CN104194621A - 一种铜雕塑用防腐耐紫外线有机硅树脂漆 - Google Patents
一种铜雕塑用防腐耐紫外线有机硅树脂漆 Download PDFInfo
- Publication number
- CN104194621A CN104194621A CN201410363443.7A CN201410363443A CN104194621A CN 104194621 A CN104194621 A CN 104194621A CN 201410363443 A CN201410363443 A CN 201410363443A CN 104194621 A CN104194621 A CN 104194621A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- organic silicon
- silicon resin
- copper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种油漆,具体涉及一种铜雕塑用防腐耐紫外线有机硅树脂漆,本发明油漆由以下重量份的原料制成:有机硅树脂24-28、铬铁黑2-3、滑石粉3-5、石墨粉2-4、苯甲酸钠1-2、苯丙三氮唑1-2、明矾2-3、柠檬酸2-4、乙二醇乙醚醋酸酯3-5、丁酸异戊酯1-2、丁氧基磷酸三乙酯10-12、甲基丙烯酸丁酯5-8、1,6己二醇二丙烯酸酯14-16、防老剂RD1.2-2.0、促进剂CZ1.5-2.0、环烷酸钴2-3、交联剂TAC1-2、促进剂TMTD1-2、助剂5-6、二甲苯10-12、乙酸丁酯10-12;本发明油漆与铜器附着力强,不易脱落,漆膜色泽丰满,缓解环境腐蚀,耐紫外辐照,户外耐候能力强,生产工艺相对简单,可以广泛用于防护各类铜雕工艺品。
Description
技术领域
本发明涉及一种油漆,具体涉及一种铜雕塑用防腐耐紫外线有机硅树脂漆及其制备工艺。
背景技术
铜雕塑是日常生活中常见的一类工艺品,具有较高的艺术价值和欣赏价值,然而,铜雕塑艺术品由于其本身材质性质及摆放环境的特点,容易出现氧化腐蚀等问题,影响美观和使用寿命,为了保护铜器,往往需要在雕塑外面涂上油漆,并且对铜雕塑用漆有一定的要求,比如附着力、耐候老化、耐日光暴晒、耐温等等,因此,需要改进油漆配方,配制出适合不同使用场合的油漆,增加其艺术价值。
发明内容
本发明的目的在于,提供一种铜雕塑用防腐耐紫外线有机硅树脂漆,以保护雕塑品,为了实现上述目的,本发明采用的技术方案如下:
一种铜雕塑用防腐耐紫外线有机硅树脂漆,其特征在于,本发明材料由以下重量份的原料制成:有机硅树脂24-28、铬铁黑2-3、滑石粉3-5、石墨粉2-4、苯甲酸钠1-2、苯丙三氮唑1-2、明矾2-3、柠檬酸2-4、乙二醇乙醚醋酸酯3-5、丁酸异戊酯1-2、丁氧基磷酸三乙酯10-12、甲基丙烯酸丁酯5-8、1,6己二醇二丙烯酸酯14-16、防老剂RD 1.2-2.0、促进剂CZ 1.5-2.0、环烷酸钴2-3、交联剂TAC 1-2、促进剂TMTD 1-2、助剂5-6、二甲苯10-12、乙酸丁酯10-12。
所述的助剂由以下重量份的原料制成:粘土13-16、轻质碳酸钙2-3、氧化锌1-2、苯胺甲基三乙氧基硅烷2-3、三乙烯四胺4-5、阳起石2-3、氢氧化铝2-3、甘油三醋酸酯35-40、没食子酸丙酯2-3、薏仁油1-2、二硼化钒2-3、表儿茶素2-3;其制备方法是将粘土、轻质碳酸钙、阳起石送入煅烧炉中在720-740℃下煅烧2-3小时,然后取出,送入10-15%的盐酸溶液中浸泡2-3小时,过滤,得滤渣,用清水洗净,烘干、研磨成400-600目粉体;所得粉体与其它剩余成分混合,加热至60-70℃,搅拌反应40-50分钟,冷却,研磨成浆料,即得。
所述的一种铜雕塑用防腐耐紫外线有机硅树脂漆,其制备工艺为:
