CN104150876B - A kind of black tire or the grey making method of tire glaze paint flawless celadon and the glaze of use thereof - Google Patents
A kind of black tire or the grey making method of tire glaze paint flawless celadon and the glaze of use thereof Download PDFInfo
- Publication number
- CN104150876B CN104150876B CN201410359529.2A CN201410359529A CN104150876B CN 104150876 B CN104150876 B CN 104150876B CN 201410359529 A CN201410359529 A CN 201410359529A CN 104150876 B CN104150876 B CN 104150876B
- Authority
- CN
- China
- Prior art keywords
- parts
- tire
- glaze
- fountain
- dragon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of black tire or the grey making method of tire glaze paint flawless celadon and the glaze of use thereof, adopt dragon's fountain Dayao china clay, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone, Wingdale, feldspar, fluorite, zircon as glaze raw material, the black tire adopting brother kiln celadon to use or grey tire, utilize when firing firing temperature to achieve continuous these steps of burning of slow intensification, high-temperature firing, slow cooling, insulation and fire and form.The effect that the present invention is useful is: be both provided with flawless celadon porcelain exquisiteness, the lucid and lively smoothness of lines, moulding dignity is simple and natural, color and luster is pure and bright-colored feature, be provided with again that the purple mouth iron foot of celadon fired by black tire or grey tire, tire look sedate, tire matter is abundant, steady, the feature of air, be provided with dual characteristic sum effect, good visual effect, main is solve black tire or grey tire celadon are not suitable for producing daily celadon drawback because of crackle glaze, is beneficial to popularization.
Description
Technical field
The present invention relates to celadon manufacturing technology field, particularly a kind of black tire or the grey making method of tire glaze paint flawless celadon and the glaze of use thereof.
Background technology
At present, the official in Song dynasty five large common cave, the feature of brother's kiln celadon are all, the purple mouth iron foots of tire look greyish black, and the overwhelming majority has glaze paint has the phenomenon of hacking, cracky, difficult retention.Glaze paint is flawless only accounts for only a few, and this type of celadon product " vegetarian noodles is without line " that is referred in the world is government porcelain kiln, especially precious, but the manufacture craft of this product and glaze formula just lost for period at Song end.
Summary of the invention
Main purpose of the present invention is to provide a kind of black tire or the grey making method of tire glaze paint flawless celadon and the glaze of use thereof, the celadon glaze paint flawless obtained, both flawless celadon porcelain had been provided with fine and smooth, the lucid and lively smoothness of lines, moulding dignity is simple and natural, the feature that color and luster is pure and bright-colored, be provided with again black tire or grey tire and fire the purple mouth iron foot of celadon, tire look sedate, tire matter is abundant, steady, the feature of air, good visual effect, the most important thing is that technique of the present invention and glaze formula change conventional black tire or grey tire celadon are not suitable for producing daily celadon drawback because of crackle glaze, reproduce this kind of celadon product that the craft died out and the fine technique was lost, the present invention is more suitable for the universal and popularization of the black tire of dragon's fountain or grey tire class celadon.
