CN104231839B - A kind of powdery paints containing jade powder with high-wear resistance - Google Patents
A kind of powdery paints containing jade powder with high-wear resistance Download PDFInfo
- Publication number
- CN104231839B CN104231839B CN201410416861.8A CN201410416861A CN104231839B CN 104231839 B CN104231839 B CN 104231839B CN 201410416861 A CN201410416861 A CN 201410416861A CN 104231839 B CN104231839 B CN 104231839B
- Authority
- CN
- China
- Prior art keywords
- jade powder
- powdery paints
- powder
- wear resistance
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of powdery paints containing jade powder with high-wear resistance, it is to be prepared by the raw material of following weight parts: dicyandiamide 1-2, jade powder 4-6, nigrosine 0.1-0.2, barium sulfate 3-5, phenolic resin 30-50, glass fibre 2-4, precipitated calcium carbonate 4-6, glyceryl monostearate 1-2, EVA resin 3-6, DAA 0.1-0.2, polyester resin 10-15, isocyanates 1-2, sodium hydroxide 1-2, nano magnesia 1-2, polyvinyl alcohol 0.1-0.2, ethylenediamine 1-2, montmorillonite powder 1-2, composite adhesive 3-6；Gained powdery paints contains the raw materials such as jade powder, by rationally composite, after extrusion, have excellence anti-wear performance and shock resistance, stable chemical nature, durable in use, superior performance.
Description
Technical field
The present invention relates to art of powder coatings, be exactly a kind of powdery paints containing jade powder with high-wear resistance.
Background technology
Powdery paints is a kind of novel without solvent 100% solid powdery coating.There is solvent-free, pollution-free, recyclable, environmental protection, the saving energy and resource, reduce labor intensity and film mechanical strength high.And cellulose must apply in coating is a lot, it is possible to play the effect of coating toughness.
Summary of the invention
It is an object of the invention to provide a kind of powdery paints containing jade powder with high-wear resistance.
Above-mentioned purpose is realized by below scheme:
A kind of powdery paints containing jade powder with high-wear resistance, it is characterised in that: it is to be prepared by the raw material of following weight parts:
Dicyandiamide 1-2, jade powder 4-6, nigrosine 0.1-0.2, barium sulfate 3-5, phenolic resin 30-50, glass fibre 2-4, precipitated calcium carbonate 4-6, glyceryl monostearate 1-2, EVA resin 3-6, DAA 0.1-0.2, polyester resin 10-15, isocyanates 1-2, sodium hydroxide 1-2, nano magnesia 1-2, polyvinyl alcohol 0.1-0.2, ethylenediamine 1-2, montmorillonite powder 1-2, composite adhesive 3-6；
Composite adhesive is to be prepared by the raw material of following weight parts:
Butadiene-styrene rubber 4-6, Benzoinum 0.1-0.5, acetone 1-2, Oleum Pini 1-2, phenolic resin 0.8-0.9, Hydroxylated acrylic resin 1-2, zinc powder 0.1-0.2, silica 1-2, uric acid 0.1-0.5, hydroxymethyl cellulose 1-2, antioxidant 1076 1-2, polyether-ether-ketone 1-2;
The preparation method of composite adhesive is: after each raw material blending, in 80-90 DEG C of mixing 10-20min, after taking-up, pulverizes, crosses 100-200 mesh sieve, to obtain final product.
Described a kind of powdery paints containing jade powder with high-wear resistance, it is characterised in that:
Preparation method comprises the following steps:
(1) all materials weigh by proportioning, are placed in high-speed mixer, 700-900 rev/min of mixing 20-25min；
(2) double screw extruder is adopted, in 130-140oAbout C extrudes；
(3) extrusion tablet is size-reduced, crosses 300-400 mesh sieve, to obtain final product.
The invention have the benefit that
Gained powdery paints contains the raw materials such as jade powder, by rationally composite, after extrusion, have excellence anti-wear performance and shock resistance, stable chemical nature, durable in use, superior performance.
Detailed description of the invention
A kind of powdery paints containing jade powder with high-wear resistance, it is to be prepared by the raw material of following weight (kg):
Dicyandiamide 2, jade powder 5, nigrosine 0.2, barium sulfate 5, phenolic resin 50, glass fibre 2, precipitated calcium carbonate 6, glyceryl monostearate 2, EVA resin 6, DAA 0.2, polyester resin 15, isocyanates 2, sodium hydroxide 1, nano magnesia 2, polyvinyl alcohol 0.2, ethylenediamine 2, montmorillonite powder 2, composite adhesive 5；
Composite adhesive is to be prepared by the raw material of following weight (kg):
Butadiene-styrene rubber 4, Benzoinum 0.1, acetone 1, Oleum Pini 1, phenolic resin 0.9, Hydroxylated acrylic resin 2, zinc powder 0.2, silicon dioxide 2, uric acid 0.5, hydroxymethyl cellulose 2, antioxidant 1076 1, polyether-ether-ketone 2;
The preparation method of composite adhesive is: after each raw material blending, in 80 DEG C of mixing 10min, after taking-up, pulverizes, crosses 100 mesh sieves, to obtain final product.
Described a kind of powdery paints containing jade powder with high-wear resistance,
Preparation method comprises the following steps:
(1) all materials weigh by proportioning, are placed in high-speed mixer, 900 revs/min of mixing 25min；
(2) double screw extruder is adopted, in 140oAbout C extrudes；
(3) extrusion tablet is size-reduced, crosses 400 mesh sieves, to obtain final product.
The coating process of the present embodiment product is general electrostatic spraying, condition of cure: 200oC/10-15min, gained coating is smooth, complete, and the artificial accelerated aging time is >=1700h.
Claims (2)
1. a powdery paints containing jade powder with high-wear resistance, it is characterised in that: it is to be prepared by the raw material of following weight parts:
Dicyandiamide 2, jade powder 5, nigrosine 0.2, barium sulfate 5, phenolic resin 50, glass fibre 2, precipitated calcium carbonate 6, glyceryl monostearate 2, EVA resin 6, DAA 0.2, polyester resin 15, isocyanates 2, sodium hydroxide 1, nano magnesia 2, polyvinyl alcohol 0.2, ethylenediamine 2, montmorillonite powder 2, composite adhesive 5；
Composite adhesive is to be prepared by the raw material of following weight parts:
Butadiene-styrene rubber 4, Benzoinum 0.1, acetone 1, Oleum Pini 1, phenolic resin 0.9, Hydroxylated acrylic resin 2, zinc powder 0.2, silicon dioxide 2, uric acid 0.5, hydroxymethyl cellulose 2, antioxidant 1076 1, polyether-ether-ketone 2；
The preparation method of composite adhesive is: after each raw material blending, in 80 DEG C of mixing 10min, after taking-up, pulverizes, crosses 100 mesh sieves, to obtain final product.
2. a kind of powdery paints containing jade powder with high-wear resistance according to claim 1, it is characterised in that:
Preparation method comprises the following steps:
(1) all materials weigh by proportioning, are placed in high-speed mixer, 900 revs/min of mixing 25min；
(2) double screw extruder is adopted, in 140 DEG C of extrusions；
(3) extrusion tablet is size-reduced, crosses 400 mesh sieves, to obtain final product.