(1)将滑石粉、柠檬酸、乙二醇乙醚醋酸酯、甲基丙烯酸丁酯、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应3-4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入丁酸异戊酯、丁氧基磷酸三乙酯、1,6己二醇二丙烯酸酯,搅拌反应3-4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应40-60分钟后,冷却至室温,研磨成20-60μm浆料,即得。
与现有技术相比,本发明提供的铜雕塑用油漆具备以下优点:与铜器附着力强,不易脱落,硬度高,漆膜色泽丰满,缓解环境腐蚀,耐紫外辐照,户外耐候能力强,生产工艺相对简单,可以广泛用于防护各类铜雕工艺品。
具体实施方式
实施例
本实施例油漆由以下重量份原料制成:有机硅树脂28、铬铁黑3、滑石粉5、石墨粉4、苯甲酸钠2、苯丙三氮唑2、明矾3、柠檬酸4、乙二醇乙醚醋酸酯5、丁酸异戊酯2、丁氧基磷酸三乙酯12、甲基丙烯酸丁酯8、1,6己二醇二丙烯酸酯16、防老剂RD 1.5、促进剂CZ 1.5、环烷酸钴3、交联剂TAC 2、促进剂TMTD 2、助剂6、二甲苯12、乙酸丁酯12。
所述的助剂由以下重量份的原料制成:粘土15、轻质碳酸钙3、氧化锌2、苯胺甲基三乙氧基硅烷3、三乙烯四胺5、阳起石3、氢氧化铝3、甘油三醋酸酯40、没食子酸丙酯3、薏仁油2、二硼化钒3、表儿茶素3;其制备方法是将粘土、轻质碳酸钙、阳起石送入煅烧炉中在720-740℃下煅烧3小时,然后取出,送入15%的盐酸溶液中浸泡3小时,过滤,得滤渣,用清水洗净,烘干、研磨成600目粉体;所得粉体与其它剩余成分混合,加热至60-70℃,搅拌反应50分钟,冷却,研磨成浆料,即得。
所述的一种铜雕塑用防腐耐紫外线有机硅树脂漆,其制备工艺为:
(1)将滑石粉、柠檬酸、乙二醇乙醚醋酸酯、甲基丙烯酸丁酯、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入丁酸异戊酯、丁氧基磷酸三乙酯、1,6己二醇二丙烯酸酯,搅拌反应4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应60分钟后,冷却至室温,研磨成60μm浆料,即得。
本发明油漆的性能测试结果为:
上述测试均遵循相关标准进行。
Claims (2)
1.一种铜雕塑用防腐耐紫外线有机硅树脂漆,其特征在于,该油漆由以下重量份的原料制成:有机硅树脂24-28、铬铁黑2-3、滑石粉3-5、石墨粉2-4、苯甲酸钠1-2、苯丙三氮唑1-2、明矾2-3、柠檬酸2-4、乙二醇乙醚醋酸酯3-5、丁酸异戊酯1-2、丁氧基磷酸三乙酯10-12、甲基丙烯酸丁酯5-8、1,6己二醇二丙烯酸酯14-16、防老剂RD 1.2-2.0、促进剂CZ 1.5-2.0、环烷酸钴2-3、交联剂TAC 1-2、促进剂TMTD 1-2、助剂5-6、二甲苯10-12、乙酸丁酯10-12;
所述的助剂由以下重量份的原料制成:粘土13-16、轻质碳酸钙2-3、氧化锌1-2、苯胺甲基三乙氧基硅烷2-3、三乙烯四胺4-5、阳起石2-3、氢氧化铝2-3、甘油三醋酸酯35-40、没食子酸丙酯2-3、薏仁油1-2、二硼化钒2-3、表儿茶素2-3;其制备方法是将粘土、轻质碳酸钙、阳起石送入煅烧炉中在720-740℃下煅烧2-3小时,然后取出,送入10-15%的盐酸溶液中浸泡2-3小时,过滤,得滤渣,用清水洗净,烘干、研磨成400-600目粉体;所得粉体与其它剩余成分混合,加热至60-70℃,搅拌反应40-50分钟,冷却,研磨成浆料,即得。
2.如权利要求1所述的一种铜雕塑用防腐耐紫外线有机硅树脂漆,其制作工艺为:
(1)将滑石粉、柠檬酸、乙二醇乙醚醋酸酯、甲基丙烯酸丁酯、助剂混合,加入到二甲苯、乙酸丁酯溶剂中,加热至120-130℃,反应3-4小时;
(2)将步骤(1)的物料冷却至70-85℃,加入丁酸异戊酯、丁氧基磷酸三乙酯、1,6己二醇二丙烯酸酯,搅拌反应3-4小时;
(3)将步骤(2)的物料降温至50-65℃,加入其它剩余物料,搅拌反应40-60分钟后,冷却至室温,研磨成20-60μm浆料,即得。