CN104230224B - A kind of antifreeze light cellular partition board - Google Patents
A kind of antifreeze light cellular partition board Download PDFInfo
- Publication number
- CN104230224B CN104230224B CN201410418804.3A CN201410418804A CN104230224B CN 104230224 B CN104230224 B CN 104230224B CN 201410418804 A CN201410418804 A CN 201410418804A CN 104230224 B CN104230224 B CN 104230224B
- Authority
- CN
- China
- Prior art keywords
- flyash
- sodium
- antifreeze
- composite modified
- modified fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of antifreeze light cellular partition board, it is obtained by the raw material of following weight parts: flyash 60-80, cement 10-20, methylcellulose gum MC? 1-2, S-WAT powder 3-5, glass powder 1-2, trolamine 0.2-0.4, sodium-chlor 1-3, sodium carbonate 0.4-0.7, methane amide 0.3-0.5, sodium metaaluminate 1-2, xylogen 0.3-0.5, aluminium powder cream 1-2, composite modified fiber grain 4-6; Partition plate lightweight of the present invention, anti-folding, resistance to frost is strong simultaneously, can improve buildings freezing tolerance, and intensity is high simultaneously, long service life.
Description
Technical field
The present invention relates to building material field, is exactly a kind of antifreeze light cellular partition board.
Background technology
Light cellular partition board is a kind of novel energy-conserving walling material, constructs simple and convenient, reduces labour intensity, accelerating construction progress, saves project total cost, meets the requirement of different client to modern architecture indoor and outdoor surroundings.Light cellular partition board is divided into interior wall and exterior wall, and the partition plate of interior wall can expand the space in house fully.But there is the shortcoming such as surperficial damp suction surface halide accumulation, water ratio height in common magnesia partition plate.
Methylcellulose gum MC is almost insoluble in dehydrated alcohol, ether, acetone.Disperse rapidly in the hot water of 80 ~ 90 DEG C, swelling, dissolve rapidly after cooling, the aqueous solution is quite stable at normal temperatures, can gel during high temperature, and this gel can change mutually with solution with the height of temperature.There is excellent wettability, dispersiveness, cementability, thickening property, emulsifying property, water-retentivity and film-forming properties, and the opacity to grease.Institute's film forming has excellent toughness, flexibility and transparency, because belonging to non-ionic type, can with other emulsifying agent compatibility, but easily saltout, solution is stable within the scope of PH2-12.
Summary of the invention
The object of the present invention is to provide a kind of antifreeze light cellular partition board.
Above-mentioned purpose is realized by following scheme:
A kind of antifreeze light cellular partition board, it is characterized in that, it is obtained by the raw material of following weight parts:
Flyash 60-80, cement 10-20, methylcellulose gum MC1-2, S-WAT powder 3-5, glass powder 1-2, trolamine 0.2-0.4, sodium-chlor 1-3, sodium carbonate 0.4-0.7, methane amide 0.3-0.5, sodium metaaluminate 1-2, xylogen 0.3-0.5, aluminium powder cream 1-2, composite modified fiber grain 4-6;
Composite modified fiber grain is obtained by the raw material of following weight parts:
Attapulgite 10-20, cement 10-20, flyash 3-4, aluminium vanadine 20-50, benzene emulsion 1-3, perlite 1-2, calcium formiate 1-2, carbon nanotube 2-4, kaolin 0.2-0.5, oxidation inhibitor T5010.5-0.7, fibrous magnesium silicate 2-3, Sumstar 190 3-5, aluminum oxide 1-2;
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminium vanadine, perlite are ground, crossing 100-120 mesh sieve, is then that the salt solution of 4-8% mixes with concentration, stir, leave standstill, filter and drying after, after all the other raw material blendings, under 500-700 rev/min, 35-45 DEG C is stirred after 15-25 minute, adds amount of water, granulation, grain diameter at 6-8mm, then is dried, and to obtain final product;
The antifreeze light cellular partition board of described one, is characterized in that:
Its preparation method is: get cement plus water and stir, then add flyash by weight, sodium-chlor, composite modified fiber grain be uniformly mixed, after finally adding surplus stock mixing, shaping, cutting, maintenance, to obtain final product.
Beneficial effect of the present invention is: partition plate lightweight of the present invention, anti-folding, and resistance to frost is strong simultaneously, can improve buildings freezing tolerance, and intensity is high simultaneously, long service life.
Embodiment
A kind of antifreeze light cellular partition board, it is obtained by the raw material of following weight (kg):
Flyash 60, cement 20, methylcellulose gum MC1, S-WAT powder 5, glass powder 1, trolamine 0.4, sodium-chlor 3, sodium carbonate 0.4, methane amide 0.5, sodium metaaluminate 1, xylogen 0.5, aluminium powder cream 2, composite modified fiber grain 6;
Composite modified fiber grain is obtained by the raw material of following weight (kg):
Attapulgite 20, cement 20, flyash 4, aluminium vanadine 40, benzene emulsion 3, perlite 2, calcium formiate 1, carbon nanotube 4, kaolin 0.2, oxidation inhibitor T5010.7, fibrous magnesium silicate 3, Sumstar 190 5, aluminum oxide 1;
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminium vanadine, perlite are ground, crossing 100 mesh sieves, is then that the salt solution of 8% mixes with concentration, stir, leave standstill, filter and drying after, after all the other raw material blendings, under 700 revs/min, 45 DEG C are stirred after 25 minutes, add amount of water, granulation, grain diameter at 6-8mm, then is dried, and to obtain final product;
The antifreeze light cellular partition board of described one,
Its preparation method is: get cement plus water and stir, then add flyash by weight, sodium-chlor, composite modified fiber grain be uniformly mixed, after finally adding surplus stock mixing, shaping, cutting, maintenance, to obtain final product.
The unit weight of the present embodiment is 480Kg/m
3, ultimate compression strength is 6.9MPa.
Claims (2)
1. an antifreeze light cellular partition board, is characterized in that, it is obtained by the raw material of following weight parts:
Flyash 60-80, cement 10-20, methylcellulose gum MC1-2, S-WAT powder 3-5, glass powder 1-2, trolamine 0.2-0.4, sodium-chlor 1-3, sodium carbonate 0.4-0.7, methane amide 0.3-0.5, sodium metaaluminate 1-2, xylogen 0.3-0.5, aluminium powder cream 1-2, composite modified fiber grain 4-6;
Composite modified fiber grain is obtained by the raw material of following weight parts:
Attapulgite 10-20, cement 10-20, flyash 3-4, aluminium vanadine 20-50, benzene emulsion 1-3, perlite 1-2, calcium formiate 1-2, carbon nanotube 2-4, kaolin 0.2-0.5, oxidation inhibitor T5010.5-0.7, fibrous magnesium silicate 2-3, Sumstar 190 3-5, aluminum oxide 1-2;
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminium vanadine, perlite are ground, crossing 100-120 mesh sieve, is then that the salt solution of 4-8% mixes with concentration, stir, leave standstill, filter and drying after, after all the other raw material blendings, under 500-700 rev/min, 35-45 DEG C is stirred after 15-25 minute, adds amount of water, granulation, grain diameter at 6-8mm, then is dried, and to obtain final product.
2. the antifreeze light cellular partition board of one according to claim 1, is characterized in that:
Its preparation method is: get cement plus water and stir, then add flyash by weight, sodium-chlor, composite modified fiber grain be uniformly mixed, after finally adding surplus stock mixing, shaping, cutting, maintenance, to obtain final product.