CN104177054A - Building heat-insulating waterproof material - Google Patents
Building heat-insulating waterproof material Download PDFInfo
- Publication number
- CN104177054A CN104177054A CN201410411468.XA CN201410411468A CN104177054A CN 104177054 A CN104177054 A CN 104177054A CN 201410411468 A CN201410411468 A CN 201410411468A CN 104177054 A CN104177054 A CN 104177054A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- waterproof material
- building heat
- insulating waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a building heat-insulating waterproof material which is prepared from the following raw materials in parts by weight: 5-10 parts of triethanolamine, 4-8 parts of scale-like aluminum, 10-12 parts of talcum powder, 20-30 parts of expanded perlite, 6-9 parts of calcium hydroxide, 2-5 parts of trichloroethyl phosphate, 10-15 parts of tourmaline powder, 3-5 parts of sodium silicate, 5-10 parts of titanium dioxide and 10-15 parts of deionized water. The building heat-insulating waterproof material disclosed by the invention has the characteristics of good ageing-resistant property, no crack at a low temperature and no bulge at a high temperature, is mainly applied to the construction of water prevention of outdoor and indoor sinks, toilets and underground constructions, water prevention and moisture prevention of maintenance constructions and the like and has the advantages of high waterproof strength, high self-protecting power and convenience for use.
Description
Technical field
The present invention relates to a kind of heat-insulating and water-proofing of building material.
Background technology
At present, the waterproof homework of all kinds of buildingss is crucial problems.Normally used water-proof material mostly is all kinds of waterproof rolls, waterproof paint, waterproof clay etc.Waterproof roll generally be take heat construction as main, roasting mainly with fire, and main deficiency is bonding not comprehensive, has seam, to some privileged sites, and the bad processing such as the position such as corner, the mouth of pipe, easily infiltration, easy-maintaining not after infiltration.The general cold construction of waterproof paint, after waterproof paint is stirred, once brushes, and without seam construction, bonding force is strong.Its weak point is that intensity is not high, and self-shield power is not strong.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is that a kind of heat-insulating and water-proofing of building material is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of heat-insulating and water-proofing of building material, by the raw material of following parts by weight, made: 5~10 parts of trolamines; 4~8 parts of flakey aluminium flakes; 10~12 parts of talcum powder; 20~30 parts of pearlstones; 6~9 parts, calcium hydroxide; 2~5 parts of Trichloroethyl Phosphates; 10~15 parts of tourmaline powders; 3~5 parts of water glass; 5~10 parts of titanium dioxides; 10~15 parts of deionized waters.
Beneficial effect of the present invention: ageing resistance is good, has low temperature and does not ftracture, and high temperature does not play bulging feature.Be mainly used in outside room, the construction such as indoor pond, toilet and underground project waterproof, maintenance engineering waterproof, protection against the tide.Have again higher waterproof intensity, self-shield power is strong, easy to use.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1, and a kind of heat-insulating and water-proofing of building material is made by the raw material of following parts by weight: 10 parts of trolamines; 8 parts of flakey aluminium flakes; 12 parts of talcum powder; 20 parts of pearlstones; 6 parts, calcium hydroxide; 2 parts of Trichloroethyl Phosphates; 15 parts of tourmaline powders; 5 parts of water glass; 10 parts of titanium dioxides; 15 parts of deionized waters.
Embodiment 2, and a kind of heat-insulating and water-proofing of building material is made by the raw material of following parts by weight: 5 parts of trolamines; 4 parts of flakey aluminium flakes; 10 parts of talcum powder; 20 parts of pearlstones; 9 parts, calcium hydroxide; 5 parts of Trichloroethyl Phosphates; 10 parts of tourmaline powders; 3 parts of water glass; 5 parts of titanium dioxides; 10 parts of deionized waters.
Embodiment 3, and a kind of heat-insulating and water-proofing of building material is made by the raw material of following parts by weight: 8 parts of trolamines; 5 parts of flakey aluminium flakes; 10 parts of talcum powder; 25 parts of pearlstones; 7 parts, calcium hydroxide; 3 parts of Trichloroethyl Phosphates; 12 parts of tourmaline powders; 5 parts of water glass; 8 parts of titanium dioxides; 13 parts of deionized waters.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (1)
1. a heat-insulating and water-proofing of building material, is characterized in that: the raw material by following parts by weight is made: 5~10 parts of trolamines; 4~8 parts of flakey aluminium flakes; 10~12 parts of talcum powder; 20~30 parts of pearlstones; 6~9 parts, calcium hydroxide; 2~5 parts of Trichloroethyl Phosphates; 10~15 parts of tourmaline powders; 3~5 parts of water glass; 5~10 parts of titanium dioxides; 10~15 parts of deionized waters.