CN104194530B - 一种丙烯酸酯外墙涂料 - Google Patents
一种丙烯酸酯外墙涂料 Download PDFInfo
- Publication number
- CN104194530B CN104194530B CN201410408715.0A CN201410408715A CN104194530B CN 104194530 B CN104194530 B CN 104194530B CN 201410408715 A CN201410408715 A CN 201410408715A CN 104194530 B CN104194530 B CN 104194530B
- Authority
- CN
- China
- Prior art keywords
- parts
- external wall
- acrylate paint
- paint
- toluene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种丙烯酸酯外墙涂料，其原料按重量份数配比如下：丙烯酸树脂溶液100份；丁酮1‑10份；丙酮5‑10份；磷酸铅2‑8份；乙二醇丁醚乙酸酯30‑40份；氯丁橡胶15‑35份；环己酮25‑35份；增塑剂15‑20份；醋酸丁酯20‑30份；聚氯乙烯50‑60份；二甲苯5‑15份；防霉剂10‑20份；丁醇15‑35份；甲苯50‑60份；产品无结块，对比率0.9‑1；表干时间1‑2h，在水中浸泡5‑7d后无起泡、脱落现象；耐碱性好，在碱水中浸泡48‑72h无异常；涂膜耐刷洗性1500‑2000次，可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于涂料领域，尤其涉及一种丙烯酸酯外墙涂料。
背景技术
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或乙二醇丁醚乙酸酯配制而成的粘稠液体。中国涂料界比较权威的《涂料工艺》一书是这样定义的：“涂料是一种材料，这种材料可以用不同的施工工艺涂覆在物件表面，形成粘附牢固、具有一定强度、连续的固态薄膜。这样形成的膜通称涂膜，又称漆膜或涂层。”涂料涂饰于物体表面能与基体材料很好粘结并形成完整而坚韧保护膜的物料，称为涂料。涂料与油漆是同一概念。油漆是人们沿用已久的习惯名称，引进我国后，就一直利用在建筑行业。涂料的作用可以概括为三个方面：保护作用，装饰作用，特殊功能作用。涂料的一般组成：包含成膜物质、颜填料、溶剂、助剂。
中国涂料产业在下游产业的推动下日益壮大，而作为其中一个分支的建筑涂料，也得到了长足的发展。统计数据显示，2011年中国建筑涂料总计产量约351.82万吨，同比增长30％以上。由此可见，中国建筑涂料产业虽然经历了2008年全球性金融危机的影响、原材料价格上涨及央行加息带来的压力，但其发展势头依然不减，且还保持着较高的增长率。
外墙涂料，是用于涂刷建筑外立墙面的，所以最重要的一项指标就是抗紫外线照射，要求达到长时间照射不变色。外墙涂料还要求有抗水性能，要求有自涤性。漆膜要硬而平整，脏污一冲就掉。外墙涂料能用于内墙涂刷使用是因为它也具有抗水性能；而内墙涂料却不具备抗晒功能，所以不能把内墙涂料当外墙涂料用。而随着人性化理念的普及，及新型和谐社会的构成，设计一种干燥时间短及耐碱性优异的丙烯酸酯外墙涂料是非常必要的。
发明内容
解决的技术问题：
本申请针对上述技术问题，提供一种丙烯酸酯外墙涂料，解决现有丙烯酸酯外墙涂料耐水性和耐碱性差、干燥时间长、不耐刷洗等技术问题。
技术方案：
一种丙烯酸酯外墙涂料，所述丙烯酸酯外墙涂料的原料按重量份数配比如下：丙烯酸树脂溶液100份；丁酮1-10份；丙酮5-10份；磷酸铅2-8份；乙二醇丁醚乙酸酯30-40份；氯丁橡胶15-35份；环己酮25-35份；增塑剂15-20份；醋酸丁酯20-30份；聚氯乙烯50-60份；二甲苯5-15份；防霉剂10-20份；丁醇15-35份；甲苯50-60份。
