CN104194518A - 一种反射隔热涂料及其制备方法 - Google Patents

一种反射隔热涂料及其制备方法 Download PDF

Info

Publication number
CN104194518A
CN104194518A CN201410473793.9A CN201410473793A CN104194518A CN 104194518 A CN104194518 A CN 104194518A CN 201410473793 A CN201410473793 A CN 201410473793A CN 104194518 A CN104194518 A CN 104194518A
Authority
CN
China
Prior art keywords
parts
heat insulating
diatomite
defoamer
propylene glycol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410473793.9A
Other languages
English (en)
Inventor
潘冬生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JURONG GEILI PACKAGING PRODUCTS FACTORY
Original Assignee
JURONG GEILI PACKAGING PRODUCTS FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JURONG GEILI PACKAGING PRODUCTS FACTORY filed Critical JURONG GEILI PACKAGING PRODUCTS FACTORY
Priority to CN201410473793.9A priority Critical patent/CN104194518A/zh
Publication of CN104194518A publication Critical patent/CN104194518A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种反射隔热涂料，包括以下组分：去离子水、丙二醇、分散剂、消泡剂、钛白粉、碳酸钙、滑石粉、硅藻土、增稠剂、空心玻璃珠和氟碳乳液。本发明的隔热保温效果优于传统的隔热涂料，配比巧妙，选料成本低廉，且制备方法简单易操作。

Description

一种反射隔热涂料及其制备方法
技术领域
本发明涉及一种涂料，具体涉及一种塑料表面用防火涂料及其制备方法。
背景技术
    现有的很多涂料。
发明内容
发明目的：本发明的目的在于解决现有技术中的不足，提供一种反射隔热涂料及其制备方法。
技术方案：本发明的一种反射隔热涂料，按照重量份数包括以下组分：去离子水20~35份、丙二醇0.2~0.4份、分散剂0.5~1.0份、消泡剂0.3~0.5份、钛白粉15~25份、碳酸钙4~8份、滑石粉2~6份、硅藻土2~5份、增稠剂0.2~0.3份、空心玻璃珠11~15份和氟碳乳液25~40份。
本发明还公开了一种反射隔热涂料的制备方法，包括以下步骤：
（1）将去离子水、分散剂、消泡剂、丙二醇置入容器中搅拌均匀；
（2）然后边慢速搅拌边依次加入增稠剂、钛白粉、碳酸钙、硅藻土和滑石粉，计入完毕后告诉搅拌20min，直至细度达到小于40μm；
（3）达到要求的细度后，再次边慢速搅拌边在步骤（2）的所得溶液中依次加入氟碳乳液和空心玻璃珠，搅拌混合均匀即可。
有益效果：本发明的隔热保温效果优于传统的隔热涂料，配比巧妙，选料成本低廉，且制备方法简单易操作。
具体实施方式
下面对本发明技术方案进行详细说明，但是本发明的保护范围不局限于所述实施例。
实施例1：
本发明的一种反射隔热涂料，按照重量份数包括以下组分：去离子水20份、丙二醇0.2份、分散剂0.5份、消泡剂0.3份、钛白粉15份、碳酸钙4份、滑石粉2份、硅藻土2份、增稠剂0.2份、空心玻璃珠11份和氟碳乳液25份。
本发明还公开了一种反射隔热涂料的制备方法，包括以下步骤：
（1）将去离子水、分散剂、消泡剂、丙二醇置入容器中搅拌均匀；
（2）然后边慢速搅拌边依次加入增稠剂、钛白粉、碳酸钙、硅藻土和滑石粉，计入完毕后告诉搅拌20min，直至细度达到小于40μm；
（3）达到要求的细度后，再次边慢速搅拌边在步骤（2）的所得溶液中依次加入氟碳乳液和空心玻璃珠，搅拌混合均匀即可。
实施例2：
本发明的一种反射隔热涂料，按照重量份数包括以下组分：去离子水35份、丙二醇0.4份、分散剂1.0份、消泡剂0.5份、钛白粉25份、碳酸钙8份、滑石粉6份、硅藻土5份、增稠剂0.3份、空心玻璃珠15份和氟碳乳液40份。
本发明还公开了一种反射隔热涂料的制备方法，包括以下步骤：
（1）将去离子水、分散剂、消泡剂、丙二醇置入容器中搅拌均匀；
（2）然后边慢速搅拌边依次加入增稠剂、钛白粉、碳酸钙、硅藻土和滑石粉，计入完毕后告诉搅拌20min，直至细度达到小于40μm；
（3）达到要求的细度后，再次边慢速搅拌边在步骤（2）的所得溶液中依次加入氟碳乳液和空心玻璃珠，搅拌混合均匀即可。
实施例3：
本发明的一种反射隔热涂料，按照重量份数包括以下组分：去离子水21份、丙二醇0.25份、分散剂0.6份、消泡剂0.35份、钛白粉17份、碳酸钙4.9份、滑石粉2.6份、硅藻土2.4份、增稠剂0.22份、空心玻璃珠12份和氟碳乳液27份。
本发明还公开了一种反射隔热涂料的制备方法，包括以下步骤：
（1）将去离子水、分散剂、消泡剂、丙二醇置入容器中搅拌均匀；
（2）然后边慢速搅拌边依次加入增稠剂、钛白粉、碳酸钙、硅藻土和滑石粉，计入完毕后告诉搅拌20min，直至细度达到小于40μm；
（3）达到要求的细度后，再次边慢速搅拌边在步骤（2）的所得溶液中依次加入氟碳乳液和空心玻璃珠，搅拌混合均匀即可。
实施例4：
本发明的一种反射隔热涂料，按照重量份数包括以下组分：去离子水33份、丙二醇0.34份、分散剂0.8份、消泡剂0.45份、钛白粉24份、碳酸钙7.8份、滑石粉5.5份、硅藻土4.5份、增稠剂0.29份、空心玻璃珠15份和氟碳乳液35份。
本发明还公开了一种反射隔热涂料的制备方法，包括以下步骤：
（1）将去离子水、分散剂、消泡剂、丙二醇置入容器中搅拌均匀；
（2）然后边慢速搅拌边依次加入增稠剂、钛白粉、碳酸钙、硅藻土和滑石粉，计入完毕后告诉搅拌20min，直至细度达到小于40μm；
（3）达到要求的细度后，再次边慢速搅拌边在步骤（2）的所得溶液中依次加入氟碳乳液和空心玻璃珠，搅拌混合均匀即可。

