CN104212015A - Steel wire rope core flame-retardant belt bonding core rubber - Google Patents
Steel wire rope core flame-retardant belt bonding core rubber Download PDFInfo
- Publication number
- CN104212015A CN104212015A CN201410513684.5A CN201410513684A CN104212015A CN 104212015 A CN104212015 A CN 104212015A CN 201410513684 A CN201410513684 A CN 201410513684A CN 104212015 A CN104212015 A CN 104212015A
- Authority
- CN
- China
- Prior art keywords
- parts
- sizing agent
- rubber
- carbon blacks
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to steel wire rope core flame-retardant belt bonding core rubber which is made of raw materials including, by weight, 0-10 parts of natural rubber, 80-90 parts of neoprene, 0-10 parts of butadiene rubber, 0.5-0.8 part of accelerant CZ, 4-6 parts of zinc oxide, 1-2 parts of stearic acid, 5-8 parts of magnesium oxide, 0.2-0.3 part of sulfur, 3-5 parts of coumarone, 35-40 parts of general carbon black, 10-15 parts of white carbon black, 3-5 parts of adhesives 112A, 4-6 parts of adhesives FR, 1-2 parts of cobalt boroacylate, 8-12 parts of chlorinated paraffin, 6-8 parts of antimonous oxide, 10-15 parts of aluminum hydroxide, 8-10 parts of zinc borate, 1-2 parts of antioxidant RD and 0.5-1 part of antioxidant 4010NA. The neoprene, the natural rubber and the butadiene rubber serve as main raw materials, reasonable elixir is added into the rubber, the strength of the core rubber is effectively improved, the produced core rubber is fine in flame resistance, adhesiveness with a steel wire rope core, flexing resistance and ageing resistance, and has fine compatibility with covering rubber.
Description
Technical field
The invention belongs to rubber item field, be specifically related to a kind of Steel cord inhibiting tape and bind core glue.
Background technology
The sizing material that existing Steel cord inhibiting tape binds core glue generally adopts the mixing sizing materials of making of material such as rubber, vulcanizing agent, anti-aging agent, fire retardant, strengthening agent, tackiness agent, through roll lower sheet compound with rubber cover after, cold pressing after laminating sulfuration with wireline, in the middle of forming, have wireline to do the fire retarding conveying band of framework material.Existing wireline inhibiting tape appears vividly and has certain fire-retardant and bond properties, but sizing material is lower to the penetrating power of wireline, particularly added a large amount of inorganic combustion inhibitors, although can improve dispersing property by the mixing method of multistage, but poor with the viscous force of wireline, poor with the consistency covering, and easily aging.
Summary of the invention
Technical problem to be solved by this invention is to overcome above-mentioned deficiency, provides a kind of Steel cord inhibiting tape to bind core glue, and take neoprene latex, natural gum, cis-butadiene cement is main raw material, by adding rational ingredients, the core glue intensity of producing is high, and flame retardant properties is good, has good consistency with rubber cover.
Technical scheme of the present invention: a kind of Steel cord inhibiting tape binds core glue, raw material by following weight part is made: 0～10 part of natural gum, 80～90 parts of neoprene latexs, 0～10 part of cis-butadiene cement, 0.5～0.8 part of accelerant CZ, 4～6 parts, zinc oxide, 1～2 part of stearic acid, 5～8 parts, magnesium oxide, 0.2～0.3 part, sulphur, 3～5 parts of coumarones, 35～40 parts of general carbon blacks, 10～15 parts of white carbon blacks, 3～5 parts of sizing agent 112A, 4～6 parts of sizing agent FR, 1～2 part of cobalt boracylate, 8～12 parts of clorafins, 6～8 parts of antimonous oxides, 10～15 parts, aluminium hydroxide, 8～10 parts of zinc borates, 1～2 part of anti-RD, 0.5～1 part of anti-4010NA.
