CN104194250A - 一种电路用导电塑料的制备方法 - Google Patents

一种电路用导电塑料的制备方法 Download PDF

Info

Publication number
CN104194250A
CN104194250A CN201410473058.8A CN201410473058A CN104194250A CN 104194250 A CN104194250 A CN 104194250A CN 201410473058 A CN201410473058 A CN 201410473058A CN 104194250 A CN104194250 A CN 104194250A
Authority
CN
China
Prior art keywords
temperature
district
preparation
parts
zone temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410473058.8A
Other languages
English (en)
Other versions
CN104194250B (zh
Inventor
于澎
田小明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGYIN RUNMA ELECTRONIC MATERIAL CO Ltd
Original Assignee
JIANGYIN RUNMA ELECTRONIC MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGYIN RUNMA ELECTRONIC MATERIAL CO Ltd filed Critical JIANGYIN RUNMA ELECTRONIC MATERIAL CO Ltd
Priority to CN201410473058.8A priority Critical patent/CN104194250B/zh
Publication of CN104194250A publication Critical patent/CN104194250A/zh
Application granted granted Critical
Publication of CN104194250B publication Critical patent/CN104194250B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种电路用导电塑料的制备方法，该方法包括：将丙烯腈-丁二烯-苯乙烯共聚物在100℃下干燥6小时，然后和苯乙烯-马来酸酐共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、三硬脂酸甘油酯混合在高速搅拌机中以800转/分钟搅拌10分钟然后加入4，4’-硫代双(6-叔丁基-3-甲基苯酚)、二甲基硅油和7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮，在1300转/分钟搅拌6分钟，然后出料到加入长径比(L/D)为40的双螺杆挤出机中，双螺杆挤出机的加工温度：一区温度170℃，二区温度为180℃，三区温度为190℃，四区温度为205℃，五区温度为215℃，六区温度为225℃，七区温度为235℃，八区温度为240℃，主机转速为350转/min；经过挤出后冷却牵条、风干切粒，即得。

Description

一种电路用导电塑料的制备方法
技术领域
本发明涉及电子材料领域，具体的说，本发明涉及一种电路用导电塑料的制备方法。
背景技术
导电塑料是将树脂和导电物质混合，用塑料的加工方式进行加工的功能型高分子材料。主要应用于电子、集成电路包装、电磁波屏蔽等领域。
发明内容
本发明的目的在于提供一种电路用导电塑料的制备方法。
为了实现本发明的目的，本发明提供一种电路用导电塑料的制备方法，该方法包括下列步骤：
称取下列重量份的原料：塑料基体200-400份、界面偶联剂20-50份、增韧剂10-30份、分散润滑剂10-20份、抗氧化剂20-50份、脱模剂1-10份和导电助剂10-30份；
将丙烯腈-丁二烯-苯乙烯共聚物在100℃下干燥6小时，然后和苯乙烯-马来酸酐共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、三硬脂酸甘油酯混合，在高速搅拌机中以800转/分钟搅拌10分钟，然后加入4，4’-硫代双(6-叔丁基-3-甲基苯酚)、二甲基硅油和7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮，在1300转/分钟搅拌6分钟，然后出料到加入长径比(L/D)为40的双螺杆挤出机中，双螺杆挤出机的加工温度：一区温度170℃，二区温度为180℃，三区温度为190℃，四区温度为205℃，五区温度为215℃，六区温度为225℃，七区温度为235℃，八区温度为240℃，主机转速为350转/min；经过挤出后冷却牵条、风干切粒，即得。
优选地，本发明所述的方法采取下列重量份的原料：塑料基体250份、界面偶联剂30份、增韧剂25份、分散润滑剂10份、抗氧化剂30份、脱模剂5份和导电助剂20份。
优选地，所述塑料基体为丙烯腈-丁二烯-苯乙烯共聚物。
优选地，所述界面偶联剂为苯乙烯-马来酸酐共聚物。
优选地，所述增韧剂为甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物。
优选地，所述分散润滑剂为三硬脂酸甘油酯。
优选地，所述抗氧化剂为4，4’-硫代双(6-叔丁基-3-甲基苯酚)。
优选地，所述脱模剂为二甲基硅油。
优选地，所述导电助剂为7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮。
本发明所述的电路用导电塑料具有优异的导电性，非常适于在电子元器件、电路中应用，在工业应用上具有广阔的前景。
具体实施方式
以下通过具体实施方式的描述对本发明作进一步说明，但这并非是对本发明的限制，本领域技术人员根据本发明的基本思想，可以做出各种修改或改进，但是只要不脱离本发明的基本思想，均在本发明的范围之内。
实施例1
取丙烯腈-丁二烯-苯乙烯共聚物2500克、苯乙烯-马来酸酐共聚物300克、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物250克、三硬脂酸甘油酯100克、4，4’-硫代双(6-叔丁基-3-甲基苯酚)300克、二甲基硅油50克和7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮20克，
将丙烯腈-丁二烯-苯乙烯共聚物在100℃下干燥6小时，然后和苯乙烯-马来酸酐共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、三硬脂酸甘油酯混合，在高速搅拌机中以800转/分钟搅拌10分钟，然后加入4，4’-硫代双(6-叔丁基-3-甲基苯酚)、二甲基硅油和7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮，在1300转/分钟搅拌6分钟，然后出料到加入长径比(L/D)为40的双螺杆挤出机中，双螺杆挤出机的加工温度：一区温度170℃，二区温度为180℃，三区温度为190℃，四区温度为205℃，五区温度为215℃，六区温度为225℃，七区温度为235℃，八区温度为240℃，主机转速为350转/min；经过挤出后冷却牵条、风干切粒，即制备本发明所述的试样。
实施例2
按照和实施例1相同的方式制备电路用导电塑料，不同之处在于不使用7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮。
实验例
按IEC60093要求进行测试表面电阻率，结果如下：实施例1的导电塑料的表面电阻率(Ω)为3.6×104，实施例2的导电塑料的表面电阻率(Ω)为6.1×106，由此可见，加入导电助剂后，本发明的塑料的导电性到显著增强，实施例1的结果与实施例2的结果进行比较，差异具有统计学意义(P＜0.05)。

