CN104234339A - Method for directly forming seamless wall brick on wall - Google Patents
Method for directly forming seamless wall brick on wall Download PDFInfo
- Publication number
- CN104234339A CN104234339A CN201410456914.9A CN201410456914A CN104234339A CN 104234339 A CN104234339 A CN 104234339A CN 201410456914 A CN201410456914 A CN 201410456914A CN 104234339 A CN104234339 A CN 104234339A
- Authority
- CN
- China
- Prior art keywords
- water
- based material
- weight
- wall brick
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the field of decoration, in particular to a method for directly forming a seamless wall brick on a wall. The method comprises the following steps of coating a substrate with putty to form a flat putty layer, solidifying, coating with a first water-based material, drying, and grinding; coating with a second water-based material in a rolling or spraying way, forming the required pattern and color, and remaining for 4-12 hours; coating with a third water-based material for one to two times in the rolling or spraying way, drying, and then completing the manufacturing of the wall patterns. The method has the advantages that by coating with the first water-based material, the good combining with the putty layer is realized, so the hardness is improved, and the generation of cracks is avoided; the second water-based material is used for coating, and the required pattern is formed in a DIY (do it yourself) way, so the randomness is high, the second water-based material can be well combined with the first water-based material, and the pattern can be well fixed after solidification; the third water-based material is used for coating, so the function of protecting the patterns is realized, the hardness of the finally obtained pattern surface reaches more than 3H, and the brightness can reach more than 95%.
Description
Technical field
The present invention relates to decoration field, in particular to a kind of method directly forming seamless wall brick on metope.
Background technology
Current domestic made parian paint (blade paint, water-water, multi-color) adopts flush coater to carry out, and this spraying process need be sprayed on various pigments on metope with heavy caliber spray gun, and forms artificial granite marble.But there is following shortcoming in this method: 1, figure colour is single; 2, artificial and material cost is high; 3, high to constructor's technical requirements; 4, the metope out-of-flatness after spraying is rough.
Summary of the invention
The object of the present invention is to provide a kind of method directly forming seamless wall brick on metope, to solve the above problems.
Provide a kind of method directly forming seamless wall brick on metope in an embodiment of the present invention, comprise the following steps:
(a), on matrix, apply putty form smooth putty layer, coating the first water-based material after solidification, polishing after dry;
B (), then roller coating or spraying the second water-based material, make required decorative pattern and color with instrument, stop 4-12h;
(c), by the 3rd water-based material roller coating or spraying 1-2 time, namely complete the making of metope pattern after drying;
Wherein, described first water-based material is mixed by the first raw material and water, the weight of described water is the 35-45% of described first raw material weight, and described first raw material comprises following material: by weight, both sides' powder 550-650 part, sierozem power 250-350 part, fine particle calcium carbonate 80-150 part, HPMC 1-5 part, pva powder 2-8 part, thixotropic lubricant 0.2-1 part, easy loosen collagen fibre 0.2-1 part;
Described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 85-100 part, butyl glycol ether 5-10 part, wetting agent 0.2-1 part, defoamer 0.3-1 part, wood fibre 0.3-1 part, slip agent 0.2-0.5 part, levelling agent 0.6-1.5 part, water 0.8-1.5 part;
Described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 50-60 part, sliding agent 0.2-0.5 part, defoamer 0.1-0.4 part, levelling agent 0.2-0.5 part, dipropylene glycol methyl ether 2-3 part, water 35-45 part.
Preferably, in described step (b), described instrument comprises any one or more in decorative pattern cylinder, sponge, brush.
Preferably, in described first water-based material, the weight of described water is the 38-40% of described first raw material weight.
Preferably, described first raw material comprises following material: by weight, both sides' powder 580-600 part, sierozem power 280-300 part, fine particle calcium carbonate 100-110 part, HPMC 2-3 part, pva powder 5-6 part, thixotropic lubricant 0.5-0.6 part, easy loosen collagen fibre 0.4-0.7 part.
