CN104277736A - Easy-to-coat carton adhesive - Google Patents

Easy-to-coat carton adhesive Download PDF

Info

Publication number
CN104277736A
CN104277736A CN201410507824.8A CN201410507824A CN104277736A CN 104277736 A CN104277736 A CN 104277736A CN 201410507824 A CN201410507824 A CN 201410507824A CN 104277736 A CN104277736 A CN 104277736A
Authority
CN
China
Prior art keywords
parts
paper box
water
add
stirring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410507824.8A
Other languages
Chinese (zh)
Inventor
唐述振
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI DONGCAI PRINTING TECHNOLOGY Co Ltd
Original Assignee
HEFEI DONGCAI PRINTING TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI DONGCAI PRINTING TECHNOLOGY Co Ltd filed Critical HEFEI DONGCAI PRINTING TECHNOLOGY Co Ltd
Priority to CN201410507824.8A priority Critical patent/CN104277736A/en
Publication of CN104277736A publication Critical patent/CN104277736A/en
Pending legal-status Critical Current

Abstract

The invention discloses an easy-to-coat carton adhesive. The easy-to-coat carton adhesive is prepared from the following raw materials in parts by weight: 100-120 parts of water, 20-30 parts of corn starch, 10-15 parts of calcium carbonate, 2-3 parts of alum, 2-3 parts of light magnesium oxide, 0.42-0.46 part of aluminum sulfate, 0.36-0.38 part of polyvinyl alcohol, 1-2 parts of sodium bicarbonate, 0.7-0.8 part of potassium permanganate and 0.6-0.8 part of borax. The easy-to-coat carton adhesive is prepared according to the following steps: pouring water into a container and adjusting water temperature to 56-64 DEG C; pouring corn starch into the water, continuously stirring to a viscous state, then adding calcium carbonate and potassium permanganate, and stirring for 15-18min to obtain an emulsion A; and adding alum and light magnesium oxide into the emulsion A, stirring for 6-8min, then adding aluminum sulfate, polyvinyl alcohol and sodium bicarbonate, uniformly stirring, then adding borax, stirring for 20-25min, standing and cooling. The easy-to-coat carton adhesive disclosed by the invention is strong in adhesive capacity and easy to coat, and can improve the compressive strength and flexural strength of carbons.

