CN104118026A - Environment-friendly inorganic inflaming retarding wheat straw particle board and producing method thereof - Google Patents
Environment-friendly inorganic inflaming retarding wheat straw particle board and producing method thereof Download PDFInfo
- Publication number
- CN104118026A CN104118026A CN201410351981.4A CN201410351981A CN104118026A CN 104118026 A CN104118026 A CN 104118026A CN 201410351981 A CN201410351981 A CN 201410351981A CN 104118026 A CN104118026 A CN 104118026A
- Authority
- CN
- China
- Prior art keywords
- wheat straw
- straw particle
- central layer
- inorganic
- locked mode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Provided are an environment-friendly inorganic inflaming retarding wheat straw particle board and a producing method thereof. The environment-friendly inorganic inflaming retarding wheat straw particle board comprises a wheat straw particle core board, melamine impregnated paper is attached to the inner surface and the outer surface of the wheat straw particle core board through inorganic inflaming retarding adhesive material layers, the wheat straw particle core board is a plate-shaped material made of wheat straw particles and inorganic inflaming retarding adhesives. According to the environment-friendly inorganic inflaming retarding wheat straw particle board and the producing method thereof, the melamine impregnated paper is attached to the surfaces of the wheat straw particle board, the problems that the wheat straw particle board is prone to absorbing water and damp, being worn and the like are solved, the board is made to has good glossiness, high mechanical strength and waterproof and moisture resistance; wheat straw is fully utilized for production and application, the additional value of the straw of crops is increased, harm caused to human beings by incineration of the straw of the crops is reduced, environmental protection is achieved, and production cost is low; the producing method is easy, and mechanized production can be achieved.
Description
Technical field
The present invention relates to a kind of wood-based plate and production method thereof, particularly the fire-retardant wheat straw flakeboard of a kind of environmental protection inorganic and production method thereof.
Background technology
Utilize the wheat straw flakeboard of wheat straw particle and inorganic fire-retarded adhesive laminating production can significantly promote resource utilization and the added value of Wheat Straw, reduced to a certain extent deforestation logging, yet, wheat straw flakeboard, because there being the defects such as rough surface, yielding, the easy moisture absorption, usually needs it to carry out Overlaying process in actual application.
Summary of the invention
Technical problem to be solved by this invention is for the deficiencies in the prior art, provides a kind of reasonable in design, has the fire-retardant wheat straw flakeboard of environmental protection inorganic of good gloss degree and mechanical strength.
Another technical problem to be solved by this invention is for the deficiencies in the prior art, provides a kind of reasonable in design, the production method of the fire-retardant wheat straw flakeboard of the simple environmental protection inorganic of technique.
Technical problem to be solved by this invention is to realize by following technical scheme, the present invention is the fire-retardant wheat straw flakeboard of a kind of environmental protection inorganic, be characterized in, comprise wheat straw particle central layer, surfaces externally and internally at wheat straw particle central layer is all pasted with melamine impregnated paper by inorganic fire-retarded adhesive material layer, the board-like material of described wheat straw particle central layer for being made by wheat straw particle and inorganic fire-retarded adhesive.
Technical problem to be solved by this invention can also further realize by following technical scheme, in the fire-retardant wheat straw flakeboard of above-described environmental protection inorganic: the thickness of described wheat straw particle central layer is 6-30mm.
Technical problem to be solved by this invention can also further realize by following technical scheme, in the fire-retardant wheat straw flakeboard of above-described environmental protection inorganic: the thickness of described melamine impregnated paper is 0.2-0.5mm.
