CN104287246A - Breathable cloth and manufacturing method thereof

Info

Publication number: CN104287246A
Application number: CN201410453953.3A
Authority: CN
Inventors: 刘广来
Original assignee: Individual
Current assignee: Individual
Priority date: 2014-09-09
Filing date: 2014-09-09
Publication date: 2015-01-21

Abstract

The invention discloses breathable cloth. The breathable cloth comprises 50-68 g of cotton, 12-19 g of celery fibers, 15-21 g of hot-blast air non-woven fabric, 25-36 g of silk, 12-16 g of wood fibers and 15-22 g of starch. The 50-68 g of cotton and the 12-19 g of celery fibers are placed into hypochlorous acid with the concentration being 5% to be soaked for 2-5 hours; the cotton and the celery fibers are taken out and then cleaned up; the 15-21 g of hot-blast air non-woven fabric which is smashed to 100-130 meshes, the 25-36 g of silk with the length being 3-5 mm and the 12-16 g of wood fibers with the length being 6-8 mm are added; after mixing is conducted, the non-woven fabric, the silk and the wood fibers are spun into threads with the diameter being 20-35 microns. The cloth is good in breathable effect, large in porosity, simple in manufacturing mode, capable of not consuming excessive manpower and material resources, suitable for being widely applied to the clothing manufacturing field, and capable of bringing a better and more breathable clothing material to people in summer.

Description

A kind of Ventilate cloth and preparation method thereof

Technical field

The invention belongs to Material Field, particularly a kind of Ventilate cloth and preparation method thereof.

Background technology

When summer, people usually can go out a lot of sweat, and clothes is bonded at very uncomfortable with it; and clothes is not easy to do; be attached to skin cutaneous eupnea last time, cause uncomfortable, if therefore there be just can not well addressing this problem of can breathing freely.

The cloth of current use, also has the product of ventilative type, but gas permeability is not very good usually, affects air circulation.

Summary of the invention

The object of this invention is to provide a kind of Ventilate cloth and preparation method thereof, the cloth air permeable effect that this method makes is good.

A kind of Ventilate cloth, comprises cotton 50-68g, celery fiber 12-19g, hot-wind nonwoven cloth 15-21g, silk 25-36g, wood-fibred 12-16g and starch 15-22g.

First cotton 50-68g, celery fiber 12-19g are placed in the hypochlorous acid of 5% concentration and soak 2-5 hour.

Clean up after taking out.

Then the wood-fibred 12-16g of 25-36g and 6-8 millimeter being crushed to 100-130 object hot-wind nonwoven cloth 15-21g, length 3-5 millimeter is added.

The line of diameter 20-35 micron is spun into after mixing.

Its advantage is:

This cloth air permeable effect is good, and porosity is large, and production method is simple, does not need to expend too much manpower and materials, is applicable to being widely used in clothing field, can bring people better more ventilative clothing materials in summer.More comfortable and easy to wear.

Detailed description of the invention

embodiment 1

A kind of Ventilate cloth, comprises cotton 50g, celery fiber 12g, hot-wind nonwoven cloth 15g, silk 25g, wood-fibred 12g and starch 15g.

First cotton 50g, celery fiber 12g are placed in the hypochlorous acid of 5% concentration and soak 2 hours.

Clean up after taking out.

Then the wood-fibred 12g of 25g and 6 millimeter being crushed to 100-object hot-wind nonwoven cloth 15g, length 3 millimeters is added.

The line of diameter 20 microns is spun into after mixing.

embodiment 2

A kind of Ventilate cloth, comprises cotton 68g, celery fiber 19g, hot-wind nonwoven cloth 21g, silk 36g, wood-fibred 16g and starch 22g.

First cotton 68g, celery fiber 19g are placed in the hypochlorous acid of 5% concentration and soak 5 hours.

Clean up after taking out.

Then the wood-fibred 16g of 25-36g and 8 millimeter being crushed to 130 object hot-wind nonwoven cloth 15-21g, length 5 millimeters is added.

The line of diameter 25 microns is spun into after mixing.

embodiment 3

A kind of Ventilate cloth, comprises cotton 51g, celery fiber 13g, hot-wind nonwoven cloth 16g, silk 26g, wood-fibred 13g and starch 16g.

First cotton 51g, celery fiber 13g are placed in the hypochlorous acid of 5% concentration and soak 2-5 hour.

Clean up after taking out.

Then the wood-fibred 13g of 26g and 7 millimeter being crushed to 120 object hot-wind nonwoven cloth 16g, length 3-5 millimeter is added.

The line of diameter 2 microns is spun into after mixing.

embodiment 4

First cotton 60g, celery fiber 15g are placed in the hypochlorous acid of 5% concentration and soak 3 hours.

Clean up after taking out.

Then the wood-fibred 14g of 30g and 8 millimeter being crushed to 110 object hot-wind nonwoven cloth 16g, length 5 millimeters is added.

The line of diameter 30 microns is spun into after mixing.

Claims

1. a Ventilate cloth, is characterized in that comprising cotton 50-68g, celery fiber 12-19g, hot-wind nonwoven cloth 15-21g, silk 25-36g, wood-fibred 12-16g and starch 15-22g.

2. the preparation method of a kind of Ventilate cloth according to claim 1, is characterized in that the following step:

First cotton 50-68g, celery fiber 12-19g are placed in the hypochlorous acid of 5% concentration and soak 2-5 hour;

Clean up after taking out;

Then the wood-fibred 12-16g of 25-36g and 6-8 millimeter being crushed to 100-130 object hot-wind nonwoven cloth 15-21g, length 3-5 millimeter is added;

The line of diameter 20-35 micron is spun into after mixing.

3. a kind of Ventilate cloth according to claim 1, is characterized in that: cotton 50g, celery fiber 12g, hot-wind nonwoven cloth 15g, silk 25g, wood-fibred 12g and starch 15g.

4. a kind of Ventilate cloth according to claim 1, is characterized in that: cotton 51g, celery fiber 13g, hot-wind nonwoven cloth 16g, silk 26g, wood-fibred 13g and starch 16g.