CN104141064A - Metal platinum alloy for jewelries - Google Patents
Metal platinum alloy for jewelries Download PDFInfo
- Publication number
- CN104141064A CN104141064A CN201410422178.5A CN201410422178A CN104141064A CN 104141064 A CN104141064 A CN 104141064A CN 201410422178 A CN201410422178 A CN 201410422178A CN 104141064 A CN104141064 A CN 104141064A
- Authority
- CN
- China
- Prior art keywords
- accounts
- platinum
- platinum alloy
- palladium
- osmium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal platinum alloy for jewelries. The metal platinum alloy for the jewelries is prepared by combining six metal components namely platinum, palladium, rhodium, iridium, osmium and nickel, wherein the metal platinum alloy for the jewelries comprises the following components in percentage by weight: 68.5-73.9% of platinum, 16.7-18.5% of palladium, 3.8-4.6% of rhodium, 2.5-3.4% of iridium, 1.9-2.8% of osmium and 1.2-2.2% of nickel. The metal platinum alloy for the jewelries consists of six metal elements namely platinum, palladium, rhodium, iridium, osmium and nickel, and has the characteristics that the metal platinum alloy is light in weight and large in strength, is not easy to rust, is convenient to carry, and is beautiful in appearance.
Description
Technical field
The present invention relates to a kind of alloy, be specifically related to a kind of jewelry gold and belong to platinum alloy.
Background technology
Platinum alloy refers to the alloy that platinum and other metal mixed form, and is usually used in jewellery industry.Instantly the platinum alloy of producing falls behind gradually in application aspect, and along with the constant growth of productivity instantly, the various aspects of performance of palladium-base alloy cannot meet the demand of society instantly equally.
Summary of the invention
The object of the present invention is to provide that a kind of quality is light, intensity is large, be difficult for getting rusty, jewelry gold easy to carry, beautiful appearance belongs to platinum alloy.
Technical scheme of the present invention is, a kind of jewelry gold belongs to platinum alloy, described jewelry gold belongs to platinum alloy and is combined by platinum, palladium, rhodium, iridium, osmium and six kinds of metal ingredients of nickel, described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is respectively: described platinum accounts for 68.5%-73.9%, described palladium accounts for 16.7%-18.5%, and described rhodium accounts for 3.8%-4.6%, and described iridium accounts for 2.5%-3.4%, described osmium accounts for 1.9%-2.8%, and described nickel accounts for 1.2%-2.2%.
In a preferred embodiment of the present invention, described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is specially: described platinum accounts for 73.3%, and described palladium accounts for 16.8%, described rhodium accounts for 3.9%, described iridium accounts for 2.6%, and described osmium accounts for 2.1%, and described nickel accounts for 1.3%.
In a preferred embodiment of the present invention, described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is specially: described platinum accounts for 69.1%, and described palladium accounts for 18.4%, described rhodium accounts for 4.5%, described iridium accounts for 3.3%, and described osmium accounts for 2.6%, and described nickel accounts for 2.1%.
Of the present inventionly belong to platinum alloy for a kind of jewelry gold, formed by six kinds of metallic elements such as platinum, palladium, rhodium, iridium, osmium and nickel, have that quality is light, intensity large, be difficult for getting rusty, the feature of easy to carry, beautiful appearance.
Embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.
Of the present inventionly belong to platinum alloy for a kind of jewelry gold, described jewelry gold belongs to platinum alloy and is combined by platinum, palladium, rhodium, iridium, osmium and six kinds of metal ingredients of nickel, described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is respectively: described platinum accounts for 68.5%-73.9%, described palladium accounts for 16.7%-18.5%, described rhodium accounts for 3.8%-4.6%, described iridium accounts for 2.5%-3.4%, and described osmium accounts for 1.9%-2.8%, and described nickel accounts for 1.2%-2.2%.
Further, described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is specially: described platinum accounts for 73.3%, and described palladium accounts for 16.8%, and described rhodium accounts for 3.9%, and described iridium accounts for 2.6%, and described osmium accounts for 2.1%, and described nickel accounts for 1.3%.
Further, described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is specially: described platinum accounts for 69.1%, and described palladium accounts for 18.4%, and described rhodium accounts for 4.5%, and described iridium accounts for 3.3%, and described osmium accounts for 2.6%, and described nickel accounts for 2.1%.
In addition, can be by regulating the Different Weight per-cent of each composition in alloy, the alloy property height obtaining is differed.
Of the present inventionly belong to platinum alloy for a kind of jewelry gold, formed by six kinds of metallic elements such as platinum, palladium, rhodium, iridium, osmium and nickel, have that quality is light, intensity large, be difficult for getting rusty, the feature of easy to carry, beautiful appearance.
The foregoing is only the specific embodiment of the present invention; but protection scope of the present invention is not limited to this; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; the variation that can expect without creative work or replacement, within all should being encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (3)
1. a jewelry gold belongs to platinum alloy, it is characterized in that: described jewelry gold belongs to platinum alloy and combined by platinum, palladium, rhodium, iridium, osmium and six kinds of metal ingredients of nickel, described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is respectively: described platinum accounts for 68.5%-73.9%, described palladium accounts for 16.7%-18.5%, described rhodium accounts for 3.8%-4.6%, described iridium accounts for 2.5%-3.4%, and described osmium accounts for 1.9%-2.8%, and described nickel accounts for 1.2%-2.2%.
2. jewelry gold according to claim 1 belongs to platinum alloy, it is characterized in that: described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is specially: described platinum accounts for 73.3%, described palladium accounts for 16.8%, described rhodium accounts for 3.9%, described iridium accounts for 2.6%, described osmium accounts for 2.1%, and described nickel accounts for 1.3%.
3. jewelry gold according to claim 1 belongs to platinum alloy, it is characterized in that: described jewelry gold belongs to the shared weight percent of each composition in platinum alloy and is specially: described platinum accounts for 69.1%, described palladium accounts for 18.4%, described rhodium accounts for 4.5%, described iridium accounts for 3.3%, described osmium accounts for 2.6%, and described nickel accounts for 2.1%.