CN104183311A - High-voltage connecting cable with ultra-soft aluminum conductor and for interior of electric automobile and manufacturing method - Google Patents

High-voltage connecting cable with ultra-soft aluminum conductor and for interior of electric automobile and manufacturing method Download PDF

Info

Publication number
CN104183311A
CN104183311A CN201410442431.3A CN201410442431A CN104183311A CN 104183311 A CN104183311 A CN 104183311A CN 201410442431 A CN201410442431 A CN 201410442431A CN 104183311 A CN104183311 A CN 104183311A
Authority
CN
China
Prior art keywords
conductor
layer
soft aluminium
cable
stranded
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410442431.3A
Other languages
Chinese (zh)
Other versions
CN104183311B (en
Inventor
李金顶
陈波瀚
刘焱鑫
张照阳
田仕鸿
孙建宇
张松松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Zhongli Group Co Ltd
Original Assignee
Zhongli Technology Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhongli Technology Group Co Ltd filed Critical Zhongli Technology Group Co Ltd
Priority to CN201410442431.3A priority Critical patent/CN104183311B/en
Publication of CN104183311A publication Critical patent/CN104183311A/en
Application granted granted Critical
Publication of CN104183311B publication Critical patent/CN104183311B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention belongs to the technical field of cables, and particularly relates to a high-voltage connecting cable with an ultra-soft aluminum conductor and for the interior of an electric automobile. The high-voltage connecting cable comprises the conductor, a wrapping belt, an insulating layer and a sheath layer and is characterized in that the conductor is formed by stranding annealed fifth-class soft aluminum wires with the diameter ranging from 0.10 mm to 0.45 mm, and the cross sectional area of the conductor ranges from 1.5 mm<2> to 120 mm<2>; both the insulating layer and the sheath layer are made of 125 DEG C environment-friendly antiflaming TPEs or 125 DEG C environment-friendly antiflaming irradiation crosslinking polyolefin, or the insulting layer is made of 125 DEG C environment-friendly antiflaming irradiation crosslinking polyolefin and the sheath layer is made of 125 DEG C environment-friendly antiflaming TPEs. The high-voltage connecting cable has the following advantages of being softer, easier to bend, lighter in dead weight, lower in cost, more resistant to high voltage and large current, better in antiflaming effect and safer in use.

Description

The electric automobile with super soft aluminium conductor is inner by high pressure stube cable and manufacture method
Technical field
The invention belongs to technical field of cables, especially relate to inner high pressure stube cable and the manufacture method used of electric automobile with super soft aluminium conductor.
Background technology
Automotive interior is a kind of for electric connection line with high pressure stube cable, the primary high-voltage transmission for vehicle interior.Communication power supply not only requires to have good flexibility with flexible cable, to conveniently lay under situation, and requires to have desirable anti-flammability in narrow space or similarly, to adapt to higher fire-protection rating requirement.
The cable for car overwhelming majority adopts copper conductor both at home and abroad at present, and copper conductor itself is heavier, and flexibility is poor; Conventionally adopt communication power supply to substitute use with flexible cable both at home and abroad.
Can in disclosed Chinese patent literature, be seen in by the technical information of flexible cable about communication power supply, for example CN201247632Y recommends have that " communication power supply is with fire-retardant, fire-resistant, shielding anti-interference flexible cable ", CN201302849Y provides " a kind of communication power supply flame-retardant refractory flexible electric cable ", CN202230791Y discloses " the flame-retardant crosslinking polyethylene insulated flexible cable of a kind of communication power supply ", CN202720953U introduces to be had " for watt form drag combustion shielded flexible cable of communication power supply ", CN202855416U discloses " communication power supply fire-resistant shield flexible cable " and CN202601277U disclosed " a kind of communication power supply flame-retardant flexible electric cable ", etc..
Although communication power supply of the prior art respectively has corresponding technique effect with flexible cable, there is following common defect: (1) due to using stranded thin copper wire as conductor, its soft degree can not meet the desired requirement.And because pliability is poor, bending radius is restricted, thus at narrow space, hindered by immovable object and even when the occasion at the place of talking in a roundabout way and so on is laid, very easily affect speed of application, particularly in the less occasion in the spaces such as vehicle; (2) owing to generally selecting the conductor as flexible cable with copper under technology prejudice, thereby not only there is the blindness that rationally uses raw material aspect, and cause the manufacturing cost of flexible cable large; Its three, because copper density is large, therefore cable weight is heavier, thereby not only logistics transportation, the cost of storage in link are high, and workmen's labour intensity is large in laid processes, to consume cost of labor high.
