CN104098985A - 一种利用回收环氧树脂制备的环氧树脂砂浆漆 - Google Patents
一种利用回收环氧树脂制备的环氧树脂砂浆漆 Download PDFInfo
- Publication number
- CN104098985A CN104098985A CN201410325038.6A CN201410325038A CN104098985A CN 104098985 A CN104098985 A CN 104098985A CN 201410325038 A CN201410325038 A CN 201410325038A CN 104098985 A CN104098985 A CN 104098985A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- parts
- paint
- component
- recovered
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种利用回收环氧树脂制备的环氧树脂砂浆漆,涉及一种树脂砂浆漆,原料包括环氧树脂、回收环氧树脂、石英砂、滑石粉、有机膨润土、硫酸钡、重钙及固化剂等,其质量分数比为:50~75、5~50、5~40、50~70、0.5~1.5、5~20、5~20。本发明公开了一种新型地坪用环氧树脂砂浆漆,本发明利用回收环氧树脂粉料制备环保型地坪涂料,解决废环氧树脂所造成的环境问题并有效降低地坪涂料的成本,废环氧树脂粉料主要来源于印刷线路板回收过程中的非金属物质。能够大量利用回收的环氧树脂,对解决废环氧树脂的环境污染及综合利用开避了新途径。
Description
技术领域
本发明涉及一种树脂砂浆漆,特别是涉及一种利用回收环氧树脂制备的环氧树脂砂浆漆。
背景技术
环氧树脂因含有极性高而不易水解的脂肪族羟基和醚键,其漆膜具有附着力好、耐化学品性高、物理机械性能和耐水性好等特点,同时由于环氧树脂与固化剂固化后,其漆膜无毒因而在许多要求无毒的场合,因而被广泛用于制备地坪涂料。目前市场出售的地坪涂料分为底漆、砂浆漆和面漆等,本发明制备的砂浆漆层既能找平地面,又能增加涂膜厚度,提高承载能力和涂膜使用期限。近年来随着国内电子产品报废高峰的快速到来,产生了大量废弃的印刷线路板,其中含有的非金属物质主要有环氧树脂,传统上这些剩余废弃物直接被填埋或焚烧处理,或占用大量的土地资源,而且还由于这些废弃物中含有很多有毒有害物质,容易对周围环境造成潜在危害,特别是印刷线路板中含有溴化阻燃剂,在焚烧过程中,极易形成对人体极为有害的物质—多溴代二苯并二恶英和多溴代二苯并呋喃将对空气造成严重污染。废弃印刷线路板做为可回收的废环氧树脂的主要来源其回收与利用社会意义及经济效益重大。
发明内容
本发明的目的在于提供一种利用回收环氧树脂制备的环氧树脂砂浆漆,本发明利用回收环氧树脂粉料制备环保型地坪涂料,解决废环氧树脂所造成的环境问题并有效降低地坪涂料的成本,废环氧树脂粉料主要来源于印刷线路板回收过程中的非金属物质。
本发明的目的是通过以下技术方案实现的:
一种利用回收环氧树脂制备的环氧树脂砂浆漆,所述的环氧树脂砂浆漆组分包括甲组份:回收废环氧树脂、环氧树脂、二甲苯、正丁醇、滑石粉、有机朋润土、硫酸钡、石英砂、重钙;乙组份:环氧树脂固化剂;各组分的质量分数:
甲组份:环氧树脂(50%含量) 30~75;
滑石粉 50~70;
有机膨润土 0.5~1.5;
硫酸钡 5~20 ;
石英砂 5~40;
废环氧树脂 5~50;
重钙 5~20;
有机酯类溶剂 1~3;
乙组份:环氧树脂固化剂;
甲、乙组分配比为:7:1~8:1。
所述的一种利用回收环氧树脂制备的环氧树脂砂浆漆,所述环氧树脂是E-21,E-44, E-51, E54。
所述的一种利用回收环氧树脂制备的环氧树脂砂浆漆,所述环氧树脂固化剂为聚酰胺类固化剂。
具体实施方式
下面结合实施例,对本发明作进一步详述。
本发明的环氧树脂砂浆涂料生产工艺如下:
按配方量称取环氧树脂、回收环氧树脂粉料、石英砂、硫酸钡、滑石粉、有机膨润土、重钙依次加入分散缸中,搅拌均匀之后高速搅拌均匀出料。
