CN103756529A - 一种铜雕塑用耐热防紫外线老化油漆 - Google Patents

一种铜雕塑用耐热防紫外线老化油漆 Download PDF

Info

Publication number
CN103756529A
CN103756529A CN201310676438.7A CN201310676438A CN103756529A CN 103756529 A CN103756529 A CN 103756529A CN 201310676438 A CN201310676438 A CN 201310676438A CN 103756529 A CN103756529 A CN 103756529A
Authority
CN
China
Prior art keywords
parts
paint
resistance
copper sculpture
copper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310676438.7A
Other languages
English (en)
Inventor
郑东平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd
Original Assignee
TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd filed Critical TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd
Priority to CN201310676438.7A priority Critical patent/CN103756529A/zh
Publication of CN103756529A publication Critical patent/CN103756529A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种油漆，具体涉及一种铜雕塑用耐热防紫外线老化油漆，本发明油漆由以下重量份的原料制成：银粉2-3、聚氨酯树脂20-23、聚环氧琥珀酸1-2、十二酸2-3、聚酯丙烯酸酯30-35、三羟甲基丙烷三丙烯酸酯12-15、二季戊四醇六丙烯酸酯5-7、聚甲基丙烯酸羟乙酯12-13、乙烯焦油1-2、古马隆6-8、促进剂CBS0.5-1.5、1,6-己二异氰酸酯4-6、苯胺甲基三乙氧基硅烷2-3、丙烯酸乙酯4-6、间氨基甲胺3-5、助剂5-6、二甲苯10-12、乙酸丁酯10-12；本发明油漆漆膜干燥快、附着力好，光泽度高，耐紫外线辐照，耐黄变，安全耐热，生产工艺相对简单，可以广泛用于各类铜雕工艺品，尤其是防护户外铜雕塑品。

Description

一种铜雕塑用耐热防紫外线老化油漆
技术领域
本发明涉及一种油漆，具体涉及一种铜雕塑用耐热防紫外线老化油漆及其制备工艺。
背景技术
铜雕塑是日常生活中常见的一类工艺品，具有较高的艺术价值和欣赏价值，然而，铜雕塑艺术品由于其本身材质性质及摆放环境的特点，容易出现氧化腐蚀等问题，影响美观和使用寿命，为了保护铜器，往往需要在雕塑外面涂上油漆，并且对铜雕塑用漆有一定的要求，比如附着力、耐候老化、耐日光暴晒、耐温等等，因此，需要改进油漆配方，配制出适合不同使用场合的油漆，增加其艺术价值。
发明内容
本发明的目的在于，提供一种铜雕塑用耐热防紫外线老化油漆，以保护雕塑品，为了实现上述目的，本发明采用的技术方案如下：
一种铜雕塑用耐热防紫外线老化油漆，其特征在于，本发明材料由以下重量份的原料制成：银粉2-3、聚氨酯树脂20-23、聚环氧琥珀酸1-2、十二酸2-3、聚酯丙烯酸酯30-35、三羟甲基丙烷三丙烯酸酯12-15、二季戊四醇六丙烯酸酯5-7、聚甲基丙烯酸羟乙酯12-13、乙烯焦油1-2、古马隆6-8、促进剂CBS0.5-1.5、1,6-己二异氰酸酯4-6、苯胺甲基三乙氧基硅烷2-3、丙烯酸乙酯4-6、间氨基甲胺3-5、助剂5-6、二甲苯10-12、乙酸丁酯10-12。
所述的助剂由以下重量份的原料制成：粘土9-12、氧化镁3-4、氧化锌1-2、铝矾土5-6、碳化钒1-2、促进剂TMTM2-3、玉石3-4、苯胺甲基三乙氧基硅烷2-3、间苯二甲酸二甲酯35-40、没食子酸丙酯1-2、薏仁油2-3、表儿茶素1-2；其制备方法是将粘土、铝矾土、玉石送入煅烧炉中在720-740℃下煅烧2-3小时，然后取出，送入10-15%的盐酸溶液中浸泡2-3小时，过滤，得滤渣，用清水洗净，烘干、研磨成400-600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
所述的一种铜雕塑用耐热防紫外线老化油漆，其制备工艺为：
（1）将十二酸、三羟甲基丙烷三丙烯酸酯、丙烯酸乙酯、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应3-4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入二季戊四醇六丙烯酸酯、乙烯焦油、古马隆、1,6-己二异氰酸酯，搅拌反应3-4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应40-60分钟后，冷却至室温，研磨成20-60μm浆料，即得。
与现有技术相比，本发明提供的铜雕塑用油漆具备以下优点：漆膜干燥快、附着力好，光泽度高，耐紫外线辐照，耐黄变，安全耐热，生产工艺相对简单，可以广泛用于各类铜雕工艺品，尤其是防护户外铜雕塑品。
具体实施方式
实施例
本实施例油漆由以下重量份原料制成：银粉3、聚氨酯树脂23、聚环氧琥珀酸2、十二酸3、聚酯丙烯酸酯32、三羟甲基丙烷三丙烯酸酯15、二季戊四醇六丙烯酸酯6、聚甲基丙烯酸羟乙酯13、乙烯焦油2、古马隆8、促进剂CBS1.5、1,6-己二异氰酸酯6、苯胺甲基三乙氧基硅烷3、丙烯酸乙酯6、间氨基甲胺5、助剂6、二甲苯12、乙酸丁酯12。
所述的助剂由以下重量份的原料制成：粘土10、氧化镁4、氧化锌2、铝矾土6、碳化钒2、促进剂TMTM3、玉石4、苯胺甲基三乙氧基硅烷3、间苯二甲酸二甲酯40、没食子酸丙酯2、薏仁油3、表儿茶素2；其制备方法是将粘土、铝矾土、玉石送入煅烧炉中在720-740℃下煅烧3小时，然后取出，送入15%的盐酸溶液中浸泡3小时，过滤，得滤渣，用清水洗净，烘干、研磨成600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应50分钟，冷却，研磨成浆料，即得。
所述的一种铜雕塑用耐热防紫外线老化油漆，其制备工艺为：
（1）将十二酸、三羟甲基丙烷三丙烯酸酯、丙烯酸乙酯、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入二季戊四醇六丙烯酸酯、乙烯焦油、古马隆、1,6-己二异氰酸酯，搅拌反应4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应60分钟后，冷却至室温，研磨成50μm浆料，即得。
本发明油漆的性能测试结果为：
Figure BDA0000434921540000031
上述测试均遵循相关标准进行。