In view of above-mentioned prior art, still have improved necessity, the applicant has done useful design for this reason, has formed technical scheme described below.
Summary of the invention
In order to address the above problem, the object of the invention is to disclose inner high pressure stube cable and the manufacture method used of electric automobile with super soft aluminium conductor, they are realized by the following technical solutions.
There is the inner high pressure stube cable of using of electric automobile of super soft aluminium conductor, comprise conductor, be coated on the band outside conductor, insulating barrier, the extrusion molding being overlayed on outside band is coated on the restrictive coating outside insulating barrier, it is characterized in that described conductor is stranded the forming of the soft aluminium wire of the 5th class that be 0.10~0.45mm by the diameter through annealing in process, and the cross-sectional area of conductor is 1.5mm 2~120mm 2, described insulating barrier and the combination of materials of restrictive coating are one of following three kinds: (1) insulating barrier is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE, and restrictive coating is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE; (2) insulating barrier is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and restrictive coating is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin; (3) insulating barrier is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and restrictive coating is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE; The rated operational voltage of described cable is 1500V, long-term work temperature≤125 DEG C of cable, ambient temperature when cable laying>=-40 DEG C, cable is stream time>=6h at 175 DEG C in temperature, the minimum bending radius of cable is the outside diameter of cable 5 times.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that described conductor is by stranded formation of the multilayer soft aluminium wire of the 5th class, and direction of lay between adjacent layer is contrary; The twisting pitch of every layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that the thickness of described insulating barrier is 0.5~3.0mm.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that the material of described band is waterstop or nonwoven fabrics or polyester belt or glass fiber tape.
The inner manufacture method with high pressure stube cable of electric automobile with super soft aluminium conductor, is characterized in that it comprises the following steps of carrying out successively:
The first step: the soft aluminium wire of the 5th class that the diameter of getting many annealed processing is 0.10~0.45mm carries out stranded formation the first stranded layer on strand winder, the diameter of the soft aluminium wire of the 5th class in the first stranded layer equates, the twisting pitch of the first stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; The soft aluminium wire of the 5th class that the diameter of separately getting many annealed processing is 0.10~0.45mm carries out stranded formation the second stranded layer outward at the first stranded layer, the diameter of the soft aluminium wire of the 5th class in the second stranded layer equates, the twisting pitch of the second stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; The like, forming N stranded layer, the diameter of the soft aluminium wire of the 5th class in N stranded layer equates, the twisting pitch of N stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; In adjacent stranded layer: outer field pitch is larger than the pitch of internal layer, and outer field pitch is 2~4 times of pitch of internal layer; Formation conductor after N stranded layer completes, the cross-sectional area of described conductor is 1.5mm 2~120mm 2; The direction of lay of adjacent stranded layer is identical;
Second step: the mode helical coated band to be wound around outside the conductor forming in the first step, the material of described band is waterstop or nonwoven fabrics or polyester belt or glass fiber tape;
The 3rd step: the outer extrusion molding of band forming at second step is coated 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE or described insulating barrier is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and the thickness of described insulating barrier is 0.5~3.0mm;
The 4th step: the coated restrictive coating that forms of extrusion molding outside the insulating barrier forming in the 3rd step, traction, cooling formation have the inner high pressure stube cable of using of electric automobile of super soft aluminium conductor; The thickness of described restrictive coating is 0.8~3.0mm.
In manufacture method of the present invention, adopted the soft aluminium wire of the 5th class to carry out multilayer stranded, and 2~4 times of identical, the outer field pitch of the direction of lay of the adjacent stranded layer pitch that is internal layer, twisting pitch are 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; Therefore, cable has high softness, still can keep good electricity and mechanical performance through low-angle repeatedly alternating bending; Manufacture method of the present invention simply, easily grasp.
In the present invention, owing to having had exhausted insulating barrier and outer jacket, therefore, fire-retardant, the fire resistance of product improve greatly.
