CN104177889A - 一种陶瓷用紫外光固化环氧丙烯酸酯涂料 - Google Patents
一种陶瓷用紫外光固化环氧丙烯酸酯涂料 Download PDFInfo
- Publication number
- CN104177889A CN104177889A CN201410455780.9A CN201410455780A CN104177889A CN 104177889 A CN104177889 A CN 104177889A CN 201410455780 A CN201410455780 A CN 201410455780A CN 104177889 A CN104177889 A CN 104177889A
- Authority
- CN
- China
- Prior art keywords
- parts
- product
- pottery
- acrylic coating
- ultraviolet cured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种陶瓷用紫外光固化环氧丙烯酸酯涂料,原料为:丙烯酸羟乙酯、乙二醇、马来酸酐、新戊二醇、环氧树脂、对苯二甲酸二甲酯、光敏剂、醋酸锌、双酚A、对苯二甲酸、交联剂、间苯二甲酸、环氧乙烷、己二酸和环氧丙烷;产品光泽度120%-130%,硬度5-7H;耐130-150℃高温,在5%盐酸溶液中浸泡2-4d无异常;在饱和氢氧化钙中浸泡4-6d不起泡、皱皮;产品耐洗擦性2200-2800次不露底,可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域,尤其涉及一种陶瓷用紫外光固化环氧丙烯酸酯涂料。
背景技术
陶瓷工业在我国发展较快,销售市场逐渐转旺。我国是一个陶瓷生产大国,对陶瓷的需求量也越来越大。从国内市场情况看,近年形势喜人,名特优新陶瓷产品供不应求,高档陶瓷和中高档卫生陶瓷十分抢手,质量好的传统产品继续畅销,滞销的只是质量差的产品。而随着人性化理念的普及,及新型和谐社会的构成,设计一种刚性好、硬度高、耐溶剂且耐热的陶瓷用紫外光固化环氧丙烯酸酯涂料是非常必要的。
发明内容
解决的技术问题:
本申请针对上述技术问题,提供一种陶瓷用紫外光固化环氧丙烯酸酯涂料,解决现有陶瓷用紫外光固化环氧丙烯酸酯涂料刚性差、硬度低、不耐溶剂且耐热性差等技术问题。
技术方案:
一种陶瓷用紫外光固化环氧丙烯酸酯涂料,所述陶瓷用紫外光固化环氧丙烯酸酯涂料的原料按重量份数配比如下:丙烯酸羟乙酯80-90份;乙二醇10-20份;马来酸酐30-40份;新戊二醇15-25份;环氧树脂100份;对苯二甲酸二甲酯25-35份;光敏剂1-10份;醋酸锌10-30份;双酚A为40-60份;对苯二甲酸15-35份;交联剂5-15份;间苯二甲酸20-40份;环氧乙烷20-30份;己二酸5-25份;环氧丙烷15-25份。
作为本发明的一种优选技术方案:所述陶瓷用紫外光固化环氧丙烯酸酯涂料的原料按重量份数配比如下:丙烯酸羟乙酯85份;乙二醇15份;马来酸酐35份;新戊二醇20份;环氧树脂100份;对苯二甲酸二甲酯30份;光敏剂5份;醋酸锌20份;双酚A为50份;对苯二甲酸25份;交联剂10份;间苯二甲酸30份;环氧乙烷25份;己二酸15份;环氧丙烷20份。
作为本发明的一种优选技术方案:所述光敏剂采用安息香乙醚或二苯甲酮。
作为本发明的一种优选技术方案:所述交联剂采用六甲氧甲基三聚氰胺或苯乙烯。
有益效果:
本发明所述一种陶瓷用紫外光固化环氧丙烯酸酯涂料采用以上技术方案与现有技术相比,具有以下技术效果:1、产品光泽度120%-130%,硬度5-7H;2、耐130-150℃高温,在5%盐酸溶液中浸泡2-4d无异常;3、在饱和氢氧化钙中浸泡4-6d不起泡、皱皮;4、产品耐洗擦性2200-2800次不露底,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种陶瓷用紫外光固化环氧丙烯酸酯涂料,其原料按重量份数配比如下:丙烯酸羟乙酯80份;乙二醇10份;马来酸酐30份;新戊二醇15份;环氧树脂100份;对苯二甲酸二甲酯25份;二苯甲酮1份;醋酸锌10份;双酚A为40份;对苯二甲酸15份;苯乙烯5份;间苯二甲酸20份;环氧乙烷20份;己二酸5份;环氧丙烷15份。
将上述原料在反应釜中混合均匀后,涂覆于陶瓷上,涂膜用紫外线照射即可。
产品光泽度120%,硬度5H;耐130℃高温,在5%盐酸溶液中浸泡2d无异常;在饱和氢氧化钙中浸泡4d不起泡、皱皮;产品耐洗擦性2200次不露底。
实施例2:
一种陶瓷用紫外光固化环氧丙烯酸酯涂料,其原料按重量份数配比如下:丙烯酸羟乙酯90份;乙二醇20份;马来酸酐40份;新戊二醇25份;环氧树脂100份;对苯二甲酸二甲酯35份;二苯甲酮10份;醋酸锌30份;双酚A为60份;对苯二甲酸35份;六甲氧甲基三聚氰胺15份;间苯二甲酸40份;环氧乙烷30份;己二酸25份;环氧丙烷25份。
将上述原料在反应釜中混合均匀后,涂覆于陶瓷上,涂膜用紫外线照射即可。
产品光泽度125%,硬度6H;耐140℃高温,在5%盐酸溶液中浸泡3d无异常;在饱和氢氧化钙中浸泡5d不起泡、皱皮;产品耐洗擦性2500次不露底。
实施例3:
一种陶瓷用紫外光固化环氧丙烯酸酯涂料,其原料按重量份数配比如下:丙烯酸羟乙酯85份;乙二醇15份;马来酸酐35份;新戊二醇20份;环氧树脂100份;对苯二甲酸二甲酯30份;安息香乙醚5份;醋酸锌20份;双酚A为50份;对苯二甲酸25份;六甲氧甲基三聚氰胺10份;间苯二甲酸30份;环氧乙烷25份;己二酸15份;环氧丙烷20份。
将上述原料在反应釜中混合均匀后,涂覆于陶瓷上,涂膜用紫外线照射即可。
产品光泽度130%,硬度7H;耐150℃高温,在5%盐酸溶液中浸泡4d无异常;在饱和氢氧化钙中浸泡6d不起泡、皱皮;产品耐洗擦性2800次不露底。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (4)
1.一种陶瓷用紫外光固化环氧丙烯酸酯涂料,其特征在于所述陶瓷用紫外光固化环氧丙烯酸酯涂料的原料按重量份数配比如下:丙烯酸羟乙酯80-90份;乙二醇10-20份;马来酸酐30-40份;新戊二醇15-25份;环氧树脂100份;对苯二甲酸二甲酯25-35份;光敏剂1-10份;醋酸锌10-30份;双酚A为40-60份;对苯二甲酸15-35份;交联剂5-15份;间苯二甲酸20-40份;环氧乙烷20-30份;己二酸5-25份;环氧丙烷15-25份。
2.根据权利要求1所述的一种陶瓷用紫外光固化环氧丙烯酸酯涂料,其特征在于所述陶瓷用紫外光固化环氧丙烯酸酯涂料的原料按重量份数配比如下:丙烯酸羟乙酯85份;乙二醇15份;马来酸酐35份;新戊二醇20份;环氧树脂100份;对苯二甲酸二甲酯30份;光敏剂5份;醋酸锌20份;双酚A为50份;对苯二甲酸25份;交联剂10份;间苯二甲酸30份;环氧乙烷25份;己二酸15份;环氧丙烷20份。
3.根据权利要求1所述的一种陶瓷用紫外光固化环氧丙烯酸酯涂料,其特征在于:所述光敏剂采用安息香乙醚或二苯甲酮。
4.根据权利要求1所述的一种陶瓷用紫外光固化环氧丙烯酸酯涂料,其特征在于:所述交联剂采用六甲氧甲基三聚氰胺或苯乙烯。