Object of the present invention is realized by following technical scheme: the making method of this black tire or grey tire glaze paint flawless celadon, and it carries out as follows:
The first step, porcelain body is chosen, and chooses the black tire of dragon's fountain brother kiln or grey tire as the porcelain body making celadon;
Second step, glaze is chosen, choose dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone, Wingdale, fluorite, feldspar, zircon prepare glaze as raw material, wherein the parts by weight of dragon's fountain Dayao china clay in ancient times are 30 parts ~ 40 parts, the parts by weight of dragon's fountain Dayao Zijin in ancient times soil are 10 parts ~ 16 parts, the parts by weight of dragon's fountain Dayao porcelain stone are 8 parts ~ 12 parts, the parts by weight of Wingdale are 18 parts ~ 22 parts, the parts by weight of fluorite are 2 parts ~ 3 parts, the parts by weight of feldspar are 8 parts ~ 12 parts, and the parts by weight of zircon are 2 parts;
3rd step, prepared by glaze, first the dragon's fountain Dayao china clay in ancient times obtained, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone are carried out biscuiting, pulverizing at the temperature of 1200 DEG C, then the dragon's fountain Dayao china clay in ancient times after pulverizing, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone and Wingdale, fluorite, feldspar, zircon are carried out Homogeneous phase mixing, wet ball grinding 24 hours ~ 30 hours, then the glaze after ball milling is crossed 150 order ~ 180 mesh sieves, obtain glaze;
4th step, porcelain body glazing, add water the glaze obtained furnishing glaze slip, the ratio of glaze and water is 1:1, biscuiting being obtained the black tire of taxi driver brother's kiln or grey tire adopts glaze method to carry out glazing again, and be placed in shady and cool ventilation place after glazing and carry out natural air drying, time of drying is 8 hours ~ 10 hours;
5th step, porcelain body is fired, the black tire of first-class glaze or grey tire are placed in kiln and fire, first the temperature of kiln is increased to 900 DEG C ~ 950 DEG C gradually from normal temperature when firing, the temperature-rise period time is 8 hours, then at the temperature of 900 DEG C ~ 950 DEG C, 2 hours are incubated, then temperature is elevated to gradually 1260 DEG C ~ 1300 DEG C, then under the state that kiln is closed, 820 DEG C ~ 880 DEG C are slow cooling to, 2 hours ~ 3 hours are incubated at the temperature of 820 DEG C ~ 880 DEG C, cool to 350 DEG C ~ 500 DEG C again, 2 hours ~ 3 hours are incubated at the temperature of 350 DEG C ~ 500 DEG C, after having fired, kiln is closed comprehensively, porcelain body is allowed to carry out naturally cooling in kiln, after porcelain body cools completely, namely taking-up obtains black tire or grey tire glaze paint flawless celadon.
The black tire used in the making method of above-mentioned black tire or grey tire glaze paint flawless celadon or grey tire glaze paint flawless glaze, it is made by following weight: 10 parts ~ 16 parts, dragon's fountain Dayao china clay in ancient times 30 parts ~ 40 parts, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone 8 parts ~ 12 parts, 18 parts ~ 22 parts, Wingdale, fluorite 2 parts ~ 3 parts, feldspar 8 parts ~ 12 parts, zircon 2 parts.
China clay in the glaze major ingredient that the black tire of the present invention or grey tire glaze paint flawless celadon use, Zijin soil, porcelain stone are that the old ore deposit near dragon's fountain Dayao ancient kiln site in ancient times gathers, add a small amount of Wingdale again, fluorite, feldspar, zircon are formulated, these ancient times, old ore deposit raw material was through the use history of more than one thousand years, prove and make celadon material the most excellent, the present invention be based upon two more than ten years to the finding many times of these old ore deposit raw materials, process, prepare, to burn till etc. on the basis of research experiment, finally make black tire or grey tire glaze paint flawless celadon.
To be that the dilation coefficient ratio of tire and glaze is inconsistent cause for the black tire that conventional brother's kiln celadon adopts or grey tire crackle Producing reason, common glaze imposes on black tire or grey tire and the dilation coefficient ratio of tire glaze can be caused inconsistent, thus cause glaze paint to occur the phenomenon of crackle, and black tire of the present invention or grey tire glaze paint flawless celadon adjust to consistent by glaze with the dilation coefficient ratio of tire, achieve slow intensification at firing temperature simultaneously, high-temperature firing, slow cooling, these steps of the continuous burning of insulation are fired and are formed, in the process fired, by the change of firing temperature, the high temperature reduction in glaze is reacted to continue to carry out, reduce the speed of reduction reaction, there will not be the phenomenon of vigorous reaction, air emersion glaze paint in such glaze, the bubble produced in glaze reduces, the coefficient of expansion of glaze starts to reduce, reach and black tire, the ash tire coefficient of expansion is consistent, would not crackle be there is in the celadon glaze paint fired like this, thus achieve flawless effect, dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone in ancient times gathers from the ore deposit in ancient times near the ancient kiln site of dragon's fountain, dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone in ancient times is under long-term physical environment effect, namely long-term under the effect of empty G&W dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, the particle diameter of dragon's fountain Dayao porcelain stone in ancient times becomes large, degree of compactness reduces, thus the degree of compactness in glaze is reduced, the mineral when firing, air, between water, reactive behavior reduces, thus glaze coefficient of expansion when firing is reduced, the coefficient of expansion of glaze just can be made to reach consistent state with the coefficient of expansion of black tire or grey tire, thus the celadon glaze paint making black tire or grey tire burn out there will not be crackle, black tire or grey tire glaze paint flawless celadon can be obtained, the celadon glaze paint flawless obtained like this, both flawless celadon porcelain had been provided with fine and smooth, the lucid and lively smoothness of lines, moulding dignity is simple and natural, the feature that color and luster is pure and bright-colored, be provided with again black tire or grey tire and fire the purple mouth iron foot of celadon, tire look sedate, tire matter is abundant, steady, the feature of air, this is modern common celadon effect that technology is beyond one's reach, the most important thing is that technique of the present invention and glaze formula change conventional black tire or grey tire celadon are not suitable for producing daily celadon drawback because of crackle glaze, reproduce this kind of celadon product that the craft died out and the fine technique was lost, the present invention is more suitable for the universal and popularization of the black tire of dragon's fountain or grey tire class celadon.
