CN104193260A - Capillary crystalline waterproof material - Google Patents
Capillary crystalline waterproof material Download PDFInfo
- Publication number
- CN104193260A CN104193260A CN201410411313.6A CN201410411313A CN104193260A CN 104193260 A CN104193260 A CN 104193260A CN 201410411313 A CN201410411313 A CN 201410411313A CN 104193260 A CN104193260 A CN 104193260A
- Authority
- CN
- China
- Prior art keywords
- parts
- waterproof material
- crystalline waterproof
- capillary crystalline
- calcium hydroxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a capillary crystalline waterproof material which is prepared from the following raw materials in parts by weight: 0.6-0.7 part of silicate cement: quartz sand, 1-5 parts of sodium 2-methyl-1-naphthalenesulfonate condensate, 7-12 parts of siloxane, 6-9 parts of calcium hydroxide, 0.08-0.1 part of silicon micropowder, 0.002-0.003 part of water repellent and 0.005-0.1 part of cellulose. The capillary crystalline waterproof material has favorable binding property, water resistance and breathability, can overcome the disadvantages of the cement-based capillary crystalline waterproof material in the prior art, is suitable for large-scale popularization and application, and has obvious economic benefits and social benefits.
Description
Technical field
The present invention relates to a kind of permeable crystalline waterproofing material, is a kind of novel permeable crystalline waterproofing material.
Background technology
GB " GB18445(2001) cementitious capillary waterproofing material " since implementing on March 1st, 2002, promoted researchdevelopment and the engineering application of this material, improved the working efficiency of waterproofing work, reduced the comprehensive cost of waterproofing work; In a way, met the requirement of modern building to weather resistance.Can say, cementitious capillary waterproofing material, with its comprehensive advantage, wins each side personage's favor, in rigidity water-proofing material, leak stopping sealing material series, has established own consequence.Dragons and fishes jumbled together in current water-proof material market, and especially cement-based penetrant water-proof material is uneven especially cannot guarantee waterproof effect, causes the complaint of a large number of users.So at present in the urgent need to a kind of novel concrete base osmotic crystalline waterproof material, solve a difficult problem for waterproofing industry, bring good economic benefit and social benefit.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is that a kind of permeable crystalline waterproofing material is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of permeable crystalline waterproofing material, raw material by following parts by weight is made: silicate cement: quartz sand: 0.6～0.7 part, 1～5 part of methyl naphthalene sulfonic acid sodium condenses, 7～12 parts of siloxanes, 6～9 parts, calcium hydroxide, silicon powder: 0.08～0.1 part, hydrophober: 0.002～0.003 part, Mierocrystalline cellulose: 0.005～0.1 part.
Beneficial effect of the present invention: there is better cohesiveness, water-repellancy and ventilation property, can overcome the shortcoming of cementitious capillary waterproofing material in prior art, be applicable to large-scale promotion application, there is significant economic benefit and social benefit.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1, and a kind of permeable crystalline waterproofing material is made by the raw material of following parts by weight: silicate cement: quartz sand: 0.6 part, 1 part of methyl naphthalene sulfonic acid sodium condenses, 7 parts of siloxanes, 6 parts, calcium hydroxide, silicon powder: 0.08 part, hydrophober: 0.003 part, Mierocrystalline cellulose: 0.005 part.
Embodiment 2, and a kind of permeable crystalline waterproofing material is made by the raw material of following parts by weight: silicate cement: quartz sand: 0.7 part, 5 parts of methyl naphthalene sulfonic acid sodium condensess, 7 parts of siloxanes, 9 parts, calcium hydroxide, silicon powder: 0.08 part, hydrophober: 0.002 part, Mierocrystalline cellulose: 0.005 part.
Embodiment 3, and a kind of permeable crystalline waterproofing material is made by the raw material of following parts by weight: silicate cement: quartz sand: 0.6 part, 3 parts of methyl naphthalene sulfonic acid sodium condensess, 10 parts of siloxanes, 7 parts, calcium hydroxide, silicon powder: 0.08 part, hydrophober: 0.002 part, Mierocrystalline cellulose: 0.007 part.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (1)
1. a permeable crystalline waterproofing material, it is characterized in that: the raw material by following parts by weight is made: silicate cement: quartz sand: 0.6～0.7 part, 1～5 part of methyl naphthalene sulfonic acid sodium condenses, 7～12 parts of siloxanes, 6～9 parts, calcium hydroxide, silicon powder: 0.08～0.1 part, hydrophober: 0.002～0.003 part, Mierocrystalline cellulose: 0.005～0.1 part.