CN104624644A - Titanium steel composite board production method - Google Patents
Titanium steel composite board production method Download PDFInfo
- Publication number
- CN104624644A CN104624644A CN201310562025.6A CN201310562025A CN104624644A CN 104624644 A CN104624644 A CN 104624644A CN 201310562025 A CN201310562025 A CN 201310562025A CN 104624644 A CN104624644 A CN 104624644A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- titanium
- plate
- composite board
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a titanium steel composite board production method. The method comprises the steps that a steel plate is rolled on a hot mill to be 6 mm thick, and air cooling is carried out on the steel plate, the surface of the steel plate obtained after air cooling is carried out and the surface of the titanium plate are cleaned thoroughly, and then the steel plate is rolled by 2-5 passes under the temperature condition being 850 DEG C; the steel plate comprises chemical components being 0.16% of C, 0.61% of Mn, 0.2% of Si, 0.23% of S, 0.019% of P, 0.3% of Cr, 0.3% of Ni, 0.3% of Cu, 0.08% of As, and the balance Fe; according to the chemical components, the titanium plate comprises 0.08% of Fe, 0.08% of O, 0.05% of C, 0.0112% of N, 0.01% of Si, 0.01% of H and the balance Ti. The chemical components of the titanium plate and the steel plate are strictly controlled, the phenomenon that the composite board is mixed with impurities is effectively avoided, and the method is simple and low in production cost.
Description
Technical field
The invention belongs to composite plate technical field, be specifically related to a kind of production method of titanium steel composite board.
Background technology
Titanium steel composite board is cheap, has the premium properties of titanium and Steel material simultaneously, is therefore widely used, but prior art composite plate is all generally adopt explosion method to produce, and production cost is high, and the kind of production is narrow, limits the kind of composite plate.
Summary of the invention
In order to overcome the above-mentioned technical problem that prior art field exists, the object of the invention is to, provide a kind of production method of titanium steel composite board, method is simple, and cost is low.
The production method of titanium steel composite board provided by the invention, comprises the following steps: steel plate is rolled into the thick steel plate of 6mm and air cooling by (1) on hot-rolling mill; (2) steel plate after air cooling and the removing surface of titanium plate is clean, rolling 2-5 road under the temperature conditions of 850 DEG C afterwards.
The chemical composition of described steel plate is: C:0.16%, Mn:0.61%, Si:0.2%, S:0.23%, P:0.019%, Cr:0.3%, Ni:0.3%, Cu:0.3%, As:0.08%, and surplus is Fe; The chemical composition of described titanium plate is: Fe:0.08%, O:0.08%, C:0.05%, N:0.0112%, Si:0.01%, H:0.01%, and surplus is Ti.
The production method of titanium steel composite board provided by the invention, its beneficial effect is, the strict chemical composition controlling titanium plate and steel plate, effectively avoids admixing impurity in composite plate, and method is simple, and production cost is low.
Detailed description of the invention
Below in conjunction with an embodiment, the production method of titanium steel composite board provided by the invention is described in detail.
Embodiment
The production method of the titanium steel composite board of the present embodiment, comprises the following steps: steel plate is rolled into the thick steel plate of 6mm and air cooling by (1) on hot-rolling mill; (2) steel plate after air cooling and the removing surface of titanium plate is clean, rolling 2-5 road under the temperature conditions of 850 DEG C afterwards.
The chemical composition of described steel plate is: C:0.16%, Mn:0.61%, Si:0.2%, S:0.23%, P:0.019%, Cr:0.3%, Ni:0.3%, Cu:0.3%, As:0.08%, and surplus is Fe; The chemical composition of described titanium plate is: Fe:0.08%, O:0.08%, C:0.05%, N:0.0112%, Si:0.01%, H:0.01%, and surplus is Ti.
Claims (2)
1. a production method for titanium steel composite board, is characterized in that: comprise the following steps: steel plate is rolled into the thick steel plate of 6mm and air cooling by (1) on hot-rolling mill; (2) steel plate after air cooling and the removing surface of titanium plate is clean, rolling 2-5 road under the temperature conditions of 850 DEG C afterwards.
2. the production method of titanium steel composite board according to claim 1, it is characterized in that: the chemical composition of described steel plate is: C:0.16%, Mn:0.61%, Si:0.2%, S:0.23%, P:0.019%, Cr:0.3%, Ni:0.3%, Cu:0.3%, As:0.08%, surplus is Fe; The chemical composition of described titanium plate is: Fe:0.08%, O:0.08%, C:0.05%, N:0.0112%, Si:0.01%, H:0.01%, and surplus is Ti.