CN104261754A - Wall thermal insulation material produced by building material waste residue and preparation method thereof - Google Patents
Wall thermal insulation material produced by building material waste residue and preparation method thereof Download PDFInfo
- Publication number
- CN104261754A CN104261754A CN201410436226.6A CN201410436226A CN104261754A CN 104261754 A CN104261754 A CN 104261754A CN 201410436226 A CN201410436226 A CN 201410436226A CN 104261754 A CN104261754 A CN 104261754A
- Authority
- CN
- China
- Prior art keywords
- waste residue
- parts
- add
- building materials
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a wall thermal insulation material produced by building material waste residue. The wall thermal insulation material is prepared from the following materials in parts by weight: 5-15 parts of modified building material waste residue, 80-100 parts of white cement, 70-90 parts of pumice, 10-15 parts of attapulgite powder, 2-4 parts of bamboo charcoal powder, 1-2 parts of monoalkyl ether phosphate, 10-15 parts of silicone acrylic emulsion, 1-2 parts of sodium oxalate, 1-3 parts of mannitol, 0.5-1 part of maltitol and 2-4 parts of hydroxypropyl methyl cellulose. The wall thermal insulation material is produced by reasonably recycling the building material waste residue, and the purposes of saving energy and protecting environment are achieved while the thermal insulation effect is ensured.
Description
Technical field
The present invention relates to building material field, be specifically related to wall heat insulation material of a kind of building materials waste residue production and preparation method thereof.
Background technology
Wall heat insulation material is as affecting building energy conservation important factor, and its development & application has more and more been subject to the most attention of countries in the world.Reasonable development wall heat insulation material, the waste residue waste material that the building industry that is effectively recycled produces, can save materials for wall in a large number, can reach again and economize on resources, and reduces the object of environmental pollution, meets the policy of national energy-saving environmental protection.
Summary of the invention
The object of this invention is to provide the wall heat insulation material that a kind of building materials waste residue is produced.
The present invention is achieved by the following technical solutions:
The wall heat insulation material that building materials waste residue is produced, it is obtained by the raw material of following weight parts:
Modification building materials waste residue 5-15, white cement 80-100, float stone 70-90, attapulgite powder 10-15, bamboo charcoal powder 2-4, monoalky lether phosphoric acid ester 1-2, organosilicon crylic acid latex 10-15, sodium oxalate 1-2, N.F,USP MANNITOL 1-3, maltose alcohol 0.5-1, hydroxypropyl methyl cellulose ether 2-4;
Modification building materials waste residue is made up of the raw material of following weight part:
Ceramic waste residue 5-10, marble waste residue 10-15, boron gypsum 1-2, whiteruss 0.5-1.5, oleic acid 0.2-0.5, tri-isopropanolamine 1-2, sodium tartrate 1-3, aluminate coupling agent 0.2-0.5;
The preparation method of modification building materials waste residue is:
By 800-1000 DEG C of calcining 2-4h after the mixing of ceramic waste residue, marble waste residue and boron gypsum, add appropriate 4-6% acetum after cooling, add tri-isopropanolamine and sodium tartrate, 200-400r/min stirs 1-2h, after dry, grinding evenly, cross 50-100 mesh sieve, then add aluminate coupling agent, 100-150 DEG C, 400-600r/min stirs 20-40min, add whiteruss and oleic acid, stir 20-40min under similarity condition, to obtain final product;
A preparation method for the wall heat insulation material that building materials waste residue is produced, comprises the following steps:
(1) 800-1000r/min after the mixing of organosilicon crylic acid latex, monoalky lether phosphoric acid ester and hydroxypropyl methyl cellulose ether is stirred 15-30min, after spraying dry, obtain active powder;
(2) by 400-600 DEG C of calcining 1-2h after attapulgite powder and bamboo charcoal powder mixing, add N.F,USP MANNITOL, maltose alcohol and sodium oxalate after cooling, after mixing, grinding evenly, crosses 100-200 mesh sieve, and add active powder and all the other raw materials, packing after stirring, to obtain final product.
Advantage of the present invention is:
1. rationally recycle building materials waste residue and produce wall heat insulation material, economize on resources, reduce the hidden danger of environmental pollution and ecological damage;
2. water-fast, good corrosion resistance, long service life, good weatherability;
3. constant product quality, is applicable to multiple environment for use.
