CN104128542B - First the be shaped processing method of flange of diameter difference list flange shaft - Google Patents
First the be shaped processing method of flange of diameter difference list flange shaft Download PDFInfo
- Publication number
- CN104128542B CN104128542B CN201410185339.3A CN201410185339A CN104128542B CN 104128542 B CN104128542 B CN 104128542B CN 201410185339 A CN201410185339 A CN 201410185339A CN 104128542 B CN104128542 B CN 104128542B
- Authority
- CN
- China
- Prior art keywords
- blank
- flange
- heating
- stove
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses be first the shaped processing method of flange of a kind of diameter difference list flange shaft, this processing method comprises the following steps: blanking; The first fire time heating: mould and die preheating and to blank the whole body pulling; Time heating of the second fire; Time heating of the 3rd fire; Time heating of the 4th fire; The 5th fire time heating: by blank heating to 1240 DEG C, be incubated 13 hours by heating furnace, after coming out of the stove, one end of blank inserted and carried out flange forming in countersunk head mould; The 6th fire time heating: the blank after flange forming is put into heating furnace and carry out local heat, wherein flange is placed in outside stove, and axle is placed in stove, and in stove, heating-up temperature is 1200 DEG C, is incubated and after 4 hours, axle body is pulled out and finishing moulding; Forge after-baking: comprise successively normalizing, tempering and modified, this local heat had both ensured that the crystal grain of flange was not thick, had solved again flange head excessive, the problem of unsuitable shove charge heating.
Description
Technical field
The present invention relates to be first the shaped processing method of flange of a kind of diameter difference list flange shaft.
Background technology
During former open die forging is produced, the poor little single flange shaft of diameter is general to be adopted when forging axle class part, while reaching after forging ratio ejection moulding, with the ejection that is as the criterion of flange end diameter, then number prints sub-material, and small end is pulled out; And the poor large single flange shaft of diameter is generally considered shaping factor, select first to pull out axle body, after enter the method for mold forming flange.
And within the scope of the production capacity at 6300T hydraulic press, be below the heavy 35T of high-effect land and sea breeze electricity main shaft blank below 3MW, by the method for countersunk head mould molding flange pulling axle body, four fire can finish substantially; Last two fire are first to pull out axle body, with maximum gauge ￠ 1500 shove charges (size of burner hearth 2350mm*3200mm*8000mm), be incubated about 2 hours, progressive die shaped flange, finishing axle body, but, for the heavy 64T of 4MW offshore wind farm main shaft blank, reach the upper limit of press and corollary equipment ability, in order to forge, crystal grain thinning, make even tissue, the operating process of whole forging all can lower efficiency, and fire time can be directly double; And cannot forge according to the method that first pulls out in the past aftershaping flange, because deformation process axle body is long, exceed the stroke 4700mm of press. So, can only pull out again axle body by first shaped flange, and in type flange shape does not in the end allow there is large deformation in a fire again, again because still need soak at least 4 hours before last fire, if and flange is after high-temperature heating crystal grain can be grown up, will cause occurring coarse grains less than suitable distortion again, organize bad, performance inconsistency lattice etc. directly to affect the problem of product quality; And the compact dimensions of flange will be more than or equal to furnace height 2350mm.
Summary of the invention
The object of the invention is to overcome the defect existing in prior art, provide one can not only preventive treatment blue grain growth, and be first the shaped processing method of flange of the diameter difference list flange shaft that can solve the excessive problem that can not put into heating furnace of flange outer diameter.
For achieving the above object, technical scheme of the present invention has been to provide be first the shaped processing method of flange of a kind of diameter difference list flange shaft, and this processing method comprises the following steps:
S1: blanking: blank is carried out to pretreatment;
S2: the first fire time heating: mould and die preheating and to blank the whole body pulling;
S3: the second fire time heating: by blank heating to 1230 DEG C, be incubated 19 hours by heating furnace, after coming out of the stove, blank carried out pressing tongs handle, excises unnecessary rising head;
S4: the 3rd fire time heating: by blank heating to 1240 DEG C, be incubated 21 hours by heating furnace, after coming out of the stove to blank carry out large forging ratio pier thick, pull out;
S5: the 4th fire time heating: by blank heating to 1250 DEG C, be incubated 15 hours by heating furnace, after coming out of the stove, blank is carried out that large forging ratio pier is thick, pulling, number seal, pulls out bound feet;
S6: the 5th fire time heating: by blank heating to 1240 DEG C, be incubated 13 hours by heating furnace, after coming out of the stove, one end of blank inserted to countersunk head die for molding flange, alignment;
S7: the 6th fire time heating: by after flange forming blank put into heating furnace and carry out local heat, wherein flange is placed in outside stove, axle is placed in stove, in stove, heating-up temperature is 1200 DEG C, is incubated and after 4 hours, axle body is pulled out and finishing moulding;
S8: forge after-baking: comprise successively normalizing, tempering and modified.
