CN104212564A - High-temperature lubricant - Google Patents
High-temperature lubricant Download PDFInfo
- Publication number
- CN104212564A CN104212564A CN201410417041.0A CN201410417041A CN104212564A CN 104212564 A CN104212564 A CN 104212564A CN 201410417041 A CN201410417041 A CN 201410417041A CN 104212564 A CN104212564 A CN 104212564A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricant
- temperature lubricant
- high temperature
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-temperature lubricant. The high-temperature lubricant is prepared from the following raw materials in parts by weight: 15-25 parts of vegetable oil base oil, 6-10 parts of calcium alkylbenzene sulfonate, 3-7 parts of sulfurized isobutylene, 4-6 parts of glycerol monostearate, 3-5 parts of chlorinated paraffin, 8-15 parts of graphite micropowder, 4-6 parts of lithium base bentonite, 1-5 parts of aluminium dihydrogen phosphate powder, 5-9 parts of ethylenediamine tetracetic acid tetrasodium and 2-4 parts of long-chain sodium alkyl sulfate. The high-temperature lubricant has the beneficial effects that the lubricant has good high temperature resistance and appropriate viscosity and oil film thickness and also has good antirust and anticorrosion properties.
Description
Technical field
The present invention relates to a kind of high temperature lubricant.
Background technology
High temperature lubricant, high temperature resistantly reaches 1500 ° of C, and lubricity is preeminent, water-based, nontoxic, pollution-free, high-environmental, has superior film forming adhesive power, and with molten metal (such as aluminium, copper, steel etc.) or glass melt oar and do not play any reaction, at high temperature still possess lubrication, release, anti-oxidant, anti-stick glutinous special-effect.Spraying this product can make the surface of contact prevent corrosion, increases work-ing life. the oilness of its uniqueness, and viscosity is not much higher than like product, bright, bright and clean after can making formed product, more aobvious top grade, especially be applied to the processing of degree of difficulty height, its effect is more notable.The scope of application: 1. aluminium bar is produced, aluminium extruded type industry, aluminium die casting, aluminum casting, magnesium, titanium, lead waits metal low pressure, gravitational casting lubricating release; 2. evaporation, sputter, Vacuum Deposition evaporation boat, plating makes protective material, coating agent; 3. high temperature protection, lubrication, the demoulding is release, anti-oxidant, the anti-welding coating of metal solder; 4. metal casting, forging, squeezes type industry; 5. glass industry, fire-resistant oxidation resistant coating, dry lubrication interface, corrosion-resistant interface; 6. high temperature sintering crucible smelting tool and not viscosity; 7. hardware lubrication, uses under the high temperature height abrasion conditions such as bearing.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, provides a kind of lubricant, and resistance to elevated temperatures is good, and has suitable viscosity and oil film thickness, has good antirust, antiseptic property simultaneously.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, a kind of high temperature lubricant is made up of the raw material of following parts by weight:
Vegetables oil base oil 15-25 part, alkyl benzene calcium sulfonate 6-10 part, sulfide isobutene 3-7 part, Zerol 4-6 part, clorafin 3-5 part, graphite microparticles 8-15 part, lithium bentonite 4-6 part, biphosphate aluminium powder 1-5 part, tetrasodium ethylenediamine tetraacetate 5-9 part, chain alkyl sodium sulfate 2-4 part.
The invention has the beneficial effects as follows, lubricant of the present invention, resistance to elevated temperatures is good, and has suitable viscosity and oil film thickness, has good antirust, antiseptic property simultaneously.
Embodiment
embodiment 1
A kind of high temperature lubricant, be made up of the raw material of following parts by weight:
Vegetables oil base oil 15 parts, alkyl benzene calcium sulfonate 6 parts, sulfide isobutene 3 parts, Zerol 4 parts, clorafin 3 parts, graphite microparticles 8 parts, lithium bentonite 4 parts, biphosphate aluminium powder 1 part, tetrasodium ethylenediamine tetraacetate 5 parts, 2 parts, chain alkyl sodium sulfate.
embodiment 2
A kind of high temperature lubricant, be made up of the raw material of following parts by weight:
Vegetables oil base oil 25 parts, alkyl benzene calcium sulfonate 10 parts, sulfide isobutene 7 parts, Zerol 6 parts, clorafin 5 parts, graphite microparticles 15 parts, lithium bentonite 6 parts, biphosphate aluminium powder 5 parts, tetrasodium ethylenediamine tetraacetate 9 parts, 4 parts, chain alkyl sodium sulfate.
Claims (1)
1. a high temperature lubricant, is characterized in that: be made up of the raw material of following parts by weight:
Vegetables oil base oil 15-25 part, alkyl benzene calcium sulfonate 6-10 part, sulfide isobutene 3-7 part, Zerol 4-6 part, clorafin 3-5 part, graphite microparticles 8-15 part, lithium bentonite 4-6 part, biphosphate aluminium powder 1-5 part, tetrasodium ethylenediamine tetraacetate 5-9 part, chain alkyl sodium sulfate 2-4 part.