Another technical problem to be solved by this invention is to realize by following technical scheme, and the present invention is the production method of the fire-retardant wheat straw flakeboard of a kind of environmental protection inorganic as above, is characterized in, its step is as follows,
(1) preparation of wheat straw particle: utilize chaffcutter that wheat straw is cut into after the wheat straw section that length is 180-220mm, deliver to the wheat straw particle of pulverizing growth 1-3mm, wide 1-2mm in hog, to be then dried to moisture content be 10-12% to drying machine;
(2) applying glue and stirring: dried wheat straw particle is delivered to mixer, in mixer, wheat straw particle and inorganic fire-retarded adhesive is carried out to glue spraying stirring by weight 3:6-3:8, until mix, make wheat straw particle mixture;
(3) machinery is mated formation: wheat straw particle mixture is transported to mechanical spreading machine through conveyer belt, and spreading machine is mated formation wheat straw particle mixture on billet uniformly, forms slab;
(4) precompressed: slab is transported to preformer through conveyer belt and carries out pre-molding, preload pressure is 1.3-1.8MPa, and squeeze time is 30-60s;
(5) locked mode of colding pressing: the slab of multiple pre-moldings is placed in locked mode folder together with billet stacking, and sends into the cold press locked mode of colding pressing, locked mode pressure reaches 2.8-3.2MPa;
(6) sheet material maintenance: first locked mode is pressed from both sides to stacking and deliver to curing room and carry out blanks and moulding and conserving, solidification temperature is 35-60 ℃, and locked mode maintenance is after 1-2 days, locked mode is pinched to cold press release, make sheet material semi-finished product, under normal temperature, in stacking natural curing 1-3 week, make wheat straw particle central layer;
(7) wheat straw particle central layer is dry: the wheat straw particle central layer after maintenance is delivered to drying machine and be dried, baking temperature is 125-135 ℃, and being dried to moisture content is 10-12%;
(8) edging of wheat straw particle central layer and sanding: dried wheat straw particle central layer is first delivered in length and breadth to edging saw and carry out in length and breadth to pre-clipping edge, and then deliver to sander and carry out two-sided fixed thick sanding;
(9) finished product preparation: utilize the surfaces externally and internally of the wheat straw particle central layer of melamine impregnated paper after edging sanding to carry out veneer, make inorganic fire-retarded wheat straw flakeboard, inorganic fire-retarded wheat straw flakeboard being delivered in length and breadth to edging saw carries out in length and breadth, to clipping edge, making finished product sheet material again.
Compared with prior art, the present invention has melamine impregnated paper by veneer, improves wheat straw flakeboard easily the absorb water moisture absorption, the characteristic such as easy to wear, makes sheet material have good glossiness, mechanical strength and water-fast moisture resistance; Make full use of Wheat Straw and produce and apply, increase the added value of agricultural crop straw, the harm that the burning of minimizing agricultural crop straw brings to the mankind, environmental protection, production cost is low; Production method is simple, can realize mechanization production.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
The specific embodiment
Referring to accompanying drawing, further describe concrete technical scheme of the present invention, so that those skilled in the art understands the present invention further, and do not form the restriction to its right.
Embodiment 1, with reference to Fig. 1, the fire-retardant wheat straw flakeboard of a kind of environmental protection inorganic, comprise wheat straw particle central layer 2, surfaces externally and internally at wheat straw particle central layer 2 is all pasted with melamine impregnated paper 1 by inorganic fire-retarded adhesive material layer, the board-like material of described wheat straw particle central layer 2 for being made by wheat straw particle and inorganic fire-retarded adhesive.
Embodiment 2, described in embodiment 1 the fire-retardant wheat straw flakeboard of environmental protection inorganic in: the thickness of described wheat straw particle central layer 2 is 6mm, and the thickness of described melamine impregnated paper 1 is 0.2mm.
Embodiment 3, described in embodiment 1 the fire-retardant wheat straw flakeboard of environmental protection inorganic in: the thickness of described wheat straw particle central layer 2 is 30mm, and the thickness of described melamine impregnated paper 1 is 0.5mm.
Embodiment 4, described in embodiment 1 the fire-retardant wheat straw flakeboard of environmental protection inorganic in: the thickness of described wheat straw particle central layer 2 is 20mm, and the thickness of described melamine impregnated paper 1 is 0.4mm.
