CN104263108A - 一种防腐杀菌涂料 - Google Patents

一种防腐杀菌涂料 Download PDF

Info

Publication number
CN104263108A
CN104263108A CN201410451798.1A CN201410451798A CN104263108A CN 104263108 A CN104263108 A CN 104263108A CN 201410451798 A CN201410451798 A CN 201410451798A CN 104263108 A CN104263108 A CN 104263108A
Authority
CN
China
Prior art keywords
parts
minute
add
monomer
corrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410451798.1A
Other languages
English (en)
Inventor
孙巨福
戴宇钧
祝盆鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianchang Julong Car and Ship Coating Co Ltd
Original Assignee
Tianchang Julong Car and Ship Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianchang Julong Car and Ship Coating Co Ltd filed Critical Tianchang Julong Car and Ship Coating Co Ltd
Priority to CN201410451798.1A priority Critical patent/CN104263108A/zh
Publication of CN104263108A publication Critical patent/CN104263108A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种防腐杀菌涂料，它是由下述重量份的原料组成的：乳酸甲氧苄啶0.7-1、聚甲醛2-3、聚磷酸铵2-3、松节油0.6-1、伊利石粉6-8、β-羟烷基酰胺1-2、2-溴-4-甲基苯酚1-2、沉淀白炭黑6-10、交联剂TAC0.5-1、二异氰酸酯0.4-1、苯乙烯140-200、环氧大豆油2-3、去离子水500-600、丙烯酸异辛酯140-200、过硫酸钠3-6、OP-105-7、粘结助剂4-5；本发明的涂料各成分复配合理，相容性好，具有很好的防腐抗菌效果，本发明的涂料粘结性强，与基材的附着力好，耐候性强，综合性能优越。