The present invention compared with prior art, because aluminium wire is more soft than copper wire, and the soft aluminium wire in the present invention is different from the aluminium cable in general industry and adopts the duralumin that has a class or two class conductors, therefore the present invention has more soft technique effect, greatly improved the pliability of whole cable, be convenient to cable in car in narrow space bending lay; In addition, aluminium wire is compared with copper wire, and aluminium wire is not oxidizable; Due to the density of aluminium, to compare copper low, and therefore, cable is lighter, material cost and cost of transportation Geng Sheng, more easily installs and lay; In the present invention, when cable insulation, outer jacket adopt environmentally-friendly flame retardant thermoplastic elastomer TPE material, can effectively play fire retardation; When cable insulation, outer jacket adopt environmental protection flame retardant cross-linking radiation polyolefine material, can effectively play fire retardation; When cable insulation adopts environmental protection flame retardant cross-linking radiation polyolefin, outer jacket to adopt environmentally-friendly flame retardant thermoplastic elastomer TPE material, can effectively play fire retardation.
Therefore, the present invention has following main beneficial effect: more soft, more flexible, more easily construct, conduct oneself with dignity lighter, cost is lower, more can high pressure resistant, large electric current; Flame retardant effect is better, it is safer to use.
Brief description of the drawings
Fig. 1 is cross-sectional structure schematic diagram of the present invention.
Embodiment
Ask for an interview Fig. 1, there is the inner high pressure stube cable of using of electric automobile of super soft aluminium conductor, comprise conductor 1, be coated on the band 2 outside conductor 1, insulating barrier 3, the extrusion molding being overlayed on outside band 2 is coated on the restrictive coating 4 outside insulating barrier 3, it is characterized in that described conductor 1 is stranded the forming of the soft aluminium wire of the 5th class that be 0.10~0.45mm by the diameter through annealing in process, and the cross-sectional area of conductor is 1.5mm 2~120mm 2, described insulating barrier 3 and the combination of materials of restrictive coating 4 are one of following three kinds: (1) insulating barrier 3 is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE, and restrictive coating 4 is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE; (2) insulating barrier 3 is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and restrictive coating 4 is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin; (3) insulating barrier 3 is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and restrictive coating 4 is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE; The rated operational voltage of described cable is 1500V, long-term work temperature≤125 DEG C of cable, ambient temperature when cable laying>=-40 DEG C, cable is stream time>=6h at 175 DEG C in temperature, the minimum bending radius of cable is the outside diameter of cable 5 times.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that the thickness of described restrictive coating 4 is 0.8~3.0mm; More typical thickness is 0.8mm or 1.0mm or 1.2mm or 1.5mm or 1.6mm or 1.8mm or 2.0mm or 2.5mm or 3.0mm.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that the thickness of described one side aluminium foil layer is 0.05~0.5mm; More typical thickness is 0.05mm or 0.08mm or 0.10mm or 0.12mm or 0.15mm or 0.20mm or 0.20mm or 0.25mm or 0.30mm or 0.40mm or 0.45mm.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that described conductor is by stranded formation of the multilayer soft aluminium wire of the 5th class, and direction of lay between adjacent layer is contrary; The twisting pitch of every layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that the soft aluminium wire of described adjacent layer the 5th class is stranded: outer field pitch is larger than the pitch of internal layer, and outer field pitch is 2~4 times of internal layer.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that the thickness of described insulating barrier is 0.5~3.0mm; More typical thickness is 0.5mm or 0.7mm or 0.8mm or 1.0mm or 1.5mm or 2.0mm or 3.0mm.
The electric automobile with super soft aluminium conductor described above is inner uses high pressure stube cable, it is characterized in that the material of described band is waterstop or nonwoven fabrics or polyester belt or glass fiber tape.
The electric automobile with super soft aluminium conductor described above is inner use high pressure stube cable, the band described in it is characterized in that be the mode helical coated that is wound around in conductor outside.