The effect that the present invention is useful is: the black tire adopting brother's kiln celadon to use in the making method of black tire of the present invention or grey tire glaze paint flawless celadon or grey tire, make use of dragon's fountain Dayao china clay in ancient times in glaze, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone in ancient times, adopts in sintering procedure and slowly heats up, high-temperature firing, slow cooling, insulation is continuous burns these steps, the coefficient of expansion of the coefficient of expansion of glaze layer and black tire or grey tire is consistent, thus fires the black tire or grey tire glaze paint flawless that obtain, the celadon glaze paint flawless obtained like this, be both provided with flawless celadon porcelain fine and smooth, the lucid and lively smoothness of lines, moulding dignity is simple and natural, the feature that color and luster is pure and bright-colored, is provided with again black tire or the purple mouth iron foot of celadon fired by grey tire, tire look sedate, tire matter is abundant, steady, the feature of air, is provided with dual characteristic sum effect, and solve black tire or grey tire celadon are not suitable for producing daily celadon drawback because of crackle glaze, this is modern common celadon effect that technology is beyond one's reach, and is beneficial to popularization.
Embodiment
The invention will be further described below:
Embodiment 1
The making method of this black tire or grey tire glaze paint flawless celadon, it carries out as follows:
The first step, porcelain body is chosen, and chooses the black tire of dragon's fountain brother kiln or grey tire as the porcelain body making celadon;
Second step, glaze is chosen, choose dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone, Wingdale, fluorite, feldspar, zircon prepare glaze as raw material, wherein the parts by weight of dragon's fountain Dayao china clay in ancient times are 30 parts, and the parts by weight of dragon's fountain Dayao Zijin in ancient times soil are 10 parts, and the parts by weight of dragon's fountain Dayao porcelain stone are 8 parts, the parts by weight of Wingdale are 18 parts, the parts by weight of fluorite are 2 parts, and the parts by weight of feldspar are 8 parts, and the parts by weight of zircon are 2 parts;
3rd step, prepared by glaze, first the dragon's fountain Dayao china clay in ancient times obtained, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone are carried out biscuiting, pulverizing at the temperature of 1200 DEG C, then the dragon's fountain Dayao china clay in ancient times after pulverizing, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone and Wingdale, fluorite, feldspar, zircon are carried out Homogeneous phase mixing, wet ball grinding 24 hours, then the glaze after ball milling is crossed 150 mesh sieves, obtain glaze;
4th step, porcelain body glazing, add water the glaze obtained furnishing glaze slip, the ratio of glaze and water is 1:1, biscuiting being obtained the black tire of taxi driver brother's kiln or grey tire adopts glaze method to carry out glazing again, and be placed in shady and cool ventilation place after glazing and carry out natural air drying, time of drying is 8 hours;
5th step, porcelain body is fired, the black tire of first-class glaze or grey tire are placed in kiln and fire, first the temperature of kiln is increased to 900 DEG C gradually from normal temperature when firing, the temperature-rise period time is 8 hours, then at the temperature of 900 DEG C, 2 hours are incubated, then temperature is elevated to 1260 DEG C gradually, then under the state that kiln is closed, 820 DEG C are slow cooling to, 2 hours are incubated at the temperature of 820 DEG C, cool to 350 DEG C again, 2 hours are incubated at the temperature of 350 DEG C, after having fired, kiln is closed comprehensively, porcelain body is allowed to carry out naturally cooling in kiln, after porcelain body cools completely, namely taking-up obtains black tire or grey tire glaze paint flawless celadon.
