CN103467901A - Power cable protection pipe - Google Patents
Power cable protection pipe Download PDFInfo
- Publication number
- CN103467901A CN103467901A CN2013104238546A CN201310423854A CN103467901A CN 103467901 A CN103467901 A CN 103467901A CN 2013104238546 A CN2013104238546 A CN 2013104238546A CN 201310423854 A CN201310423854 A CN 201310423854A CN 103467901 A CN103467901 A CN 103467901A
- Authority
- CN
- China
- Prior art keywords
- power cable
- parts
- cable protection
- protection pipe
- cable protecting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a power cable protection pipe. The power cable protection pipe is prepared from the following raw materials in part by weight: 50-85 parts of PP-B, 10-50 parts of PP-R, 5-15 parts of fillers, 0.2-0.25 parts of an antioxidant and 1.5-2.0 parts of color master batch. A preparation method of the power cable protection pipe comprises the steps of stirring and mixing the PP-B, the PP-R, the filler, the antioxidant and the color master batch into a mixer, conveying the mixture into a pipe extruding machine for extrusion, then carrying out vacuum cooling and forming to obtain the product. According to the power cable protection pipe, the PP-B and the PP-R with certain ratio are mixed, then certain parts of the fillers, the antioxidant and the color master batch are added, so that the tensile strength and the welding tensile strength of the obtained pipes after processing are greatly improved, and other mechanical properties are also improved to a certain extent; the technical indexes of the power cable protection pipe are superior to those of the ideal underground trenchless pipes, and the products are difficult to deform after being formed.
Description
Technical field
The present invention relates to a kind of plastic pipe, particularly a kind of power cable protecting pipe.
Background technology
Current power cable protecting pipe tubing is all to use MPP directly to pass through extruder for shaping basically.Owing to there not being the MPP raw material designed for producing MPP electric power protection pipe specially on market, so the electric power protection pipe of producing has a lot of performances not reach standard-required, especially tensile strength and welding tensile strength.And tensile strength and welding tensile strength to be non-excavation buried by of paramount importance performance index in pipe technology, so this class tubing does not reach technical requirements.
Summary of the invention
Technical problem to be solved by this invention is for the deficiencies in the prior art, provides a kind of reasonable in design, tensile strength and the large power cable protecting pipe of welding tensile strength.
Technical problem to be solved by this invention is to realize by following technical scheme, the present invention is a kind of power cable protecting pipe, be characterized in: it is to be made by the raw material of following parts by weight: PP-B:50 ~ 85, PP-R:10 ~ 50, weighting agent: 5 ~ 15, oxidation inhibitor: 0.2 ~ 0.25, colour batch: 1.5 ~ 2.0; During preparation, PP-B, PP-R, weighting agent, oxidation inhibitor and colour batch are added in mixer and be uniformly mixed, first under 200 ~ 500r/min speed, stir 2.5-3.5min, stir 1.5-2.5min again under 60 ~ 200r/min speed, after be transported in pipe extruder, through pipe extruder extrude, vacuum cooling typing obtains product.
Technical problem to be solved by this invention can also further realize by following technical scheme, 1, described weighting agent is calcium carbonate;
2, described weight of calcium carbonate umber is 8 ~ 10;
3, the order number of described calcium carbonate >=1200 orders;
4, described oxidation inhibitor is antioxidant 1010;
5, described colour batch is orange or safran colour batch;
6, the parts by weight of described colour batch are 1.5.
The PP-B raw material is block copolymerization polypropylene, and the PP-R raw material is atactic copolymerized polypropene.
The present invention is mixed PP-B according to a certain percentage with PP-R, and PP-B has preferably snappiness but undercapacity, and PP-R has higher intensity but the snappiness deficiency.Bi-material is organically combined can be complementary not enough, thereby the material over-all properties is effectively improved.
Compared with prior art, the present invention mixes PP-B and PP-R according to a certain percentage, the weighting agent, oxidation inhibitor and the colour batch that add certain umber simultaneously, through the resulting tubing of processing treatment, on tensile strength and welding tensile strength, be greatly improved, other mechanical property also obtains certain raising simultaneously, and can surpass the buried technical indicator with pipeline of desirable non-excavation, and its production technique is simple, production cost reduces, product is not yielding after moulding.
