CN1042641C - Method for production of color antistatic permeable adhesive - Google Patents
Method for production of color antistatic permeable adhesive Download PDFInfo
- Publication number
- CN1042641C CN1042641C CN92108558A CN92108558A CN1042641C CN 1042641 C CN1042641 C CN 1042641C CN 92108558 A CN92108558 A CN 92108558A CN 92108558 A CN92108558 A CN 92108558A CN 1042641 C CN1042641 C CN 1042641C
- Authority
- CN
- China
- Prior art keywords
- add
- added
- color
- components
- uniform mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
With the gradually wide application of electronic computers, the harm of indoor static electricity of computer rooms, etc. to the aspects of computers, element manufacture, device maintenance, automatic control systems, command and control systems, etc. is gradually regarded by people. At present, in various static electricity prevention and treatment methods, a color antistatic permeable adhesive is a material which has decorative color, strong adhesive force and certain antistatic performance and can be directly sprayed or coated on working reference planes. The adhesive becomes a required color antistatic permeable adhesive by that dispersion agents, pigments, fillers and defoamers are orderly added in pure water, benzene-acrylate emulsion film-forming base materials and film-forming auxiliaries are added after the components are mixed evenly, amide class antistatic agents are added after the components are mixed evenly, color paste and defoamers are added through filtration and sanding after the components are mixed evenly, and thickening agents are added to regulate viscosity after the components are mixed evenly.
Description
The present invention relates to a kind of chromatic manufacture method with antistatic permeable adhesive.
Widespread use along with robot calculator, indoor at the computer house that uses robot calculator, operation department, command and control center, electronic equipment maintenance chamber (workshop), automatic assembly line etc., static more and more causes people's attention to the interference and the harm of computer, thereby the electrostatic control becomes an important problem.At present, in order to solve electrostatic harm, guiding static successfully leaks, and the method for employing has the wallpaper of anlistatig floor and anti-electrostatic etc., and these methods all realize by means of certain base material (floor, wallpaper etc.); The conductive fiber material that also has the employing adsorption of metal ions to make on tacryl paper sticks to the method on the metope, leaks with the guiding electrostatic, as the clear 58-5734 of Japanese Patent.Above-mentioned these methods all bother, and technology is complicated.
The objective of the invention is, provide a kind of manufacturing process simple, constructing operation is simple, a kind of not only to have had anti-static function, but also can directly spray or be painted on the working reference plane, strong adhesion and have the antistatic adhesive agent of certain ornamental color.
The manufacture method of color antistatic permeable adhesive of the present invention, be in pure water, to add dispersion agents such as polyacrylate and Sodium hexametaphosphate 99 while stirring in proper order, titanium white powder pigment, fillers such as ultra-fine wollastonite powder, wollastonite powder, process white, talcum powder, OT rod soil, tributyl phosphate defoamers etc. stir; Add benzene-acrylic emulsion film forming base-material, phenylcarbinol and ethylene glycol film coalescence aid, mixing; Add the amides static inhibitor again, after mixing, after filtration and sand milling, add mill base and tributyl phosphate defoamer, mixing; Add the acrylate thickening material again and adjust viscosity.
The manufacture method of color antistatic permeable adhesive of the present invention, its flow process is seen shown in Figure 1.With specific conductivity<100 micro-ohms
-1/ centimetre pure water put into the reactor (2) that has agitator (3), make agitator speed be controlled at 250~400 rev/mins by stirring velocity controller (1), add Sodium hexametaphosphate 99 more successively, churning time is 10~60 minutes, Sodium hexametaphosphate 99 is dissolved fully, open valve (9) then, deposit in the container (14), use as dispersion agent.Afterwards, film coalescence aid ethylene glycol is added in the reactor (2), and the rotating speed of setting agitator (3) is 250~400 rev/mins, adds quantitative amides static inhibitor again and carries out stirring in 15 minutes, solution is mixed fully, open valve (9) then and deposit in another container.Afterwards, add specific conductivity<100 micro-ohms
-1/ centimetre pure water, the rotating speed of setting agitator (3) is 760~960 rev/mins, when stirring, drops into the raw material of formula ratio in order: dispersion agent polyacrylate and Sodium hexametaphosphate 99; As the titanium dioxide of pigment with as ultra-fine wollastonite powder, wollastonite powder, process white, talcum powder, the 0T rod soil of filler; Tributyl phosphate as defoamer.Then, make agitator (3) speed in the reactor in the time of 1300~1500 rev/mins, stirred 30~60 minutes, solution is mixed.Make agitator (3) speed reduce to 760~960 rev/mins again, in reactor, add film forming base-material benzene-acrylic emulsion and film coalescence aid phenylcarbinol and ethylene glycol, restir 5~20 minutes.Afterwards, in reactor, add the amides static inhibitor that has prepared, stirred 5~20 minutes.After treating that solution mixes, open valve (10), the material that stirs is sent into strainer (4), the screen size of filtering net is 80~100 orders in the strainer, material is sent in the sand mill (5) through injection pump (13) again, sand milling materials flow amount is 15~25kg/ branch, and the sand milling time is 40~65 minutes, again the sand milling material is injected toning container (7) through injection pump (12).In the molten device of toning (7), the mill base and the froth breaking tributyl phosphate that add proportional quantity, at this moment, by the stirring controller (11) in the toning container, make agitator speed be adjusted into 40~70 rev/mins, and stirred 30~60 minutes, add the thickening material acrylate again, make soltion viscosity adjust to 20~60 seconds (the coating-4 viscosity meter method by GB1723 is measured).So just make color antistatic permeable adhesive.
