CN104099042A - 一种高性能节能灯头用胶粘剂 - Google Patents
一种高性能节能灯头用胶粘剂 Download PDFInfo
- Publication number
- CN104099042A CN104099042A CN201310117494.7A CN201310117494A CN104099042A CN 104099042 A CN104099042 A CN 104099042A CN 201310117494 A CN201310117494 A CN 201310117494A CN 104099042 A CN104099042 A CN 104099042A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- saving lamp
- mass ratio
- adhesive
- performance energy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高性能节能灯头用胶粘剂,尤其是一种混合聚醋酸乙烯(PVAc)乳液、乙酸乙烯酯-乙烯共聚乳液(VAE乳液)和苯乙烯丙烯酸共聚乳液为主料,分散剂、填充料和水为辅料的粘胶剂。该粘胶剂通过乳液共混的理念,研制出具有活性休眠功能且耐高温使用寿命长的特点,该粘胶剂原料易得,使用工艺简单,成本低廉,且固化过程中无有害物质释放,属于环保产品,且使用该粘胶剂的节能灯经实验可达到持续使用12000小时以上不脱胶,具有显著的进步意义。
Description
技术领域
本发明涉及一种胶粘剂,尤其是一种混合聚醋酸乙烯(PVAc)乳液、乙酸乙烯酯-乙烯共聚乳液(VAE乳液)和苯乙烯丙烯酸共聚乳液为主料,氧化铝、氢氧化铝、分散剂和填充料为辅料的高性能节能灯头专用粘胶剂。
背景技术
现金中国每年生产的节能灯超过全世界的90%,达到50亿只以上,而节能灯灯头与灯管的连接主要是靠灯头胶粘接。近年来国内节能灯产家都开始采用乳液添加无机填充料和各种助剂的水基胶,现有的乳液灯头胶还存在施工不便,在进行灯头注胶之前要进行共聚乳液粘胶兑水进行配比后用搅拌机搅拌至特定的粘稠膏状物;耐热性低,节能灯功率越大粘胶剂的寿命越短;以及必须加入防老剂、防霉剂防止灯头胶发黄、霉变等特点。节能灯的寿命主要受灯管寿命和镇流器寿命影响,而灯管寿命更多是因为灯管与灯座连接部位的灯头胶老化脱落的因素,现有的灯头胶技术基本上只能达到持续8000小时工作寿命,而节能灯作为一种废弃后会造成环境污染的产品,寿命越长对社会的意义越大。
发明内容
本发明的目的在于提供一种原料易得,使用工艺简单,成本低廉,且固化过程中无有害物质释放,属于环保产品,且使用该粘胶剂的节能灯经实验可达到持续使用12000小时以上不脱胶的产品。
本发明提供的技术方案如下:
一种高性能节能灯头用胶粘剂,其包括:聚醋酸乙烯(PVAc)乳液、乙酸乙烯酯-乙烯共聚乳液(VAE乳液)和苯乙烯丙烯酸共聚乳液为主料,水、亲水性分散剂和填充料为辅料组成,其中聚醋酸乙烯(PVAc)乳液占总质量比的55~65%,乙酸乙烯酯-乙烯共聚乳液(VAE乳液)占总质量比的5~10%,苯乙烯丙烯酸共聚乳液占总质量比的25~35;分散剂占总质量比的0.1~0.25%;以上混合物再与填充料采用1:3.3的比例混合。
所述聚醋酸乙烯(PVAc)乳液,其固含量为40~50(wt%),密度为0.95~1.05,粘度为1500~2500mPa·s,灰分<0.1,残留VAc数量<0.5;其成分组成的重量比为聚乙烯醇3~6%,醋酸乙烯40~70%,丙烯酸酯类0~26%,增塑剂1~2%,乳化剂1~2%,缓冲剂0.2~0.3,疏水剂10~40%,水40~60%;以上物料放置于反应釜中用70~80℃的蒸汽加热反应,制成具备活性休眠特性的成品。
所述乙酸乙烯酯-乙烯共聚乳液(VAE乳液)其固含量为50~60(wt%),粘度为2500~3300mPa·s,最低成膜温度<0℃,残留单体数量<1%。
