CN103397271A - Ferromagnetic vibration damping alloy - Google Patents
Ferromagnetic vibration damping alloy Download PDFInfo
- Publication number
- CN103397271A CN103397271A CN201310342322XA CN201310342322A CN103397271A CN 103397271 A CN103397271 A CN 103397271A CN 201310342322X A CN201310342322X A CN 201310342322XA CN 201310342322 A CN201310342322 A CN 201310342322A CN 103397271 A CN103397271 A CN 103397271A
- Authority
- CN
- China
- Prior art keywords
- type damping
- ferromagnetic type
- damping
- alloy
- alloy material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a ferromagnetic vibration damping alloy comprising the components of, by mass: 12.5 -13.5% of Cr, 6.3-6.8% of Co, 5.0-5.5% of Al, 1.8-2.3% of Mo, 0.4-0.6% of Mn, 0.08-0.12% of Si, 0.8-1.0% of Ni, 0.2-0.4% of Ti, 0.015-0.02% of C, no more than 0.01% of S, no more than 0.02% of P, and balance of Fe. With the components, cost can be reduced, and alloy material strength, corrosion resistance, abrasion resistance, oxidation resistance, and welding performance can be improved, such that the alloy material has good elasticity modulus, good processability, and high damping property. Therefore, damping performance of the alloy can be sufficiently developed.
Description
Technical field
The present invention relates to metal material field, particularly relate to a kind of ferromagnetic type Damping Alloys.
Background technology
Along with the development of modern science and technology, and the enhancing of people's environmental consciousness, vibration and noise controlly become a urgent problem.Especially in fields such as navigation, space flight, aviation and nuclear industry, the research of noise reduction technology has obtained general attention.
Damp alloy material has good vibration-damping function, and has as the due intensity of structured material, and it can be converted into other forms of energy expenditure to vibrational energy by in-fighting.Therefore, damping alloy, as an emerging field of functional materials, has obtained development at full speed.
The damping capacity of existing Fe base damp alloy material is less, and its at high temperature damping capacity can be affected, can't give play to good damping property, and the processing characteristics of existing Fe base damp alloy material is very poor, can't meet service requirements.
Summary of the invention
The technical problem that the present invention mainly solves is: for the deficiencies in the prior art, a kind of ferromagnetic type Damping Alloys is provided, can reduce costs, improve intensity, erosion resistance, wearability, oxidation-resistance and the weldability of alloy material, make alloy material have good elasticity modulus, processing characteristics, and high damping properties, can give full play to its damping property.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: a kind of ferromagnetic type Damping Alloys is provided, and described ferromagnetic type Damping Alloys comprises the following ingredients that forms by mass percentage: Cr:12.5%-13.5%, Co:6.3%-6.8%, Al:5.0%-5.5%, Mo:1.8%-2.3%, Mn:0.4%-0.6%, Si:0.08%-0.12%, Ni:0.8%-1.0%, Ti:0.2%-0.4%, C:0.015%-0.02%, S :≤0.01%, P :≤0.02%, surplus Fe.
In a preferred embodiment of the present invention, described ferromagnetic type Damping Alloys comprises the following ingredients that forms by mass percentage: Cr:12.7%, Co:6.6%, Al:5.2%, Mo:2.1%, Mn:0.6%, Si:0.1%, Ni:0.85%, Ti:0.37%, C:0.018%, S :≤0.01%, P :≤0.02%, surplus Fe.
In a preferred embodiment of the present invention, described ferromagnetic type Damping Alloys comprises the following ingredients that forms by mass percentage: Cr:13.2%, Co:6.4%, Al:5.4%, Mo:1.9%, Mn:0.5%, Si:0.09%, Ni:0.9%, Ti:0.22%, C:0.02%, S :≤0.01%, P :≤0.02%, surplus Fe.
The invention has the beneficial effects as follows: by the reasonably optimizing coupling of alloy element, can reduce costs, improve intensity, erosion resistance, wearability, oxidation-resistance and the weldability of alloy material, make alloy material have good elasticity modulus, processing characteristics, and high damping properties, can give full play to its damping property.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made more explicit defining.
The embodiment of the present invention comprises:
A kind of ferromagnetic type Damping Alloys, described ferromagnetic type Damping Alloys comprise the following ingredients that forms by mass percentage: Cr:12.5%-13.5%, Co:6.3%-6.8%, Al:5.0%-5.5%, Mo:1.8%-2.3%, Mn:0.4%-0.6%, Si:0.08%-0.12%, Ni:0.8%-1.0%, Ti:0.2%-0.4%, C:0.015%-0.02%, S :≤0.01%, P :≤0.02%, surplus Fe.
Embodiment one:
A kind of ferromagnetic type Damping Alloys, described ferromagnetic type Damping Alloys comprise the following ingredients that forms by mass percentage: Cr:12.7%, Co:6.6%, Al:5.2%, Mo:2.1%, Mn:0.6%, Si:0.1%, Ni:0.85%, Ti:0.37%, C:0.018%, S :≤0.01%, P :≤0.02%, surplus Fe.
Embodiment two:
A kind of ferromagnetic type Damping Alloys, described ferromagnetic type Damping Alloys comprise the following ingredients that forms by mass percentage: Cr:13.2%, Co:6.4%, Al:5.4%, Mo:1.9%, Mn:0.5%, Si:0.09%, Ni:0.9%, Ti:0.22%, C:0.02%, S :≤0.01%, P :≤0.02%, surplus Fe.
Ferromagnetic type Damping Alloys of the present invention, its performance is as follows:
The present invention has disclosed a kind of ferromagnetic type Damping Alloys, reasonably optimizing coupling by the alloy element, can reduce costs, improve intensity, erosion resistance, wearability, oxidation-resistance and the weldability of alloy material, make alloy material have good elasticity modulus, processing characteristics, and high damping properties, can give full play to its damping property.
The foregoing is only embodiments of the invention; not thereby limit the scope of the claims of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in scope of patent protection of the present invention.
Claims (3)
1. a ferromagnetic type Damping Alloys, is characterized in that, described ferromagnetic type Damping Alloys comprises the following ingredients that forms by mass percentage: Cr:12.5%-13.5%, Co:6.3%-6.8%, Al:5.0%-5.5%, Mo:1.8%-2.3%, Mn:0.4%-0.6%, Si:0.08%-0.12%, Ni:0.8%-1.0%, Ti:0.2%-0.4%, C:0.015%-0.02%, S :≤0.01%, P :≤0.02%, surplus Fe.
2. ferromagnetic type Damping Alloys according to claim 1, is characterized in that, described ferromagnetic type Damping Alloys comprises the following ingredients that forms by mass percentage: Cr:12.7%, Co:6.6%, Al:5.2%, Mo:2.1%, Mn:0.6%, Si:0.1%, Ni:0.85%, Ti:0.37%, C:0.018%, S :≤0.01%, P :≤0.02%, surplus Fe.
3. ferromagnetic type Damping Alloys according to claim 1, is characterized in that, described ferromagnetic type Damping Alloys comprises the following ingredients that forms by mass percentage: Cr:13.2%, Co:6.4%, Al:5.4%, Mo:1.9%, Mn:0.5%, Si:0.09%, Ni:0.9%, Ti:0.22%, C:0.02%, S :≤0.01%, P :≤0.02%, surplus Fe.