Embodiment 5, and the production method of the environmental protection inorganic fire-retardant wheat straw flakeboard of a kind of embodiment 1-4 described in any one is characterized in, its step is as follows,
(1) preparation of wheat straw particle: utilize chaffcutter that wheat straw is cut into after the wheat straw section that length is 180mm, deliver to the wheat straw particle of pulverizing growth 1mm, wide 1mm in hog, to be then dried to moisture content be 10% to drying machine;
(2) applying glue and stirring: dried wheat straw particle is delivered to mixer, in mixer, wheat straw particle and inorganic fire-retarded adhesive is carried out to glue spraying stirring by weight 3:6, until mix, make wheat straw particle mixture;
(3) machinery is mated formation: wheat straw particle mixture is transported to mechanical spreading machine through conveyer belt, and spreading machine is mated formation wheat straw particle mixture on billet uniformly, forms slab;
(4) precompressed: slab is transported to preformer through conveyer belt and carries out pre-molding, preload pressure is 1.3MPa, and squeeze time is 30s;
(5) locked mode of colding pressing: the slab of multiple pre-moldings is placed in locked mode folder together with billet stacking, and sends into the cold press locked mode of colding pressing, locked mode pressure reaches 2.8MPa;
(6) sheet material maintenance: first locked mode is pressed from both sides to stacking and deliver to curing room and carry out blanks and moulding and conserving, solidification temperature is 35 ℃, and locked mode maintenance is after 1 day, locked mode is pinched to cold press release, make sheet material semi-finished product, under normal temperature, stacking natural curing is 1 week, makes wheat straw particle central layer;
(7) wheat straw particle central layer is dry: the wheat straw particle central layer after maintenance is delivered to drying machine and be dried, baking temperature is 125 ℃, and being dried to moisture content is 10%;
(8) edging of wheat straw particle central layer and sanding: dried wheat straw particle central layer is first delivered in length and breadth to edging saw and carry out in length and breadth to pre-clipping edge, and then deliver to sander and carry out two-sided fixed thick sanding;
(9) finished product preparation: utilize the surfaces externally and internally of the wheat straw particle central layer of melamine impregnated paper after edging sanding to carry out veneer, make inorganic fire-retarded wheat straw flakeboard, inorganic fire-retarded wheat straw flakeboard being delivered in length and breadth to edging saw carries out in length and breadth, to clipping edge, making finished product sheet material again.
Embodiment 6, and the production method of the environmental protection inorganic fire-retardant wheat straw flakeboard of a kind of embodiment 1-4 described in any one is characterized in, its step is as follows,
(1) preparation of wheat straw particle: utilize chaffcutter that wheat straw is cut into after the wheat straw section that length is 220mm, deliver to the wheat straw particle of pulverizing growth 3mm, wide 2mm in hog, to be then dried to moisture content be 12% to drying machine;
(2) applying glue and stirring: dried wheat straw particle is delivered to mixer, in mixer, wheat straw particle and inorganic fire-retarded adhesive is carried out to glue spraying stirring by weight 3:8, until mix, make wheat straw particle mixture;
(3) machinery is mated formation: wheat straw particle mixture is transported to mechanical spreading machine through conveyer belt, and spreading machine is mated formation wheat straw particle mixture on billet uniformly, forms slab;
(4) precompressed: slab is transported to preformer through conveyer belt and carries out pre-molding, preload pressure is 1.8MPa, and squeeze time is 60s;
(5) locked mode of colding pressing: the slab of multiple pre-moldings is placed in locked mode folder together with billet stacking, and sends into the cold press locked mode of colding pressing, locked mode pressure reaches 3.2MPa;
(6) sheet material maintenance: first locked mode is pressed from both sides to stacking and deliver to curing room and carry out blanks and moulding and conserving, solidification temperature is 60 ℃, and locked mode maintenance is after 2 days, locked mode is pinched to cold press release, make sheet material semi-finished product, under normal temperature, stacking natural curing is 3 weeks, makes wheat straw particle central layer;
(7) wheat straw particle central layer is dry: the wheat straw particle central layer after maintenance is delivered to drying machine and be dried, baking temperature is 135 ℃, and being dried to moisture content is 12%;
(8) edging of wheat straw particle central layer and sanding: dried wheat straw particle central layer is first delivered in length and breadth to edging saw and carry out in length and breadth to pre-clipping edge, and then deliver to sander and carry out two-sided fixed thick sanding;
(9) finished product preparation: utilize the surfaces externally and internally of the wheat straw particle central layer of melamine impregnated paper after edging sanding to carry out veneer, make inorganic fire-retarded wheat straw flakeboard, inorganic fire-retarded wheat straw flakeboard being delivered in length and breadth to edging saw carries out in length and breadth, to clipping edge, making finished product sheet material again.
