CN103666184B - A kind of sand grain metal powder paint - Google Patents
A kind of sand grain metal powder paint Download PDFInfo
- Publication number
- CN103666184B CN103666184B CN201310396025.3A CN201310396025A CN103666184B CN 103666184 B CN103666184 B CN 103666184B CN 201310396025 A CN201310396025 A CN 201310396025A CN 103666184 B CN103666184 B CN 103666184B
- Authority
- CN
- China
- Prior art keywords
- powder
- raw material
- sand grain
- compounded mix
- metal powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of sand grain metal powder paint, it is made up of the raw material of following weight parts: resol 80-90, vibrin 20-30, red iron oxide 1-2, diethylenetriamine 2-3, Calcium Chloride Powder Anhydrous 3-4, urotropine 6-9, gac 1-2, copper naphthenate 2-3, boric acid 1-2, tetrafluoroethylene wax 0.1-0.5, process white 20-30, light calcium carbonate 20-30, aluminium powder 2-3, compounded mix 20-35, aerosil 0.1-0.2; Coating quality of the present invention is stablized, coating decoration excellent, and after film forming, surface brightness significantly improves, and 60 degree of angle gloss is brought up to be greater than 150% from being less than 100%, has strong metal sense, is similar to electroplating effect.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of sand grain metal powder paint.
Background technology
Powder coating is a kind of novel not containing solvent 100% solid powdery coating.There is solvent-free, pollution-free, recyclable, environmental protection, the saving energy and resource, reduce labor intensity and film physical strength high, and the performance improving powder coating by adding different auxiliary agents improves performance powder coating reasonable mode at present.
Summary of the invention
The object of the invention is exactly to provide a kind of sand grain metal powder paint.
The present invention is achieved by the following technical solutions:
A kind of sand grain metal powder paint, is characterized in that what it was made up of the raw material of following weight parts:
Resol 80-90, vibrin 20-30, red iron oxide 1-2, diethylenetriamine 2-3, Calcium Chloride Powder Anhydrous 3-4, urotropine 6-9, gac 1-2, copper naphthenate 2-3, boric acid 1-2, tetrafluoroethylene wax 0.1-0.5, process white 10-20, light calcium carbonate 10-20, aluminium powder 2-3, compounded mix 10-15, aerosil 0.1-0.2;
Described compounded mix is made up of the raw material of following weight parts:
Clay 40-50, iron ore ground-slag 40-50, Calucium Silicate powder 10-20, cuprichexafluorosilicate 2-3, aluminum nitride powder 1-2, nanometer jade powder 5-7, Imarcaptoacetate dioctyltin 0.2-0.3, Flos Rosae Rugosae quintessence oil 0.6-1, water are appropriate;
Above-mentioned Calucium Silicate powder is mixed with cuprichexafluorosilicate, aluminum nitride powder is joined in 3-5 times of water, join in the mixture of Calucium Silicate powder and cuprichexafluorosilicate after stirring, after stirring, add nanometer jade powder, stirring heating 30-40 minute at 80-100 DEG C, must a be expected; Mixed with iron ore ground-slag by clay, 600-700 DEG C of calcining 2-3 hour, mixes with above-mentioned material a, Flos Rosae Rugosae quintessence oil, fully grinds, and adds each raw material of residue, fully stirs, dry, obtain described compounded mix.
A preparation method for sand grain metal powder paint, comprises the following steps:
Above-mentioned resol, vibrin, red iron oxide, diethylenetriamine, urotropine, process white, light calcium carbonate, compounded mix are carried out high-speed mixing, through melt extruding, compressing tablet is pulverized, mill screen gets screening thing, screening thing and each raw material of residue are dry mixed, sieve, obtain described sand grain metal powder paint.
Advantage of the present invention is:
Coating quality of the present invention is stablized, coating decoration excellent, and after film forming, surface brightness significantly improves, and 60 degree of angle gloss is brought up to be greater than 150% from being less than 100%, has strong metal sense, is similar to electroplating effect.