Description

一种防腐杀菌涂料
技术领域
    本发明主要涉及涂料领域，尤其涉及一种防腐杀菌涂料。
背景技术
    涂于物体表面能形成具有保护、装饰或特殊性能(如绝缘、防腐、标志等)的固态涂膜的一类液体或固体材料的总称，包括油(性)漆、水性漆、粉末涂料。漆是可流动的液体涂料，包括油(性)漆及水性漆。油漆是以有机溶剂为介质或高固体、无溶剂的油性漆。水性漆是可用水溶解或用水分散的涂料。涂料作为家庭装修的主材之一，在装饰装修中占的比例较大，购买涂料的合格与否直接影响到整体装修效果和居室的环境，有时甚至会对人体的健康产生极大的危害。目前随着各种各样涂料的产生，对涂料的品质要求也不断提高，而不断提高涂料质量对于建筑、生活都可以起到很大的帮助作用。
发明内容
本发明目的就是提供一种防腐杀菌涂料。
本发明是通过以下技术方案实现的：
一种防腐杀菌涂料，其特征在于它是由下述重量份的原料组成的：
乳酸甲氧苄啶0.7-1、聚甲醛2-3、聚磷酸铵2-3、松节油0.6-1、伊利石粉6-8、β- 羟烷基酰胺1-2、2-溴-4-甲基苯酚1-2、沉淀白炭黑6-10、交联剂 TAC0.5-1、二异氰酸酯0.4-1、苯乙烯140-200、环氧大豆油2-3、去离子水500-600、丙烯酸异辛酯140-200、过硫酸钠3-6、OP-10 5-7、粘结助剂4-5；
所述的粘结助剂是由下述重量份的各原料组成的：
铝溶胶20-30、硫酸铝铵1-3、羊毛脂1-2、聚乙二醇二甲基丙烯酸酯0.6-1、无水乙醇3-4、丙烯酸异辛酯2-4、过硫酸钾2-3、乳化剂OP-100.5-1、香樟木微粉2-4、去离子水15-20；
将无水乙醇加热到70-75℃，加入羊毛脂，搅拌均匀，得醇脂溶液；
将香樟木微粉加入到铝溶胶中，加入聚乙二醇二甲基丙烯酸酯，升高温度为55-60℃，100-200转/分搅拌分散3-5分钟，得分散液；
将过硫酸钾与丙烯酸异辛酯混合，在60-70℃下搅拌混合2-3分钟，加入分散液，搅拌至常温，加入上述醇脂溶液，60-100转/分搅拌混合5-10分钟，加入剩余各原料，200-400转/分搅拌分散3-5分钟，即得所述粘结助剂。
一种防腐杀菌涂料的制备方法，其特征在于包括以下步骤：
（1）取上述苯乙烯、丙烯酸异辛酯、环氧大豆油混合，得单体a；
（2）取OP-10，加入上述去离子水重量的30-40%，搅拌均匀后加入乳酸甲氧苄啶，在50-60℃保温搅拌3-5分钟，冷却至常温，得预乳液；
（3）取过硫酸钠，加入剩余去离子水重量的10-20%，搅拌均匀，得引发剂溶液；
（4）取上述单体a重量的70-80%、预乳液重量的40-50%、引发剂溶液重量的50-60%，混合，加入1,3-二溴-5,5-二甲基海因，在75-80℃下保温搅拌10-20分钟，得预混单体；
（5）将剩余的单体a与聚磷酸铵、松节油混合，升高温度为50-60℃，70-100转/分搅拌分散3-6分钟，与剩余的预乳液、剩余的引发剂溶液混合，70-90℃下保温搅拌30-50分钟，滴加上述预混单体，滴加时间为2-3小时，滴加完毕后在80-85℃下保温2-3小时，降低温度至40-50℃，调节pH 值至7-8，用200-250 目过滤筛过滤；
（6）将上述步骤（5）得到的物料与剩余各原料混合，800-1200转/分搅拌分散20-30分钟，即得所述防腐杀菌涂料。
本发明的优点是：
    本发明的涂料各成分复配合理，相容性好，具有很好的防腐抗菌效果，本发明的涂料粘结性强，与基材的附着力好，耐候性强，综合性能优越。本发明的粘结助剂中加入的香樟木微粉具有良好的抗磨性、热稳定性好化学稳定性，铝溶胶与硫酸铝铵、羊毛脂、丙烯酸异辛酯、过硫酸钾混合，具有优异的粘结性能，可以增强涂层表面抗性和稳定性。
具体实施方式
实施例1
一种防腐杀菌涂料，其特征在于它是由下述重量份的原料组成的：
乳酸甲氧苄啶0.7、聚甲醛2、聚磷酸铵3、松节油0.6、伊利石粉6、β- 羟烷基酰胺1、2-溴-4-甲基苯酚1、沉淀白炭黑10、交联剂 TAC0.5、二异氰酸酯0.4、苯乙烯200、环氧大豆油2、去离子水600、丙烯酸异辛酯200、过硫酸钠6、OP-10 5、粘结助剂5；
所述的粘结助剂是由下述重量份的各原料组成的：
铝溶胶30、硫酸铝铵1、羊毛脂1、聚乙二醇二甲基丙烯酸酯0.6、无水乙醇4、丙烯酸异辛酯4、过硫酸钾3、乳化剂OP-100.5、香樟木微粉2、去离子水20；
将无水乙醇加热到75℃，加入羊毛脂，搅拌均匀，得醇脂溶液；
将香樟木微粉加入到铝溶胶中，加入聚乙二醇二甲基丙烯酸酯，升高温度为60℃，200转/分搅拌分散3分钟，得分散液；
将过硫酸钾与丙烯酸异辛酯混合，在70℃下搅拌混合3分钟，加入分散液，搅拌至常温，加入上述醇脂溶液，100转/分搅拌混合10分钟，加入剩余各原料，400转/分搅拌分散5分钟，即得所述粘结助剂。
一种防腐杀菌涂料的制备方法，其特征在于包括以下步骤：
（1）取上述苯乙烯、丙烯酸异辛酯、环氧大豆油混合，得单体a；
（2）取OP-10，加入上述去离子水重量的40%，搅拌均匀后加入乳酸甲氧苄啶，在60℃保温搅拌5分钟，冷却至常温，得预乳液；
（3）取过硫酸钠，加入剩余去离子水重量的20%，搅拌均匀，得引发剂溶液；
（4）取上述单体a重量的80%、预乳液重量的50%、引发剂溶液重量的60%，混合，加入1,3-二溴-5,5-二甲基海因，在80℃下保温搅拌20分钟，得预混单体；
（5）将剩余的单体a与聚磷酸铵、松节油混合，升高温度为60℃，100转/分搅拌分散3分钟，与剩余的预乳液、剩余的引发剂溶液混合，90℃下保温搅拌50分钟，滴加上述预混单体，滴加时间为3小时，滴加完毕后在85℃下保温2小时，降低温度至50℃，调节pH 值至8，用250 目过滤筛过滤；
（6）将上述步骤（5）得到的物料与剩余各原料混合，1200转/分搅拌分散30分钟，即得所述防腐杀菌涂料。
性能测试：
延伸率：≥300％ ；
不透水性：0.3MPa( 一个小时不透水)。