Described Steel cord inhibiting tape binds the screening formulation of core glue: 10 parts of natural gums, 80 parts of neoprene latexs, 10 parts of cis-butadiene cements, 0.6 part of accelerant CZ; 4 parts, zinc oxide, 1 part of stearic acid, 6 parts, magnesium oxide, 0.2 part, sulphur; 5 parts of coumarones, 35 parts of general carbon blacks, 15 parts of white carbon blacks; 3.5 parts of sizing agent 112A, 5 parts of sizing agent FR, 2 parts of cobalt boracylates; 10 parts of clorafins, 8 parts of antimonous oxides, 15 parts, aluminium hydroxide; 10 parts of zinc borates, 1.5 parts of anti-RD, 0.5 part of anti-4010NA.
Further, described Steel cord inhibiting tape binds the screening formulation of core glue: 10 parts of natural gums, 90 parts of neoprene latexs, 0.8 part of accelerant CZ; 6 parts, zinc oxide, 1.5 parts of stearic acid, 5 parts, magnesium oxide, 0.2 part, sulphur; 4 parts of coumarones, 40 parts of general carbon blacks, 10 parts of white carbon blacks; 4 parts of sizing agent 112A, 6 parts of sizing agent FR, 2 parts of cobalt boracylates; 12 parts of clorafins, 8 parts of antimonous oxides, 14 parts, aluminium hydroxide; 9 parts of zinc borates, 1.8 parts of anti-RD, 0.7 part of anti-4010NA.
Further, described Steel cord inhibiting tape binds the screening formulation of core glue: 5 parts of natural gums, 85 parts of neoprene latexs, 10 parts of cis-butadiene cements; 0.5 part of accelerant CZ, 4 parts, zinc oxide, 1.8 parts of stearic acid, 6 parts, magnesium oxide; 0.25 part, sulphur, 5 parts of coumarones, 38 parts of general carbon blacks, 12 parts of white carbon blacks; 5 parts of sizing agent 112A, 5 parts of sizing agent FR, 2 parts of cobalt boracylates; 12 parts of clorafins, 7 parts of antimonous oxides, 15 parts, aluminium hydroxide; 9 parts of zinc borates, 1.3 parts of anti-RD, 0.7 part of anti-4010NA.
Further, described Steel cord inhibiting tape binds the screening formulation of core glue: 8 parts of natural gums, 86 parts of neoprene latexs, 6 parts of cis-butadiene cements; 0.6 part of accelerant CZ, 4 parts, zinc oxide, 1.2 parts of stearic acid, 6 parts, magnesium oxide; 0.2 part, sulphur, 5 parts of coumarones, 36 parts of general carbon blacks, 14 parts of white carbon blacks; 4 parts of sizing agent 112A, 6 parts of sizing agent FR, 2 parts of cobalt boracylates; 10.5 parts of clorafins, 6 parts of antimonous oxides, 13 parts, aluminium hydroxide; 10 parts of zinc borates, 1.5 parts of anti-RD, 0.5 part of anti-4010NA.
The present invention compared with prior art has following beneficial effect: the present invention be take neoprene latex, natural gum and cis-butadiene cement as main raw material, by add rational ingredients in sizing material, effectively improved the intensity of core glue, and core glue and the good flame resistance of producing, binding property with Steel cord, resistance toly subdue with aging well, there is good consistency with rubber cover.
Embodiment
Embodiment 1
Steel cord inhibiting tape binds a core glue, is made: 10 parts of natural gums, 80 parts of neoprene latexs, 10 parts of cis-butadiene cements by the raw material with weight part; 0.6 part of accelerant CZ, 4 parts, zinc oxide, 1 part of stearic acid, 6 parts, magnesium oxide; 0.2 part, sulphur, 5 parts of coumarones, 35 parts of general carbon blacks, 15 parts of white carbon blacks; 3.5 parts of sizing agent 112A, 5 parts of sizing agent FR, 2 parts of cobalt boracylates; 10 parts of clorafins, 8 parts of antimonous oxides, 15 parts, aluminium hydroxide; 10 parts of zinc borates, 1.5 parts of anti-RD, 0.5 part of anti-4010NA.