Embodiment 7, and the production method of the environmental protection inorganic fire-retardant wheat straw flakeboard of a kind of embodiment 1-4 described in any one is characterized in, its step is as follows,
(1) preparation of wheat straw particle: utilize chaffcutter that wheat straw is cut into after the wheat straw section that length is 200mm, deliver to the wheat straw particle of pulverizing growth 1.5mm, wide 1.5mm in hog, to be then dried to moisture content be 11% to drying machine;
(2) applying glue and stirring: dried wheat straw particle is delivered to mixer, in mixer, wheat straw particle and inorganic fire-retarded adhesive is carried out to glue spraying stirring by weight 3:7, until mix, make wheat straw particle mixture;
(3) machinery is mated formation: wheat straw particle mixture is transported to mechanical spreading machine through conveyer belt, and spreading machine is mated formation wheat straw particle mixture on billet uniformly, forms slab;
(4) precompressed: slab is transported to preformer through conveyer belt and carries out pre-molding, preload pressure is 1.5MPa, and squeeze time is 50s;
(5) locked mode of colding pressing: the slab of multiple pre-moldings is placed in locked mode folder together with billet stacking, and sends into the cold press locked mode of colding pressing, locked mode pressure reaches 3.0MPa;
(6) sheet material maintenance: first locked mode is pressed from both sides to stacking and deliver to curing room and carry out blanks and moulding and conserving, solidification temperature is 45 ℃, and locked mode maintenance is after 1.5 days, locked mode is pinched to cold press release, make sheet material semi-finished product, under normal temperature, stacking natural curing is 2 weeks, makes wheat straw particle central layer;
(7) wheat straw particle central layer is dry: the wheat straw particle central layer after maintenance is delivered to drying machine and be dried, baking temperature is 130 ℃, and being dried to moisture content is 11%;
(8) edging of wheat straw particle central layer and sanding: dried wheat straw particle central layer is first delivered in length and breadth to edging saw and carry out in length and breadth to pre-clipping edge, and then deliver to sander and carry out two-sided fixed thick sanding;
(9) finished product preparation: utilize the surfaces externally and internally of the wheat straw particle central layer of melamine impregnated paper after edging sanding to carry out veneer, make inorganic fire-retarded wheat straw flakeboard, inorganic fire-retarded wheat straw flakeboard being delivered in length and breadth to edging saw carries out in length and breadth, to clipping edge, making finished product sheet material again.
Embodiment 8, and the production method of the environmental protection inorganic fire-retardant wheat straw flakeboard of a kind of embodiment 1-4 described in any one is characterized in, its step is as follows,
(1) preparation of wheat straw particle: utilize chaffcutter that wheat straw is cut into after the wheat straw section that length is 190mm, deliver to the wheat straw particle of pulverizing growth 1.5mm, wide 1.2mm in hog, to be then dried to moisture content be 10% to drying machine;
(2) applying glue and stirring: dried wheat straw particle is delivered to mixer, in mixer, wheat straw particle and inorganic fire-retarded adhesive is carried out to glue spraying stirring by weight 3:8, until mix, make wheat straw particle mixture;
(3) machinery is mated formation: wheat straw particle mixture is transported to mechanical spreading machine through conveyer belt, and spreading machine is mated formation wheat straw particle mixture on billet uniformly, forms slab;
(4) precompressed: slab is transported to preformer through conveyer belt and carries out pre-molding, preload pressure is 1.7MPa, and squeeze time is 55s;
(5) locked mode of colding pressing: the slab of multiple pre-moldings is placed in locked mode folder together with billet stacking, and sends into the cold press locked mode of colding pressing, locked mode pressure reaches 2.9MPa;
(6) sheet material maintenance: first locked mode is pressed from both sides to stacking and deliver to curing room and carry out blanks and moulding and conserving, solidification temperature is 45 ℃, and locked mode maintenance is after 1 day, locked mode is pinched to cold press release, make sheet material semi-finished product, under normal temperature, stacking natural curing is 2 weeks, makes wheat straw particle central layer;
(7) wheat straw particle central layer is dry: the wheat straw particle central layer after maintenance is delivered to drying machine and be dried, baking temperature is 128 ℃, and being dried to moisture content is 11%;
(8) edging of wheat straw particle central layer and sanding: dried wheat straw particle central layer is first delivered in length and breadth to edging saw and carry out in length and breadth to pre-clipping edge, and then deliver to sander and carry out two-sided fixed thick sanding;
(9) finished product preparation: utilize the surfaces externally and internally of the wheat straw particle central layer of melamine impregnated paper after edging sanding to carry out veneer, make inorganic fire-retarded wheat straw flakeboard, inorganic fire-retarded wheat straw flakeboard being delivered in length and breadth to edging saw carries out in length and breadth, to clipping edge, making finished product sheet material again.
