CN104278215A - Special wear-resistant steel tube for baby stroller - Google Patents
Special wear-resistant steel tube for baby stroller Download PDFInfo
- Publication number
- CN104278215A CN104278215A CN201410487051.1A CN201410487051A CN104278215A CN 104278215 A CN104278215 A CN 104278215A CN 201410487051 A CN201410487051 A CN 201410487051A CN 104278215 A CN104278215 A CN 104278215A
- Authority
- CN
- China
- Prior art keywords
- wear
- steel tube
- resistant steel
- baby stroller
- doll carriage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a special wear-resistant steel tube for a baby stroller. The special wear-resistant steel tube is prepared from the following components in percentage by mass: 0.8-1.0% of C, 4-4.5% of Cr, 1.4-1.6% of Mn, 3.5-3.8% of Si, 0.4-0.5% of Cu, 0.4-0.6% of Ni, 0.02-0.03% of Re, less than or equal to 0.04% of S, less than or equal to 0.04% of P and the balance of Fe. The wear-resistant stele tube disclosed by the invention is reasonable in formula, the shrinkage porosity and shrinkage cavities of the produced steel tube are reduced, the steel tube is good in mechanical property, good in wear resistance and toughness, the hardness is 44-48HRC, the impact value is greater than or equal to 18J/cm<2>, and the service life is prolonged by 1.5-2 times; and the integral safety performance of the baby stroller is improved.
Description
Technical field
The present invention relates to doll carriage technical field, be specifically related to a kind of wear-resistant steel pipe being exclusively used in doll carriage.
Background technology
Doll carriage is baby's " vehicles ", and needing people and assist to push or haul the car just can walked, doll carriage, is baby's favorite doll carriage stroll vehicles, requisite when mother goes shopping with baby especially.But according to the growth of baby, use, doll carriage can be divided into many types again, as: twin babies go-cart, high view doll carriage, sunshade doll carriage etc.Be mainly standard according to weight-carrying capacity, general test standard is nine to ten five kilograms, and general perambulator approximately can use 3 to five years.
High-abrasive material is the core of field of new, plays important promotion and supporting role to the development of new and high technology, and in global new material research field, high-abrasive material accounts for 85%.Along with the arrival of information society, the development of special, wear-resistant material to new and high technology plays important promotion and supporting role, be 21st century information, biology, the energy, environmental protection, the high-tech sector such as space critical material, becoming the emphasis of countries in the world field of new researchdevelopment, is also the focus of Strategic Competition in the high technology development of countries in the world.
In prior art, doll carriage is not enough by steel pipe mechanical performance, haves much room for improvement.
Summary of the invention
For the problems referred to above, the invention provides a kind of wear-resistant steel pipe being exclusively used in doll carriage, good mechanical property, improve the safety performance of go-cart.
In order to solve the problem, technical scheme provided by the invention is:
Be exclusively used in a wear-resistant steel pipe for doll carriage, each composition and mass percent thereof are: C:0.8-1.0%, Cr:4-4.5%, Mn:1.4-1.6%, Si:3.5-3.8%, Cu:0.4-0.5%, Ni:0.4-0.6%, Re:0.02-0.03%, S :≤0.04%, P :≤0.04%; Surplus is Fe.
Preferably, each composition and mass percent thereof are: C:0.85-1.0%, Cr:4.2-4.5%, Mn:1.45-1.6%, Si:3.6-3.8%, Cu:0.42-0.5%, Ni:0.45-0.6%, Re:0.02-0.03%, S :≤0.04%, P :≤0.04%; Surplus is Fe.
Preferably, each composition and mass percent thereof are: C:0.85%, Cr:4.4%, Mn:1.45%, Si:3.6%, Cu:0.48%, Ni:0.45%, Re:0.028%, S:0.04%, P:0.02%; Surplus is Fe.
