CN104259431A - 一种三螺杆泵铜铝复合衬套低压铸造工艺 - Google Patents

一种三螺杆泵铜铝复合衬套低压铸造工艺 Download PDF

Info

Publication number
CN104259431A
CN104259431A CN201410406860.5A CN201410406860A CN104259431A CN 104259431 A CN104259431 A CN 104259431A CN 201410406860 A CN201410406860 A CN 201410406860A CN 104259431 A CN104259431 A CN 104259431A
Authority
CN
China
Prior art keywords
copper
screw pump
aluminum compound
pressure casting
casting process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410406860.5A
Other languages
English (en)
Other versions
CN104259431B (zh
Inventor
乐文欢
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Nade Metal Products Co., Ltd.
Original Assignee
乐文欢
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 乐文欢 filed Critical 乐文欢
Priority to CN201410406860.5A priority Critical patent/CN104259431B/zh
Publication of CN104259431A publication Critical patent/CN104259431A/zh
Application granted granted Critical
Publication of CN104259431B publication Critical patent/CN104259431B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种螺杆泵铜铝复合衬套铸造工艺，特指一种三螺杆泵铜铝复合衬套低压铸造工艺，工艺步骤如下：首先根据需求把铜芯浇铸好，再根据铝衬套的需要开好相应的模具，并把模具安装在低压铸造机上，接着把浇铸好的铜芯放在烘箱内加热，加热后的铜芯置在铝衬套的模具内固定，压入铝液并通过低压铸造机保压，最后脱模，成型，成型后的衬套精度高、次品少，并且整体工艺也较为简单。

Description

一种三螺杆泵铜铝复合衬套低压铸造工艺
技术领域
本发明涉及一种螺杆泵铜铝复合衬套铸造工艺，特指一种三螺杆泵铜铝复合衬套低压铸造工艺。 
背景技术
在螺杆泵制造领域，复合材料的衬套以较低的成本逐渐取代了全铜材质的衬套，但在制造过程中，由于铜铝的熔点不一样，收缩率不同，很难做到紧密结合，而衬套又是螺杆泵的重要部件，精密度要求高，铜芯内部需要高速旋转，且要耐磨和耐腐蚀，所以铜和铝一定要结合很精密，因此他的高效生产一直没有解决，现在普遍采用的是翻砂铸造工艺，缺点是铜铝结合不精密，气孔多，次品率高，尺寸差异大，精加工加工量大，外观不标准，最重要的一点是材质达不到标准，以至于产品所要求的耐磨耐腐蚀性能也达不到。 
发明内容
本发明所要解决的技术问题是提供一种加工简便，铸件合格率高，外观漂亮，精密度高，产品所要求的机械性能和力学性能都达标，单个铸件成本省60％的螺杆泵衬套铸造工艺。 
为达到上述目的本发明提供一种低压铸造工艺：首先根据需求把铜芯浇铸好，再根据铝衬套的需要开好相应的模具，并把模具安装在低压铸造机上，接着把浇铸好的铜芯放在烘箱内加热，加热后的铜芯置在铝衬套的模具内固定，压入铝液并通过低压铸造机保压，最后脱模，成型。 
在加工小号衬套时，铜芯恒温至500-600度，铝液温度控制在660-720度，压力控制在1.5MP，保压时间是10-15分钟。 
在加工中号衬套时，铜芯恒温至400-500度，铝液温度控制在700-730度， 压力控制在2MP，保压时间是15-20分钟。 
在加工大号衬套时，铜芯恒温至300-400度，铝液温度控制在730-780度，压力控制在3MP，保压时间是20分钟。 
作为优选，铜铝复合衬套在其浇铸好后，只有在铝衬套顶部到三分之二处是置有铜芯的。 
与现有的浇铸工艺相比，本发明采用低压铸造机、烘箱和模具，通过不同型号的衬套采用不同的温度、压力、保压时间确保其质量，工艺也较为简单，而且现在一般的开模精度都较高，能很好的保证衬套精度。 
具体实施方式
下面通过实施例，对本发明的技术方案作进一步说明。 
权利要求和发明内容中提到的小号衬套参数为：长度200-300CM，直径100-150CM，中号衬套参数为：长度300到400CM，直径150-250CM，大号衬套参数为：长度400CM以上，直径250CM以上。 
实施例1：当加工小号的三螺杆铜铝复合衬套时，首先根据需求把铜芯浇铸好，再根据铝衬套的需要开好相应的模具，并把模具安装在低压铸造机上，接着把浇铸好的铜芯放在烘箱内加热，恒温到600度的铜芯置在铝衬套的模具内固定，压入660度的铝液并通过低压铸造机保压10分钟，保压压力在1.5MP，最后脱模，成型。 
实施例2：加工中号的三螺杆铜铝复合衬套时只需把铜芯恒温至500度，铝液温度控制在720度，压力控制在2MP，保压时间是15分钟。 
实施例3：加工大号的三螺杆铜铝复合衬套时只需把铜芯恒温至300度，铝液温度控制在780度，压力控制在3MP，保压时间是20分钟。 
进一步说明，铜芯的材料可为锡青铜，其浇铸可以采用精密铸和、砂型铸 造和拉伸铸造，铝液成分可以为国标牌号108或109。 
以上所述的实施例仅仅是对本发明的优选实施方式进行描述，并非对本发明的范围进行限定，在不脱离本发明设计精神的前提下，本领域普通技术人员对本发明的技术方案作出的各种变形和改进，均应落入本发明的权利要求书确定的保护范围内。 

Claims (5)

1.一种三螺杆泵铜铝复合衬套低压铸造工艺：
首先根据需求把铜芯浇铸好，再根据铝衬套的需要开好相应的模具，并把模具安装在低压铸造机上，接着把浇铸好的铜芯放在烘箱内加热，加热后的铜芯置在铝衬套的模具内固定，压入铝液并通过低压铸造机保压，最后脱模，成型。
2.根据权利要求1所述的一种三螺杆泵铜铝复合衬套低压铸造工艺，其特征在于：所述的铜铝复合衬套在加工小型号时，铜芯恒温至500-600度，铝液温度控制在660-720度，压力控制在1.5MP，保压时间是10-15分钟。
3.根据权利要求1所述的一种三螺杆泵铜铝复合衬套低压铸造工艺，其特征在于：所述的铜铝复合衬套在加工中型号时，铜芯恒温至400-500度，铝液温度控制在700-730度，压力控制在2MP，保压时间是15-20分钟。
4.根据权利要求1所述的一种三螺杆泵铜铝复合衬套低压铸造工艺，其特征在于：所述的铜铝复合衬套在加工大型号时，铜芯恒温至300-400度，铝液温度控制在730-780度，压力控制在3MP，保压时间是20分钟。
5.根据权利要求1所述的一种三螺杆泵铜铝复合衬套低压铸造工艺，其特征在于：铜铝复合衬套在其浇铸好后，只有在铝衬套顶部到三分之二处是置有铜芯的。
CN201410406860.5A 2014-08-13 2014-08-13 一种三螺杆泵铜铝复合衬套低压铸造工艺 Active CN104259431B (zh)