The inner manufacture method with high pressure stube cable of electric automobile with super soft aluminium conductor, is characterized in that it comprises the following steps of carrying out successively:
The first step: the soft aluminium wire of the 5th class that the diameter of getting many annealed processing is 0.10~0.45mm carries out stranded formation the first stranded layer on strand winder, the diameter of the soft aluminium wire of the 5th class in the first stranded layer equates, the twisting pitch of the first stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; The soft aluminium wire of the 5th class that the diameter of separately getting many annealed processing is 0.10~0.45mm carries out stranded formation the second stranded layer outward at the first stranded layer, the diameter of the soft aluminium wire of the 5th class in the second stranded layer equates, the twisting pitch of the second stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; The like, forming N stranded layer, the diameter of the soft aluminium wire of the 5th class in N stranded layer equates, the twisting pitch of N stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; In adjacent stranded layer: outer field pitch is larger than the pitch of internal layer, and outer field pitch is 2~4 times of pitch of internal layer; Formation conductor after N stranded layer completes, the cross-sectional area of described conductor is 1.5mm 2~120mm 2; The direction of lay of adjacent stranded layer is identical;
Second step: the mode helical coated band to be wound around outside the conductor forming in the first step, the material of described band is waterstop or nonwoven fabrics or polyester belt or glass fiber tape;
The 3rd step: the outer extrusion molding of band forming at second step is coated 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE or described insulating barrier is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and the thickness of described insulating barrier is 0.5~3.0mm;
The 4th step: the coated restrictive coating that forms of extrusion molding outside the insulating barrier forming in the 3rd step, traction, cooling formation have the inner high pressure stube cable of using of electric automobile of super soft aluminium conductor; The thickness of described restrictive coating is 0.8~3.0mm.
In manufacture method of the present invention, adopted the soft aluminium wire of the 5th class to carry out multilayer stranded, and 2~4 times of identical, the outer field pitch of the direction of lay of the adjacent stranded layer pitch that is internal layer, twisting pitch are 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; Therefore, cable has high softness, still can keep good electricity and mechanical performance through low-angle repeatedly alternating bending; Manufacture method of the present invention simply, easily grasp.
In the present invention, owing to having had exhausted insulating barrier and outer jacket, therefore, fire-retardant, the fire resistance of product improve greatly.
The present invention compared with prior art, because aluminium wire is more soft than copper wire, and the soft aluminium wire in the present invention is different from the aluminium cable in general industry and adopts the duralumin that has a class or two class conductors, therefore the present invention has more soft technique effect, greatly improved the pliability of whole cable, be convenient to cable in car in narrow space bending lay; In addition, aluminium wire is compared with copper wire, and aluminium wire is not oxidizable; Due to the density of aluminium, to compare copper low, and therefore, cable is lighter, material cost and cost of transportation Geng Sheng, more easily installs and lay; In the present invention, when cable insulation, outer jacket adopt environmentally-friendly flame retardant thermoplastic elastomer TPE material, can effectively play fire retardation; When cable insulation, outer jacket adopt environmental protection flame retardant cross-linking radiation polyolefine material, can effectively play fire retardation; When cable insulation adopts environmental protection flame retardant cross-linking radiation polyolefin, outer jacket to adopt environmentally-friendly flame retardant thermoplastic elastomer TPE material, can effectively play fire retardation.
125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE, are the one in commercially available model cable raw material, and place technical field personnel can purchase and arrive according to its full name on market.
Therefore, the present invention has following main beneficial effect: more soft, more flexible, more easily construct, conduct oneself with dignity lighter, cost is lower, more can high pressure resistant, large electric current; Flame retardant effect is better, it is safer to use.
The present invention is not limited to above-mentioned preferred forms, should be appreciated that design of the present invention can be by other various forms enforcement utilizations, and they drop in protection scope of the present invention equally.

Claims (10)

1. there is the inner high pressure stube cable of using of electric automobile of super soft aluminium conductor, comprise conductor, be coated on the band outside conductor, insulating barrier, the extrusion molding being overlayed on outside band is coated on the restrictive coating outside insulating barrier, it is characterized in that described conductor is stranded the forming of the soft aluminium wire of the 5th class that be 0.10~0.45mm by the diameter through annealing in process, and the cross-sectional area of conductor is 1.5mm 2~120mm 2, described insulating barrier and the combination of materials of restrictive coating are one of following three kinds: (1) insulating barrier is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE, and restrictive coating is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE; (2) insulating barrier is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and restrictive coating is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin; (3) insulating barrier is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and restrictive coating is 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE; The rated operational voltage of described cable is 1500V, long-term work temperature≤125 DEG C of cable, ambient temperature when cable laying>=-40 DEG C, cable is stream time>=6h at 175 DEG C in temperature, the minimum bending radius of cable is the outside diameter of cable 5 times.