The black tire used in the making method of above-mentioned black tire or grey tire glaze paint flawless celadon or grey tire glaze paint flawless glaze, it is made by following weight: 10 parts ~ 16 parts, dragon's fountain Dayao china clay in ancient times 30 parts ~ 40 parts, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone 8 parts ~ 12 parts, 18 parts ~ 22 parts, Wingdale, fluorite 2 parts ~ 3 parts, feldspar 8 parts ~ 12 parts, zircon 2 parts.
In embodiment one, 1 part is 500 grams.
Embodiment 2
The making method of this black tire or grey tire glaze paint flawless celadon, it carries out as follows:
The first step, porcelain body is chosen, and chooses the black tire of dragon's fountain brother kiln or grey tire as the porcelain body making celadon;
Second step, glaze is chosen, choose dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone, Wingdale, fluorite, feldspar, zircon prepare glaze as raw material, wherein the parts by weight of dragon's fountain Dayao china clay in ancient times are 35 parts, and the parts by weight of dragon's fountain Dayao Zijin in ancient times soil are 14 parts, and the parts by weight of dragon's fountain Dayao porcelain stone are 10 parts, the parts by weight of Wingdale are 20 parts, the parts by weight of fluorite are 3 parts, and the parts by weight of feldspar are 10 parts, and the parts by weight of zircon are 2 parts;
3rd step, prepared by glaze, first the dragon's fountain Dayao china clay in ancient times obtained, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone are carried out biscuiting, pulverizing at the temperature of 1200 DEG C, then the dragon's fountain Dayao china clay in ancient times after pulverizing, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone and Wingdale, fluorite, feldspar, zircon are carried out Homogeneous phase mixing, wet ball grinding 26 hours, then the glaze after ball milling is crossed 160 mesh sieves, obtain glaze;
4th step, porcelain body glazing, add water the glaze obtained furnishing glaze slip, the ratio of glaze and water is 1:1, biscuiting being obtained the black tire of taxi driver brother's kiln or grey tire adopts glaze method to carry out glazing again, and be placed in shady and cool ventilation place after glazing and carry out natural air drying, time of drying is 9 hours;
5th step, porcelain body is fired, the black tire of first-class glaze or grey tire are placed in kiln and fire, first the temperature of kiln is increased to 920 DEG C gradually from normal temperature when firing, the temperature-rise period time is 8 hours, then at the temperature of 920 DEG C, 2 hours are incubated, then temperature is elevated to 1280 DEG C gradually, then under the state that kiln is closed, 860 DEG C are slow cooling to, 3 hours are incubated at the temperature of 860 DEG C, cool to 430 DEG C again, 3 hours are incubated at the temperature of 430 DEG C, after having fired, kiln is closed comprehensively, porcelain body is allowed to carry out naturally cooling in kiln, after porcelain body cools completely, namely taking-up obtains black tire or grey tire glaze paint flawless celadon.
The black tire used in the making method of above-mentioned black tire or grey tire glaze paint flawless celadon or grey tire glaze paint flawless glaze, it is made by following weight: 14 parts, dragon's fountain Dayao china clay in ancient times 35 parts, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone 10 parts, 20 parts, Wingdale, fluorite 3 parts, feldspar 10 parts, zircon 2 parts.
In embodiment two, 1 part is 500 grams.
