Summary of the invention
The invention provides a kind of COTTON FABRIC smoothing wrinkle finishing agent, effectively can remove the fold of COTTON FABRIC; For this reason, the present invention also provides its preparation method.
The invention provides a kind of COTTON FABRIC smoothing wrinkle finishing agent, described finishing agent is made up of each component of following mass fraction: dioctadecyl dimethyl ammonium chloride 5-8 part, potassium nitrate 3-4 part, polyoxyethylene ether 1-2 part, dimethyl urea 2-3 part, sodium phosphate 3-5 part, Sodium Polyacrylate 6-8 part, Sodium Benzoate 0.8-1.2 part, sodium laurate 0.5-0.8 part, ethanol 10-15 part, distilled water 90-100 part.
Preferably, described finishing agent is made up of each component of following mass fraction: dioctadecyl dimethyl ammonium chloride 6 parts, 3.5 parts, potassium nitrate, polyoxyethylene ether 1.5 parts, dimethyl urea 2.5 parts, sodium phosphate 4 parts, Sodium Polyacrylate 7 parts, Sodium Benzoate 1.0 parts, sodium laurate 0.6 part, ethanol 12 parts, distilled water 95 parts.
The present invention also provides the preparation method of above-mentioned COTTON FABRIC smoothing wrinkle finishing agent, step is as follows: be that the dioctadecyl dimethyl ammonium chloride of formula ratio, dimethyl urea and ethanol are heated to 60-70 DEG C, stir 1-2 hour, after being cooled to 50-55 DEG C, add all the other components of formula ratio, stir 30-50min, after being cooled to room temperature and get final product.
Table 1 is the Contrast on effect before and after application smoothing wrinkle finishing agent process COTTON FABRIC of the present invention.
COTTON FABRIC as can be seen from Table 1 after smoothing wrinkle finishing agent of the present invention process, dry, wet crease recovery angle (degree) increases, and illustrate that the elasticity of fabric improves, smoothing wrinkle performance is good; After soaping, crease recovery angle is substantially constant, illustrates that the washability persistence of fabric smoothing wrinkle is good; And the change of the suspended coefficient of fabric, gas permeability is little, this shows the cotton-spinning fabric after smoothing wrinkle finishing agent of the present invention process, still maintains vertical sense and the gas permeability of fabric.
Detailed description of the invention
Following embodiment is convenient to understand the present invention better, but does not limit the present invention.Experimental technique in following embodiment, if no special instructions, is conventional method.
embodiment 1
The formula of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
Dioctadecyl dimethyl ammonium chloride 6kg, potassium nitrate 3.5kg, polyoxyethylene ether 1.5kg, dimethyl urea 2.5kg, sodium phosphate 4kg, Sodium Polyacrylate 7kg, Sodium Benzoate 1.0kg, sodium laurate 0.6kg, ethanol 12kg, distilled water 95kg.
The preparation method of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
The dioctadecyl dimethyl ammonium chloride of formula ratio, dimethyl urea and ethanol are heated to 65 DEG C, stir 1.5 hours, after being cooled to 52 DEG C, add all the other components of formula ratio, stir 40min, after being cooled to room temperature and get final product.
embodiment 2
The formula of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
Dioctadecyl dimethyl ammonium chloride 5kg, potassium nitrate 3kg, polyoxyethylene ether 1kg, dimethyl urea 2kg, sodium phosphate 5kg, Sodium Polyacrylate 8kg, Sodium Benzoate 1.2kg, sodium laurate 0.5kg, ethanol 10kg, distilled water 100kg.
The preparation method of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
The dioctadecyl dimethyl ammonium chloride of formula ratio, dimethyl urea and ethanol are heated to 60 DEG C, stir 2 hours, after being cooled to 55 DEG C, add all the other components of formula ratio, stir 30min, after being cooled to room temperature and get final product.
embodiment 3
The formula of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
Dioctadecyl dimethyl ammonium chloride 8kg, potassium nitrate 4kg, polyoxyethylene ether 2kg, dimethyl urea 3kg, sodium phosphate 3kg, Sodium Polyacrylate 6kg, Sodium Benzoate 0.8kg, sodium laurate 0.8kg, ethanol 15kg, distilled water 90kg.
The preparation method of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
The dioctadecyl dimethyl ammonium chloride of formula ratio, dimethyl urea and ethanol are heated to 70 DEG C, stir 1 hour, after being cooled to 50 DEG C, add all the other components of formula ratio, stir 50min, after being cooled to room temperature and get final product.
embodiment 4
The formula of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
Dioctadecyl dimethyl ammonium chloride 7kg, potassium nitrate 4kg, polyoxyethylene ether 1.6kg, dimethyl urea 2.7kg, sodium phosphate 3kg, Sodium Polyacrylate 6kg, Sodium Benzoate 0.8kg, sodium laurate 0.9kg, ethanol 13kg, distilled water 98kg.
The preparation method of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
The dioctadecyl dimethyl ammonium chloride of formula ratio, dimethyl urea and ethanol are heated to 68 DEG C, stir 1 hour, after being cooled to 52 DEG C, add all the other components of formula ratio, stir 45min, after being cooled to room temperature and get final product.
embodiment 5
The formula of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
Dioctadecyl dimethyl ammonium chloride 6kg, potassium nitrate 3.4kg, polyoxyethylene ether 1.3kg, dimethyl urea 2.4kg, sodium phosphate 3kg, Sodium Polyacrylate 7kg, Sodium Benzoate 0.8kg, sodium laurate 0.9kg, ethanol 14kg, distilled water 92kg.
The preparation method of COTTON FABRIC smoothing wrinkle finishing agent of the present invention is as follows:
The dioctadecyl dimethyl ammonium chloride of formula ratio, dimethyl urea and ethanol are heated to 62 DEG C, stir 2 hours, after being cooled to 52 DEG C, add all the other components of formula ratio, stir 35min, after being cooled to room temperature and get final product.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.