CN104119717A - Nanometer-based waterproof coating - Google Patents
Nanometer-based waterproof coating Download PDFInfo
- Publication number
- CN104119717A CN104119717A CN201410293839.9A CN201410293839A CN104119717A CN 104119717 A CN104119717 A CN 104119717A CN 201410293839 A CN201410293839 A CN 201410293839A CN 104119717 A CN104119717 A CN 104119717A
- Authority
- CN
- China
- Prior art keywords
- parts
- nanometer
- minute
- nano
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a nanometer-based waterproof coating which comprises the following raw materials in parts by weight: 63-70 parts of silicone acrylic emulsions, 1.3-2 parts of pyrrolidone hydroxy acid sodium, 0.1-0.2 part of aminoethyl piperazine, 0.1-0.2 part of monoalkyl ether phosphate, 0.6-1 part of sea buckthron oil, 0.5-1 part of ammonium tungstate, 0.2-0.5 part of coco fatty acid diethanol amide, 2-3 parts of magnesium silicate, 0.6-1 part of 2-vinylpyridine, 5-7 part of nanometer calcium phosphate, 2-3 parts of polyether glycol, 5-8 parts of nanometer diatomite, 5-8 parts of film-forming auxiliary agents and 10-17 parts of deionized water. Since nanometer diatomite and nanometer calcium phosphate are added to the nanometer-based waterproof coating disclosed by the invention, the cracking resistant property and abrasion resistant property of a coated film can be enhanced effectively; and the nanometer-based waterproof coating has the advantages of reasonable raw material compounding, good environmental friendliness, excellent frost resistance and low-temperature flexibility, good constructability, no blistering, good film-forming effect and high water resistance.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of nano based waterproof paint.
Background technology
Traditional water-proof material mainly contains the flexible waterproof materials such as waterproof roll, waterproof paint, sealing cement, and taking cement matrix as main, adds the rigidity water-proofing material of liquid medicine agent and other auxiliary agent.The most of waterproofing work of China all adopts conventional waterproof material, conventional waterproof material exist loss of properties on aging, tensile strength low, to shortcomings such as temperature sensitives.Conventional waterproof coating is used for roof waterproof, easily cause aging, dry and cracked, be out of shape, fracture, the phenomenon such as layering, for indoor waterproof, for complex-shaped place, constructional difficulties, and to Seepage, quality is more difficult to ensure, people will spend a large amount of funds every several years and labor force reprocesses, and have not only confused people's orthobiosis, work and the production order, and affect the work-ing life of whole building nano based thing.In order to meet the requirement of every profession and trade to waterproof paint, production high-performance, widely used waterproof paint is necessary.
Summary of the invention
The object of the invention is just to provide a kind of nano based waterproof paint.
The present invention is achieved by the following technical solutions:
A kind of nano based waterproof paint, it is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 63-70, pyrrolidone hydroxy acid sodium 1.3-2, aminoethyl piperazine 0.1-0.2, monoalky lether phosphoesterase 30 .1-0.2, Oleum Hippophae 0.6-1, ammonium tungstate 0.5-1, lauric acid amide of ethanol 0.2-0.5, Magnesium Silicate q-agent 2-3,2-vinyl pyridine 0.6-1, nano-calcium phosphate 5-7, polyether Glycols 2-3, nano diatomite 5-8, film coalescence aid 5-8, deionized water 10-17;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 30-35, extract solution from aloe 0.3-2, ethyl p-hydroxybenzoate 1-2, Sodium Silicofluoride 0.8-1, tetramethylolmethane 2-3, dibutyl tin laurate 0.1-0.2, micropowder silica gel 2-4, trimethyl benzyl ammonia chloride 0.8-2, deionized water 70-75;
Micropowder silica gel is mixed with tetramethylolmethane, at 65-70 DEG C, be uniformly mixed 2-4 minute, add 30-40%, the trimethyl benzyl ammonia chloride of above-mentioned deionized water weight, 100-200 rev/min of dispersed with stirring 6-12 minute, obtains dispersion liquid;
Ethyl p-hydroxybenzoate is mixed with extract solution from aloe, after stirring, join in organosilicon crylic acid latex, insulated and stirred 10-15 minute at 35-40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, be stirred to normal temperature, add the each raw material of residue, 300-400 rev/min of dispersed with stirring 7-10 minute, obtains described film coalescence aid.
A preparation method for nano based waterproof paint, comprises the following steps:
Nano-calcium phosphate, Magnesium Silicate q-agent, nano diatomite are mixed, join in deionized water, after stirring, add lauric acid amide of ethanol, ammonium tungstate, at 70-76 DEG C, be uniformly mixed 4-5 minute;
Pyrrolidone hydroxy acid sodium is mixed with Oleum Hippophae, join in organosilicon crylic acid latex, 100-120 rev/min is uniformly mixed 3-5 minute, adds monoalky lether phosphoric acid ester, stirs;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described nano based waterproof paint.