Embodiment 3
The making method of this black tire or grey tire glaze paint flawless celadon, it carries out as follows:
The first step, porcelain body is chosen, and chooses the black tire of dragon's fountain brother kiln or grey tire as the porcelain body making celadon;
Second step, glaze is chosen, choose dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone, Wingdale, fluorite, feldspar, zircon prepare glaze as raw material, wherein the parts by weight of dragon's fountain Dayao china clay in ancient times are 40 parts, and the parts by weight of dragon's fountain Dayao Zijin in ancient times soil are 16 parts, and the parts by weight of dragon's fountain Dayao porcelain stone are 12 parts, the parts by weight of Wingdale are 22 parts, the parts by weight of fluorite are 3 parts, and the parts by weight of feldspar are 12 parts, and the parts by weight of zircon are 2 parts;
3rd step, prepared by glaze, first the dragon's fountain Dayao china clay in ancient times obtained, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone are carried out biscuiting, pulverizing at the temperature of 1200 DEG C, then the dragon's fountain Dayao china clay in ancient times after pulverizing, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone and Wingdale, fluorite, feldspar, zircon are carried out Homogeneous phase mixing, wet ball grinding 30 hours, then the glaze after ball milling is crossed 180 mesh sieves, obtain glaze;
4th step, porcelain body glazing, add water the glaze obtained furnishing glaze slip, the ratio of glaze and water is 1:1, biscuiting being obtained the black tire of taxi driver brother's kiln or grey tire adopts glaze method to carry out glazing again, and be placed in shady and cool ventilation place after glazing and carry out natural air drying, time of drying is 10 hours;
5th step, porcelain body is fired, the black tire of first-class glaze or grey tire are placed in kiln and fire, first the temperature of kiln is increased to 950 DEG C gradually from normal temperature when firing, the temperature-rise period time is 8 hours, then at the temperature of 950 DEG C, 2 hours are incubated, then temperature is elevated to 1300 DEG C gradually, then under the state that kiln is closed, 880 DEG C are slow cooling to, 3 hours are incubated at the temperature of 880 DEG C, cool to 500 DEG C again, 3 hours are incubated at the temperature of 500 DEG C, after having fired, kiln is closed comprehensively, porcelain body is allowed to carry out naturally cooling in kiln, after porcelain body cools completely, namely taking-up obtains black tire or grey tire glaze paint flawless celadon.
The black tire used in the making method of above-mentioned black tire or grey tire glaze paint flawless celadon or grey tire glaze paint flawless glaze, it is made by following weight: 16 parts, dragon's fountain Dayao china clay in ancient times 40 parts, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone 12 parts, 22 parts, Wingdale, fluorite 3 parts, feldspar 12 parts, zircon 2 parts.
In embodiment three, 1 part is 500 grams.
Dragon's fountain Dayao china clay in ancient times takes from the china clay in mine near Dayao kiln site in ancient times in Dayao village, Longquan City little Mei town, Zhejiang Province, dragon's fountain Dayao Zijin in ancient times soil takes from the Zijin soil in mine near Dayao kiln site in ancient times in Dayao village, Longquan City little Mei town, Zhejiang Province, dragon's fountain Dayao porcelain stone take from Dayao village, Longquan City little Mei town, Zhejiang Province near Dayao kiln site in ancient times mine porcelain stone, the black tire that black tire and grey tire select brother's kiln celadon to use and grey tire, Wingdale, fluorite, feldspar, zircon selects Wingdale common on the market, fluorite, feldspar, zircon, the major ingredient of glaze is dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone in ancient times, Wingdale, fluorite, feldspar, zircon uses as auxiliary material, the shrinking percentage of glaze can be reduced, make the coefficient of expansion of glaze layer reach the state be consistent with black tire or grey tire when firing, thus make the black tire that obtains or grey tire celadon glaze paint flawless.
Artwork distinguishes judgement mainly through apparent visual, chooses 100 parts of embodiment of the present invention one, embodiment two, embodiment three fire the celadon that obtains and adopt common celadon, adopt the celadon of black tire or grey tire and common glaze to compare, table specific as follows:
As can be known from the above table, the black tire of the embodiment of the present invention or the making method of grey tire glaze paint flawless celadon and the glaze used, it is fine and smooth that the celadon adopting making method of the present invention to obtain both had been provided with flawless celadon porcelain, the lucid and lively smoothness of lines, moulding dignity is simple and natural, the feature that color and luster is pure and bright-colored, be provided with again black tire or grey tire and fire the purple mouth iron foot of celadon, tire look sedate, tire matter is abundant, steady, the feature of air, be provided with dual characteristic sum effect, this is modern common celadon effect that technology is beyond one's reach, visual effect is all better with the celadon adopting black tire or the common glaze of grey tire to obtain than common celadon, the most important thing is that technique of the present invention and glaze formula change conventional black tire or grey tire celadon are not suitable for producing daily celadon drawback because of crackle glaze, reproduce this kind of celadon product that the craft died out and the fine technique was lost, the present invention is more suitable for the universal and popularization of the black tire of dragon's fountain or grey tire class celadon.
