CN104262857A - Highly wear-resistant PVC (Polyvinyl Chloride) sole material and manufacturing method thereof - Google Patents
Highly wear-resistant PVC (Polyvinyl Chloride) sole material and manufacturing method thereof Download PDFInfo
- Publication number
- CN104262857A CN104262857A CN201410566334.5A CN201410566334A CN104262857A CN 104262857 A CN104262857 A CN 104262857A CN 201410566334 A CN201410566334 A CN 201410566334A CN 104262857 A CN104262857 A CN 104262857A
- Authority
- CN
- China
- Prior art keywords
- sole material
- high abrasion
- pvc
- pvc sole
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a highly-wear-resistant PVC (Polyvinyl Chloride) sole material which comprises the following components in parts by weight: 50-70 parts of PVC, 0.5-2 parts of nano silicon dioxide, 0.5-2 parts of silane coupling agent, 0.5-5 part of vulcanizing agent, 0.5-5 part of promoter, 1-20 parts of plasticizer, 0.1-3 part of anti-aging agent and 5-15 parts of carbon black. The invention also discloses a manufacturing method of the highly wear-resistant PVC sole material. The wear resistance of the PVC sole material provided by the invention is very good.
Description
Technical field:
The present invention relates to a kind of material for sole of shoe, particularly relate to a kind of high abrasion PVC sole material and manufacture method thereof.
Background technology:
PVC and Polyvinylchlorid, its major ingredient is that polyvinyl chloride gathers hydrogen ethene, and chemical stability is very high, has good plasticity-.The electrical insulating property of PVC is excellent, generally can not burn, and flame can burn and release HCl, but leaves flame namely from putting out, and is a kind of " self-extinguishing ", " flame retardancy " material.Based on These characteristics, PVC is mainly for the production of fields such as section bar, profiled material, pipe part, sheet material, sheet material, cable sheath, hard or soft pipe, blood transfusion equipment, film, material for sole of shoe.The material for sole of shoe be made up of PVC has excellent mechanical property, the advantage such as easy to process and with low cost, therefore in the ratio that material for sole of shoe market share is larger, but common PVC sole material wear-resistant performance is not fine, can not meet the requirement that modern humans is more and more higher to wear resisting property well.
Summary of the invention:
The technical problem to be solved in the present invention is to provide a kind of high abrasion PVC sole material, has extraordinary wear resisting property.
For solving the problems of the technologies described above, technical scheme of the present invention is:
A kind of high abrasion PVC sole material, its weight part consists of:
Preferably, vulcanizing agent of the present invention is sulphur.
Preferably, promotor of the present invention is promotor TRA or altax.
Preferably, softening agent of the present invention is at least one in dioctyl phthalate (DOP), dibutyl phthalate, dioctyl sebacate.
Preferably, anti-aging agent of the present invention is antioxidant 264.
Another technical problem that the present invention will solve is to provide the manufacture method of above-mentioned high abrasion PVC sole material.
For solving the problems of the technologies described above, technical scheme is:
A manufacture method for high abrasion PVC sole material, comprises the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.
Therefore compared with prior art, the present invention has following beneficial effect:
The volume effect of nano silicon and quantum tunneling effect make it produce osmosis, macromolecular compound can be goed deep into, overlap with its electronic cloud, form reticulated structure, thus increasing substantially mechanical strength, the wear resisting property of macromolecular material, the material for sole of shoe adding nano silicon is provided with good wear resisting property; But nano-silicon nitride self is easily assembled, also there is stronger hydrogen bond action, therefore its dispersiveness in elastomeric material is poor, so the present invention carries out surface modification by silane coupling agent to it, effectively can improve its dispersiveness in PVC rubber, improve wear resisting property further.
Embodiment:
Describe the present invention in detail below in conjunction with specific embodiment, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as a limitation of the invention.
Embodiment 1
A kind of high abrasion PVC sole material, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.
Embodiment 2
A kind of high abrasion PVC sole material, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.
Embodiment 3
A kind of high abrasion PVC sole material, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.
Embodiment 4
A kind of high abrasion PVC sole material, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.
Embodiment 5
A kind of high abrasion PVC sole material, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.
Embodiment 6
A kind of high abrasion PVC sole material, its weight part consists of:
Its manufacture method comprises the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.
Above-described embodiment is illustrative principle of the present invention and effect thereof only, but not for limiting the present invention.Any person skilled in the art scholar all without prejudice under spirit of the present invention and category, can modify above-described embodiment or changes.Therefore, such as have in art usually know the knowledgeable do not depart from complete under disclosed spirit and technological thought all equivalence modify or change, must be contained by claim of the present invention.
Claims (6)
1. a high abrasion PVC sole material, is characterized in that: its weight part consists of:
2. a kind of high abrasion PVC sole material according to claim 1, is characterized in that: described vulcanizing agent is sulphur.
3. a kind of high abrasion PVC sole material according to claim 1, is characterized in that: described promotor is promotor TRA or altax.
4. a kind of high abrasion PVC sole material according to claim 1, is characterized in that: described softening agent is at least one in dioctyl phthalate (DOP), dibutyl phthalate, dioctyl sebacate.
5. a kind of high abrasion PVC sole material according to claim 1, is characterized in that: described anti-aging agent is antioxidant 264.
6. the manufacture method of a kind of high abrasion PVC sole material according to Claims 1 to 5 any one, is characterized in that: comprise the following steps:
(1) nano silicon is dissolved in stirring heating in dehydrated alcohol, drips silane coupling agent, take out after stirring and dry, after removing solvent, obtain modified manometer silicon dioxide powder;
(2) PVC and modified manometer silicon dioxide powder are put into rubber mixing machine mixing, then other components in formula are added mixing, obtain compound;
(3) compound that step (2) obtains is added extruding pelletization in forcing machine, obtain high abrasion PVC sole material.