CN106220988A - A kind of improvement warm water crosslinking black insulated aerial cable material - Google Patents
A kind of improvement warm water crosslinking black insulated aerial cable material Download PDFInfo
- Publication number
- CN106220988A CN106220988A CN201610706096.2A CN201610706096A CN106220988A CN 106220988 A CN106220988 A CN 106220988A CN 201610706096 A CN201610706096 A CN 201610706096A CN 106220988 A CN106220988 A CN 106220988A
- Authority
- CN
- China
- Prior art keywords
- black
- aerial cable
- warm water
- carbon black
- improvement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of improvement warm water crosslinking black insulated aerial cable material, change the most traditional method and i.e. base material A and B are expected to add high-carbon black pigment, carry out in proportion using attached suction method processing mode to become warm water crosslinking black aerial cable material after pelletize.The value that aerial cable and other black crosslinked polyethylene jacketed cable are widely used.
Description
Technical field
The present invention relates to electric wire and manufacture field, the warm water crosslinking black insulated aerial cable of a kind of improvement
Material.
Background technology
The existing traditional method of electric wire manufacturing manufactures black aerial cable, is respectively adopted two step method or one-step method
Add black masterbatch after silane crosslinked insulating material and carry out on-the-spot agitating use.
Two step method and one-step method silanes crosslinked Insulation Material also exist a fatal weakness jointly.
1, be respectively adopted A material B material mixing addition black color masterbatch, generation distributing precision is difficult to control to, special black masterbatch adds
Before to carry out drying otherwise water content and be difficult to produce preferable qualified products, easily give crosslinking.
2, specify according to cable product standard: black aerial cable material content of carbon black has certain requirement, use black masterbatch
Grain does not reaches requirement at all, can disperse inequality when black agglomerate is added, and content of carbon black is the most uneven, more have a strong impact on friendship
Connection degree gel calorimetric extends instability, causes product defective.
Summary of the invention
The present invention is to solve problem of the prior art, it is provided that a kind of improvement warm water crosslinking black insulated aerial cable
Material, content of carbon black is evenly distributed, and heat extends stable, and conforming product rate is high.
The present invention includes the component of following mass fraction:
Primary base material 20-80 part;
Primary B expects 10-50 part;
Silane 1-10 part;
Cross-linking agent 1-10 part;
Described primary base material includes the component of following mass fraction;
LDPE melting means (8-20) 10-80 part;
LDPE melting means (1.5-2.5) 20-30 part;
White carbon black height pigment 2-20 part;
Described primary B material includes the component of following mass fraction;
LLDPE 50-90 part;
LDPE 10-50 part;
Copper resistant agent 1-5 part;
Organotin 1-15 part;
Antioxidant 1-5 part;
Rheological agent 1-5 part;
White carbon black 2-20 part.
The present invention has the beneficial effects that: changes the most traditional method and i.e. base material A and B is expected to add high-carbon black pigment double
Screw pelletizer mixing granulation, carries out using attached suction method processing mode to become warm water crosslinking black insulated aerial cable the most in proportion
Material, content of carbon black is evenly distributed, and heat extends stable, and conforming product rate is high, protects aerial cable and other black crosslinked polyethylene
The value that set cable is widely used.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention will be further described.
Embodiment 1
Use basis ethylene pellet and the primary base material A of high-carbon black pigment preparation, including LDPE melting means (8-20) 10 parts, LDPE melting means
(1.5-2.5) 20 parts, white carbon black height pigment 20 parts.
Use basis ethylene pellet and high-carbon black pigment preparation primary B material, including LLDPE50 part, LDPE10 part, copper resistant agent
1 part, organotin 1 part, 5 parts of antioxidant, rheological agent 3 parts, white carbon black 20 parts.
Primary base material A and primary B material are stirred discharging in 2 hours vacuum packaging finished product through bipyramid roller equipment, each group
Part includes: primary base material 20 parts, and primary B expects 50 parts, 1 part of silane, cross-linking agent 5 parts.
Embodiment 2
Use the primary base material of base material high-carbon black pigment preparation, including LDPE melting means (8-20) 80 parts, LDPE melting means (1.5-2.5) 30
Part, white carbon black height pigment 20 parts.
Use base material high-carbon black pigment preparation primary B material, including LLDPE90 part, LDPE50 part, copper resistant agent 2 parts, organotin
15 parts, 1 part of antioxidant, rheological agent 1 part, white carbon black 2 parts.
Primary base material and primary B material are stirred discharging in 2 hours vacuum packaging finished product, each component through bipyramid roller equipment
Including: primary base material 80 parts, primary B expects 10 parts, 10 parts of silane, cross-linking agent 1 part.
Embodiment 3
Use the primary base material of base material high-carbon black pigment preparation, including LDPE melting means (8-20) 50 parts, LDPE melting means (1.5-2.5) 25
Part, white carbon black height pigment 10 parts.
Use base material high-carbon black pigment preparation primary B material, including LLDPE75 part, LDPE30 part, copper resistant agent 1 part, organotin
8 parts, 2 parts of antioxidant, rheological agent 2 parts, white carbon black 10 parts.
Primary base material and primary B material are stirred discharging in 2 hours vacuum packaging finished product, each component through bipyramid roller equipment
Including: primary base material 50 parts, primary B expects 30 parts, 5 parts of silane, cross-linking agent 2 parts.
Concrete typical case's test comparison result
Through Experimental Comparison, the material white carbon black of improvement is uniform, and performance is substantially better than traditional material.Optical screen ageing-resistant performance substantially carries
Height, gel content is also with raising.
The concrete application approach of the present invention is a lot, and the above is only the preferred embodiment of the present invention, and part ought be pointed out, for
For those skilled in the art, under the premise without departing from the principles of the invention, it is also possible to make some improvement, this
A little improvement also should be regarded as protection scope of the present invention.
Claims (1)
1. an improvement warm water crosslinking black insulated aerial cable material, it is characterised in that include the component of following mass fraction:
Primary base material A 20-80 part;
Primary B expects 10-50 part;
Silane 1-10 part;
Cross-linking agent 1-5 part;
Described primary base material A includes the component of following mass fraction;
Melt index is LDPE 10-80 part of 8-20;
Melt index is LDPE 20-30 part of 1.5-2.5;
White carbon black height pigment 2-20 part;
Described primary B material includes the component of following mass fraction;
LLDPE 50-90 part;
LDPE 10-50 part;
Copper resistant agent 1-2 part;
Organotin 1-15 part;
Antioxidant 1-5 part;
Rheological agent 1-3 part;
White carbon black 2-20 part.