CN104109487A - Durable industrial adhesive tape and preparation method thereof - Google Patents
Durable industrial adhesive tape and preparation method thereof Download PDFInfo
- Publication number
- CN104109487A CN104109487A CN201410286284.5A CN201410286284A CN104109487A CN 104109487 A CN104109487 A CN 104109487A CN 201410286284 A CN201410286284 A CN 201410286284A CN 104109487 A CN104109487 A CN 104109487A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixing
- gummed tape
- preparation
- industrial gummed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a durable industrial adhesive tape, which comprises the following components by weight ratio: 7-14 parts of polyurethane, 3-5 parts of 3-hydroxyl-propionitrile, 2-3 parts of calcium stearate, 6-9 parts of polypropylene, 5-8 parts of polypropylene glycol 2000, 5-6 parts of ethylene oxide and 3-4 parts of o-phenylphenol. A preparation method of the industrial adhesive tape comprises the following steps: 1)turning on a mixing roll, preheating the mixing roll, respectively weighting polyurethane, 3-hydroxyl-propionitrile and calcium stearate, mixing under high temperature at 150-170 DEG C; 2)adding polypropylene, ethylene oxide and o-phenylphenol in the mixing roll for mixing again; 3)adding polypropylene glycol 2000 in the mixing roll for mixing again; and 4)after mixing is completed, compacting and molding the adhesive tape by using a mole to obtain the durable industrial adhesive tape.
Description
Technical field
The invention belongs to adhesive tape field, relate to a kind of adhesive tape and preparation method thereof, particularly relate to a kind of durable industrial gummed tape and preparation method thereof.
Background technology
Industrial gummed tape has important effect in the process industry of product and industrial operational process.For example, in electric works and Logistics Engineering, industrial gummed tape has more purposes.Industry glue, in the equipment in these fields and the assembling of element, plays a part outbalance.
The classification of industrial gummed tape is more, for example, have tape, warning adhesive tape, cloth base adhesive tape, aluminum foil and adhesive tape etc.The use range that different industrial gummed tapes is especially corresponding.The weather resistance of conventional industrial gummed tape is conventionally poor, needs to continue to improve the durable degree of its use.Endurance quality is poor, after increasing between in use, industrial gummed tape can produce become fragile, the problem such as distortion, limited the application of industrial gummed tape.
Summary of the invention
The technical problem solving: the weather resistance of conventional industrial gummed tape is conventionally poor, needs to continue to improve the durable degree of its use.Endurance quality is poor, after increasing between in use, industrial gummed tape can produce become fragile, the problem such as distortion, limited the application of industrial gummed tape.
Technical scheme: for the problems referred to above, the invention discloses a kind of durable industrial gummed tape, described durable industrial gummed tape is made up of according to weight ratio following composition:
Urethane is that 7 parts～14 parts, 3-hydroxypropionitrile are that 3 parts～5 parts, calcium stearate are that 2 parts～3 parts, polypropylene are that 6 parts～9 parts, polypropylene glycol 2000 are that 5 parts～8 parts, oxyethane are that 5 parts～6 parts, orthoxenol are 3 parts～4 parts.
A preparation method for durable industrial gummed tape, the preparation method of described durable industrial gummed tape comprises the following steps:
(1) open mixing roll, mixing roll is carried out to preheating, taking respectively urethane and be 7 parts～14 parts, 3-hydroxypropionitrile and be 3 parts～5 parts, calcium stearate is 2 parts～3 parts, and urethane, 3-hydroxypropionitrile, three kinds of compositions of calcium stearate are carried out to high-temperature mixing, and melting temperature is 150 DEG C～170 DEG C;
(2) be that 6 parts～9 parts, oxyethane are that 5 parts～6 parts, orthoxenol are 3 parts～4 parts to adding polypropylene in mixing roll, add after polypropylene, oxyethane, orthoxenol, keep temperature-resistant, then carry out mixing;
(3) in mixing roll, add polypropylene glycol 2000 to be 5 parts～8 parts again, again mixing;
(4) after mixing end, will mix adhesive tape mould compression moulding, be durable industrial gummed tape.
The preparation method of described a kind of durable industrial gummed tape, the melting temperature described in preparation process is preferably 160 DEG C～170 DEG C.
The preparation method of described a kind of durable industrial gummed tape, the urethane described in preparation process is preferably 14 parts.
The preparation method of described a kind of durable industrial gummed tape, the oxyethane described in preparation process is preferably 6 parts.
Beneficial effect: moiety and its preparation technology by the industrial gummed tape to conventional rationally screen and optimize, the industrial gummed tape that the inventive method prepares has overcome the non-resistant feature of conventional adhesive tape, in the thermostat container of industrial gummed tape of the present invention at 70 DEG C, place after 400h to 600h, industrial gummed tape of the present invention does not have distortion, becomes fragile, the phenomenon of variable color, cracking, has improved the weather resistance of industrial gummed tape.