Described melamine impregnated paper is commercially available prod; Described inorganic fire-retarded adhesive can be any adhesive material that contains inorganic combustion inhibitor disclosed or commercially available in prior art; Central layer thickness is 2 times of plate thickness, can guarantee that this sheet material has good mechanical strength.
Claims (4)
1. the fire-retardant wheat straw flakeboard of environmental protection inorganic, it is characterized in that: comprise wheat straw particle central layer, surfaces externally and internally at wheat straw particle central layer is all pasted with melamine impregnated paper by inorganic fire-retarded adhesive material layer, the board-like material of described wheat straw particle central layer for being made by wheat straw particle and inorganic fire-retarded adhesive.
2. the fire-retardant wheat straw flakeboard of environmental protection inorganic according to claim 1, is characterized in that: the thickness of described wheat straw particle central layer is 6-30mm.
3. the fire-retardant wheat straw flakeboard of environmental protection inorganic according to claim 1, is characterized in that: the thickness of described melamine impregnated paper is 0.2-0.5mm.
4. a production method for the environmental protection inorganic fire-retardant wheat straw flakeboard of claim 1-3 described in any one, is characterized in that: its step is as follows,
(1) preparation of wheat straw particle: utilize chaffcutter that wheat straw is cut into after the wheat straw section that length is 180-220mm, deliver to the wheat straw particle of pulverizing growth 1-3mm, wide 1-2mm in hog, to be then dried to moisture content be 10-12% to drying machine;
(2) applying glue and stirring: dried wheat straw particle is delivered to mixer, in mixer, wheat straw particle and inorganic fire-retarded adhesive is carried out to glue spraying stirring by weight 3:6-3:8, until mix, make wheat straw particle mixture;
(3) machinery is mated formation: wheat straw particle mixture is transported to mechanical spreading machine through conveyer belt, and spreading machine is mated formation wheat straw particle mixture on billet uniformly, forms slab;
(4) precompressed: slab is transported to preformer through conveyer belt and carries out pre-molding, preload pressure is 1.3-1.8MPa, and squeeze time is 30-60s;
(5) locked mode of colding pressing: the slab of multiple pre-moldings is placed in locked mode folder together with billet stacking, and sends into the cold press locked mode of colding pressing, locked mode pressure reaches 2.8-3.2MPa;
(6) sheet material maintenance: first locked mode is pressed from both sides to stacking and deliver to curing room and carry out blanks and moulding and conserving, solidification temperature is 35-60 ℃, and locked mode maintenance is after 1-2 days, locked mode is pinched to cold press release, make sheet material semi-finished product, under normal temperature, in stacking natural curing 1-3 week, make wheat straw particle central layer;
(7) wheat straw particle central layer is dry: the wheat straw particle central layer after maintenance is delivered to drying machine and be dried, baking temperature is 125-135 ℃, and being dried to moisture content is 10-12%;
(8) edging of wheat straw particle central layer and sanding: dried wheat straw particle central layer is first delivered in length and breadth to edging saw and carry out in length and breadth to pre-clipping edge, and then deliver to sander and carry out two-sided fixed thick sanding;
(9) finished product preparation: utilize the surfaces externally and internally of the wheat straw particle central layer of melamine impregnated paper after edging sanding to carry out veneer, make inorganic fire-retarded wheat straw flakeboard, inorganic fire-retarded wheat straw flakeboard being delivered in length and breadth to edging saw carries out in length and breadth, to clipping edge, making finished product sheet material again.