Embodiment 2
Steel cord inhibiting tape binds a core glue, is made: 10 parts of natural gums, 90 parts of neoprene latexs, 0.8 part of accelerant CZ by the raw material with weight part; 6 parts, zinc oxide, 1.5 parts of stearic acid, 5 parts, magnesium oxide, 0.2 part, sulphur; 4 parts of coumarones, 40 parts of general carbon blacks, 10 parts of white carbon blacks; 4 parts of sizing agent 112A, 6 parts of sizing agent FR, 2 parts of cobalt boracylates; 12 parts of clorafins, 8 parts of antimonous oxides, 14 parts, aluminium hydroxide; 9 parts of zinc borates, 1.8 parts of anti-RD, 0.7 part of anti-4010NA.
Embodiment 3
Steel cord inhibiting tape binds a core glue, is made: 5 parts of natural gums, 85 parts of neoprene latexs, 10 parts of cis-butadiene cements by the raw material with weight part; 0.5 part of accelerant CZ, 4 parts, zinc oxide, 1.8 parts of stearic acid, 6 parts, magnesium oxide; 0.25 part, sulphur, 5 parts of coumarones, 38 parts of general carbon blacks, 12 parts of white carbon blacks; 5 parts of sizing agent 112A, 5 parts of sizing agent FR, 2 parts of cobalt boracylates; 12 parts of clorafins, 7 parts of antimonous oxides, 15 parts, aluminium hydroxide; 9 parts of zinc borates, 1.3 parts of anti-RD, 0.7 part of anti-4010NA.
Embodiment 4
Steel cord inhibiting tape binds a core glue, is made: 8 parts of natural gums, 86 parts of neoprene latexs, 6 parts of cis-butadiene cements by the raw material with weight part; 0.6 part of accelerant CZ, 4 parts, zinc oxide, 1.2 parts of stearic acid, 6 parts, magnesium oxide; 0.2 part, sulphur, 5 parts of coumarones, 36 parts of general carbon blacks, 14 parts of white carbon blacks; 4 parts of sizing agent 112A, 6 parts of sizing agent FR, 2 parts of cobalt boracylates; 10.5 parts of clorafins, 6 parts of antimonous oxides, 13 parts, aluminium hydroxide; 10 parts of zinc borates, 1.5 parts of anti-RD, 0.5 part of anti-4010NA.
The preparation method of above-described embodiment: 1) natural gum of above-mentioned weight part, neoprene latex and cis-butadiene cement are dropped in mill and plasticated, the sizing material of plasticating is standby; 2) sizing material of plasticating is dropped in Banbury mixer, add successively above-mentioned weight part in by carbon black and white carbon black, accelerant CZ, zinc oxide, stearic acid, magnesium oxide, coumarone, sizing agent 112A, sizing agent FR, cobalt boracylate,, clorafin, antimonous oxide, aluminium hydroxide, zinc borate, anti-RD, anti-4010NA, sulphur, after stirring, obtain rubber unvulcanizate; 3) sizing material mixing is squeezed out to the film of respective thickness by mill, obtain Steel cord inhibiting tape and bind core glue.
Above-mentioned equipment used is conventional use equipment, the routine selection that the thickness that the time in operation and institute go out film is those skilled in the art.
It is high that the Steel cord inhibiting tape that our company produces binds core glue intensity, and good flame resistance, with the binding property of Steel cord, is resistance toly subdued with aging well, has good consistency with rubber cover.Through paying a return visit, use producer, flame retardant properties, intensity, hardness, tensile strength, elongation rate of tensile failure, bond strength, aging rear (the 100 ° of C * 168h) tensile strength of all reacting core glue meet the requirements, and all reach physicals and the using property data of conveying belt national Specification.