Embodiment
Non-limiting examples of the present invention is as follows:
Embodiment 1
The wall heat insulation material that building materials waste residue is produced, is prepared from by the component raw material of following weight (kg):
Modification building materials waste residue 10, white cement 90, float stone 80, attapulgite powder 12, bamboo charcoal powder 3, monoalky lether phosphoric acid ester 1.5, organosilicon crylic acid latex 12, sodium oxalate 1.5, N.F,USP MANNITOL 2, maltose alcohol 0.8, hydroxypropyl methyl cellulose ether 3;
Wherein, modification building materials waste residue is made up of the raw material of following weight (kg):
Ceramic waste residue 7, marble waste residue 12, boron gypsum 1.5, whiteruss 1, oleic acid 0.3, tri-isopropanolamine 1.5, sodium tartrate 2, aluminate coupling agent 0.4;
The preparation method of modification building materials waste residue:
By rear for the mixing of ceramic waste residue, marble waste residue and boron gypsum 800 DEG C of calcining 3h, add appropriate 4% acetum after cooling, add tri-isopropanolamine and sodium tartrate, 200r/min stirs 2h, after dry, grinding evenly, cross 100 mesh sieves, then add aluminate coupling agent, 100 DEG C, 600r/min stirs 30min, add whiteruss and oleic acid, stir 30min under similarity condition, to obtain final product.
The preparation method of the wall heat insulation material that building materials waste residue is produced comprises the following steps:
(1) 1000r/min after the mixing of organosilicon crylic acid latex, monoalky lether phosphoric acid ester and hydroxypropyl methyl cellulose ether is stirred 15min, after spraying dry, obtain active powder;
(2) by attapulgite powder and the rear 400 DEG C of calcining 2h of bamboo charcoal powder mixing, add N.F,USP MANNITOL, maltose alcohol and sodium oxalate after cooling, after mixing, grinding evenly, crosses 100 mesh sieves, and add active powder and all the other raw materials, packing after stirring, to obtain final product.
Embodiment is dry powder material, and need add water at the construction field (site) during use is modulated into slip, can construct.
Carry out product performance test according to DB34/T1279-2010, the test result of above-mentioned enforcement is as follows:
Dry apparent density (kg/m
3): 283;
Linear shrinkage (%): 0.15;
Ultimate compression strength (MPa): 0.97;
Cohesive strength (KPa): 85;
Thermal conductivity (w/m ﹒ k): 0.062;
Coefficient of softening: 0.63.
Claims (2)
1. a wall heat insulation material for building materials waste residue production, it is characterized in that, it is obtained by the raw material of following weight parts:
Modification building materials waste residue 5-15, white cement 80-100, float stone 70-90, attapulgite powder 10-15, bamboo charcoal powder 2-4, monoalky lether phosphoric acid ester 1-2, organosilicon crylic acid latex 10-15, sodium oxalate 1-2, N.F,USP MANNITOL 1-3, maltose alcohol 0.5-1, hydroxypropyl methyl cellulose ether 2-4;
Described modification building materials waste residue is made up of the raw material of following weight part:
Ceramic waste residue 5-10, marble waste residue 10-15, boron gypsum 1-2, whiteruss 0.5-1.5, oleic acid 0.2-0.5, tri-isopropanolamine 1-2, sodium tartrate 1-3, aluminate coupling agent 0.2-0.5;
The preparation method of described modification building materials waste residue is:
By 800-1000 DEG C of calcining 2-4h after the mixing of ceramic waste residue, marble waste residue and boron gypsum, add appropriate 4-6% acetum after cooling, add tri-isopropanolamine and sodium tartrate, 200-400r/min stirs 1-2h, after dry, grinding evenly, cross 50-100 mesh sieve, then add aluminate coupling agent, 100-150 DEG C, 400-600r/min stirs 20-40min, add whiteruss and oleic acid, stir 20-40min under similarity condition, to obtain final product.
2. the preparation method of the wall heat insulation material of a kind of building materials waste residue production according to claim 1, is characterized in that, comprise the following steps:
(1) 800-1000r/min after the mixing of organosilicon crylic acid latex, monoalky lether phosphoric acid ester and hydroxypropyl methyl cellulose ether is stirred 15-30min, after spraying dry, obtain active powder;
(2) by 400-600 DEG C of calcining 1-2h after attapulgite powder and bamboo charcoal powder mixing, add N.F,USP MANNITOL, maltose alcohol and sodium oxalate after cooling, after mixing, grinding evenly, crosses 100-200 mesh sieve, and add active powder and all the other raw materials, packing after stirring, to obtain final product.