Claims (2)

1.一种防腐杀菌涂料，其特征在于它是由下述重量份的原料组成的：
乳酸甲氧苄啶0.7-1、聚甲醛2-3、聚磷酸铵2-3、松节油0.6-1、伊利石粉6-8、β- 羟烷基酰胺1-2、2-溴-4-甲基苯酚1-2、沉淀白炭黑6-10、交联剂 TAC0.5-1、二异氰酸酯0.4-1、苯乙烯140-200、环氧大豆油2-3、去离子水500-600、丙烯酸异辛酯140-200、过硫酸钠3-6、OP-10 5-7、粘结助剂4-5；
所述的粘结助剂是由下述重量份的各原料组成的：
铝溶胶20-30、硫酸铝铵1-3、羊毛脂1-2、聚乙二醇二甲基丙烯酸酯0.6-1、无水乙醇3-4、丙烯酸异辛酯2-4、过硫酸钾2-3、乳化剂OP-100.5-1、香樟木微粉2-4、去离子水15-20；
将无水乙醇加热到70-75℃，加入羊毛脂，搅拌均匀，得醇脂溶液；
将香樟木微粉加入到铝溶胶中，加入聚乙二醇二甲基丙烯酸酯，升高温度为55-60℃，100-200转/分搅拌分散3-5分钟，得分散液；
将过硫酸钾与丙烯酸异辛酯混合，在60-70℃下搅拌混合2-3分钟，加入分散液，搅拌至常温，加入上述醇脂溶液，60-100转/分搅拌混合5-10分钟，加入剩余各原料，200-400转/分搅拌分散3-5分钟，即得所述粘结助剂。
2.一种如权利要求1所述的防腐杀菌涂料的制备方法，其特征在于包括以下步骤：
（1）取上述苯乙烯、丙烯酸异辛酯、环氧大豆油混合，得单体a；
（2）取OP-10，加入上述去离子水重量的30-40%，搅拌均匀后加入乳酸甲氧苄啶，在50-60℃保温搅拌3-5分钟，冷却至常温，得预乳液；
（3）取过硫酸钠，加入剩余去离子水重量的10-20%，搅拌均匀，得引发剂溶液；
（4）取上述单体a重量的70-80%、预乳液重量的40-50%、引发剂溶液重量的50-60%，混合，加入1,3-二溴-5,5-二甲基海因，在75-80℃下保温搅拌10-20分钟，得预混单体；
（5）将剩余的单体a与聚磷酸铵、松节油混合，升高温度为50-60℃，70-100转/分搅拌分散3-6分钟，与剩余的预乳液、剩余的引发剂溶液混合，70-90℃下保温搅拌30-50分钟，滴加上述预混单体，滴加时间为2-3小时，滴加完毕后在80-85℃下保温2-3小时，降低温度至40-50℃，调节pH 值至7-8，用200-250 目过滤筛过滤；
（6）将上述步骤（5）得到的物料与剩余各原料混合，800-1200转/分搅拌分散20-30分钟，即得所述防腐杀菌涂料。
CN201410451798.1A 2014-09-05 2014-09-05 一种防腐杀菌涂料 Pending CN104263108A (zh)