Embodiment
Below further describe concrete technical scheme of the present invention, so that those skilled in the art understands the present invention further, and do not form the restriction to its right.
Embodiment 1, a kind of power cable protecting pipe, and it is to be made by the raw material of following parts by weight: PP-B:50 ~ 85, PP-R:10 ~ 50, weighting agent: 5 ~ 15, oxidation inhibitor: 0.2 ~ 0.25, colour batch: 1.5 ~ 2.0; During preparation, PP-B, PP-R, weighting agent, oxidation inhibitor and colour batch are added in mixer and be uniformly mixed, first under 200 ~ 500r/min speed, stir 2.5-3.5min, stir 1.5-2.5min again under 60 ~ 200r/min speed, after be transported in pipe extruder, through pipe extruder extrude, vacuum cooling typing obtains product.
Embodiment 2, a kind of power cable protecting pipe as described in Example 1, and described weighting agent, for through the active inorganic materials of processing, is preferably calcium carbonate.Adding of weighting agent can effectively reduce production cost, the while raising strength of materials to a certain degree.
Embodiment 3, a kind of power cable protecting pipe as described in Example 2, and described weight of calcium carbonate umber is 8 ~ 10, can also be preferably 8 parts.
Embodiment 4, a kind of power cable protecting pipe as described in Example 2, the order number of described calcium carbonate >=1200 orders.
Embodiment 5, and a kind of as power cable protecting pipe as described in embodiment 1-4, described oxidation inhibitor is antioxidant 1010, can effectively suppress tubing oxidation in air or soil, and the preferred weight umber is 0.2 part.
Embodiment 6, and a kind of as power cable protecting pipe as described in embodiment 1-5, described colour batch is orange or safran colour batch, painted for tubing.
Embodiment 7, and a kind of as power cable protecting pipe as described in embodiment 1-6, the parts by weight of described colour batch are 1.5.
Embodiment 8, a kind of as power cable protecting pipe as described in embodiment 1-7, the parts by weight that table one is MPP tubing and six embodiment raw materials of the present invention, the mechanical property contrast table that table two is corresponding MPP tubing and six embodiment gained tubing;
Table one: Comparative Examples MPP tubing and six embodiment raw material weight umbers
Table two: the mechanical property contrast table of Comparative Examples MPP tubing and six embodiment gained tubing
The tubing that raw material of the present invention makes as can be seen here is all large than MPP tubing intensity on tensile strength and welding tensile strength.
Simultaneously embodiments of the invention are not limited only to above-described embodiment, and such as various material weight umbers are made concrete adjustment as the case may be, or weighting agent, oxidation inhibitor, colour batch are used other replacement of the same type.
Be more than the preferred embodiments of the present invention, but design concept of the present invention is not limited only to this, allly utilizes this design to make insubstantial modifications to the present invention, also all fall into protection scope of the present invention.
Claims (7)
1. a power cable protecting pipe, it is characterized in that: it is to be made by the raw material of following parts by weight: PP-B:50 ~ 85, PP-R:10 ~ 50, weighting agent: 5 ~ 15, oxidation inhibitor: 0.2 ~ 0.25, colour batch: 1.5 ~ 2.0; During preparation, PP-B, PP-R, weighting agent, oxidation inhibitor and colour batch are added in mixer and be uniformly mixed, first under 200 ~ 500r/min speed, stir 2.5-3.5min, stir 1.5-2.5min again under 60 ~ 200r/min speed, after be transported in pipe extruder, through pipe extruder extrude, vacuum cooling typing obtains product.
2. power cable protecting pipe according to claim 1, it is characterized in that: described weighting agent is calcium carbonate.
3. power cable protecting pipe according to claim 2, it is characterized in that: described weight of calcium carbonate umber is 8 ~ 10.
4. power cable protecting pipe according to claim 2, is characterized in that: the order number of described calcium carbonate >=1200 orders.
5. power cable protecting pipe according to claim 1, it is characterized in that: described oxidation inhibitor is antioxidant 1010.
6. power cable protecting pipe according to claim 1, it is characterized in that: described colour batch is orange or safran colour batch.
7. power cable protecting pipe according to claim 1, it is characterized in that: the parts by weight of described colour batch are 1.5.