Preferably, described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 88-90 part, butyl glycol ether 7-8 part, wetting agent 0.4-0.5 part, defoamer 0.5-0.8 part, wood fibre 0.5-0.8 part, slip agent 0.3-0.4 part, levelling agent 0.8-1.0 part, water 1.0-1.1 part.
Preferably, described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 54-58 part, sliding agent 0.3-0.4 part, defoamer 0.2-0.3 part, levelling agent 0.3-0.4 part, dipropylene glycol methyl ether 2-3 part, water 39-42 part.
Preferably, the described wetting agent in described second water-based material is organic modified polyorganosiloxane alcohol ethereal solution.
Preferably, the defoamer in described second water-based material and/or described 3rd water-based material is modified dimethyl polysiloxane solution.
Preferably, the described slip agent in described second water-based material is water-based oxidized polyethylene wax emulsion.
Preferably, the levelling agent in described second water-based material and/or described 3rd water-based material is acrylic acid levelling agent.
The direct method forming seamless wall brick on metope that the embodiment of the present invention provides, by applying the first water-based material, makes it well be combined with putty layer, improves hardness, the generation of crackle preventing; Then the second water-based material is smeared and DIY goes out required pattern, random strong, and the second water-based material well can merge with the first water-based material, can well fix after the pattern cured obtained; Then smear the 3rd water-based material, play the effect of protection pattern, the patterned surfaces hardness finally obtained can reach more than 3H, and brightness can reach more than 95%.
Detailed description of the invention
Below by specific embodiment, the present invention is described in further detail.
Provide a kind of method directly forming seamless wall brick on metope in an embodiment of the present invention, comprise the following steps:
(a), on matrix, apply putty form smooth putty layer, coating the first water-based material after solidification, polishing after dry;
B (), then roller coating or spraying the second water-based material, make required decorative pattern and color with instrument, stop 4-12h;
(c), by the 3rd water-based material roller coating or spraying 1-2 time, namely complete the making of metope pattern after drying;
Wherein, described first water-based material is mixed by the first raw material and water, the weight of described water is the 35-45% of described first raw material weight, and described first raw material comprises following material: by weight, both sides' powder 550-650 part, sierozem power 250-350 part, fine particle calcium carbonate 80-150 part, HPMC 1-5 part, pva powder 2-8 part, thixotropic lubricant 0.2-1 part, easy loosen collagen fibre 0.2-1 part;
Described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 85-100 part, butyl glycol ether 5-10 part, wetting agent 0.2-1 part, defoamer 0.3-1 part, wood fibre 0.3-1 part, slip agent 0.2-0.5 part, levelling agent 0.6-1.5 part, water 0.8-1.5 part;
Described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 50-60 part, sliding agent 0.2-0.5 part, defoamer 0.1-0.4 part, levelling agent 0.2-0.5 part, dipropylene glycol methyl ether 2-3 part, water 35-45 part.
The direct method forming seamless wall brick on metope that the embodiment of the present invention provides, first water-based material is by the cooperation between each component, after making to apply the first water-based material in putty layer, both well combine, part first water-based material infiltrates putty layer, make putty layer hardening, and can crack be prevented; Apply first water-based material room temperature stop 10-15 hour namely curable, the first water-based material layer hardness obtained is high, is beneficial to the drafting of next step pattern; Then smear the second water-based material and DIY goes out required pattern, in the second water-based material, each composition cooperatively interacts, and itself and the first water-based material are well merged, and its mobility is suitable for, facilitate the drafting of pattern, pattern is drawn as requested, random strong; It is good that rear formability drawn by pattern, and after the second water-based material solidification, pattern can keep good mouldability, is not easily destroyed; Then the 3rd water-based material is smeared; play the effect of protection pattern, each composition chemiluminescence of the 3rd water-based material, the patterned surfaces hardness finally obtained can reach more than 3H; brightness can reach more than 95%, solves the problem that water paint hardness and brightness in prior art are inadequate very well.The thickness of three kinds of water-based materials is only 3 millimeter, and combine strong each other, its hardness and brightness all can reach the performance of ceramic tile, and waterproof, sets fire, moistureproof, scrubbing resistance.
