iso-cyanuric acid triallyl ester of diatomaceous earth weight 12-15%, stirs 60-80 minute under 12000-15000 rev/min, to obtain final product.
The preparation method of described cable insulation compositions, it is characterised in that comprise the following steps: smoke sheet rubber, nanometer are glued
Cob brick ground-slag end, silicon carbide powder, 4-polyisoprene rubber, cyanuric acid zinc, sepiolite powder, p-tert-butyl benzoic acid, acetic acid
Cellulose at 70-80 DEG C mixing 15-20 minute, obtains compound A；Other material mixing 15-20 at 110-130 DEG C is divided
Clock, obtains compound B；Compound A, B are mixed, after placing 12-15 hour, mixing 5-8 minute at 110-128 DEG C, then,
Send into double screw extruder CABLE MATERIALS at 120-150 DEG C described in extruding pelletization acquisition.
The present invention uses cis-Isosorbide-5-Nitrae-polyisoprene rubber to add the fragility improving high density polyethylene (HDPE), improves electricity
The flexible toughness of cable material, increases silicon carbide powder, can preferably improve its anti-wear performance, expand the range of CABLE MATERIALS.
Detailed description of the invention
A kind of cable insulation compositions, is made up of the raw material of following weight portion (kilogram):
High density polyethylene (HDPE) 55, antioxidant 1010 2, sepiolite powder 26, smoke sheet rubber 3, nanoclay brick ground-slag end 1, carbonization
Si powder 2, vanadium diboride 4, zirconium diboride 3, p-tert-butyl benzoic acid 1, cellulose acetate 3, isocyanates 1, aluminium hydrate powder
2, cis-Isosorbide-5-Nitrae-polyisoprene rubber 14, cyanuric acid zinc 2, sepiolite powder 23, vermiculite power 12, celestite powder 6, captax 4,
Antioxidant MB 2, anti-scorching agent CTP 2, vinyl three ('beta '-methoxy ethyoxyl) silane 3, propionate 1, modification infusorial earth
8。
Described modification infusorial earth is prepared by following methods:
Kieselguhr is put into 450-500 DEG C calcine 3-4 hour, take out, cooling, put into immersion 1-in 10-12% hydrochloric acid solution
2 hours, take out, clean with pure water, dry and be ground into powder；Add be equivalent to the aluminium nitride of kieselguhr weight 40%, 3% hard
Ester acid calcium, the Zirconium tetrafluoride. of 3%, the alum powder of 4%, mixed grinding 30-40 minute, spray into the most again and be equivalent to kieselguhr weight
The iso-cyanuric acid triallyl ester of 15%, stirs 60-80 minute under 12000-15000 rev/min, to obtain final product.
The preparation method of cable insulation compositions, comprises the following steps: by smoke sheet rubber, nanoclay brick ground-slag end, carbonization
Si powder, 4-polyisoprene rubber, cyanuric acid zinc, sepiolite powder, p-tert-butyl benzoic acid, cellulose acetate are at 70-80 DEG C
Under mixing 15-20 minute, obtain compound A；By other material at 110-130 DEG C mixing 15-20 minute, obtain compound B；
Compound A, B are mixed, after placing 12-15 hour, mixes at 110-128 DEG C 5-8 minute, then, send into twin-screw extrusion
Machine at 120-150 DEG C extruding pelletization obtain described in CABLE MATERIALS.
The CABLE MATERIALS performance of the present invention:
| Project | Unit | CABLE MATERIALS of the present invention |
| Green tensile intensity | MPa is not less than | 15.00 |
| Original broken percentage elongation | % is not less than | 460 |
| After resistance to 158 DEG C × 168h is aging | ||
| Fracture strength | MPa is not less than | 13 |
| Elongation at break | % is not less than | 440 |
| 20 DEG C of specific insulations | Ω·m | 1.0×1014 |
| 200 DEG C of heat-stable times | Min | 60 |
Claims (2)
1. a cable insulation compositions, it is characterised in that be prepared by the raw materials in: high density polyethylene (HDPE) 50-55,
Antioxidant 1010 1-2, sepiolite powder 23-26, smoke sheet rubber 2-3, nanoclay brick ground-slag end 1-2, silicon carbide powder 1-2, two boron
Change vanadium 3-4, zirconium diboride 2-3, p-tert-butyl benzoic acid 1-2, cellulose acetate 2-3, isocyanates 1-2, aluminium hydrate powder 1-
2, cis-Isosorbide-5-Nitrae-polyisoprene rubber 12-14, cyanuric acid zinc 1-2, sepiolite powder 23-25, vermiculite power 10-12, celestite powder 4-
6, captax 3-4, antioxidant MB 1-2, anti-scorching agent CTP 1-2, vinyl three ('beta '-methoxy ethyoxyl) silane 3-4, propanoic acid
Vinyl acetate 1-2, modification infusorial earth 6-8；
Described modification infusorial earth is prepared by following methods: kieselguhr is put into 450-500 DEG C and calcines 3-4 hour, take out, cold
But, put in 10-12% hydrochloric acid solution and soak 1-2 hour, take out, clean with pure water, dry and be ground into powder；Add quite
In the aluminium nitride of kieselguhr weight 35-40%, the calcium stearate of 2-3%, the Zirconium tetrafluoride. of 2-3%, the alum powder of 3-4%, mixing is ground
Grind 30-40 minute, spray into the iso-cyanuric acid triallyl ester being equivalent to kieselguhr weight 12-15% the most again, at 12000-
Stir 60-80 minute under 15000 revs/min, to obtain final product.
The preparation method of cable insulation compositions the most according to claim 1, it is characterised in that comprise the following steps: by cigarette
Sheet glue, nanoclay brick ground-slag end, silicon carbide powder, cis-Isosorbide-5-Nitrae-polyisoprene rubber, cyanuric acid zinc, sepiolite powder, to uncle
Butylbenzoic acid, cellulose acetate at 70-80 DEG C mixing 15-20 minute, obtain compound A；By other material at 110-130
At DEG C mixing 15-20 minute, obtain compound B；Compound A, B are mixed, after placing 12-15 hour, mixed at 110-128 DEG C
Close 5-8 minute, then, send into double screw extruder cable insulation compositions at 120-150 DEG C described in extruding pelletization acquisition.