CN104211337A - Crack-resistant light partition board containing polystyrene fibers - Google Patents
Crack-resistant light partition board containing polystyrene fibers Download PDFInfo
- Publication number
- CN104211337A CN104211337A CN201410419369.6A CN201410419369A CN104211337A CN 104211337 A CN104211337 A CN 104211337A CN 201410419369 A CN201410419369 A CN 201410419369A CN 104211337 A CN104211337 A CN 104211337A
- Authority
- CN
- China
- Prior art keywords
- partition board
- raw material
- grain
- board containing
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a crack-resistant light partition board containing polystyrene fibers. The polystyrene fibers, rubber particles and vegetable glue powder are particularly added to increase the crack resistance, and meanwhile, materials such as hollow glass beads are added, so that the crack-resistant light partition board disclosed by the invention has the characteristics of being light in weight, high in strength, heat-insulating, sound-isolating and heat-preserving, convenient to install and fast in construction speed.
Description
Technical field
The present invention relates to building material field, is exactly a kind of cracking resistance light cellular partition board containing poly-third vinyl fiber.
Background technology
Light cellular partition board is a kind of novel energy-conserving walling material, constructs simple and convenient, reduces labour intensity, accelerating construction progress, saves project total cost, meets the requirement of different client to modern architecture indoor and outdoor surroundings.Light cellular partition board is divided into interior wall and exterior wall, and the partition plate of interior wall can expand the space in house fully.But there is the shortcoming such as surperficial damp suction surface halide accumulation, water ratio height in common magnesia partition plate.
Poly-third vinyl fiber polypropylene fibre, being also called technical fiber, concrete fiber, anti-crack fiber, defend and split fibre or synthon, plastic optical fibre etc., is be exclusively used in plasticity crack resistence fiber in cement concrete.
Summary of the invention
The object of the present invention is to provide a kind of cracking resistance light cellular partition board containing poly-third vinyl fiber.
Above-mentioned purpose is realized by following scheme:
A cracking resistance light cellular partition board containing poly-third vinyl fiber, it is characterized in that, it is obtained by the raw material of following weight parts:
Pearlstone 10-20, carbide slag 10-12, hollow glass micropearl 20-30, poly-third vinyl fiber 1-2, gummy powder 0.2-0.4, pure-acrylic emulsion 1-2, sanitas al687 0.1-0.2, rubber grain 1-2, magnesium silicofluoride 0.1-0.2, nano zine oxide 1-3, cement 2-4, Calucium Silicate powder 1-2, humic acid 0.1-0.2, trimeric cyanamide 1-2, oligose 0.5-1, aluminium powder cream 0.5-0.8, composite modified fiber grain 10-12;
Composite modified fiber grain is obtained by the raw material of following weight parts:
Attapulgite 10-20, flyash 3-4, aluminium vanadine 2-5, benzene emulsion 1-3, perlite 1-2, calcium formiate 1-2, carbon nanotube 2-4, kaolin 0.2-0.5, oxidation inhibitor T501 0.5-0.7, fibrous magnesium silicate 2-3, Sumstar 190 3-5, aluminum oxide 1-2;
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminium vanadine, perlite are ground, crossing 100-120 mesh sieve, is then that the salt solution of 4-8% mixes with concentration, stir, leave standstill, filter and drying after, after all the other raw material blendings, under 500-700 rev/min, 35-45 DEG C is stirred after 15-25 minute, adds amount of water, granulation, grain diameter at 3-5mm, then is dried, and to obtain final product.
Described a kind of cracking resistance light cellular partition board containing poly-third vinyl fiber, is characterized in that:
Its preparation method is:
Power taking rock ballast is broken, putting into concentration is that the sodium hydroxide solution of 4-6% soaks 5-8 hour, filter, wash 3-5 time, dry, more even with cement mixing, add all the other raw material stirring except aluminium powder cream again to mix, finally add aluminium powder cream to stir to obtain slip, cutting shaping through single-lead-screw extruding briquetting machine, natural curing, to obtain final product.
Beneficial effect of the present invention is: the present invention adds poly-third vinyl fiber, rubber grain and gummy powder especially, while increasing splitting resistance, add the material such as hollow glass micropearl, the present invention being has that high-strength light, anti-inflammation are heat insulation, sound-insulating, be convenient to the feature of installing, speed of application is fast.
