CN104276743A - 铸造蠕墨铸铁玻璃瓶对开模的方法 - Google Patents

铸造蠕墨铸铁玻璃瓶对开模的方法 Download PDF

Info

Publication number
CN104276743A
CN104276743A CN201310298012.2A CN201310298012A CN104276743A CN 104276743 A CN104276743 A CN 104276743A CN 201310298012 A CN201310298012 A CN 201310298012A CN 104276743 A CN104276743 A CN 104276743A
Authority
CN
China
Prior art keywords
casting
cast iron
vial
split cavity
sand mold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310298012.2A
Other languages
English (en)
Inventor
刘家峰
陈硕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310298012.2A priority Critical patent/CN104276743A/zh
Publication of CN104276743A publication Critical patent/CN104276743A/zh
Pending legal-status Critical Current

Abstract

一种铸造蠕墨铸铁玻璃瓶对开模的方法，其特征在于使用出气孔、直浇道、上湿砂型、铸造蠕墨铸铁玻璃瓶对开模、横浇道、内浇道、下湿砂型、粘土砂湿砂型单一砂、箱外定位销；使用23稀土硅铁合金蠕化剂中稀土元素含量高和不含有镁元素，在蠕化反应时平稳，蠕化率高，白口倾向小；铸造蠕墨铸铁玻璃瓶对开模在高温情况下工作，提高了使用寿命，提高了经济效益。

Description

铸造蠕墨铸铁玻璃瓶对开模的方法
技术领域
本发明涉及一种铸造铸铁产品的方法，尤其是铸造蠕墨铸铁玻璃瓶对开模的方法。
背景技术
玻璃瓶对开模在高温情况下工作，用普通铸铁材质制作的玻璃瓶对开模因为容易变形和开裂不能使用，造成经常更换新的玻璃瓶对开模。
发明内容
本发明供一种铸造蠕墨铸铁玻璃瓶对开模的方法，生产的铸造蠕墨铸铁玻璃瓶对开模在高温情况下工作，提高了使用寿命，提高了经济效益。
本发明解决其技术问题所采用的技术方案是：一种铸造蠕墨铸铁玻璃瓶对开模的方法，其特征在于使用出气孔、直浇道、上湿砂型、铸造蠕墨铸铁玻璃瓶对开模、横浇道、内浇道、下湿砂型、粘土砂湿砂型单一砂、箱外定位销；铸造蠕墨铸铁玻璃瓶对开模连接内浇道连接横浇道设在下湿砂型上，直浇道，出气孔设在上湿砂型上，用粘土砂湿砂型单一砂舂砂造型，上湿砂型与下湿砂型以箱外定位销定位合型；感应电炉熔炼炉料，铸造蠕墨铸铁玻璃瓶对开模材质的铁水是在吊包内用蠕化剂蠕化铁水后再用75硅铁合金孕育剂孕育铁水；铸造蠕墨铸铁玻璃瓶对开模材质的铁水进入直浇道，进入横浇道，进入内浇道后充满铸造蠕墨铸铁玻璃瓶对开模型腔。
蠕化剂是：23稀土硅铁合金。
铸造蠕铁铸铁玻璃瓶对开模的化学成分：C：3.3-3.6％，Si：2.4-2.7％，Mn：≤0.6％，P：≤0.07％，S：≤0.03％，RE：0.02-0.04％，其余为铁和不可避免的杂质。
铸造蠕墨铸铁玻璃瓶对开模石墨形状金相组织是：蠕虫状石墨≥80％。
本发明的有益效果是，铸造蠕墨铸铁玻璃瓶对开模比普通铸铁玻璃瓶对开模使用寿命提高了4倍，提高了经济效益。
附图说明
下面结合附图和实施例对本发明作进一步说明。
附图是铸造蠕墨铸铁玻璃瓶对开模的方法的结构图。
图1是图2的C-C剖视图。
图2是图1的A-A剖视图。
图3是图1的B-B剖视图。
图中1、出气孔，2、直浇道，3、上湿砂型，4、铸造蠕墨铸铁玻璃瓶对开模，5、横浇道，6、内浇道，7、下湿砂型，8、粘土砂湿砂型单一砂，9、箱外定位销。
具体实施方式
附图是铸造蠕墨铸铁水果罐头玻璃瓶对开模的方法的结构图。在图1、2、3中，铸造蠕墨铸铁水果罐头玻璃瓶对开模(4)，瓶高140毫米瓶身直径Φ100毫米瓶口直径Φ80毫米的铸造蠕墨铸铁水果罐头玻璃瓶对开模(4)模样连接内浇道(6)模样连接横浇道(5)模样设在下湿砂型(7)上，用挖砂造型方法及粘土砂湿型单一砂(8)舂砂造下湿砂型(7)；以箱外定位销(9)定位把上湿砂型(3)砂箱放在下湿砂型(7)砂箱上面，在横浇道(5)模样中间位置上放上直浇道(2)模样，铸造蠕墨铸铁水果罐头玻璃瓶对开模(4)模样瓶身中间位置上方放上出气孔(1)模样，并撒分层砂，用粘土砂湿型单一砂(8)舂砂造上湿砂型(3)；拔出直浇道(2)模样和出气孔(1)模样，敞开上湿砂型(3)，起出铸造蠕墨铸铁水果罐头玻璃瓶对开模(4)模样，起出内浇道(6)模样，起出横浇道(5)模样，上湿砂型(3)以箱外定位销(9)定位与下湿砂型合型；炉料配比是：22铸造用生铁70％，回炉料20％，废钢10％；用500Kg中频感应电炉熔炼炉料，铁水温度1500℃±10℃时熔炼10分钟；在吊包内挡坝右侧凹坑内放上占铁水总重量1.5％的粒度25毫米至35毫米的蠕化剂，铁水温度降至1450℃±10℃时，把电炉内三分之二铁水倒入吊包内挡坝左侧凹坑内，蠕化剂在铁水中平稳熔化后搅拌铁水均匀，放入占铁水总重量0.8％的75硅铁合金粒度2至5毫米的孕育剂，向吊包内倒入电炉内剩余的三分之一铁水，把铁水搅拌均匀后扒渣覆盖一层保温材料，用三角试片检查合格后进行浇注，铸造蠕墨铸铁水果罐头玻璃瓶对开模(4)材质的铁水进入直浇道(2)，进入横浇道(5)，进入内浇道(6)后充满铸造蠕墨铸铁水果罐头玻璃瓶对开模(4)型腔。
蠕化剂是：23稀土硅铁合金。
铸造蠕墨铸铁玻璃瓶对开模的化学成分：C：3.3-3.6％，Si：2.4-2.7％，Mn：≤0.4％，P：≤0.07％，S：≤0.03％，RE：0.02-0.04％，其余为铁和不可避免的杂质。
铸造蠕墨铸铁玻璃瓶对开模石墨形状金相组织是：蠕虫状石墨≥80％。

