CN104231380A - Silane crosslinked polyethylene cable material - Google Patents
Silane crosslinked polyethylene cable material Download PDFInfo
- Publication number
- CN104231380A CN104231380A CN201310250708.8A CN201310250708A CN104231380A CN 104231380 A CN104231380 A CN 104231380A CN 201310250708 A CN201310250708 A CN 201310250708A CN 104231380 A CN104231380 A CN 104231380A
- Authority
- CN
- China
- Prior art keywords
- silane
- cable material
- crosslinked polyethylene
- polyethylene cable
- silane crosslinked
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of insulating materials, and in particular relates to a silane crosslinked polyethylene cable material. The silane crosslinked polyethylene cable material is prepared from a base material, a catalyst master batch, silane and a crosslinking agent by virtue of proportioning and crosslinking. The silane crosslinked polyethylene cable material comprises the following components in parts by weight: 2.5-5 parts of the base material, 0.2-1 part of the catalyst master batch, 0.3 part of silane and 0.1-0.3 part of the crosslinking agent, wherein silane is vinyl trimethoxy silane. According to the silane crosslinked polyethylene cable material disclosed by the invention, the gel content of the cable material is not more than 30% by virtue of control over the component proportioning and granulating process.
Description
Technical field
The present invention relates to Insulation Material technical field, especially a kind of organosilane cross-linked poly-ethylene cable material.
Background technology
Traditions of the past production method is two-step approach, namely divides matrix masterbatch and catalytic crosslinking masterbatch, in cable cabling process, and upper cable after two kinds of masterbatch mixing, then complicated through aftertreatment, granulation process and cabling process.
Summary of the invention
In order to overcome the deficiency of existing technology, the invention provides a kind of organosilane cross-linked poly-ethylene cable material.
The technical solution adopted for the present invention to solve the technical problems is: a kind of organosilane cross-linked poly-ethylene cable material, and coordinate crosslinked forming by base-material, catalyst masterbatch and crosslinked with silicane, each component is as follows:
Base-material 2.5 ~ 5
Catalyst masterbatch 0.2 ~ 1
Silane 0.3
Linking agent 0.1 ~ 0.3
According to another embodiment of the invention, described silane is comprised further for being vinyltrimethoxy silane.
The invention has the beneficial effects as follows, the present invention passes through the control of said components proportioning and granulation process, makes the gel content of its CABLE MATERIALS be not more than 30.
Embodiment
A kind of organosilane cross-linked poly-ethylene cable material, coordinate crosslinked forming by base-material, catalyst masterbatch and crosslinked with silicane, each component is as follows:
Base-material 2.5 ~ 5
Catalyst masterbatch 0.2 ~ 1
Silane 0.3
Linking agent 0.1 ~ 0.3
Described silane is for being vinyltrimethoxy silane.
The present invention passes through the control of said components proportioning and granulation process, makes the gel content of its CABLE MATERIALS be not more than 30.
Claims (2)
1. an organosilane cross-linked poly-ethylene cable material, coordinate crosslinked forming by base-material, catalyst masterbatch and crosslinked with silicane, it is characterized in that, each component is as follows:
Base-material 2.5 ~ 5
Catalyst masterbatch 0.2 ~ 1
Silane 0.3
Linking agent 0.1 ~ 0.3.
2. organosilane cross-linked poly-ethylene cable material according to claim 1, is characterized in that, described silane is for being vinyltrimethoxy silane.