Description

One is easily coated with adhesive for paper box
Technical field
The invention belongs to technical field of adhesive, particularly relate to one and be easily coated with adhesive for paper box.
Background technology
Tackiness agent is the requisite material of Carbon enterprise, and it is mainly used on the compound working procedure of face Paper or cardboard.At present, the bonding for cardboard mainly adopts amylan.But because this type of adhesives power is weak, crushing resistance, moisture protection are poor, and therefore the quality product of production department can not be guaranteed.In prior art, tackiness agent use after, carton outward appearance is smooth not, resistance to compression and folding strength undesirable, need improve.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, provide one and be easily coated with adhesive for paper box, its adhesive capacity is strong, is easily coated with, and can improves resistance to compression and the folding strength of carton.
The present invention proposes one and be easily coated with adhesive for paper box, be made up of the raw material of following weight part: water: 100-120 part; W-Gum: 20-30 part; Calcium carbonate: 10-15 part; Alum: 2-3 part; Light magnesium oxide: 2-3 part; Tai-Ace S 150: 0.42-0.46 part; Polyvinyl alcohol: 0.36-0.38 part; Sodium bicarbonate: 1-2 part; Potassium permanganate: 0.7-0.8 part; Borax: 0.6-0.8 part;
According to above-mentioned raw materials proportioning, prepare described easy coating adhesive for paper box according to following technique:
S1: water is poured in container, and to adjust water temperature be 56-64 DEG C;
S2: add W-Gum in the water of S1, and be constantly stirred to thick, then add calcium carbonate and potassium permanganate, after stirring 15-18min, obtain latex A;
S3: add alum, light magnesium oxide in the latex A that S2 obtains, stirs after 6-8min and adds Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate, stir, then add borax, stirs 20-25min, leaves standstill, obtains described easy coating adhesive for paper box after cooling.
Preferably, be made up of the raw material of following weight part: water: 105-113 part; W-Gum: 23-26 part; Calcium carbonate: 12-14 part; Alum: 2.3-2.8 part; Light magnesium oxide: 2.3-2.6 part; Tai-Ace S 150: 0.43-0.45 part; Polyvinyl alcohol: 0.37-0.38 part; Sodium bicarbonate: 1.4-1.7 part; Potassium permanganate: 0.73-0.78 part; Borax: 0.65-0.78 part.
Preferably, be made up of the raw material of following weight part: water: 110 parts; W-Gum: 25 parts; Calcium carbonate: 12 parts; Alum: 2.5 parts; Light magnesium oxide: 2.5 parts; Tai-Ace S 150: 0.44 part; Polyvinyl alcohol: 0.37 part; Sodium bicarbonate: 1.5 parts; Potassium permanganate: 0.75 part; Borax: 0.68 part.
Preferably, in S1, water is poured in container, and to adjust water temperature be 58-61 DEG C.
Preferably, in S1, water is poured in container, and to adjust water temperature be 59 DEG C.
Preferably, in S2, after stirring 15.6-17.8min, obtain latex A.
Preferably, in S2, after stirring 16min, obtain latex A.
Preferably, in S3, in the latex A that S2 obtains, add alum, light magnesium oxide, add Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate after stirring 6.7-7.3min, stir, then add borax, stir 21-23min, leave standstill, cool.
Preferably, in S3, in the latex A that S2 obtains, add alum, light magnesium oxide, add Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate after stirring 7min, stir, then add borax, stir 22min, leave standstill, cool.
Easy coating adhesive for paper box of the present invention, in its raw material, the weight part of water can be 102.3,104,106,107.8,109,110,111.3,112,113,113.8,114,115,115.6,117,118,118.4,119.3 parts; The weight part of W-Gum can be 20.5,21,21.3,22,22.4,23,23.5,24,24.1,25,26,27.3,28,28.6,29,29.2 parts; The weight part of calcium carbonate can be 10.3,10.9,11,11.2,11.7,12,12.6,13,13.5,14,14.6 parts; The weight part of alum can be 2.2,2.4,2.5,2.6,2.75,2.8,2.9,2.93 parts; The weight part of light magnesium oxide can be 2.1,2.15,2.2,2.3,2.45,2.6,2.7,2.78,2.8,2.93 parts; The weight part of Tai-Ace S 150 can be 0.43,0.44,0.45 part; The weight part of polyvinyl alcohol can be 0.37,0.375 part; The weight part of sodium bicarbonate can be 1.1,1.25,1.3,1.4,1.56,1.6,1.78,1.8,1.9 parts; The weight part of potassium permanganate can be 0.72,0.73,0.74,0.75,0.76,0.77,0.78,0.79 part; The weight part of borax can be 0.63,0.65,0.66,0.67,0.68,0.69,0.7,0.72,0.73,0.75,0.76,0.78 part.
In the present invention, carry out choose reasonable by the components by weight percent of commute coating adhesive for paper box, and adopt proper step to allocate, make the cohesive strength of tackiness agent high; Meanwhile, obtained tackiness agent is nontoxic, not easily occurs the phenomenon that glue is separated, and in whole allocation process, to stir, technique is simple, and processing condition are low, product with stable quality, and the cardboard compressive resistance obtained after bonding is large, and the resistance to power of exposing is strong.
Embodiment
Below in conjunction with specific examples, the present invention is described in detail; should understand; embodiment is only for illustration of the present invention, instead of for limiting the present invention, any amendment, equivalent replacement etc. made on basis of the present invention is all in protection scope of the present invention.
Embodiment 1
One is easily coated with adhesive for paper box, is made up: water of the raw material of following weight part: 110 parts; W-Gum: 25 parts; Calcium carbonate: 12 parts; Alum: 2.5 parts; Light magnesium oxide: 2.5 parts; Tai-Ace S 150: 0.44 part; Polyvinyl alcohol: 0.37 part; Sodium bicarbonate: 1.5 parts; Potassium permanganate: 0.75 part; Borax: 0.68 part;
According to above-mentioned raw materials proportioning, prepare described easy coating adhesive for paper box according to following technique:
S1: water is poured in container, and to adjust water temperature be 59 DEG C;
S2: add W-Gum in the water of S1, and be constantly stirred to thick, then add calcium carbonate and potassium permanganate, after stirring 16min, obtain latex A;
S3: add alum, light magnesium oxide in the latex A that S2 obtains, stirs after 7min and adds Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate, stir, then add borax, stirs 22min, leaves standstill, obtains described easy coating adhesive for paper box after cooling.
Embodiment 2
One is easily coated with adhesive for paper box, is made up: water of the raw material of following weight part: 120 parts; W-Gum: 20 parts; Calcium carbonate: 15 parts; Alum: 2 parts; Light magnesium oxide: 3 parts; Tai-Ace S 150: 0.42 part; Polyvinyl alcohol: 0.38 part; Sodium bicarbonate: 1 part; Potassium permanganate: 0.8 part; Borax: 0.6 part;
According to above-mentioned raw materials proportioning, prepare described easy coating adhesive for paper box according to following technique:
S1: water is poured in container, and to adjust water temperature be 56 DEG C;
S2: add W-Gum in the water of S1, and be constantly stirred to thick, then add calcium carbonate and potassium permanganate, after stirring 15min, obtain latex A;
S3: add alum, light magnesium oxide in the latex A that S2 obtains, stirs after 8min and adds Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate, stir, then add borax, stirs 25min, leaves standstill, obtains described easy coating adhesive for paper box after cooling.
Embodiment 3
One is easily coated with adhesive for paper box, is made up: water of the raw material of following weight part: 100 parts; W-Gum: 30 parts; Calcium carbonate: 10 parts; Alum: 3 parts; Light magnesium oxide: 2 parts; Tai-Ace S 150: 0.46 part; Polyvinyl alcohol: 0.36 part; Sodium bicarbonate: 2 parts; Potassium permanganate: 0.7 part; Borax: 0.8 part;
According to above-mentioned raw materials proportioning, prepare described easy coating adhesive for paper box according to following technique:
S1: water is poured in container, and to adjust water temperature be 64 DEG C;
S2: add W-Gum in the water of S1, and be constantly stirred to thick, then add calcium carbonate and potassium permanganate, after stirring 18min, obtain latex A;
S3: add alum, light magnesium oxide in the latex A that S2 obtains, stirs after 6min and adds Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate, stir, then add borax, stirs 20min, leaves standstill, obtains described easy coating adhesive for paper box after cooling.
Embodiment 4
One is easily coated with adhesive for paper box, is made up: water of the raw material of following weight part: 107.8 parts; W-Gum: 22 parts; Calcium carbonate: 12.6 parts; Alum: 2.6 parts; Light magnesium oxide: 2.45 parts; Tai-Ace S 150: 0.44 part; Polyvinyl alcohol: 0.375 part; Sodium bicarbonate: 1.6 parts; Potassium permanganate: 0.76 part; Borax: 0.72 part;
According to above-mentioned raw materials proportioning, prepare described easy coating adhesive for paper box according to following technique:
S1: water is poured in container, and to adjust water temperature be 58 DEG C;
S2: add W-Gum in the water of S1, and be constantly stirred to thick, then add calcium carbonate and potassium permanganate, after stirring 16.3min, obtain latex A;
S3: add alum, light magnesium oxide in the latex A that S2 obtains, stirs after 7.1min and adds Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate, stir, then add borax, stirs 23min, leaves standstill, obtains described easy coating adhesive for paper box after cooling.

