CN104108215A - 一种高转光率农用大棚膜及其制备方法 - Google Patents
一种高转光率农用大棚膜及其制备方法 Download PDFInfo
- Publication number
- CN104108215A CN104108215A CN201410305503.XA CN201410305503A CN104108215A CN 104108215 A CN104108215 A CN 104108215A CN 201410305503 A CN201410305503 A CN 201410305503A CN 104108215 A CN104108215 A CN 104108215A
- Authority
- CN
- China
- Prior art keywords
- film
- layer film
- low density
- density polyethylene
- greenhouse film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高转光率农用大棚膜及其制备方法,涉及大棚膜生产技术领域,由外层膜、中层膜和内层膜三层结构组成,其制备方法为分别称取外层膜、中层膜和内层膜的原料,将原料充分混合均匀后加入到三层共挤吹膜机中,经升温、挤出、吹塑、上牵引、下牵引和卷绕成膜。本发明制备得到的大棚膜由于添加了有机稀土元素,明显提高了农作物的光合作用强度,使农作物生长快、坐果好、结果多、早熟、增产和品质好,并且解决了一般大棚膜容易出现雾滴、透光率低、抗氧化性差和使用寿命短等问题。
Description
技术领域:
本发明涉及大棚膜生产技术领域,具体涉及一种高转光率农用大棚膜及其制备方法。
背景技术:
转光膜是一种在生产普通大棚膜的原材料中添加“转光功能性母料”后制成的大棚膜。当阳光透过转光膜时,阳光中的紫外线和绿光被膜中的“转光功能性母料”吸收转换,释放出对植物生长有力的蓝紫光和红橙光,使棚内的蓝光和红光光谱成分增加,提高了光能利用率。并且研究表明,采用转光膜覆盖的大棚,作物生长快、坐果好、结果多、抗逆性强、早熟、增产和品质好。
早期的转光膜一般选用的是无机转光剂,即氯化稀土。由于其中氯离子的存在,在吹膜加工时氯离子在温度较高时容易挥发,并且无机稀土与高分子材料聚乙烯相容性不好,不能持久保持转光效果。另外,转光膜也存在一般农用大棚膜容易出现雾滴、透光率低、抗氧化性差、使用寿命短的缺点。
发明内容:
本发明所要解决的技术问题在于提供一种工艺简单、使用寿命长、有利于植物生长的高转光率农用大棚膜及其制备方法。
本发明所要解决的技术问题采用以下的技术方案来实现:
一种高转光率农用大棚膜,包括外层膜、中层膜和内层膜三层结构,所述外层膜、中层膜和内层膜由如下质量百分比的成分组成:
外层膜:线型低密度聚乙烯20%-30%、低密度聚乙烯60%-70%、邻苯二甲酸二辛脂8%-10%、有机稀土助剂2%-5%、纳米二氧化硅0.5%-2%、聚乙二醇2%-7%、氧化聚乙烯蜡1%-3%、抗氧化剂B2152%-5%、紫外吸收剂UV5310.5%-2%、光稳定剂GW-5441%-3%、热稳定剂2%-5%、滑石粉0.5%-2%;
中层膜:乙烯-醋酸乙烯共聚物50%-60%、线型低密度聚乙烯15%-20%、低密度聚乙烯12%-20%、邻苯二甲酸二辛脂8%-10%、聚乙二醇2%-7%、氧化聚乙烯蜡1%-2%、抗氧化剂B2151%-2%、光稳定剂GW5441%-2%、热稳定剂1%-2%、消雾剂AF-230.8%-2%、流滴剂KF6502%-4%、硅藻土0.3%-1%;
内层膜:乙烯-醋酸乙烯共聚物60%-70%、线型低密度聚乙烯20%-25%、邻苯二甲酸二辛脂8%-10%、聚乙二醇2%-7%、氧化聚乙烯蜡1%-2%、抗氧化剂B2151%-2%、光稳定剂GW-5441%-2%、热稳定剂1%-2%、消雾剂AF-231%-2.5%、流滴剂KF6502%-5%、硅藻土0.3%-1%。