Wherein, matrix can be woodwork plate, gypsum plank, cement board, PVC board and sand-lime wall etc., directly constructs, easy and simple to handle.
For ease of drawing a design, instrument is easy to get, and the pattern obtained has good third dimension, and preferably, in described step (b), described instrument comprises any one or more in decorative pattern cylinder, sponge, brush.Decorative pattern cylinder can be the cylinder of various decorative pattern, and other instruments with same or similar function are also in protection scope of the present invention.
In order to make the first water-based material have more suitable denseness, so that coating, it is made better to be combined with putty layer, prevent crack, the first water-based material layer hardness obtained is high, preferably, in described first water-based material, the weight of described water is the 38-40% of described first raw material weight.
In order to make better coordinated between each composition of the first water-based material, the first water-based material obtained better being combined with putty layer, preventing crack, the the first water-based material layer hardness obtained is high, preferably, described first raw material comprises following material: by weight, both sides' powder 580-600 part, sierozem power 280-300 part, fine particle calcium carbonate 100-110 part, HPMC2-3 part, pva powder 5-6 part, thixotropic lubricant 0.5-0.6 part, easy loosen collagen fibre 0.4-0.7 part.
In order to make each composition in the second water-based material better cooperatively interact, itself and the first water-based material are well merged, and its mobility is suitable for, and facilitates the drafting of pattern; And it is good to make the pattern obtained draw rear formability, not easily be destroyed, preferably, described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 88-90 part, butyl glycol ether 7-8 part, wetting agent 0.4-0.5 part, defoamer 0.5-0.8 part, wood fibre 0.5-0.8 part, slip agent 0.3-0.4 part, levelling agent 0.8-1.0 part, water 1.0-1.1 part.
Preferably, described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 54-58 part, sliding agent 0.3-0.4 part, defoamer 0.2-0.3 part, levelling agent 0.3-0.4 part, dipropylene glycol methyl ether 2-3 part, water 39-42 part.Between its each composition of the 3rd water-based material of this proportioning, there is better chemiluminescence, increase hardness and the brightness of patterned surfaces further, better protect pattern, there is better waterproof, set fire, moistureproof, the advantages such as scrubbing resistance.
Preferably, the described wetting agent in described second water-based material is organic modified polyorganosiloxane alcohol ethereal solution.Organic modified polyorganosiloxane alcohol ethereal solution, as wetting agent, strongly can reduce the surface tension of system, thus provide very strong wettability, and each composition of the second water-based material is better merged, and the second water-based material quality obtained is more homogeneous.
Preferably, the defoamer in described second water-based material and/or described 3rd water-based material is modified dimethyl polysiloxane solution.Modified dimethyl polysiloxane solution selected by defoamer, has the following advantages: froth breaking is fast, and suds suppressing properties is good; Do not affect the fundamental property of bubbling system; Diffusivity, good penetrability; Chemical stabilization; Without physiologically active, corrosion-free, nontoxic, without adverse side effect, do not fire, not quick-fried, safety is high.
Preferably, the described slip agent in described second water-based material is water-based oxidized polyethylene wax emulsion.Water-based oxidized polyethylene wax emulsion aqueous, environmental protective, well can improve wear-resisting, smooth, feel, gloss etc.
Preferably, the levelling agent in described second water-based material and/or described 3rd water-based material is acrylic acid levelling agent.Acrylic acid levelling agent can impel coating in drying and forming-film process, form smooth, smooth, a uniform film, better protects pattern.