Claims (9)

1. be easily coated with an adhesive for paper box, it is characterized in that, be made up of the raw material of following weight part: water: 100-120 part; W-Gum: 20-30 part; Calcium carbonate: 10-15 part; Alum: 2-3 part; Light magnesium oxide: 2-3 part; Tai-Ace S 150: 0.42-0.46 part; Polyvinyl alcohol: 0.36-0.38 part; Sodium bicarbonate: 1-2 part; Potassium permanganate: 0.7-0.8 part; Borax: 0.6-0.8 part;
According to above-mentioned raw materials proportioning, prepare described easy coating adhesive for paper box according to following technique:
S1: water is poured in container, and to adjust water temperature be 56-64 DEG C;
S2: add W-Gum in the water of S1, and be constantly stirred to thick, then add calcium carbonate and potassium permanganate, after stirring 15-18min, obtain latex A;
S3: add alum, light magnesium oxide in the latex A that S2 obtains, stirs after 6-8min and adds Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate, stir, then add borax, stirs 20-25min, leaves standstill, obtains described easy coating adhesive for paper box after cooling.
2. easy coating adhesive for paper box according to claim 1, is characterized in that, be made up: water of the raw material of following weight part: 105-113 part; W-Gum: 23-26 part; Calcium carbonate: 12-14 part; Alum: 2.3-2.8 part; Light magnesium oxide: 2.3-2.6 part; Tai-Ace S 150: 0.43-0.45 part; Polyvinyl alcohol: 0.37-0.38 part; Sodium bicarbonate: 1.4-1.7 part; Potassium permanganate: 0.73-0.78 part; Borax: 0.65-0.78 part.
3. easy coating adhesive for paper box according to claim 1 and 2, is characterized in that, be made up: water of the raw material of following weight part: 110 parts; W-Gum: 25 parts; Calcium carbonate: 12 parts; Alum: 2.5 parts; Light magnesium oxide: 2.5 parts; Tai-Ace S 150: 0.44 part; Polyvinyl alcohol: 0.37 part; Sodium bicarbonate: 1.5 parts; Potassium permanganate: 0.75 part; Borax: 0.68 part.
4. the easy coating adhesive for paper box according to any one of claim 1-3, is characterized in that, in S1, poured in container by water, and to adjust water temperature be 58-61 DEG C.
5. the easy coating adhesive for paper box according to any one of claim 1-4, is characterized in that, in S1, poured in container by water, and to adjust water temperature be 59 DEG C.
6. the easy coating adhesive for paper box according to any one of claim 1-5, is characterized in that, in S2, obtains latex A after stirring 15.6-17.8min.
7. the easy coating adhesive for paper box according to any one of claim 1-6, is characterized in that, in S2, obtains latex A after stirring 16min.
8. the easy coating adhesive for paper box according to any one of claim 1-7, it is characterized in that, in S3, alum, light magnesium oxide is added in the latex A that S2 obtains, add Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate after stirring 6.7-7.3min, stir, then add borax, stir 21-23min, leave standstill, cool.
9. the easy coating adhesive for paper box according to any one of claim 1-8, it is characterized in that, in S3, alum, light magnesium oxide is added in the latex A that S2 obtains, add Tai-Ace S 150, polyvinyl alcohol, sodium bicarbonate after stirring 7min, stir, then add borax, stir 22min, leave standstill, cool.
CN201410507824.8A 2014-09-27 2014-09-27 Easy-to-coat carton adhesive Pending CN104277736A (en)