以下给出7个实施例,但须指出,本发明的实施不限于以下实施方式。
实施例1
按下列质量份配料:甲组份:环氧树脂:64份,醇酸树脂:13份,滑石粉:50份,有机膨润土:1份,重钙:20份,回收环氧树脂:5份,有机酯2份:。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的测试按照国家标准《中华人民共和国建材行业标准JC/T1015-2006 -环氧树脂地面涂层材料》进行测试,测试结果见表1。
实施例2
按下列质量份配料:环氧树脂:64份,醇酸树脂:13份,滑石粉:50份,有机膨润土:1份,重钙:20份,回收环氧树脂:20份,有机酯:2份。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的性能测试标准与实施例1相同,此处不再赘述。所得性能测试结果见表1。
实施例3
按下列质量份配料:环氧树脂:64份,醇酸树脂:13份,滑石粉:50份,有机膨润土:1份,重钙:20份,回收环氧树脂:30份,有机酯:2份。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的性能测试标准与实施例1相同,此处不再赘述。所得性能测试结果见表1。
实施例4
按下列质量份配料:环氧树脂:64份,醇酸树脂:13份,滑石粉:50份,有机膨润土:1份,重钙:20份,回收环氧树脂:50份,有机酯:2份。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的性能测试标准与实施例1相同,此处不再赘述。所得性能测试结果见表1。
实施例5
按下列质量份配料:环氧树脂:64份,醇酸树脂:13份,滑石粉:50份,有机膨润土:1份,重钙:20份,回收环氧树脂:50份,有机酯:2份。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的性能测试标准与实施例1相同,此处不再赘述。所得性能测试结果见表1。
实施例6
按下列质量份配料:环氧树脂:64份,醇酸树脂:20份,滑石粉:60份,有机膨润土:1份,硫酸钡:10份,回收环氧树脂:30份,石英砂:10份,有机酯:2份。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的性能测试标准与实施例1相同,此处不再赘述。所得性能测试结果见表1。
实施例6
按下列质量份配料:环氧树脂:64份,醇酸树脂:20份,滑石粉:60份,有机膨润土:1份,硫酸钡:10份,回收环氧树脂:20份,石英砂:20份,有机酯:2份。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的性能测试标准与实施例1相同,此处不再赘述。所得性能测试结果见表1。
实施例7
按下列质量份配料:环氧树脂:64份,醇酸树脂:20份,滑石粉:60份,有机膨润土:1份,硫酸钡:10份,回收环氧树脂:5份,石英砂:35份,有机酯:2份。乙组份:聚酰胺类环氧树脂固化剂。
甲乙组分比:7.5:1。
本实施例的性能测试标准与实施例1相同,此处不再赘述。所得性能测试结果见表1。
表1
Claims (3)
1.一种利用回收环氧树脂制备的环氧树脂砂浆漆,其特征在于,所述的环氧树脂砂浆漆组分包括甲组份:回收废环氧树脂、环氧树脂、二甲苯、正丁醇、滑石粉、有机朋润土、硫酸钡、石英砂、重钙;乙组份:环氧树脂固化剂;各组分的质量分数:
甲组份:环氧树脂(50%含量) 30~75;
滑石粉 50~70;
有机膨润土 0.5~1.5;
硫酸钡 5~20 ;
石英砂 5~40;
废环氧树脂 5~50;
重钙 5~20;
有机酯类溶剂 1~3;
乙组份:环氧树脂固化剂;
甲、乙组分配比为:7:1~8:1。
2.根据权利要求1所述的一种利用回收环氧树脂制备的环氧树脂砂浆漆,其特征在于,所述环氧树脂是E-21,E-44, E-51, E54。
3.根据权利要求1所述的一种利用回收环氧树脂制备的环氧树脂砂浆漆,其特征在于,所述环氧树脂固化剂为聚酰胺类固化剂。