The embodiment of the present invention provide direct on metope, form seamless wall brick method and obtained patterned layer have the following advantages:
1, material therefor is Environmental Protective Water-paint, not containing hazardous substancess such as formaldehyde, benzene, mercury, lead, nontoxic, does not need to add multiple auxiliary agent, without any volatilization pungent in process for preparation; And ceramic tile has radiation, there is harm to human body.
2, the hardness of patterned layer and brightness all can reach the performance of ceramic tile, and waterproof, sets fire, moistureproof, scrubbing resistance.
3, the thickness of the patterned layer of three kinds of water-based material formation is only 3 millimeter, can save space, make house become larger, and the thickness of wall brick is 6 centimetres-8 centimetres.
4, the color of patterned layer and texture have randomness, can the demand different according to client make; Ceramic tile is without this function.
5, the size of patterned layer and moulding have randomness, can make the metope of seamless entirety, also can like according to the difference of client, produce square, circular, the difformities such as rhombus; Ceramic tile is without this function.
6, the making of patterned layer can at woodwork plate, gypsum plank, cement board, and the substrates such as PVC board and sand-lime wall are directly constructed; Ceramic tile has limitation.
7, the replacing of patterned layer is simple and convenient, directly criticizes putty or roller coating at metope; It is large that difficulty changed by wall brick, not only takes a lot of work but also require great effort.
8, construct simple and convenient, directly construct on matrix with special coating, different decorative pattern instruments, construction technology is easy to learn; Ceramic tile is heavy, and difficulty of mating formation is large, and technical data difficulty controls.
9, patterned layer is directly constructed on matrix according to construction area special coating, not waste; Ceramic tile needs sand, cement, cutting machine etc., loaded down with trivial details heaviness of constructing, and has certain waste, causes damage.
Each composition in the first water-based material related in the present invention, the second water-based material and the 3rd water-based material is commercially available prod.
Embodiment 1
On metope, directly form a method for seamless wall brick, comprise the following steps:
(a), on matrix, apply putty form smooth putty layer, coating the first water-based material after solidification, drying at room temperature 10h, polishing;
B (), then roller coating second water-based material, make required decorative pattern and color with decorative pattern cylinder, stop 4h;
(c), by the 3rd water-based material roller coating 2 times, after drying, namely complete the making of metope pattern;
Wherein, described first water-based material is mixed by the first raw material and water, the weight of described water is 35% of described first raw material weight, and described first raw material comprises following material: by weight, 550 parts, both sides' powder, sierozem power 250 parts, fine particle calcium carbonate 80 parts, HPMC 1 part, pva powder 2 parts, thixotropic lubricant 0.2 part, easy loosen collagen fibre 0.2 part;
Described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 85 parts, butyl glycol ether 5 parts, organic modified polyorganosiloxane alcohol ethereal solution 0.2 part, modified dimethyl polysiloxane solution 0.3 part, wood fibre 0.3 part, water-based oxidized polyethylene wax emulsion 0.2 part, acrylic acid levelling agent 0.6 part, 0.8 part, water;
Described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 50 parts, sliding agent 0.2 part, modified dimethyl polysiloxane solution 0.1 part, acrylic acid levelling agent 0.2 part, dipropylene glycol methyl ether 2 parts, 35 parts, water.
The thickness of the patterned layer that three kinds of finally obtained water-based materials are formed is 4mm, and measuring its case hardness is 3H, and brightness is 95%.