Preferably, each composition and mass percent thereof are: C:0.95%, Cr:4.2%, Mn:1.55%, Si:3.7%, Cu:0.42%, Ni:0.55%, Re:0.025%, S:0.02%, P:0.04%; Surplus is Fe.
Compared with prior art, beneficial effect of the present invention is:
Wear-resistant steel pipe of the present invention, formulation selection is reasonable, and the shrinkage porosite of the steel pipe produced, shrinkage cavity produce and reduce, and good mechanical property, hardness: 44-48HRC, wear resistance is good, good toughness, impact value>=18J/cm
2, work-ing life improves 1.5-2 times, improves the general safety performance of doll carriage.
Embodiment
The present invention will be further described below:
Embodiment 1:
Be exclusively used in a wear-resistant steel pipe for doll carriage, each composition and mass percent thereof are: C:1.0%, Cr:4%, Mn:1.6%, Si:3.5%, Cu:0.5%, Ni:0.4%, Re:0.03%, S:0.04%, P:0.02%; Surplus is Fe.
Embodiment 2:
Be exclusively used in a wear-resistant steel pipe for doll carriage, each composition and mass percent thereof are: C:0.8%, Cr:4.5%, Mn:1.4%, Si:33.8%, Cu:0.4%, Ni:0.6%, Re:0.02%, S:0.01%, P:0.04%; Surplus is Fe.
Embodiment 3:
Be exclusively used in a wear-resistant steel pipe for doll carriage, each composition and mass percent thereof are: C:0.9%, Cr:4.2%, Mn:1.5%, Si:3.6%, Cu:0.45%, Ni:0.5%, Re:0.025%, S:0.04%, P:0.04%; Surplus is Fe.
Embodiment 4:
Be exclusively used in a wear-resistant steel pipe for doll carriage, each composition and mass percent thereof are: C:0.85%, Cr:4.4%, Mn:1.45%, Si:3.6%, Cu:0.48%, Ni:0.45%, Re:0.028%, S:0.04%, P:0.02%; Surplus is Fe.
Embodiment 5:
Be exclusively used in a wear-resistant steel pipe for doll carriage, each composition and mass percent thereof are: C:0.95%, Cr:4.2%, Mn:1.55%, Si:3.7%, Cu:0.42%, Ni:0.55%, Re:0.025%, S:0.02%, P:0.04%; Surplus is Fe.
More than show and describe ultimate principle of the present invention, principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (4)
1. be exclusively used in a wear-resistant steel pipe for doll carriage, it is characterized in that: each composition and mass percent thereof are: C:0.8-1.0%, Cr:4-4.5%, Mn:1.4-1.6%, Si:3.5-3.8%, Cu:0.4-0.5%, Ni:0.4-0.6%, Re:0.02-0.03%, S :≤0.04%, P :≤0.04%; Surplus is Fe.
2. the wear-resistant steel pipe being exclusively used in doll carriage according to claim 1, is characterized in that: each composition and mass percent thereof are: C:0.85-1.0%, Cr:4.2-4.5%, Mn:1.45-1.6%, Si:3.6-3.8%, Cu:0.42-0.5%, Ni:0.45-0.6%, Re:0.02-0.03%, S :≤0.04%, P :≤0.04%; Surplus is Fe.
3. the wear-resistant steel pipe being exclusively used in doll carriage according to claim 1 and 2, is characterized in that: each composition and mass percent thereof are: C:0.85%, Cr:4.4%, Mn:1.45%, Si:3.6%, Cu:0.48%, Ni:0.45%, Re:0.028%, S:0.04%, P:0.02%; Surplus is Fe.
4. the wear-resistant steel pipe being exclusively used in doll carriage according to claim 1 and 2, is characterized in that: each composition and mass percent thereof are: C:0.95%, Cr:4.2%, Mn:1.55%, Si:3.7%, Cu:0.42%, Ni:0.55%, Re:0.025%, S:0.02%, P:0.04%; Surplus is Fe.