CN104212116A - Plastic alloy - Google Patents
Plastic alloy Download PDFInfo
- Publication number
- CN104212116A CN104212116A CN201410430378.5A CN201410430378A CN104212116A CN 104212116 A CN104212116 A CN 104212116A CN 201410430378 A CN201410430378 A CN 201410430378A CN 104212116 A CN104212116 A CN 104212116A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyblend
- oxidation inhibitor
- fire retardant
- pentene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plastic alloy which comprises the following components in parts by weight: 8-15 parts of high-density polyethylene, 6-10 parts of methyltriethoxysilane, 3-7 parts of sodium methacrylate, 0.5-1.3 parts of zinc stearate, 1.3-5.6 parts of glycerol monostearate, 2.2-6 parts of epoxidized soybean oil, 15-25 parts of ABS, 3.5-6 parts of a thickening agent, 6-10 parts of poly-4-methyl-1-pentene, 1-4 parts of white oil, 1.4-2.6 parts of antioxidant and 3.5-8 parts of fire retardant. The plastic alloy disclosed by the invention has the advantages of high impact strength, good tensile and bending resistance, excellent acid alkali resistance, and stable comprehensive properties and can be widely applied to the fields of automobiles, electronics and the like.
Description
Technical field
The present invention relates to a kind of polyblend.
Background technology
Polyblend utilizes the method for physical blending or chemical graft and a class novel material of the high-performance obtained, functionalization, customizations.Polyblend product can be widely used in the fields such as automobile, electronics, precision instrument, office equipment, wrapping material, material of construction.It can improve or improve the performance of existing plastics and reduce costs, and has become one of kind enlivened the most in plastics industry, has increased very rapid.China's plastic industry will be got a clear understanding of the situation, and finds gap accurately, seizes the opportunity, and strengthens input in science and technology, accelerates development Plastics Industry, world development level of emulating.
Summary of the invention
For the deficiencies in the prior art, the technical problem to be solved in the present invention is, provides a kind of polyblend, and shock strength is large, stretching-resisting bending-resisting performance is good, and acid-proof alkaline is excellent, have stable over-all properties, is widely used in the field such as automobile, electronics.
For solving the problems of the technologies described above, technical scheme of the present invention is, a kind of polyblend, and following component consumption is with weight parts:
High density polyethylene(HDPE) 8-15 part, Union carbide A-162 6-10 part, sodium methacrylate 3-7 part, Zinic stearas 0.5-1.3 part, glyceryl monostearate 1.3-5.6 part, epoxy soybean oil 2.2-6 part, ABS15-25 part, thickening material 3.5-6 part, poly-4-methyl-1-pentene 6-10 part, white oil 1-4 part, oxidation inhibitor 1.4-2.6 part, fire retardant 3.5-8 part.
Optimisation technique scheme of the present invention is, a kind of polyblend, and following component consumption is with weight parts:
High density polyethylene(HDPE) 12 parts, Union carbide A-162 8 parts, sodium methacrylate 5 parts, Zinic stearas 0.9 part, glyceryl monostearate 3.2 parts, epoxy soybean oil 4.3 parts, ABS20 part, thickening material 4.8 parts, poly-4-methyl-1-pentene 8 parts, white oil 2.5 parts, 1.9 parts, oxidation inhibitor, fire retardant 5.5 parts.
Optimisation technique scheme of the present invention is, described fire retardant is aluminium hydroxide.
Optimisation technique scheme of the present invention is, described oxidation inhibitor is Phosphorus oxidation inhibitor.
The invention has the beneficial effects as follows, polyblend shock strength of the present invention is large, stretching-resisting bending-resisting performance is good, and acid-proof alkaline is excellent, have stable over-all properties, is widely used in the field such as automobile, electronics.
Embodiment
embodiment 1
A kind of polyblend, following component consumption is with weight parts:
High density polyethylene(HDPE) 8 parts, Union carbide A-162 6 parts, sodium methacrylate 3 parts, Zinic stearas 0.5 part, glyceryl monostearate 1.3 parts, epoxy soybean oil 2.2 parts, ABS15 part, thickening material 3.5 parts, poly-4-methyl-1-pentene 6 parts, white oil 1 part, 1.4 parts, oxidation inhibitor, fire retardant 3.5 parts.
embodiment 2
A kind of polyblend, following component consumption is with weight parts:
High density polyethylene(HDPE) 15 parts, Union carbide A-162 10 parts, sodium methacrylate 7 parts, Zinic stearas 1.3 parts, glyceryl monostearate 5.6 parts, epoxy soybean oil 6 parts, ABS25 part, thickening material 6 parts, poly-4-methyl-1-pentene 10 parts, white oil 4 parts, 2.6 parts, oxidation inhibitor, fire retardant 8 parts.
embodiment 3
A kind of polyblend, following component consumption is with weight parts:
High density polyethylene(HDPE) 12 parts, Union carbide A-162 8 parts, sodium methacrylate 5 parts, Zinic stearas 0.9 part, glyceryl monostearate 3.2 parts, epoxy soybean oil 4.3 parts, ABS20 part, thickening material 4.8 parts, poly-4-methyl-1-pentene 8 parts, white oil 2.5 parts, 1.9 parts, oxidation inhibitor, fire retardant 5.5 parts.
Claims (4)
1. a polyblend, is characterized in that: following component consumption is with weight parts:
High density polyethylene(HDPE) 8-15 part, Union carbide A-162 6-10 part, sodium methacrylate 3-7 part, Zinic stearas 0.5-1.3 part, glyceryl monostearate 1.3-5.6 part, epoxy soybean oil 2.2-6 part, ABS15-25 part, thickening material 3.5-6 part, poly-4-methyl-1-pentene 6-10 part, white oil 1-4 part, oxidation inhibitor 1.4-2.6 part, fire retardant 3.5-8 part.
2. polyblend according to claim 1, is characterized in that: described plastics are made up of each component of following parts by weight:
High density polyethylene(HDPE) 12 parts, Union carbide A-162 8 parts, sodium methacrylate 5 parts, Zinic stearas 0.9 part, glyceryl monostearate 3.2 parts, epoxy soybean oil 4.3 parts, ABS20 part, thickening material 4.8 parts, poly-4-methyl-1-pentene 8 parts, white oil 2.5 parts, 1.9 parts, oxidation inhibitor, fire retardant 5.5 parts.
3. polyblend according to claim 1, is characterized in that: described fire retardant is aluminium hydroxide.
4. polyblend according to claim 1, is characterized in that: described oxidation inhibitor is Phosphorus oxidation inhibitor.