Embodiment
Embodiment 1
(1) open mixing roll, mixing roll is carried out to preheating, taking respectively urethane is that 7kg, 3-hydroxypropionitrile are that 5kg, calcium stearate are 2kg, and urethane, 3-hydroxypropionitrile, three kinds of compositions of calcium stearate are carried out to high-temperature mixing, and melting temperature is 170 DEG C;
(2) be that 6kg, oxyethane are that 6kg, orthoxenol are 4kg to adding polypropylene in mixing roll, add after polypropylene, oxyethane, orthoxenol, keep temperature-resistant, then carry out mixing;
(3) in mixing roll, add polypropylene glycol 2000 for 5kg again, again mixing;
(4) after mixing end, will mix adhesive tape mould compression moulding, be durable industrial gummed tape.
Embodiment 2
(1) open mixing roll, mixing roll is carried out to preheating, taking respectively urethane is that 10kg, 3-hydroxypropionitrile are that 3kg, calcium stearate are 3kg, and urethane, 3-hydroxypropionitrile, three kinds of compositions of calcium stearate are carried out to high-temperature mixing, and melting temperature is 170 DEG C;
(2) be that 8kg, oxyethane are that 5kg, orthoxenol are 3kg to adding polypropylene in mixing roll, add after polypropylene, oxyethane, orthoxenol, keep temperature-resistant, then carry out mixing;
(3) in mixing roll, add polypropylene glycol 2000 for 8kg again, again mixing;
(4) after mixing end, will mix adhesive tape mould compression moulding, be durable industrial gummed tape.
Embodiment 3
(1) open mixing roll, mixing roll is carried out to preheating, taking respectively urethane is that 14kg, 3-hydroxypropionitrile are that 4kg, calcium stearate are 2kg, and urethane, 3-hydroxypropionitrile, three kinds of compositions of calcium stearate are carried out to high-temperature mixing, and melting temperature is 170 DEG C;
(2) be that 9kg, oxyethane are that 6kg, orthoxenol are 3kg to adding polypropylene in mixing roll, add after polypropylene, oxyethane, orthoxenol, keep temperature-resistant, then carry out mixing;
(3) in mixing roll, add polypropylene glycol 2000 for 5kg again, again mixing;
(4) after mixing end, will mix adhesive tape mould compression moulding, be durable industrial gummed tape.
The industrial gummed tape that embodiment 1, embodiment 2, embodiment 3 are prepared is placed 400h, 500h, 600h in the thermostat container at 70 DEG C respectively, sees below that industrial gummed tape has or not distortion, becomes fragile, the phenomenon of variable color, cracking while observing.Situation is as follows.
| ? | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Endurance quality | 400h industrial gummed tape without being out of shape, becoming fragile, the phenomenon of variable color, cracking | 500h industrial gummed tape without being out of shape, becoming fragile, the phenomenon of variable color, cracking | 600h industrial gummed tape without being out of shape, becoming fragile, the phenomenon of variable color, cracking |
It can be seen from the table, the industrial gummed tape that adopts composition and engineering of the present invention to prepare has good durable feature, has improved the application performance of industrial gummed tape.
Claims (5)
1. a durable industrial gummed tape, is characterized in that described durable industrial gummed tape is made up of according to weight ratio following composition:
Urethane is that 7 parts～14 parts, 3-hydroxypropionitrile are that 3 parts～5 parts, calcium stearate are that 2 parts～3 parts, polypropylene are that 6 parts～9 parts, polypropylene glycol 2000 are that 5 parts～8 parts, oxyethane are that 5 parts～6 parts, orthoxenol are 3 parts～4 parts.
2. a preparation method for durable industrial gummed tape, is characterized in that the preparation method of described durable industrial gummed tape comprises the following steps:
(1) open mixing roll, mixing roll is carried out to preheating, taking respectively urethane and be 7 parts～14 parts, 3-hydroxypropionitrile and be 3 parts～5 parts, calcium stearate is 2 parts～3 parts, and urethane, 3-hydroxypropionitrile, three kinds of compositions of calcium stearate are carried out to high-temperature mixing, and melting temperature is 150 DEG C～170 DEG C;
(2) be that 6 parts～9 parts, oxyethane are that 5 parts～6 parts, orthoxenol are 3 parts～4 parts to adding polypropylene in mixing roll, add after polypropylene, oxyethane, orthoxenol, keep temperature-resistant, then carry out mixing;
(3) in mixing roll, add polypropylene glycol 2000 to be 5 parts～8 parts again, again mixing;
(4) after mixing end, will mix adhesive tape mould compression moulding, be durable industrial gummed tape.
3. the preparation method of a kind of durable industrial gummed tape according to claim 2, is characterized in that the melting temperature described in preparation process is 160 DEG C～170 DEG C.
4. the preparation method of a kind of durable industrial gummed tape according to claim 2, is characterized in that the urethane described in preparation process is 14 parts.
5. the preparation method of a kind of durable industrial gummed tape according to claim 2, is characterized in that the oxyethane described in preparation process is 6 parts.