As preferably, in step S1, blank is carried out to pretreatment and comprise and blank is carried out to chop at the mouth of a river, rising head trimming, then blank is inserted in heating furnace and be heated to 1230 DEG C, be incubated after 13 hours and start to forge.
As preferably, 890 DEG C ± 10 DEG C insulations of normalizing 26 hours in step S8,660 DEG C ± 10 DEG C insulations of tempering 50 hours.
Advantage of the present invention and beneficial effect are: this local heat had both ensured that the crystal grain of flange was not thick, had solved again flange head excessive, the problem of unsuitable shove charge heating.
Detailed description of the invention
Below in conjunction with drawings and Examples, the specific embodiment of the present invention is further described. Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
First the be shaped processing method of flange of diameter difference list flange shaft, this processing method comprises the following steps:
S1: blanking: blank is carried out to pretreatment;
S2: the first fire time heating: mould and die preheating and to blank the whole body pulling;
S3: the second fire time heating: by blank heating to 1230 DEG C, be incubated 19 hours by heating furnace, after coming out of the stove, blank carried out pressing tongs handle, excises unnecessary rising head;
S4: the 3rd fire time heating: by blank heating to 1240 DEG C, be incubated 21 hours by heating furnace, after coming out of the stove to blank carry out large forging ratio pier thick, pull out;
S5: the 4th fire time heating: by blank heating to 1250 DEG C, be incubated 15 hours by heating furnace, after coming out of the stove, blank is carried out that large forging ratio pier is thick, pulling, number seal, pulls out bound feet;
S6: the 5th fire time heating: by blank heating to 1240 DEG C, be incubated 13 hours by heating furnace, after coming out of the stove, one end of blank inserted to countersunk head die for molding flange, alignment;
S7: the 6th fire time heating: by after flange forming blank put into heating furnace and carry out local heat, wherein flange is placed in outside stove, axle is placed in stove, in stove, heating-up temperature is 1200 DEG C, is incubated and after 4 hours, axle body is pulled out and finishing moulding;
S8: forge after-baking: comprise successively normalizing, tempering and modified.
In step S1, blank is carried out to pretreatment and comprise and blank is carried out to chop at the mouth of a river, rising head trimming, then blank is inserted in heating furnace and be heated to 1230 DEG C, be incubated after 13 hours and start to forge.
890 DEG C ± 10 DEG C insulations of normalizing 26 hours in step S8,660 DEG C ± 10 DEG C insulations of tempering 50 hours.
This local heat focuses on flange outside stove, axle body is in stove, fire door is that type semienclosed heating furnace fan main shaft carries out local heat, when fan main shaft normal heating, when temperature is 1200 DEG C of technological temperatures in stove, flange temperature only reaches 600-700 DEG C, do not reach the lowest temperature of this steel grade grain growth, can not only the preventive treatment blue grain growth of the method, and can solve the excessive problem that can not put into heating furnace of flange outer diameter, in addition be conducive to the limited press of stroke and realized the forging to 4MW blower fan main shaft, and innovate diameter difference list flange shaft Forging Technology.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (3)
1. the diameter difference list flange shaft processing method for flange that is first shaped, is characterized in that: this processing method comprises the following steps:
S1: blanking: blank is carried out to pretreatment;
S2: the first fire time heating: mould and die preheating and to blank the whole body pulling;
S3: the second fire time heating: by blank heating to 1230 DEG C, be incubated 19 hours by heating furnace, after coming out of the stove, blank carried out pressing tongs handle, excises unnecessary rising head;
S4: the 3rd fire time heating: by blank heating to 1240 DEG C, be incubated 21 hours by heating furnace, after coming out of the stove to blank carry out large forging ratio pier thick, pull out;
S5: the 4th fire time heating: by blank heating to 1250 DEG C, be incubated 15 hours by heating furnace, after coming out of the stove, blank is carried out that large forging ratio pier is thick, pulling, number seal, pulls out bound feet;
S6: the 5th fire time heating: by blank heating to 1240 DEG C, be incubated 13 hours by heating furnace, after coming out of the stove, one end of blank inserted to countersunk head die for molding flange, alignment;
S7: the 6th fire time heating: by after flange forming blank put into heating furnace and carry out local heat, wherein flange is placed in outside stove, axle is placed in stove, in stove, heating-up temperature is 1200 DEG C, is incubated and after 4 hours, axle body is pulled out and finishing moulding;
S8: forge after-baking: comprise successively normalizing, tempering and modified.
2. the diameter difference list flange shaft as claimed in claim 1 processing method of flange that is first shaped, it is characterized in that: in step S1, blank is carried out to pretreatment and comprise and blank is carried out to chop at the mouth of a river, rising head trimming, then blank is inserted in heating furnace and be heated to 1230 DEG C, be incubated after 13 hours and start to forge.
3. the diameter difference list flange shaft as claimed in claim 1 processing method of flange that is first shaped, is characterized in that: 890 DEG C ± 10 DEG C insulations of normalizing 26 hours in step S8,660 DEG C ± 10 DEG C insulations of tempering 50 hours.