CN104109893B - 刹车盘表面硬化处理工艺技术 - Google Patents

刹车盘表面硬化处理工艺技术 Download PDF

Info

Publication number
CN104109893B
CN104109893B CN201310159868.1A CN201310159868A CN104109893B CN 104109893 B CN104109893 B CN 104109893B CN 201310159868 A CN201310159868 A CN 201310159868A CN 104109893 B CN104109893 B CN 104109893B
Authority
CN
China
Prior art keywords
brake disc
workpiece
electrolyte
treatment
oxidation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310159868.1A
Other languages
English (en)
Other versions
CN104109893A (zh
Inventor
孙德杰
张�杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310159868.1A priority Critical patent/CN104109893B/zh
Publication of CN104109893A publication Critical patent/CN104109893A/zh
Application granted granted Critical
Publication of CN104109893B publication Critical patent/CN104109893B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种刹车盘表面硬化处理工艺技术，处理工艺如下：使用铝合金铸棒锻造材料，锻造出刹车盘的毛坯工件，然后根据车辆需要的尺寸规格进行切削加工，再通过磨面抛光、清洗程序制出刹车盘工件；将Na2SiO31.2％、NaOH0.1％、Na2P4O70.4％、Na2EDTA0.2％、NaF0.075％、C6H5O7Na3·2H2O0.1％、H3BO30.2％、H2O97.725％按重量比混合均匀，制成电解液；将电解液置于处理槽内，加入水进行混合，水与电解液的混合重量比为1∶1，制成氧化处理液，然后将刹车盘工件置入专用工装卡环内，再将刹车盘工件浸入处理槽内进行氧化处理，阳极电压设为460～465V，阴极电压设为100～102V，电流为2.4A，氧化处理液的温度控制在40～50℃，氧化处理时间40～60min，再将镀膜后的刹车盘工件用水清洗处理后，即制成表面硬度较高的耐磨刹车盘。

Description

刹车盘表面硬化处理工艺技术
技术领域
本发明涉及一种刹车盘表面硬化处理工艺技术，属于机动车刹车盘加工处理技术领域。
背景技术
机动车刹车盘是汽车或其它车辆刹车系非常重要的一个部件，刹车盘的质量直接关系到车辆的安全性能，且与驾驶者的生命安全息息相关。
现有的机动车刹车盘一般是采用铸铁制成，质量比较重，耐磨效果差，刹车时易产生的噪音，机动车在高速行驶的情况下如果紧急刹车，刹车盘的温度会急剧升高，所产生的高温会使刹车盘本身出现热衰退效应，降低刹车盘的耐磨性和耐磨强度。现有刹车盘容易损坏，更换率高，安全性能差，已经不能适应现代机动车辆生产发展的需要。
发明内容
本发明的目的是为了提供一种刹车盘表面硬化处理工艺技术；使用该工艺技术加工处理刹车盘，刹车盘的质量轻，噪音小，具有较高的强度，优良的冲击韧性、耐疲劳强度和良好的耐磨性能，可大大提高机动车的刹车安全性。
为了达到上述目的，本发明是采用如下技术方案实现的。
刹车盘表面硬化处理工艺技术，采用处理工艺如下：
(1)、制备工件
使用铝合金铸棒锻造材料，通过专用机械锻造设备锻造出刹车盘的毛坯工件，然后根据车辆需要的尺寸规格用车床进行切削加工，再通过磨面抛光、清洗程序制出刹车盘工件；
(2)、制备电解液
将Na2SiO31.2％、NaOH0.1％、Na2P4O70.4％、Na2EDTA0.2％、NaF0.075％、C6H5O7Na3·2H2O0.1％、H3BO30.2％、H2O97.725％按重量比混合搅拌均匀，制成电解液备用；
(3)、处理工件
将电解液置于处理槽内，加入水进行混合，水与电解液的混合重量比为1∶1，制成氧化处理液，然后将刹车盘工件置入专用工装卡环内，再将刹车盘工件浸入处理槽内的氧化处理液中进行氧化处理，阳极电压设为460～465V，阴极电压设为100～102V，电流为2.4A，氧化处理液的温度控制在40～50℃，氧化处理时间40～60min，通过该工艺氧化处理后，即可将刹车盘工件表面镀上一层厚度为35μm的膜，再将镀膜后的刹车盘工件用水清洗处理后，即制成表面硬度较高的耐磨刹车盘。
本发明主要具有以下有益效果：
使用该工艺技术加工处理刹车盘，刹车盘的质量轻，噪音小，具有较高的强度，优良的冲击韧性、耐疲劳强度和良好的耐磨性能，可大大提高机动车的刹车安全性能。
下面结合实施例对本发明作进一步的详细描述。
具体实施方式
实施例
刹车盘表面硬化处理工艺技术，采用处理工艺如下：
(1)、制备工件
使用铝合金铸棒锻造材料，通过专用机械锻造设备锻造出刹车盘的毛坯工件，然后根据车辆需要的尺寸规格用车床进行切削加工，再通过磨面抛光、清洗程序制出刹车盘工件；
(2)、制备电解液
将Na2SiO31.2％、NaOH0.1％、Na2P4O70.4％、Na2EDTA0.2％、NaF0.075％、C6H5O7Na3·2H2O0.1％、H3BO30.2％、H2O97.725％按重量比混合搅拌均匀，制成电解液备用；
(3)、处理工件
将电解液置于处理槽内，加入水进行混合，水与电解液的混合重量比为1∶ 1，制成氧化处理液，然后将刹车盘工件置入专用工装卡环内，再将刹车盘工件浸入处理槽内的氧化处理液中进行氧化处理，阳极电压设为460～465V，阴极电压设为100～102V，电流为2.4A，氧化处理液的温度控制在40～50℃，氧化处理时间40～60min，通过该工艺氧化处理后，即可将刹车盘工件表面镀上一层厚度为35μm的膜，再将镀膜后的刹车盘工件用水清洗处理后，即制成表面硬度较高的耐磨刹车盘。

Claims (1)

1.刹车盘表面硬化处理工艺技术，其特征在于：采用如下处理工艺：
(1)、制备工件
使用铝合金铸棒锻造材料，通过专用机械锻造设备锻造出刹车盘的毛坯工件，然后根据车辆需要的尺寸规格用车床进行切削加工，再通过磨面抛光、清洗程序制出刹车盘工件；
(2)、制备电解液
将Na2SiO31.2％、NaOH0.1％、Na2P4O70.4％、Na2EDTA0.2％、NaF0.075％、C6H5O7Na3·2H2O0.1％、H3BO30.2％、H2O97.725％按重量比混合搅拌均匀，制成电解液备用；
(3)、处理工件
将电解液置于处理槽内，加入水进行混合，水与电解液的混合重量比为1∶1，制成氧化处理液，然后将刹车盘工件置入专用工装卡环内，再将刹车盘工件浸入处理槽内的氧化处理液中进行氧化处理，阳极电压设为460～465V，阴极电压设为100～102V，电流为2.4A，氧化处理液的温度控制在40～50℃，氧化处理时间40～60min，通过该工艺氧化处理后，即可将刹车盘工件表面镀上一层厚度为35μm的膜，再将镀膜后的刹车盘工件用水清洗处理后，即制成表面硬度较高的耐磨刹车盘。
CN201310159868.1A 2013-04-17 2013-04-17 刹车盘表面硬化处理工艺技术 Active CN104109893B (zh)