CN104264164A - Nut surface treatment process - Google Patents
Nut surface treatment process Download PDFInfo
- Publication number
- CN104264164A CN104264164A CN201410416653.8A CN201410416653A CN104264164A CN 104264164 A CN104264164 A CN 104264164A CN 201410416653 A CN201410416653 A CN 201410416653A CN 104264164 A CN104264164 A CN 104264164A
- Authority
- CN
- China
- Prior art keywords
- nut
- surface treatment
- mass concentration
- hydrochloric acid
- caustic soda
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A nut surface treatment process is disclosed. The process comprises following steps of: 1) rinsing with tap water, and drying by blowing by an air inducing device; 2) dipping with gasoline for 2-3 h; 3) diluting oil removing powder with water in an oil removing barrel according to a weight ratio of 3:1, adding a nut into the oil removing barrel, and dipping for 30-40 min; 4) cleaning at 20-40 DEG C for 2-3 times with a caustic soda solution having a mass concentration of 0.2-0.5%, and cleaning at 20-40 DEG C for 4-5 times with a hydrochloric acid solution having a mass concentration of 0.2-0.5%; and 5) taking the nut out and airing naturally for 20-30 min. By the manner, contaminants on the surface of the nut can be cleaned rapidly and conveniently, and the decontamination effects are good.
Description
Technical field
The present invention relates to standardized component field, particularly relate to a kind of nut process of surface treatment.
Background technology
Nut be screwed in bolt or screw rod together be used for the part that plays the role of fastening, be widely used in machine industry.Mobile phone is requisite means of communication in people's daily life, more and more to frivolous development, as the nut in mobile phone when proof strength also towards frivolous development, the performance in this respect of titanium nut is very good, is more and more subject to the welcome of mobile phone manufacturing.But existing titanium nut surface treatment aspect is after processing unsatisfactory, and the treatment time is long, reduces working efficiency; The step control of process is poor, reduces the work-ing life of titanium nut.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of nut process of surface treatment, can solve the problem.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of nut process of surface treatment, comprise the steps:
1) use tap water to carry out rinsing, then use air inducing equipment to dry up;
2) gasoline is used to carry out immersion 2-3 hour;
3) at the weight ratio dilute with water degreasing powder according to 3:1 in oil drum, then nut is put into except oil drum, invade bubble 30-40 minute;
4) be that the caustic soda soln of 0.2-0.5% cleans 2-3 time at the temperature of 20-40 DEG C by mass concentration, then be that the hydrochloric acid soln of 0.2-0.5% is cleaning 4-5 time at the temperature of 20-40 DEG C by mass concentration;
5) take out nature and dry 20-30 minute.
In a preferred embodiment of the present invention, the optimum concn of described caustic soda soln is 0.4%, and the optimum concn of hydrochloric acid soln is 0.4%.
In a preferred embodiment of the present invention, the Best Times that bubble invaded by described gasoline is 30 minutes.
The invention has the beneficial effects as follows: the present invention conveniently can clean the pollutent of the nut table people, and clean effect is good.
Embodiment
A kind of nut process of surface treatment, comprises the steps:
1) use tap water to carry out rinsing, then use air inducing equipment to dry up;
2) gasoline is used to carry out immersion 2-3 hour;
3) at the weight ratio dilute with water degreasing powder according to 3:1 in oil drum, then nut is put into except oil drum, invade bubble 30-40 minute;
4) be that the caustic soda soln of 0.2-0.5% cleans 2-3 time at the temperature of 20-40 DEG C by mass concentration, then be that the hydrochloric acid soln of 0.2-0.5% is cleaning 4-5 time at the temperature of 20-40 DEG C by mass concentration;
5) take out nature and dry 20-30 minute.
The optimum concn of described caustic soda soln is 0.4%, and the optimum concn of hydrochloric acid soln is 0.4%.
The Best Times that bubble invaded by described gasoline is 30 minutes.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (3)
1. nut process of surface treatment, is characterized in that, comprises the steps:
1) use tap water to carry out rinsing, then use air inducing equipment to dry up;
2) gasoline is used to carry out immersion 2-3 hour;
3) at the weight ratio dilute with water degreasing powder according to 3:1 in oil drum, then nut is put into except oil drum, invade bubble 30-40 minute;
4) be that the caustic soda soln of 0.2-0.5% cleans 2-3 time at the temperature of 20-40 DEG C by mass concentration, then be that the hydrochloric acid soln of 0.2-0.5% is cleaning 4-5 time at the temperature of 20-40 DEG C by mass concentration;
5) take out nature and dry 20-30 minute.
2. nut process of surface treatment according to claim 1, is characterized in that, the optimum concn of described caustic soda soln is 0.4%, and the optimum concn of hydrochloric acid soln is 0.4%.
3. nut process of surface treatment according to claim 1, is characterized in that, the Best Times that bubble invaded by described gasoline is 30 minutes.