2. high pressure stube cable is used in the electric automobile inside with super soft aluminium conductor according to claim 1, it is characterized in that the thickness of described restrictive coating is 0.8~3.0mm.
3. high pressure stube cable is used in the electric automobile inside with super soft aluminium conductor according to claim 2, it is characterized in that the thickness of described restrictive coating is 0.8mm or 1.0mm or 1.2mm or 1.5mm or 1.6mm or 1.8mm or 2.0mm or 2.5mm or 3.0mm.
4. use high pressure stube cable according to claim 1 to the electric automobile with super soft aluminium conductor described in claim 3 any one is inner, it is characterized in that the thickness of described insulating barrier is 0.5~3.0mm.
5. high pressure stube cable is used in the electric automobile inside with super soft aluminium conductor according to claim 4, and the thickness that it is characterized in that described insulating barrier is 0.5mm or 0.7mm or 0.8mm or 1.0mm or 1.5mm or 2.0mm or 3.0mm.
6. use high pressure stube cable according to claim 1 to the electric automobile with super soft aluminium conductor described in claim 3 any one is inner, the material that it is characterized in that described band is waterstop or nonwoven fabrics or polyester belt or glass fiber tape.
7. the electric automobile with super soft aluminium conductor according to claim 6 is inner use high pressure stube cable, the band described in it is characterized in that be the mode helical coated that is wound around in conductor outside.
8. the electric automobile with super soft aluminium conductor according to claim 7 is inner uses high pressure stube cable, it is characterized in that described conductor is by stranded formation of the multilayer soft aluminium wire of the 5th class, and direction of lay between adjacent layer is contrary; The twisting pitch of every layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer.
9. the electric automobile with super soft aluminium conductor according to claim 8 is inner uses high pressure stube cable, it is characterized in that the soft aluminium wire of described adjacent layer the 5th class is stranded: outer field pitch is larger than the pitch of internal layer, and outer field pitch is 2~4 times of internal layer.
10. the inner manufacture method with high pressure stube cable of electric automobile with super soft aluminium conductor, is characterized in that it comprises the following steps of carrying out successively:
The first step: the soft aluminium wire of the 5th class that the diameter of getting many annealed processing is 0.10~0.45mm carries out stranded formation the first stranded layer on strand winder, the diameter of the soft aluminium wire of the 5th class in the first stranded layer equates, the twisting pitch of the first stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; The soft aluminium wire of the 5th class that the diameter of separately getting many annealed processing is 0.10~0.45mm carries out stranded formation the second stranded layer outward at the first stranded layer, the diameter of the soft aluminium wire of the 5th class in the second stranded layer equates, the twisting pitch of the second stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; The like, forming N stranded layer, the diameter of the soft aluminium wire of the 5th class in N stranded layer equates, the twisting pitch of N stranded layer is 10~25 times of the soft aluminium wire diameter of the 5th class in this layer; In adjacent stranded layer: outer field pitch is larger than the pitch of internal layer, and outer field pitch is 2~4 times of pitch of internal layer; Formation conductor after N stranded layer completes, the cross-sectional area of described conductor is 1.5mm 2~120mm 2; The direction of lay of adjacent stranded layer is identical;
Second step: the mode helical coated band to be wound around outside the conductor forming in the first step, the material of described band is waterstop or nonwoven fabrics or polyester belt or glass fiber tape;
The 3rd step: the outer extrusion molding of band forming at second step is coated 125 DEG C of environmentally-friendly flame retardant thermoplastic elastomer TPE or described insulating barrier is 125 DEG C of environmental protection flame retardant cross-linking radiation polyolefin, and the thickness of described insulating barrier is 0.5~3.0mm;
The 4th step: the coated restrictive coating that forms of extrusion molding outside the insulating barrier forming in the 3rd step, traction, cooling formation have the inner high pressure stube cable of using of electric automobile of super soft aluminium conductor; The thickness of described restrictive coating is 0.8~3.0mm.
CN201410442431.3A 2014-09-03 2014-09-03 Have inside the electric automobile of super soft aluminium conductor and connect cable and manufacture method with high pressure Active CN104183311B (en)