Claims (3)

1.一种反射隔热涂料，其特征在于：按照重量份数包括以下组分：去离子水20~35份、丙二醇0.2~0.4份、分散剂0.5~1.0份、消泡剂0.3~0.5份、钛白粉15~25份、碳酸钙4~8份、滑石粉2~6份、硅藻土2~5份、增稠剂0.2~0.3份、空心玻璃珠11~15份和氟碳乳液25~40份。
2.根据权利要求1所述的反射隔热涂料，其特征在于：所述去离子水21~33份、丙二醇0.25~0.34份、分散剂0.6~0.8份、消泡剂0.35~0.45份、钛白粉17~24份、碳酸钙4.9~7.8份、滑石粉2.6~5.5份、硅藻土2.4~4.5份、增稠剂0.22~0.29份、空心玻璃珠12~15份和氟碳乳液27~35份。
3.一种如权利要求1和2任意一项所述的反射隔热涂料的制备方法，其特征在于：包括以下步骤：
（1）将去离子水、分散剂、消泡剂、丙二醇置入容器中搅拌均匀；
（2）然后边慢速搅拌边依次加入增稠剂、钛白粉、碳酸钙、硅藻土和滑石粉，计入完毕后告诉搅拌20min，直至细度达到小于40μm；
（3）达到要求的细度后，再次边慢速搅拌边在步骤（2）的所得溶液中依次加入氟碳乳液和空心玻璃珠，搅拌混合均匀即可。
CN201410473793.9A 2014-09-17 2014-09-17 一种反射隔热涂料及其制备方法 Pending CN104194518A (zh)