Embodiment 2
On metope, directly form a method for seamless wall brick, comprise the following steps:
(a), on matrix, apply putty form smooth putty layer, after solidification, coating the first water-based material, polishes after drying at room temperature 12h;
(b), then spray the second water-based material, make required decorative pattern and color with decorative pattern cylinder and sponge, stop 8h;
(c), the 3rd water-based material is sprayed 1 time, namely complete the making of metope pattern after drying;
Wherein, described first water-based material is mixed by the first raw material and water, the weight of described water is 38% of described first raw material weight, and described first raw material comprises following material: by weight, 580 parts, both sides' powder, sierozem power 280 parts, fine particle calcium carbonate 100 parts, HPMC 2 parts, pva powder 5 parts, thixotropic lubricant 0.5 part, easy loosen collagen fibre 0.4 part;
Described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 88 parts, butyl glycol ether 7 parts, organic modified polyorganosiloxane alcohol ethereal solution 0.4 part, modified dimethyl polysiloxane solution 0.5 part, wood fibre 0.5 part, water-based oxidized polyethylene wax emulsion 0.3 part, acrylic acid levelling agent 0.8 part, 1.0 parts, water;
Described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 54 parts, sliding agent 0.3 part, modified dimethyl polysiloxane solution 0.2 part, acrylic acid levelling agent 0.3 part, dipropylene glycol methyl ether 2 parts, 39 parts, water.
The thickness of the patterned layer that three kinds of finally obtained water-based materials are formed is 3mm, and measuring its case hardness is 3.1H, and brightness is 95%.
Embodiment 3
On metope, directly form a method for seamless wall brick, comprise the following steps:
(a), on matrix, apply putty form smooth putty layer, after solidification, coating the first water-based material, polishes after drying at room temperature 14h;
(b), then spray the second water-based material, make required decorative pattern and color with decorative pattern cylinder, sponge and brush, stop 10h;
(c), by the 3rd water-based material roller coating 2 times, after drying, namely complete the making of metope pattern;
Wherein, described first water-based material is mixed by the first raw material and water, the weight of described water is 40% of described first raw material weight, and described first raw material comprises following material: by weight, 600 parts, both sides' powder, sierozem power 300 parts, fine particle calcium carbonate 110 parts, HPMC3 part, pva powder 6 parts, thixotropic lubricant 0.6 part, easy loosen collagen fibre 0.7 part;
Described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 90 parts, butyl glycol ether 8 parts, organic modified polyorganosiloxane alcohol ethereal solution 0.5 part, modified dimethyl polysiloxane solution 0.8 part, wood fibre 0.8 part, water-based oxidized polyethylene wax emulsion 0.4 part, acrylic acid levelling agent 1.0 parts, 1.1 parts, water;
Described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 58 parts, sliding agent 0.4 part, modified dimethyl polysiloxane solution 0.3 part, acrylic acid levelling agent 0.4 part, dipropylene glycol methyl ether 3 parts, 42 parts, water.
The thickness of the patterned layer that three kinds of finally obtained water-based materials are formed is 3.4mm, and measuring its case hardness is 3.4H, and brightness is 97%.
Embodiment 4
On metope, directly form a method for seamless wall brick, comprise the following steps:
(a), on matrix, apply putty form smooth putty layer, after solidification, coating the first water-based material, polishes after drying at room temperature 15h;
B (), then roller coating second water-based material, make required decorative pattern and color with sponge and brush, stop 12h;
(c), the 3rd water-based material is sprayed 1 time, namely complete the making of metope pattern after drying;
Wherein, described first water-based material is mixed by the first raw material and water, the weight of described water is 45% of described first raw material weight, and described first raw material comprises following material: by weight, 650 parts, both sides' powder, sierozem power 350 parts, fine particle calcium carbonate 150 parts, HPMC5 part, pva powder 8 parts, thixotropic lubricant 1 part, easy loosen collagen fibre 1 part;
Described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 100 parts, butyl glycol ether 10 parts, organic modified polyorganosiloxane alcohol ethereal solution 1 part, modified dimethyl polysiloxane solution 1 part, wood fibre 1 part, water-based oxidized polyethylene wax emulsion 0.5 part, acrylic acid levelling agent 1.5 parts, 1.5 parts, water;
Described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 60 parts, sliding agent 0.5 part, modified dimethyl polysiloxane solution 0.4 part, acrylic acid levelling agent 0.5 part, dipropylene glycol methyl ether 3 parts, 45 parts, water.