所述有机稀土助剂的结构为
所述热稳定剂的组分及各组分所占质量百分比为硬脂酸钡70%、硬脂酸锌30%。
一种高转光率农用大棚膜的制备方法,包括如下步骤:
步骤a:按照所述外层膜、中层膜和内层膜的组分比例称取各组分,分别加入到配料釜中,搅拌混合10-15min,放料,得到混合均匀的外层膜、中层膜和内层膜配料;
步骤b:将步骤a得到的混合均匀的配料分别加入到三层共挤吹膜机中,经升温、挤出、吹塑、上牵引、下牵引和卷绕成膜。
本发明的有益效果是:本发明制备得到的大棚膜由于添加了有机稀土元素,将阳光中植物光合作用不需要的紫外光和黄绿光转换为蓝紫光和红橙光,明显提高了农作物的光合作用强度,使农作物生长快、坐果好、结果多、早熟、增产和品质好,并且解决了一般大棚膜容易出现雾滴、透光率低、抗氧化性差和使用寿命短等问题。
具体实施方式:
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面进一步阐述本发明。
实施例1
外层膜:线型低密度聚乙烯20%、低密度聚乙烯60%、邻苯二甲酸二辛脂8%、有机稀土助剂2%、纳米二氧化硅0.5%、聚乙二醇2%、氧化聚乙烯蜡1%、抗氧化剂B2152%、紫外吸收剂UV5310.5%、光稳定剂GW-5441%、热稳定剂2%、滑石粉0.5%;
中层膜:乙烯-醋酸乙烯共聚物50%、线型低密度聚乙烯15%、低密度聚乙烯12%、邻苯二甲酸二辛脂8%、聚乙二醇2%、氧化聚乙烯蜡1%、抗氧化剂B2151%、光稳定剂GW5441%、热稳定剂1%、消雾剂AF-230.8%、流滴剂KF6502%、硅藻土0.3%;
内层膜:乙烯-醋酸乙烯共聚物60%、线型低密度聚乙烯20%、邻苯二甲酸二辛脂8%、聚乙二醇2%、氧化聚乙烯蜡1%、抗氧化剂B2151%、光稳定剂GW-5441%、热稳定剂1%、消雾剂AF-231%、流滴剂KF6502%、硅藻土0.3%。
实施例2
外层膜:线型低密度聚乙烯25%、低密度聚乙烯65%、邻苯二甲酸二辛脂9%、有机稀土助剂4%、纳米二氧化硅1%、聚乙二醇5%、氧化聚乙烯蜡2%、抗氧化剂B2153%、紫外吸收剂UV5311%、光稳定剂GW-5442%、热稳定剂3%、滑石粉1%;
中层膜:乙烯-醋酸乙烯共聚物55%、线型低密度聚乙烯17%、低密度聚乙烯16%、邻苯二甲酸二辛脂9%、聚乙二醇4%、氧化聚乙烯蜡1.5%、抗氧化剂B2151%、光稳定剂GW5441%、热稳定剂1.5%、消雾剂AF-231.5%、流滴剂KF6503%、硅藻土0.7%;
内层膜:乙烯-醋酸乙烯共聚物65%、线型低密度聚乙烯22%、邻苯二甲酸二辛脂9%、聚乙二醇4%、氧化聚乙烯蜡1%、抗氧化剂B2151%、光稳定剂GW-5441.5%、热稳定剂2%、消雾剂AF-232%、流滴剂KF6503%、硅藻土0.5%。
实施例3
外层膜:线型低密度聚乙烯30%、低密度聚乙烯70%、邻苯二甲酸二辛脂10%、有机稀土助剂5%、纳米二氧化硅2%、聚乙二醇7%、氧化聚乙烯蜡3%、抗氧化剂B2155%、紫外吸收剂UV5312%、光稳定剂GW-5443%、热稳定剂5%、滑石粉2%;
中层膜:乙烯-醋酸乙烯共聚物60%、线型低密度聚乙烯20%、低密度聚乙烯20%、邻苯二甲酸二辛脂10%、聚乙二醇7%、氧化聚乙烯蜡2%、抗氧化剂B2152%、光稳定剂GW5442%、热稳定剂2%、消雾剂AF-232%、流滴剂KF6504%、硅藻土1%;
内层膜:乙烯-醋酸乙烯共聚物70%、线型低密度聚乙烯25%、邻苯二甲酸二辛脂10%、聚乙二醇7%、氧化聚乙烯蜡-2%、抗氧化剂B2152%、光稳定剂GW-5442%、热稳定剂2%、消雾剂AF-232.5%、流滴剂KF6505%、硅藻土1%。
其中,有机稀土助剂的结构为
热稳定剂的组分及各组分所占质量百分比为硬脂酸钡70%、硬脂酸锌30%。
一种高转光率农用大棚膜的制备方法,包括如下步骤:
步骤a:按照所述外层膜、中层膜和内层膜的组分比例称取各组分,分别加入到配料釜中,搅拌混合10-15min,放料,得到混合均匀的外层膜、中层膜和内层膜配料;