Advantage of the present invention is:
Nano diatomite, nano-calcium phosphate that waterproof paint of the present invention adds, can effectively improve cracking resistance, the abrasion resistance of film, and each raw material is composite rationally, the feature of environmental protection is good, also has good frost resistance and low temperature flexibility, and application property is good, non-foaming, film-formation result good, water-repellancy is strong.
Embodiment
Embodiment 1
A kind of nano based waterproof paint, it by following weight parts (kilogram) raw material form:
Organosilicon crylic acid latex 70, pyrrolidone hydroxy acid sodium 1.3, aminoethyl piperazine 0.2, monoalky lether phosphoesterase 30 .2, Oleum Hippophae 0.6, ammonium tungstate 0.5, lauric acid amide of ethanol 0.5, Magnesium Silicate q-agent 3,2-vinyl pyridine 0.6, nano-calcium phosphate 5, polyether Glycols 2-3, nano diatomite 5, film coalescence aid 8, deionized water 17;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 35, extract solution from aloe 0.3, ethyl p-hydroxybenzoate 2, Sodium Silicofluoride 0.8, tetramethylolmethane 2, dibutyl tin laurate 0.1, micropowder silica gel 2, trimethyl benzyl ammonia chloride 0.8-2, deionized water 75;
Micropowder silica gel is mixed with tetramethylolmethane, at 70 DEG C, is uniformly mixed 4 minutes, add above-mentioned deionized water weight 40%, trimethyl benzyl ammonia chloride, 100 revs/min of dispersed with stirring 12 minutes, obtain dispersion liquid;
Ethyl p-hydroxybenzoate is mixed with extract solution from aloe, after stirring, join in organosilicon crylic acid latex, insulated and stirred 15 minutes at 40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, be stirred to normal temperature, add the each raw material of residue, 400 revs/min of dispersed with stirring 10 minutes, obtain described film coalescence aid.
A preparation method for nano based waterproof paint, comprises the following steps:
Nano-calcium phosphate, Magnesium Silicate q-agent, nano diatomite are mixed, join in deionized water, after stirring, add lauric acid amide of ethanol, ammonium tungstate, at 76 DEG C, be uniformly mixed 4 minutes;
Pyrrolidone hydroxy acid sodium is mixed with Oleum Hippophae, join in organosilicon crylic acid latex, 120 revs/min are uniformly mixed 3 minutes, add monoalky lether phosphoric acid ester, stir;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 600 revs/min of dispersed with stirring 30 minutes, obtain described nano based waterproof paint.
Performance test:
Unit elongation: >=300%;
Watertightness: 0.3MPa (one hour waterproof).
Claims (2)
1. a nano based waterproof paint, is characterized in that what it was made up of the raw material of following weight parts:
Organosilicon crylic acid latex 63-70, pyrrolidone hydroxy acid sodium 1.3-2, aminoethyl piperazine 0.1-0.2, monoalky lether phosphoesterase 30 .1-0.2, Oleum Hippophae 0.6-1, ammonium tungstate 0.5-1, lauric acid amide of ethanol 0.2-0.5, Magnesium Silicate q-agent 2-3,2-vinyl pyridine 0.6-1, nano-calcium phosphate 5-7, polyether Glycols 2-3, nano diatomite 5-8, film coalescence aid 5-8, deionized water 10-17;
Described film coalescence aid is made up of the raw material of following weight parts:
Organosilicon crylic acid latex 30-35, extract solution from aloe 0.3-2, ethyl p-hydroxybenzoate 1-2, Sodium Silicofluoride 0.8-1, tetramethylolmethane 2-3, dibutyl tin laurate 0.1-0.2, micropowder silica gel 2-4, trimethyl benzyl ammonia chloride 0.8-2, deionized water 70-75;
Micropowder silica gel is mixed with tetramethylolmethane, at 65-70 DEG C, be uniformly mixed 2-4 minute, add 30-40%, the trimethyl benzyl ammonia chloride of above-mentioned deionized water weight, 100-200 rev/min of dispersed with stirring 6-12 minute, obtains dispersion liquid;
Ethyl p-hydroxybenzoate is mixed with extract solution from aloe, after stirring, join in organosilicon crylic acid latex, insulated and stirred 10-15 minute at 35-40 DEG C, add above-mentioned dispersion liquid, dibutyl tin laurate, be stirred to normal temperature, add the each raw material of residue, 300-400 rev/min of dispersed with stirring 7-10 minute, obtains described film coalescence aid.
2. a preparation method for nano based waterproof paint as claimed in claim 1, is characterized in that comprising the following steps:
Nano-calcium phosphate, Magnesium Silicate q-agent, nano diatomite are mixed, join in deionized water, after stirring, add lauric acid amide of ethanol, ammonium tungstate, at 70-76 DEG C, be uniformly mixed 4-5 minute;
Pyrrolidone hydroxy acid sodium is mixed with Oleum Hippophae, join in organosilicon crylic acid latex, 100-120 rev/min is uniformly mixed 3-5 minute, adds monoalky lether phosphoric acid ester, stirs;
Above-mentioned each raw material after treatment is mixed with the each raw material of residue, and 500-600 rev/min of dispersed with stirring 20-30 minute, obtains described nano based waterproof paint.