CN104177027A - Cement-base permeation crystallizing waterproof material - Google Patents
Cement-base permeation crystallizing waterproof material Download PDFInfo
- Publication number
- CN104177027A CN104177027A CN201410411321.0A CN201410411321A CN104177027A CN 104177027 A CN104177027 A CN 104177027A CN 201410411321 A CN201410411321 A CN 201410411321A CN 104177027 A CN104177027 A CN 104177027A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- waterproof material
- crystallizing
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cement-base permeation crystallizing waterproof material which is prepared from the following raw materials in parts by weight: 100 parts of Portland cement, 40-50 parts of quartz sand, 5-10 parts of calcium hydroxide, 1-5 parts of active component A, 1-3 parts of talcum powder, 3-8 parts of polypropylene wax, 10-20 parts of bentonite, 1-5 parts of active component B, 5-15 parts of silica fume, 1-3 parts of water reducer and 0.2-1 part of sugar calcium retarder. The waterproof material has the advantages of favorable effect, simple construction process, low requirements for environment, favorable waterproof quality, high durability and the like.
Description
Technical field
The present invention relates to building material technical field, be specifically related to a kind of cement-base infiltration crystallization water-proof material.
Background technology
Skeleton construction is invented in 19 end of the centurys people, due to its have intensity high, be convenient to draw materials, the plurality of advantages such as different shape strong adaptability, making, once the favor that occurs being just subject to immediately people, has become current most of constructure body structure material.But various buildingss are all contacting with dissimilar water, as water vapour, surface water, underground water etc.These water are by different way in harmful to the structure generation of buildings in varying degrees effect, as hygroscopic effect, wicking action, erosion action, osmosis, freeze thawing are got rid of etc.This effect gently affects the use of buildings beginning, heavy shorten working life of buildings, even cannot ensure the mankind's the security of the lives and property.Publication number is that the document of CN101759414B discloses a kind of cementitious capillary crystalline waterproofing agent, and this water-resisting agent has certain impermeability and anti-steel bar corrosion, but this water-resisting agent Recipe complexity causes production cost too high, and economic benefit is not high.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is that a kind of cement-base infiltration crystallization water-proof material is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of cement-base infiltration crystallization water-proof material, made by the raw material of following parts by weight: 100 parts of silicate cements, quartz sand 40-50 part, calcium hydroxide 5-10 part, active component A 1-5 part, talcum powder 1-3 part, Poly Propylene Wax 3-8 part, wilkinite 10-20 part, active ingredient B 1-5 part, silicon ash 5-15 part, water reducer 1-3 part, sugared calcium retardant 0.2-1 part.
Beneficial effect of the present invention: have respond well, construction is simple, to premium propertiess such as low, the good water resistance of environmental requirement and weather resistance.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1, a kind of cement-base infiltration crystallization water-proof material, is made up of the raw material of following parts by weight: 100 parts of silicate cements, 40 parts of quartz sands, 10 parts, calcium hydroxide, 1 part of active component A, 3 parts of talcum powder, 3 parts of Poly Propylene Waxes, 10 parts of wilkinites, 3 parts of active ingredient B, 10 parts of silicon ashes, 2 parts of water reducers, 0.2 part of sugared calcium retardant.
Embodiment 2, a kind of cement-base infiltration crystallization water-proof material, is made up of the raw material of following parts by weight: 100 parts of silicate cements, 50 parts of quartz sands, 10 parts, calcium hydroxide, 2 parts of active component A, 2 parts of talcum powder, 5 parts of Poly Propylene Waxes, 10 parts of wilkinites, 2 parts of active ingredient B, 10 parts of silicon ashes, 2 parts of water reducers, 0.5 part of sugared calcium retardant.
Embodiment 3, a kind of cement-base infiltration crystallization water-proof material, is made up of the raw material of following parts by weight: 100 parts of silicate cements, 45 parts of quartz sands, 8 parts, calcium hydroxide, 4 parts of active component A, 2 parts of talcum powder, 5 parts of Poly Propylene Waxes, 15 parts of wilkinites, 4 parts of active ingredient B, 12 parts of silicon ashes, 2 parts of water reducers, 0.8 part of sugared calcium retardant.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, variation, change, interpolation or the replacement made, all should belong to protection scope of the present invention.
Claims (1)
1. a cement-base infiltration crystallization water-proof material, it is characterized in that: the raw material by following parts by weight is made: 100 parts of silicate cements, quartz sand 40-50 part, calcium hydroxide 5-10 part, active component A 1-5 part, talcum powder 1-3 part, Poly Propylene Wax 3-8 part, wilkinite 10-20 part, active ingredient B 1-5 part, silicon ash 5-15 part, water reducer 1-3 part, sugared calcium retardant 0.2-1 part.