Claims (5)
1. a Steel cord inhibiting tape binds core glue, it is characterized in that it is made by the raw material of following weight part: 0～10 part of natural gum, 80～90 parts of neoprene latexs, 0～10 part of cis-butadiene cement, 0.5～0.8 part of accelerant CZ, 4～6 parts, zinc oxide, 1～2 part of stearic acid, 5～8 parts, magnesium oxide, 0.2～0.3 part, sulphur, 3～5 parts of coumarones, 35～40 parts of general carbon blacks, 10～15 parts of white carbon blacks, 3～5 parts of sizing agent 112A, 4～6 parts of sizing agent FR, 1～2 part of cobalt boracylate, 8～12 parts of clorafins, 6～8 parts of antimonous oxides, 10～15 parts, aluminium hydroxide, 8～10 parts of zinc borates, 1～2 part of anti-RD, 0.5～1 part of anti-4010NA.
2. Steel cord inhibiting tape according to claim 1 binds core glue, it is characterized in that it is made by the raw material of following weight part: 10 parts of natural gums, 80 parts of neoprene latexs; 10 parts of cis-butadiene cements; 0.6 part of accelerant CZ, 4 parts, zinc oxide, 1 part of stearic acid; 6 parts, magnesium oxide; 0.2 part, sulphur, 5 parts of coumarones, 35 parts of general carbon blacks; 15 parts of white carbon blacks; 3.5 parts of sizing agent 112A, 5 parts of sizing agent FR, 2 parts of cobalt boracylates; 10 parts of clorafins; 8 parts of antimonous oxides, 15 parts, aluminium hydroxide, 10 parts of zinc borates; 1.5 parts of anti-RD, 0.5 part of anti-4010NA.
3. Steel cord inhibiting tape according to claim 1 binds core glue; it is characterized in that it is made by the raw material of following weight part: 10 parts of natural gums, 90 parts of neoprene latexs, 0.8 part of accelerant CZ; 6 parts, zinc oxide; 1.5 parts of stearic acid, 5 parts, magnesium oxide, 0.2 part, sulphur; 4 parts of coumarones; 40 parts of general carbon blacks, 10 parts of white carbon blacks, 4 parts of sizing agent 112A; 6 parts of sizing agent FR; 2 parts of cobalt boracylates, 12 parts of clorafins, 8 parts of antimonous oxides; 14 parts, aluminium hydroxide; 9 parts of zinc borates, 1.8 parts of anti-RD, 0.7 part of anti-4010NA.
4. Steel cord inhibiting tape according to claim 1 binds core glue, it is characterized in that it is made by the raw material of following weight part: 5 parts of natural gums, 85 parts of neoprene latexs; 10 parts of cis-butadiene cements; 0.5 part of accelerant CZ, 4 parts, zinc oxide, 1.8 parts of stearic acid; 6 parts, magnesium oxide; 0.25 part, sulphur, 5 parts of coumarones, 38 parts of general carbon blacks; 12 parts of white carbon blacks; 5 parts of sizing agent 112A, 5 parts of sizing agent FR, 2 parts of cobalt boracylates; 12 parts of clorafins; 7 parts of antimonous oxides, 15 parts, aluminium hydroxide, 9 parts of zinc borates; 1.3 parts of anti-RD, 0.7 part of anti-4010NA.
5. Steel cord inhibiting tape according to claim 1 binds core glue, it is characterized in that it is made by the raw material of following weight part: 8 parts of natural gums, 86 parts of neoprene latexs; 6 parts of cis-butadiene cements; 0.6 part of accelerant CZ, 4 parts, zinc oxide, 1.2 parts of stearic acid; 6 parts, magnesium oxide; 0.2 part, sulphur, 5 parts of coumarones, 36 parts of general carbon blacks; 14 parts of white carbon blacks; 4 parts of sizing agent 112A, 6 parts of sizing agent FR, 2 parts of cobalt boracylates; 10.5 parts of clorafins; 6 parts of antimonous oxides, 13 parts, aluminium hydroxide, 10 parts of zinc borates; 1.5 parts of anti-RD, 0.5 part of anti-4010NA.