Embodiment
A cracking resistance light cellular partition board containing poly-third vinyl fiber, it is obtained by the raw material of following weight (kg):
Pearlstone 20, carbide slag 12, hollow glass micropearl 30, poly-third vinyl fiber 2, gummy powder 0.2, pure-acrylic emulsion 2, sanitas al687 0.1, rubber grain 2, magnesium silicofluoride 0.1, nano zine oxide 3, cement 4, Calucium Silicate powder 1, humic acid 0.2, trimeric cyanamide 1, oligose 1, aluminium powder cream 0.8, composite modified fiber grain 12;
Composite modified fiber grain is obtained by the raw material of following weight (kg):
Attapulgite 20, flyash 4, aluminium vanadine 5, benzene emulsion 1, perlite 2, calcium formiate 1, carbon nanotube 3, kaolin 0.5, oxidation inhibitor T501 0.7, fibrous magnesium silicate 2, Sumstar 190 3.5, aluminum oxide 2;
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminium vanadine, perlite are ground, crossing 120 mesh sieves, is then that the salt solution of 7% mixes with concentration, stir, leave standstill, filter and drying after, after all the other raw material blendings, under 600 revs/min, 37 DEG C are stirred after 18 minutes, add amount of water, granulation, grain diameter at 3-5mm, then is dried, and to obtain final product.
Described a kind of cracking resistance light cellular partition board containing poly-third vinyl fiber, its preparation method is:
Power taking rock ballast is broken, putting into concentration is that the sodium hydroxide solution of 4-6% soaks, 7 hours, filter, wash 5 times, dry, even with cement mixing again, then add all the other raw material stirring except aluminium powder cream and mix, finally add aluminium powder cream and to stir to obtain slip, shaping through single-lead-screw extruding briquetting machine, cutting, natural curing, to obtain final product.
The unit weight of the present embodiment is 560Kg/m
3, ultimate compression strength is 7.1MPa.
Claims (2)
1. the cracking resistance light cellular partition board containing poly-third vinyl fiber, it is characterized in that, it is obtained by the raw material of following weight parts:
Pearlstone 10-20, carbide slag 10-12, hollow glass micropearl 20-30, poly-third vinyl fiber 1-2, gummy powder 0.2-0.4, pure-acrylic emulsion 1-2, sanitas al687 0.1-0.2, rubber grain 1-2, magnesium silicofluoride 0.1-0.2, nano zine oxide 1-3, cement 2-4, Calucium Silicate powder 1-2, humic acid 0.1-0.2, trimeric cyanamide 1-2, oligose 0.5-1, aluminium powder cream 0.5-0.8, composite modified fiber grain 10-12;
Composite modified fiber grain is obtained by the raw material of following weight parts:
Attapulgite 10-20, flyash 3-4, aluminium vanadine 2-5, benzene emulsion 1-3, perlite 1-2, calcium formiate 1-2, carbon nanotube 2-4, kaolin 0.2-0.5, oxidation inhibitor T501 0.5-0.7, fibrous magnesium silicate 2-3, Sumstar 190 3-5, aluminum oxide 1-2;
The preparation method of composite modified fiber grain is:
Attapulgite, flyash, aluminium vanadine, perlite are ground, crossing 100-120 mesh sieve, is then that the salt solution of 4-8% mixes with concentration, stir, leave standstill, filter and drying after, after all the other raw material blendings, under 500-700 rev/min, 35-45 DEG C is stirred after 15-25 minute, adds amount of water, granulation, grain diameter at 3-5mm, then is dried, and to obtain final product.
2. a kind of cracking resistance light cellular partition board containing poly-third vinyl fiber according to claim 1, is characterized in that:
Its preparation method is:
Power taking rock ballast is broken, putting into concentration is that the sodium hydroxide solution of 4-6% soaks 5-8 hour, filter, wash 3-5 time, dry, more even with cement mixing, add all the other raw material stirring except aluminium powder cream again to mix, finally add aluminium powder cream to stir to obtain slip, cutting shaping through single-lead-screw extruding briquetting machine, natural curing, to obtain final product.