After measured, the performance of this adhesive agent is as shown in table 1 below, and the dried coating performance sees Table 2.
Table 1
Performance | Index |
Opacifying power | 250g/m 2 |
Sticking power (surveying) with cross-hatching | 100% |
Viscosity (being coated with-4 viscometer methods by GB1723 measures) | 20~60 seconds |
PH value | 8.5~9.5 |
Solid content | >45% |
Table 2
Performance | Index |
Time of drying, (25 ℃) surface drying was done solid work | <2 hours<24 hours |
The surface insulation resistance value | <10 9Ω |
Water tolerance | >250 hours |
Alkali resistance | >250 hours |
The adhesive agent spraying that will make with aforesaid method or evenly be painted on the working reference plane, through after 24 hours dryings, just form on the working reference plane the required color of one deck, have than strong adhesive force and have filming of good resistance antistatic property.
The synoptic diagram 1. of Fig. 1 color antistatic permeable adhesive manufacturing process stirs controller 2. reactors 3. agitators 4. strainers 5. sand mills 6. sand milling material containers 7. toning containers 8. agitators 9. valves 10. valves 11. and stirs controller 12. injection pumps 13. valves 14. containers
Embodiment:, in reactor, add pure water (specific conductivity<100 micro-ohms for making a certain amount of color antistatic permeable adhesive
-1/ centimetre) 38.20%, making the agitator speed in the reactor is 960 rev/mins, simultaneously, in reactor, add polyacrylate 0.15%, Sodium hexametaphosphate 99 1.00%, titanium dioxide 3.00%, ultra-fine wollastonite powder 10.00%, wollastonite powder 15.00%, process white 10.00%, talcum powder 4.00%, OT rod soil 1.20%, tributyl phosphate 0.05% in order, then, when making agitator speed be 1400 rev/mins, high-speed stirring 45 minutes.Afterwards, when agitator speed is reduced to 960 rev/mins, in reactor, add benzene-acrylic emulsion (press proportional quantity 14.00%), phenylcarbinol 0.35% and ethylene glycol 0.70%, behind reinforced the finishing, stirred 5~10 minutes.Then, in reactor, add the amide containing class static inhibitor (wherein the amides static inhibitor is 62: 38 with the ratio of ethylene glycol) 0.50% that amides static inhibitor and ethylene glycol mix, stirred 10 minutes.It is to filter in the 100 purpose strainers that the material that stirs is sent into the order number.Send filter material to sand mill with injection pump again, sand milling materials flow amount is that 20kg/ branch, sand mill rotating speed are 1400 rev/mins, behind the sand milling 50 minutes, through transition container, with pump the sand milling material is injected the toning container, add 1.25% mill base and 0.05% tributyl phosphate again, and make the agitator speed in the toning container be adjusted into 50 rev/mins, stirred 40 minutes.At last, add 0.55% acrylate, make viscosity adjustment to 20~60 second (the coating-4 viscosity meter method of pressing the GB1723 regulation is measured) of material, just become color antistatic permeable adhesive.
The above-mentioned adhesive agent of spraying on working reference plane, it is chromatic, adhere firmly and have a coating of good electrostatic discharged leaking performance just to become one deck after the drying.
Claims (4)
1. the manufacture method of a color antistatic permeable adhesive is characterized in that, at specific conductivity<100 micro-ohms
-1/ centimetre pure water 38.20% in while stirring order add dispersion agent polyacrylate 0.15%, Sodium hexametaphosphate 99 1%, titanium white powder pigment 3%, the ultra-fine wollastonite powder 10% of filler, wollastonite powder 15%, process white 10%, talcum powder 4%, OT rod soil 1.2% and defoamer tributyl phosphate 0.05%, uniform mixing, add film forming base-material benzene-acrylic emulsion 14% again, film coalescence aid phenylcarbinol 0.35%, with ethylene glycol 0.7% uniform mixing, add again by amides static inhibitor and ethylene glycol mixtures 0.5%, the amides static inhibitor is 62: 38 with the ratio of ethylene glycol in the mixed solution, through uniform mixing, behind filtration and the sand milling, add mill base 1.25% and tributyl phosphate 0.05%, behind the uniform mixing, add thickening material acrylic acid salt again and carry out the viscosity adjustment.
2, the manufacture method of adhesive agent according to claim 1 is characterized in that, compound adds amides static inhibitor and ethylene glycol mixtures and behind uniform mixing, filter, and the order number of filter screen is 80~100 orders.
3, the manufacture method of adhesive agent according to claim 1 is characterized in that, compound also will carry out the sand mill sand milling after filtering, and the flow of sand milling material is 15~25 kilograms/minute, and the sand milling time is 40~65 minutes.
4, the manufacture method of caking agent according to claim 1 is characterized in that, compound need add the thickening material acrylate at last and adjust viscosity, and the control indexes of viscosity was 20~60 seconds (pressing coating-4 viscosity meter method mensuration among the GB1723).