作为本发明的一种优选技术方案：所述丙烯酸酯外墙涂料的原料按重量份数配比如下：丙烯酸树脂溶液100份；丁酮6份；丙酮7份；磷酸铅5份；乙二醇丁醚乙酸酯35份；氯丁橡胶25份；环己酮30份；增塑剂18份；醋酸丁酯25份；聚氯乙烯55份；二甲苯10份；防霉剂12份；丁醇25份；甲苯55份。
作为本发明的一种优选技术方案：所述增塑剂采用己二酸二异辛酯。
作为本发明的一种优选技术方案：所述防霉剂采用环烷酸锌。
有益效果：
本发明所述一种丙烯酸酯外墙涂料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品无结块，对比率0.9-1；2、表干时间1-2h，在水中浸泡5-7d后无起泡、脱落现象；3、耐碱性好，在碱水中浸泡48-72h无异常；4、涂膜耐刷洗性1500-2000次，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种丙烯酸酯外墙涂料，其原料按重量份数配比如下：丙烯酸树脂溶液100份；丁酮1份；丙酮5份；磷酸铅2份；乙二醇丁醚乙酸酯30份；氯丁橡胶15份；环己酮25份；己二酸二异辛酯15份；醋酸丁酯20份；聚氯乙烯50份；二甲苯5份；环烷酸锌10份；丁醇15份；甲苯50份。
将丁酮、丙酮、磷酸铅、乙二醇丁醚乙酸酯、氯丁橡胶和环己酮装入球磨中，球磨30min，然后加入己二酸二异辛酯、醋酸丁酯、聚氯乙烯、二甲苯和环烷酸锌，球磨30min后加丙烯酸树脂溶液，继续球磨4h，最后，将余下的原料全部投入球磨机中球磨30min，既得成品。
产品表干时间2h，在水中浸泡5d后无起泡、脱落现象；在碱水中浸泡48h无异常，涂膜耐刷洗性1500次。
实施例2:
一种丙烯酸酯外墙涂料，其原料按重量份数配比如下：丙烯酸树脂溶液100份；丁酮10份；丙酮10份；磷酸铅8份；乙二醇丁醚乙酸酯40份；氯丁橡胶35份；环己酮35份；己二酸二异辛酯20份；醋酸丁酯30份；聚氯乙烯60份；二甲苯15份；环烷酸锌20份；丁醇35份；甲苯60份。
将丁酮、丙酮、磷酸铅、乙二醇丁醚乙酸酯、氯丁橡胶和环己酮装入球磨中，球磨30min，然后加入己二酸二异辛酯、醋酸丁酯、聚氯乙烯、二甲苯和环烷酸锌，球磨30min后加丙烯酸树脂溶液，继续球磨5h，最后，将余下的原料全部投入球磨机中球磨30min，既得成品。
产品表干时间1.5h，在水中浸泡6d后无起泡、脱落现象；在碱水中浸泡60h无异常，涂膜耐刷洗性1800次。
实施例3:
一种丙烯酸酯外墙涂料，其原料按重量份数配比如下：丙烯酸树脂溶液100份；丁酮6份；丙酮7份；磷酸铅5份；乙二醇丁醚乙酸酯35份；氯丁橡胶25份；环己酮30份；己二酸二异辛酯18份；醋酸丁酯25份；聚氯乙烯55份；二甲苯10份；环烷酸锌12份；丁醇25份；甲苯55份。
将丁酮、丙酮、磷酸铅、乙二醇丁醚乙酸酯、氯丁橡胶和环己酮装入球磨中，球磨30min，然后加入己二酸二异辛酯、醋酸丁酯、聚氯乙烯、二甲苯和环烷酸锌，球磨30min后加丙烯酸树脂溶液，继续球磨4.5h，最后，将余下的原料全部投入球磨机中球磨30min，既得成品。
产品表干时间1h，在水中浸泡7d后无起泡、脱落现象；在碱水中浸泡72h无异常，涂膜耐刷洗性2000次。
以上实施例中的组合物所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (1)
1.一种丙烯酸酯外墙涂料，其特征在于所述丙烯酸酯外墙涂料的原料按重量份数配比如下：丙烯酸树脂溶液100份；丁酮6份；丙酮7份；磷酸铅5份；乙二醇丁醚乙酸酯35份；氯丁橡胶25份；环己酮30份；增塑剂18份；醋酸丁酯25份；聚氯乙烯55份；二甲苯10份；防霉剂12份；丁醇25份；甲苯55份；所述增塑剂采用己二酸二异辛酯；所述防霉剂采用环烷酸锌。