所述苯乙烯丙烯酸共聚乳液其固含量为50~53(wt%), 粘度为700~1500mPa·s,PH值为7~8,最低成膜温度<-20℃,残留单体数量<1%。
所述填充料为氧化铝、重钙和轻钙的混合物,其中氧化铝的质量比为0.1~0.4%,轻钙的质量比为2~5%,重钙的质量比为95~98%;填充料的细度为400~800目,含水量<0.23%。
本发明的粘胶剂原料易得,生产工艺简单,使用者易操作,所用的设备均为常规物品,可实现工业化量产,所制取的粘胶剂具有环保、活性可休眠、保存期长、成本低且使用寿命长的特点。
具体实施方式
本发明的一种较佳实施例:
1、在室温下,将重量比为4%的聚乙烯醇、55%的醋酸乙烯、16%的丙烯酸酯类、1.4%的增塑剂、1.4%的乳化剂、0.2%的缓冲剂,10~40%的疏水剂,水40~60%;以上物料放置于反应釜中用70~80℃的蒸汽加热反应,制得PVAc乳液,该乳液在0~40℃环境下保存会慢慢固化,在需要使用时取相应量的固化乳液用力揉动数次即可软化回乳液状态。
2、在室温下将步骤1制得的PVAc取75Kg与15Kg706型VAE和30Kg400D型苯乙烯丙烯酸共聚乳液放入立式双桨搅拌锅中以56R/min的转速搅拌5分钟,而后不停机下加入25kg的蒸馏水、400Kg400目含水率低于0.23%的填充料,搅拌10分钟,待物料略为均匀后加入1Kg的亲水性分散剂,保持转速后搅拌一小时,待物料呈白色粘稠的膏状物后出料包装。
3、性能测试,将以上方法制成的灯头胶分别涂在100只双U和三U型节能灯灯头内用于固定灯管和灯座,每只节能灯的用量为6g,灯头胶在120℃烘干30min,而后整灯经10000小时持续工作及热老化未出现灯管松动、破裂和脱胶现象。经飞利浦公司和漳州东林电子有限公司委托广州道标标准技术服务有限公司就持续工作/热老化项目测试,经10000小时持续工作检测,未出现松管、破裂和脱胶现象。该灯头胶完全符合欧盟有关节能灯粘胶剂环保技术方面的标准,产品性能及操作简便性大为优于市面现有产品。
上述仅为本发明的一个具体实施例,但本发明并不局限于此,凡对本发明进行非实质性的改动,均应属于侵犯本发明保护范围的行为。
Claims (5)
1.一种高性能节能灯头用胶粘剂,其包括:聚醋酸乙烯(PVAc)乳液、乙酸乙烯酯-乙烯共聚乳液(VAE乳液)和苯乙烯丙烯酸共聚乳液为主料,亲水性分散剂、填充料和水为辅料组成,其特征在于:聚醋酸乙烯(PVAc)乳液占总质量比的55~65%,乙酸乙烯酯-乙烯共聚乳液(VAE乳液)占总质量比的5~10%,苯乙烯丙烯酸共聚乳液占总质量比的25~35%;分散剂占总质量比的0.1~0.25%;以上混合物再与填充料采用1:3.3的比例混合。
2.根据权利要求1所述的一种高性能节能灯头用粘胶剂,其特征在于:所述聚醋酸乙烯(PVAc)乳液,其固含量为40~50(wt%),密度为0.95~1.05,粘度为1500~2500mPa·s,灰分<0.1,残留VAc数量<0.5;其成分组成的重量比为聚乙烯醇3~6%,醋酸乙烯40~70%,丙烯酸酯类0~26%,增塑剂1~2%,乳化剂1~2%,缓冲剂0.2~0.3,疏水剂10~40%,水40~60%;以上物料放置于反应釜中用70~80℃的蒸汽加热反应,制成具备活性休眠特性的成品。
3.根据权利要求1所述的一种高性能节能灯头用粘胶剂,其特征在于:所述乙酸乙烯酯-乙烯共聚乳液(VAE乳液)其固含量为50~60(wt%),粘度为2500~3300mPa·s,最低成膜温度<0℃,残留单体数量<1%。
4.根据权利要求1所述的一种高性能节能灯头用粘胶剂,其特征在于:所述苯乙烯丙烯酸共聚乳液其固含量为50~53(wt%), 粘度为700~1500mPa·s,PH值为7~8,最低成膜温度<-20℃,残留单体数量<1%。
5.根据权利要求1所述的一种高性能节能灯头用粘胶剂,其特征在于:所述填充料为氧化铝、重钙和轻钙的混合物,其中氧化铝的质量比为0.1~0.4%,轻钙的质量比为2~5%,重钙的质量比为95~98%;填充料的细度为400~800目,含水量<0.23%。