Claims (9)

1.一种电路用导电塑料的制备方法，其特征在于，该方法包括下列步骤：
称取下列重量份的原料：塑料基体200-400份、界面偶联剂20-50份、增韧剂10-30份、分散润滑剂10-20份、抗氧化剂20-50份、脱模剂1-10份和导电助剂10-30份；
将丙烯腈-丁二烯-苯乙烯共聚物在100℃下干燥6小时，然后和苯乙烯-马来酸酐共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物、三硬脂酸甘油酯混合，在高速搅拌机中以800转/分钟搅拌10分钟，然后加入4，4’-硫代双(6-叔丁基-3-甲基苯酚)、二甲基硅油和7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮，在1300转/分钟搅拌6分钟，然后出料到加入长径比(L/D)为40的双螺杆挤出机中，双螺杆挤出机的加工温度：一区温度170℃，二区温度为180℃，三区温度为190℃，四区温度为205℃，五区温度为215℃，六区温度为225℃，七区温度为235℃，八区温度为240℃，主机转速为350转/min；经过挤出后冷却牵条、风干切粒，即得。
2.根据权利要求1所述的制备方法，其特征在于，由下列重量份的原料制成：塑料基体250份、界面偶联剂30份、增韧剂25份、分散润滑剂10份、抗氧化剂30份、脱模剂5份和导电助剂20份。
3.根据权利要求2所述的制备方法，其特征在于，所述塑料基体为丙烯腈-丁二烯-苯乙烯共聚物。
4.根据权利要求2所述的制备方法，其特征在于，所述界面偶联剂为苯乙烯-马来酸酐共聚物。
5.根据权利要求2所述的制备方法，其特征在于，所述增韧剂为甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物。
6.根据权利要求2所述的制备方法，其特征在于，所述分散润滑剂为三硬脂酸甘油酯。
7.根据权利要求2所述的制备方法，其特征在于，所述抗氧化剂为4，4’-硫代双(6-叔丁基-3-甲基苯酚)。
8.根据权利要求2所述的制备方法，其特征在于，所述脱模剂为二甲基硅油。
9.根据权利要求2所述的制备方法，其特征在于，所述导电助剂为7-(4-氯-苄氧基)-4，5-二氢-2H-[1，2，4]-三唑[4，3-a]并喹啉-1-酮。
CN201410473058.8A 2014-09-16 2014-09-16 一种电路用导电塑料的制备方法 Active CN104194250B (zh)