Although the present invention is described by reference to preferred embodiment, those skilled in the art should understand, and in the scope of claims, can do the various change in form and details.
Claims (2)
1. a making method for black tire or grey tire glaze paint flawless celadon, is characterized in that it carries out as follows:
(1) porcelain body is chosen, and chooses the black tire of dragon's fountain brother kiln or grey tire as the porcelain body making celadon;
(2) glaze is chosen, choose dragon's fountain Dayao china clay in ancient times, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone, Wingdale, fluorite, feldspar, zircon prepare glaze as raw material, wherein the parts by weight of dragon's fountain Dayao china clay in ancient times are 30 parts ~ 40 parts, the parts by weight of dragon's fountain Dayao Zijin in ancient times soil are 10 parts ~ 16 parts, the parts by weight of dragon's fountain Dayao porcelain stone are 8 parts ~ 12 parts, the parts by weight of Wingdale are 18 parts ~ 22 parts, the parts by weight of fluorite are 2 parts ~ 3 parts, the parts by weight of feldspar are 8 parts ~ 12 parts, and the parts by weight of zircon are 2 parts;
(3) glaze preparation, first the dragon's fountain Dayao china clay in ancient times obtained, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone are carried out biscuiting, pulverizing at the temperature of 1200 DEG C, then the dragon's fountain Dayao china clay in ancient times after pulverizing, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone and Wingdale, fluorite, feldspar, zircon are carried out Homogeneous phase mixing, wet ball grinding 24 hours ~ 30 hours, then the glaze after ball milling is crossed 150 order ~ 180 mesh sieves, obtain glaze;
(4) porcelain body glazing, add water the glaze obtained furnishing glaze slip, and the ratio of glaze and water is 1:1, then biscuiting is obtained the black tire of taxi driver brother's kiln or grey tire and adopt glaze method to carry out glazing, be placed in shady and cool ventilation place after glazing and carry out natural air drying, time of drying is 8 hours ~ 10 hours;
(5) porcelain body is fired, the black tire of first-class glaze or grey tire are placed in kiln and fire, first the temperature of kiln is increased to 900 DEG C ~ 950 DEG C gradually from normal temperature when firing, the temperature-rise period time is 8 hours, then at the temperature of 900 DEG C ~ 950 DEG C, 2 hours are incubated, then temperature is elevated to gradually 1260 DEG C ~ 1300 DEG C, then under the state that kiln is closed, 820 DEG C ~ 880 DEG C are slow cooling to, 2 hours ~ 3 hours are incubated at the temperature of 820 DEG C ~ 880 DEG C, cool to 350 DEG C ~ 500 DEG C again, 2 hours ~ 3 hours are incubated at the temperature of 350 DEG C ~ 500 DEG C, after having fired, kiln is closed comprehensively, porcelain body is allowed to carry out naturally cooling in kiln, after porcelain body cools completely, namely taking-up obtains black tire or grey tire glaze paint flawless celadon.
2. the black tire used in the making method of black tire according to claim 1 or grey tire glaze paint flawless celadon or grey tire glaze paint flawless glaze, it is characterized in that it is made by following weight: 10 parts ~ 16 parts, dragon's fountain Dayao china clay in ancient times 30 parts ~ 40 parts, dragon's fountain Dayao Zijin in ancient times soil, dragon's fountain Dayao porcelain stone 8 parts ~ 12 parts, 18 parts ~ 22 parts, Wingdale, fluorite 2 parts ~ 3 parts, feldspar 8 parts ~ 12 parts, zircon 2 parts.