Embodiment
A kind of sand grain metal powder paint, it is made up of the raw material of following weight parts (kilogram):
Resol 90, vibrin 30, red iron oxide 1, diethylenetriamine 3, Calcium Chloride Powder Anhydrous 4, urotropine 6, gac 1, copper naphthenate 2, boric acid 1, tetrafluoroethylene wax 0.5, process white 20, light calcium carbonate 10, aluminium powder 2, compounded mix 15, aerosil 0.2;
Described compounded mix is made up of the raw material of following weight parts:
Clay 50, iron ore ground-slag 50, Calucium Silicate powder 20, cuprichexafluorosilicate 2, aluminum nitride powder 1, nanometer jade powder 5, Imarcaptoacetate dioctyltin 0.2-0.3, Flos Rosae Rugosae quintessence oil 0.6, water are appropriate;
Mixed with cuprichexafluorosilicate by above-mentioned Calucium Silicate powder, joined by aluminum nitride powder in 3 times of water, join in the mixture of Calucium Silicate powder and cuprichexafluorosilicate, add nanometer jade powder after stirring after stirring, at 100 DEG C, stirring heating 40 minutes, must expect a; Clay is mixed with iron ore ground-slag, calcines 3 hours, mix with above-mentioned material a, Flos Rosae Rugosae quintessence oil, fully grind for 600 DEG C, add each raw material of residue, fully stir, dry, obtain described compounded mix.
A preparation method for sand grain metal powder paint, comprises the following steps:
Above-mentioned resol, vibrin, red iron oxide, diethylenetriamine, urotropine, process white, light calcium carbonate, compounded mix are carried out high-speed mixing, through melt extruding, compressing tablet is pulverized, mill screen gets screening thing, screening thing and each raw material of residue are dry mixed, sieve, obtain described sand grain metal powder paint.
Performance test:
Artificial accelerated aging time >=580h;
Exposure to weather(ing) 16 months is non-foaming, non-corrosive, do not ftracture, do not peel off.
Claims (2)
1. a sand grain metal powder paint, is characterized in that what it was made up of the raw material of following weight parts:
Resol 80-90, vibrin 20-30, red iron oxide 1-2, diethylenetriamine 2-3, Calcium Chloride Powder Anhydrous 3-4, urotropine 6-9, gac 1-2, copper naphthenate 2-3, boric acid 1-2, tetrafluoroethylene wax 0.1-0.5, process white 10-20, light calcium carbonate 10-20, aluminium powder 2-3, compounded mix 10-15, aerosil 0.1-0.2;
Described compounded mix is made up of the raw material of following weight parts:
Clay 40-50, iron ore ground-slag 40-50, Calucium Silicate powder 10-20, cuprichexafluorosilicate 2-3, aluminum nitride powder 1-2, nanometer jade powder 5-7, Imarcaptoacetate dioctyltin 0.2-0.3, Flos Rosae Rugosae quintessence oil 0.6-1, water are appropriate;
Above-mentioned Calucium Silicate powder is mixed with cuprichexafluorosilicate, aluminum nitride powder is joined in 3-5 times of water, join in the mixture of Calucium Silicate powder and cuprichexafluorosilicate after stirring, after stirring, add nanometer jade powder, stirring heating 30-40 minute at 80-100 DEG C, must a be expected; Mixed with iron ore ground-slag by clay, 600-700 DEG C of calcining 2-3 hour, mixes with above-mentioned material a, Flos Rosae Rugosae quintessence oil, fully grinds, and adds each raw material of residue, fully stirs, dry, obtain described compounded mix.
2. a preparation method for sand grain metal powder paint as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned resol, vibrin, red iron oxide, diethylenetriamine, urotropine, process white, light calcium carbonate, compounded mix are carried out high-speed mixing, through melt extruding, compressing tablet is pulverized, mill screen gets screening thing, screening thing and each raw material of residue are dry mixed, sieve, obtain described sand grain metal powder paint.