Claims (2)

1.一种铜雕塑用耐热防紫外线老化油漆，其特征在于，该油漆由以下重量份的原料制成：银粉2-3、聚氨酯树脂20-23、聚环氧琥珀酸1-2、十二酸2-3、聚酯丙烯酸酯30-35、三羟甲基丙烷三丙烯酸酯12-15、二季戊四醇六丙烯酸酯5-7、聚甲基丙烯酸羟乙酯12-13、乙烯焦油1-2、古马隆6-8、促进剂CBS 0.5-1.5、1,6-己二异氰酸酯4-6、苯胺甲基三乙氧基硅烷2-3、丙烯酸乙酯4-6、间氨基甲胺3-5、助剂5-6、二甲苯10-12、乙酸丁酯10-12；
所述的助剂由以下重量份的原料制成：粘土9-12、氧化镁3-4、氧化锌1-2、铝矾土5-6、碳化钒1-2、促进剂TMTM 2-3、玉石3-4、苯胺甲基三乙氧基硅烷2-3、间苯二甲酸二甲酯35-40、没食子酸丙酯1-2、薏仁油2-3、表儿茶素1-2；其制备方法是将粘土、铝矾土、玉石送入煅烧炉中在720-740℃下煅烧2-3小时，然后取出，送入10-15%的盐酸溶液中浸泡2-3小时，过滤，得滤渣，用清水洗净，烘干、研磨成400-600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
2.如权利要求1所述的一种铜雕塑用耐热防紫外线老化油漆，其制作工艺为：
（1）将十二酸、三羟甲基丙烷三丙烯酸酯、丙烯酸乙酯、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应3-4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入二季戊四醇六丙烯酸酯、乙烯焦油、古马隆、1,6-己二异氰酸酯，搅拌反应3-4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应40-60分钟后，冷却至室温，研磨成20-60μm浆料，即得。
CN201310676438.7A 2013-12-07 2013-12-07 一种铜雕塑用耐热防紫外线老化油漆 Pending CN103756529A (zh)