Claims (4)

1.一种铸造蠕墨铸铁玻璃瓶对开模的方法，其特征在于使用出气孔、直浇道、上湿砂型、铸造蠕墨铸铁玻璃瓶对开模、横浇道、内浇道、下湿砂型、粘土砂湿砂型单一砂、箱外定位销；铸造蠕墨铸铁玻璃瓶对开模连接内浇道连接横浇道设在下湿砂型上，直浇道，出气孔设在上湿砂型上，用粘土砂湿砂型单一砂舂砂造型，上湿砂型与下湿砂型以箱外定位销定位合型；感应电炉熔炼炉料，铸造蠕墨铸铁玻璃瓶对开模材质的铁水是在吊包内用蠕化剂蠕化铁水后再用75硅铁合金孕育剂孕育铁水；铸造蠕墨铸铁玻璃瓶对开模材质的铁水进入直浇道，进入横浇道，进入内浇道后充满铸造蠕墨铸铁玻璃瓶对开模型腔。
2.根据权利要求1所述的铸造蠕墨铸铁玻璃瓶对开模的方法，其特征是：蠕化剂是：23稀土硅铁合金。
3.根据权利要求1所述的铸造蠕墨铸铁玻璃瓶对开模的方法，其特征是：铸造蠕墨铸铁玻璃瓶对开模的化学成分：C：3.3-3.6％，Si：2.4-2.7％，Mn：≤0.6％，P：：≤0.07％，S：≤0.03％，RE：0.02-0.04％，其余为铁和不可避免的杂质。
4.根据权利要求1所述的铸造蠕墨铸铁玻璃瓶对开模的方法，其特征是：铸造蠕墨铁玻璃瓶对开模石墨形状金相组织是：蠕虫状石墨≥80％。
CN201310298012.2A 2013-07-05 2013-07-05 铸造蠕墨铸铁玻璃瓶对开模的方法 Pending CN104276743A (zh)