步骤b:将步骤a得到的混合均匀的配料分别加入到三层共挤吹膜机中,经升温、挤出、吹塑、上牵引、下牵引和卷绕成膜。
将上述制得的大棚膜进行如下性能测定,测定结果如下表所示。
测试性能 | 实施例1 | 实施例2 | 实施例3 |
透光率(%) | 93 | 92 | 92 |
雾度(%) | 20 | 19 | 21 |
光转换率(%) | 95 | 98 | 94 |
紫外光透过率(%) | 0 | 0 | 0 |
蓝紫光透过率(%) | 91 | 92 | 91 |
红橙光透过率(%) | 98 | 97 | 98 |
由上表可以看出,本发明制得的大棚膜的透光率达到92%,雾度在20%左右,光转换率在95%左右,并且不透紫外光,而蓝紫光和红橙光的透过率都在90%以上。
使用3个实施例制得的大棚膜和普通大棚膜,分别种植蔬菜(西红柿、黄瓜、茄子、辣椒、生菜、芹菜)和水果(葡萄、草莓、油桃、西瓜、杏子),对它们的果熟时间、产量和病害情况进行统计,3个实施例制得的大棚膜与普通大棚膜的比较结果如下表所示。
农作物 | 增产量(%) | 早熟(天) | 病害情况 |
西红柿 | 21-30 | 7-10 | 减少 |
黄瓜 | 34-42 | 9-12 | 减少 |
茄子 | 25-36 | 5-9 | 减少 |
辣椒 | 35-41 | 7-11 | 减少 |
生菜 | 35-43 | 9-15 | 减少 |
芹菜 | 26-32 | 7-13 | 减少 |
葡萄 | 31-37 | 7-15 | 减少 |
草莓 | 34-40 | 9-15 | 减少 |
油桃 | 26-34 | 7-13 | 减少 |
西瓜 | 30-36 | 5-10 | 减少 |
杏子 | 25-32 | 5-9 | 减少 |
由上表可以看出,本发明制得的大棚膜与普通大棚膜相比,农作物的产量增加,生长期缩短,品质好且病害情况减少。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (4)
1.一种高转光率农用大棚膜,包括外层膜、中层膜和内层膜三层结构,其特征在于所述外层膜、中层膜和内层膜由如下质量百分比的成分组成:
外层膜:线型低密度聚乙烯20%-30%、低密度聚乙烯60%-70%、邻苯二甲酸二辛脂8%-10%、有机稀土助剂2%-5%、纳米二氧化硅0.5%-2%、聚乙二醇2%-7%、氧化聚乙烯蜡1%-3%、抗氧化剂B2152%-5%、紫外吸收剂UV5310.5%-2%、光稳定剂GW-5441%-3%、热稳定剂2%-5%、滑石粉0.5%-2%;
中层膜:乙烯-醋酸乙烯共聚物50%-60%、线型低密度聚乙烯15%-20%、低密度聚乙烯12%-20%、邻苯二甲酸二辛脂8%-10%、聚乙二醇2%-7%、氧化聚乙烯蜡1%-2%、抗氧化剂B2151%-2%、光稳定剂GW5441%-2%、热稳定剂1%-2%、消雾剂AF-230.8%-2%、流滴剂KF6502%-4%、硅藻土0.3%-1%;
内层膜:乙烯-醋酸乙烯共聚物60%-70%、线型低密度聚乙烯20%-25%、邻苯二甲酸二辛脂8%-10%、聚乙二醇2%-7%、氧化聚乙烯蜡1%-2%、抗氧化剂B2151%-2%、光稳定剂GW-5441%-2%、热稳定剂1%-2%、消雾剂AF-231%-2.5%、流滴剂KF6502%-5%、硅藻土0.3%-1%。
2.根据权利要求1所述的一种高转光率农用大棚膜,其特征在于:所述有机稀土助剂的结构为
3.根据权利要求1所述的一种高转光率农用大棚膜,其特征在于:所述热稳定剂的组分及各组分所占质量百分比为硬脂酸钡70%、硬脂酸锌30%。
4.一种高转光率农用大棚膜的制备方法,其特征在于包括如下步骤:
步骤a:按照所述外层膜、中层膜和内层膜的组分比例称取各组分,分别加入到配料釜中,搅拌混合10-15min,放料,得到混合均匀的外层膜、中层膜和内层膜配料;
步骤b:将步骤a得到的混合均匀的配料分别加入到三层共挤吹膜机中,经升温、挤出、吹塑、上牵引、下牵引和卷绕成膜。