The thickness of the patterned layer that three kinds of finally obtained water-based materials are formed is 3.2mm, and measuring its case hardness is 3.2H, and brightness is 96%.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (10)
1. on metope, directly form a method for seamless wall brick, it is characterized in that, comprise the following steps:
(a), on matrix, apply putty form smooth putty layer, coating the first water-based material after solidification, polishing after dry;
B (), then roller coating or spraying the second water-based material, make required decorative pattern and color with instrument, stop 4-12h;
(c), by the 3rd water-based material roller coating or spraying 1-2 time, namely complete the making of metope pattern after drying;
Wherein, described first water-based material is mixed by the first raw material and water, the weight of described water is the 35-45% of described first raw material weight, and described first raw material comprises following material: by weight, both sides' powder 550-650 part, sierozem power 250-350 part, fine particle calcium carbonate 80-150 part, HPMC 1-5 part, pva powder 2-8 part, thixotropic lubricant 0.2-1 part, easy loosen collagen fibre 0.2-1 part;
Described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 85-100 part, butyl glycol ether 5-10 part, wetting agent 0.2-1 part, defoamer 0.3-1 part, wood fibre 0.3-1 part, slip agent 0.2-0.5 part, levelling agent 0.6-1.5 part, water 0.8-1.5 part;
Described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 50-60 part, sliding agent 0.2-0.5 part, defoamer 0.1-0.4 part, levelling agent 0.2-0.5 part, dipropylene glycol methyl ether 2-3 part, water 35-45 part.
2. the method directly forming seamless wall brick on metope according to claim 1, it is characterized in that, in described step (b), described instrument comprises any one or more in decorative pattern cylinder, sponge, brush.
3. the method directly forming seamless wall brick on metope according to claim 1, it is characterized in that, in described first water-based material, the weight of described water is the 38-40% of described first raw material weight.
4. the method directly forming seamless wall brick on metope according to claim 3, it is characterized in that, described first raw material comprises following material: by weight, both sides' powder 580-600 part, sierozem power 280-300 part, fine particle calcium carbonate 100-110 part, HPMC 2-3 part, pva powder 5-6 part, thixotropic lubricant 0.5-0.6 part, easy loosen collagen fibre 0.4-0.7 part.
5. the method directly forming seamless wall brick on metope according to claim 1, it is characterized in that, described second water-based material is mixed by following composition: by weight, acrylic acid modified polyurethane 88-90 part, butyl glycol ether 7-8 part, wetting agent 0.4-0.5 part, defoamer 0.5-0.8 part, wood fibre 0.5-0.8 part, slip agent 0.3-0.4 part, levelling agent 0.8-1.0 part, water 1.0-1.1 part.
6. the method directly forming seamless wall brick on metope according to claim 1, it is characterized in that, described 3rd water-based material is mixed by following composition: by weight, water-borne acrylic resin 54-58 part, sliding agent 0.3-0.4 part, defoamer 0.2-0.3 part, levelling agent 0.3-0.4 part, dipropylene glycol methyl ether 2-3 part, water 39-42 part.
7. the direct method forming seamless wall brick on metope according to any one of claim 1-6, is characterized in that, the described wetting agent in described second water-based material is organic modified polyorganosiloxane alcohol ethereal solution.
8. the direct method forming seamless wall brick on metope according to any one of claim 1-6, is characterized in that, the defoamer in described second water-based material and/or described 3rd water-based material is modified dimethyl polysiloxane solution.
9. the direct method forming seamless wall brick on metope according to any one of claim 1-6, is characterized in that, the described slip agent in described second water-based material is water-based oxidized polyethylene wax emulsion.
10. the direct method forming seamless wall brick on metope according to any one of claim 1-6, is characterized in that, the levelling agent in described second water-based material and/or described 3rd water-based material is acrylic acid levelling agent.